A deodorizing latex sheet material, insoles for use in reducing foot odor, and methods of making these products. shoe inserts are produced comprising a sole-shaped sheet or the like of foamed latex impregnated with activated charcoal. When such a shaped sheet is used as a shoe insert or insole it is found to substantially reduce or even eliminate foot odors frequently associated with perspiring feet.
|
7. An effective deodorizer sheet material, said sheet material having interstitial spaces therein allowing for the passage of air therethrough, said sheet material comprising:
a. an open-celled latex foam through the open cells of which air can pass; and b. finely ground activated charcoal for deodorizing, said charcoal being homogeneously dispersed throughout the latex material comprising said foam.
11. An effective deodorizer sheet material, said sheet material having interstitial spaces therein allowing for the passage of air therethrough, said sheet material comprising:
a. an open-celled latex foam through the open cells of which air can pass; and b. at least about 10.2 percent finely ground activated charcoal for deodorizing, said charcoal being homogeneously dispersed throughout the latex material comprising said foam.
14. An effective deodorizer sheet material, said sheet material having interstitial spaces therein allowing for the passage of air therethrough, said sheet material comprising:
a. an open-celled latex foam through the open cells of which air can pass; and b. from at least about 10.2 percent to about 35 percent finely ground activated charcoal for deodorizing, said charcoal being homogeneously dispersed throughout the latex material comprising said foam.
17. An effective foot-deodorizing insole, said insole being shaped to conform to the basic outline of a foot, adapted for insertion into a shoe and having interstitial spaces therein allowing for the passage of air therethrough, said insole comprising:
a. an open-celled foam through the open cells of which air can pass; and b. finely ground activated charcoal for deodorizing, said charcoal being homogeneously dispersed throughout the material comprising said foam.
16. An effective deodorizer sheet material, said sheet material having interstitial spaces therein allowing for the passage of air therethrough, said sheet material comprising:
a. an open-celled latex foam through the open cells of which air can pass; b. from at least about 10.2 percent to about 35 percent finely ground activated charcoal for deodorizing, said charcoal being homogeneously dispersed throughout the latex material comprising said foam; and c. a backing material.
24. An effective foot-deodorizing insole, said insole being shaped to conform to the basic outline of a foot, adapted for insertion into a shoe and having interstitial spaces therein allowing for the passage of air therethrough, said insole comprising:
a. an open-celled foam through the open cells of which air can pass; and b. at least about 10.2 percent finely ground activated charcoal for deodorizing, said charcoal being homogeneously dispersed throughout the material comprising said foam.
38. A sheet for absorbing odors resulting from a perspiring portion of a human body comprising a cured sheet of open-celled foam, said foam containing homogeneously distributed through the solid part thereof finely divided activated charcoal particles in an amount effective to absorb odors when said sheet is subjected to contact with body perspiration and to passage of odor-filled air through interstitial spaces within said foam, said charcoal particles having been incorporated prior to frothing and curing of said foam.
30. An effective foot-deodorizing insole, said insole being shaped to conform to the basic outline of a foot, adapted for insertion into a shoe and having interstitial spaces therein allowing for the passage of air therethrough, said insole comprising:
a. an open-celled foam through the open cells of which air can pass; and b. from at least about 10.2 percent to about 35 percent finely ground activated charcoal for deodorizing, said charcoal being homogeneously dispersed throughout the material comprising said foam.
37. An effective foot-deodorizing insole, said insole being shaped to conform to the basic outline of a foot, adapted for insertion into a shoe and having interstitial spaces therein allowing for the passage of air therethrough, said insole comprising:
a. an open-celled latex foam through the open cells of which air can pass; b. at least about 10.2 percent finely ground activated charcoal for deodorizing, said charcoal being homogeneously dispersed throughout the material comprising said foam; and c. a backing material.
34. An effective foot-deodorizing insole, said insole being shaped to conform to the basic outline of a foot, adapted for insertion into a shoe and having interstitial spaces therein allowing for the passage of air therethrough, said insole comprising:
a. an open-celled foam through the open cells of which air can pass; b. from at least about 10.2 percent to about 35 percent finely ground activated charcoal for deodorizing, said charcoal being homogeneously dispersed throughout the material comprising said foam; and c. a backing material.
36. An effective foot-deodorizing insole, said insole being shaped to conform to the basic outline of a foot, adapted for insertion into a shoe and having interstitial spaces therein allowing for the passage of air therethrough, said insole comprising:
a. an open-celled foam, comprising at least one member of the group consisting of latex and polyurethane foams, through the open cells of which air can pass; b. at least about 10.2 percent finely ground activated charcoal for deodorizing, said charcoal being homogeneously dispersed throughout the material comprising said foam; and c. a backing material.
1. A shoe insert for absorbing odors resulting from perspiring feet comprising a cured sheet of opencelled open-celled foam, at least one side of the sheet having a relatively smooth skin formed during curing which is impervious to passage of charcoal particles, said foam containing homogeneously distributed through the solid part thereof finely divided activated charcoal particles in an amount effective to absorb odors when said sheet is subjected to contact with foot perspiration and to passage of odor-filled air through interstitial spaces within said foam, said charcoal particles having been incorporated prior to frothing and curing of said foam.
2. The article of
3. The article of
4. The product of
6. The product of
8. A deodorizer sheet material according to
9. A deodorizer sheet material according to
10. A deodorizer sheet material according to
12. A deodorizer sheet material according to
13. A deodorizer sheet material according to
15. A deodorizer sheet material according to
18. An insole according to
19. An insole according to
20. An insole according to
21. An insole according to
22. An insole according to
23. An insole according to
25. An insole according to
26. An insole according to
27. An insole according to
28. An insole according to
29. An insole according to
31. An insole according to
32. An insole according to
33. An insole according to
35. An insole according to
39. The article of
40. The article of
41. The product of
42. The product of
43. The product of
|
|||||||||||||||||||||||
Activated charcoal has long been used as a filter aid with both liquids and gases for the purpose of clarifying liquids and deodorizing liquids and gases.
In recent times it has been proposed as for example in British Specification No. 1,270,809 to incorporate activated charcoal into a fibre web or mat, the web or mat being supported by a backing material such as cloth obtained from natural sources as cotton, or formed of a synthetic such as nylon, and shaped so that the resulting web fits into and covers the inner sole of a shoe. It has also been proposed to attach a layer or coating of a foam material such as polyurethane foam to such a web for the purpose of providing increased strength and springiness.
My invention is directed to a unique shoe insert, or insole, which effectively and economically minimizes odors which are often associated with feet and which occur in conjunction with or as a result of perspiration. In general, my shoe insert comprises a foamed material, conveniently in the form of a sheet which has been cut or otherwise shaped to conform to the basic outline of a foot, and is adapted for insertion into a shoe. The shoe insert formed by incorporating activated charcoal into a chemical mix used to produce an open-celled foam through whose interstitial spaces air can pass.
After incorporation of the charcoal into a latex-containing chemical mix, the material is homogenized and spread uniformly into a web of cloth or the like, and then passed under a doctor blade to produce a desired thickness. The resulting product is then heat processed in order to produce a latex foam which is bonded to the web.
The resulting latex-foam sheets, containing charcoal dispersed therethrough, are then cut into such sizes as are appropriate for fitting comfortably into shoes, male or female. In use the insole is inserted into the shoe with the impregnated latex facing downward in the shoe to thereby permit contact of the web or backing material with the foot, and with the sock covering it.
The especially excellent effectiveness of my shoe insert seems to result from the circulation of air and vapors through and around the highly absorbable carbon particles, which occurs when the shoe containing such insert is worn.
So that my invention may be fully understood I shall hereinafter describe a specific example illustrating the practice of my invention. This illustration is for that purpose only, and is not intended to either limit the scope of the invention or of the claims appended hereto.
| EXAMPLE I |
| ______________________________________ |
| Ingredients Dry Weight |
| ______________________________________ |
| GR-S Latex 100.0 lbs. |
| Sulfur 1.5 lbs. |
| Zinc Oxide 4.0-5.0 lbs. |
| Surfactant 9.0 lbs. |
| Filler 100.0 lbs. |
| Activated Charcoal 25.0-32.0 lbs. |
| Antioxidant 1.2 lbs. |
| Accelerator 2.5 lbs. |
| ______________________________________ |
Where "percent" is taken as the amount of a given component over the weight of the chemical mix producing the foam (dry basis), multiplied by 100, activated charcoal is present in the above compositions in the amount of about 10.2 (10.22) to about 12.8 (12.78) percent.
The GR-S latex, a synthetic cold-type styrene-butodienebutadiene manufactured by the Goodyear Company of Akron, Ohio, is used in the form of an aqueous slurry (143.0 lbs.). And the activated charcoal, available under the tradename Nu-Char, is also used in the form of an aqueous slurry (150.0 lbs.).
The procedure used is as follows: The latex slurry is weighed out into a suitable mixing vessel and there is then added 9.0 lbs. of the surfactant, dioctyl-sodium-sulfo-succinate, available from the American Cyanamid Company of New York, under the trade name of Aerosol OT. There is then added 2.5 lbs. of potassium persulfate as the a suitable accelerator, such as 1.25 lbs. each Zetax (a zinc salt of mercapto benzothiazole) and Ethyl Zimate (zinc diethyldithiocarbamate), followed by additions of 1.5 lbs. of rubber makers grade sulfur, 4.0 to 5.0 lbs. of zinc oxide (American Process) and 1.2 lbs. of dioctyl trioctyl phosphite antioxidant.
Silica flour filler (100.0 lbs.) is then added, followed by addition of the activated charcoal aqueous slurry (143 25-32 lbs. of which is Nu-Char).
If it is desired to increase the viscosity of the foregoing mix, a suitable thickener, e.g., Methocel may be added.
The above components are then mixed to form a homogeneous mass, and which is then fed into a hopper, thence into a homogenizer, preferably an Oaks Oakes mixer, which is a rotor stator type homogenizer. Preferable Preferably two mixers are used in series. At the first mixer (called a prefrother) air is injected to control the pour density of the product. The base weight of the finished product is controlled by regulation of this air.
The material is then pumped into the second mixer, also a homogenizer, where the froth is refined, controlling the cell structure size.
After the mix leaves the second mixer and onto a flat surface (belt or table) covered with a layer of fabric which serves as a backing for the finished insert the thickness of the flow is controlled by a doctor blade set to give a finished foam guage of 80/1000 inch.
Instead of applying the mix onto a flat surface covered with a layer of fabric, as described above, the latex mix may be applied to a transfer paper instead. In other words, my sheet material can be produced with or without a fabric laminate.
Cup weights are taken after the mix leaves the second mixer; cup weights between 85 and 90 grams are acceptable, 87 grams being preferred. The tare weight (cup) is 24 grams.
The resulting material is then cured and dried in a forced hot air oven at temperatures ranging from 310° F to 350° F, with approximately 3 minutes of dwell time.
When a sheet material according to the invention is made by the general method described herein, there inherently results a product with at least one side of the sheet having a relatively smooth skin formed during curing which is impervious to passage of charcoal particles.
It will be understood, of course, by those skilled in the art that variations in the exact amounts and precise kinds of ingredients used in producing my charcoal-loaded latex foam are possible. Thus the levels of finely ground activated charcoal used may be varied rather widely, for example 35 percent or higher, by weight of the chemical mix producing the latex foam (dry basis) may be used, limited of course by the difficulty of incorporation into the latex mix, economic considerations, appearance and the like.
And though one specific latex foam formulation has been set forth in the foregoing example, those persons skilled in the art will understood that other foam formulations may be used, preferably those which can be processed to form an open-celled foam which breathes and allows for the passage of air through its interstitial spaces.
While it is presently preferred that the open-celled foam in sheet form comprising my invention be produced using latex, it is also contemplated, and is within the broad concept of my invention, that other open-celled foams may be used, such as polyurethane foams and vinyl chloride plastisol foams, especially where a slightly more rigid firm product is desired.
| Patent | Priority | Assignee | Title |
| 4186499, | May 22 1978 | Day International Corporation | Construction for absorbing odors caused by perspiration and method of making same |
| 4285144, | Aug 16 1978 | POWER-SOLER, INC | Inner sole for foot wear |
| 4533351, | Apr 26 1982 | Fisons Corporation | Foam rubber insoles containing Ottacide-P |
| 5078132, | Jun 08 1989 | Minnesota Mining and Manufacturing Company | Bonded adsorbent structures and respirators incorporating same |
| 5154960, | Jun 21 1990 | Eileen, Mucci | Drapeable soft odor absorbing sheet material |
| 5197208, | Feb 06 1991 | Combe Incorporated | Odor-adsorbent activated charcoal |
| 7160366, | Jul 16 2002 | MAST CARBON INTERNATIONAL LTD | Filter element |
| 7699913, | Mar 28 2007 | ILLUSION OUTDOORS LLC | Moisture and odor adsorbing insert |
| Patent | Priority | Assignee | Title |
| 2748502, | |||
| 3143812, | |||
| 3640920, | |||
| 3735511, | |||
| 3852897, | |||
| DT1,937,373, | |||
| UK1,270,809, | |||
| UK168,725, | |||
| UK728,075, |
| Executed on | Assignor | Assignee | Conveyance | Frame | Reel | Doc |
| Oct 20 1976 | Combe Incorporated | (assignment on the face of the patent) | / |
| Date | Maintenance Fee Events |
| Date | Maintenance Schedule |
| Dec 27 1980 | 4 years fee payment window open |
| Jun 27 1981 | 6 months grace period start (w surcharge) |
| Dec 27 1981 | patent expiry (for year 4) |
| Dec 27 1983 | 2 years to revive unintentionally abandoned end. (for year 4) |
| Dec 27 1984 | 8 years fee payment window open |
| Jun 27 1985 | 6 months grace period start (w surcharge) |
| Dec 27 1985 | patent expiry (for year 8) |
| Dec 27 1987 | 2 years to revive unintentionally abandoned end. (for year 8) |
| Dec 27 1988 | 12 years fee payment window open |
| Jun 27 1989 | 6 months grace period start (w surcharge) |
| Dec 27 1989 | patent expiry (for year 12) |
| Dec 27 1991 | 2 years to revive unintentionally abandoned end. (for year 12) |