Method of manufacturing fluorescent screens of cathode ray tubes

Abstract

A fluorescent screen of a cathode ray tube is prepared by forming a film of photosensitive sticky substance, for example, an aqueous solution of a copolymer of a complex salt of diazonium salt and zinc chloride, oN an inner surface of a face plate of the tube, exposing the film to light to render portions thereof sticky, applying a powdery substance, for example, phosphors of three colors graphite, onto the film to cause the powdery substance to adhere to the portions of the film rendered sticky, removing excess powder to form a film pattern of the powdery substance, causing the substance responsible for stickiness to ooze out onto the film pattern, applying another powdery substance, for example, graphite titanium oxide onto the film pattern and removing an excess of another powder substance, thus forming the fluorescent screen. The invention is applicable to the manufacture of a fluorescent screen for use in a color picture tube, a monochromatic picture tube and a penetration tube.

Description

standstill stationary, the substance responsible for stickiness or sticky liquid rises along the surfaces of the particles that constitute the film owing to capillary phenomenon, and when the film is sufficiently thin, the sticky liquid would ooze out to the top surface of the film with the result that the film itself manifests stickiness. When another type of powder is applied to such a sticky film and excess particles are blown away with air, a second film 15 of another type of the powder is formed on the first film (FIG. 1d). When the second film is sufficiently thin the sticky liquid further oozes out to the surface of the second film so that still another powder can be applied. The above preparation process can be repeated until the sticky liquid does not ooze out to prepare a multilayer film. Where a photosensitive sticky substance is coated on the substrate to a sufficient thickness and the amount of exposure light is increased, the amount of the sticky liquid increases so that it is possible to increase the number of layers. Accordingly, the number of layers can be determined as desired by varying the thickness and concentration of the photosensitive sticky substance and the amount of exposure light.

For better understanding of the invention, the following examples are given.

EXAMPLE 1

An aqueous solution of a photosensitive sticky substance having the following composition was coated on the inner surface of the panel glass of the color picture tube and the thickness of the film was adjusted to 0.5 to 0.8 microns with a conventional rotary spinning machine, followed by drying.

______________________________________
arginic acid-polypropylene glycol ester
0.2     wt. %
polyvinyl alcohol      0.06    wt. %
P--dimethyl aminobenzene diazonium
3.3     wt. %
chloride, zinc chloride
water                  balance
______________________________________

After mounting a stripe shadow mask, portions of the film other than the portion approximately corresponding to locations for three colors of green, blue and red stripes were successively exposed to light. At this time, the position of a light force source was shifted from the ordinary positions of the light source for exposure of portions at which stripes of phosphors of respective colors are to be formed, by half the distance between the positions in a direction perpendicular to the stripes. After exposure, the shadow mask was dismounted and a fine powder of graphite having a particle size of 0.2 to 0.3 microns was sprayed and excess powder was removed by compressed air, thus forming an ordinary black matrix stripe. After one minute, sticky liquid created by the previous exposure oozed out onto the surface of the black matrix stripe. Then, a fine powder of titanium oxide having a particle size of 0.1 to 0.2 microns was applied and excess powder was removed by compressed air to form titanium oxide layer acting as a reflection layer on the graphite layer. Thereafter, the film was exposed to light in a conventional manner to form phosphor stripes of three colors between black matrix stripes. Conventional steps were followed to complete a fluorescent screen.

EXAMPLE 2

This example concerns manufacture of a penetration tube. Firstly, an aqueous solution of photosensitive sticky substance having the same composition as in Example 1 was applied to the inner surface of a face plate of the tube to a thickness of 1 to 1.5 microns, the resulting film was dried and then uniformly exposed to light. A powder of phosphor acting as a blue phosphor and consisting of zinc sulfide and silver and having a particle size of about 0.1 micron was sprayed to a thickness of about 0.9 microns and excess powder was removed by compressed air. The assembly was left standstill for about one minute to cause the sticky liquid to ooze out. Then, a powder of silica having a particle size of about 0.05 microns was applied to a thickness of about 0.25 microns and excess powder was removed by compressed air to form silica films acting as barriers for increasing the potential difference between phosphor layers. The assembly was left standstill stationary for one minute to cause the sticky liquid to ooze out. Then, a powder of green phosphor consisting of zinc silicate and manganese was applied to a thickness of about 0.25 microns and then developed. The assembly was left standstill stationary for 30 seconds, and then in the same manner as described above, a powder of silica was applied to a thickness of about 0.7 microns to form a silica film. Then, the assembly was left standstill for one minute, and a powder of red phosphor having a particle size of 0.1 micron and consisting of silicates of magnesium, cadmium and zinc, and manganese was applied to a thickness of about 0.5 microns to form a multilayer construction, followed by predetermined steps to obtain a fluorescent screen.

EXAMPLE 3

An aqueous solution of the photosensitive sticky substance, the same as that of Example 1, was coated to a thickness of about 0.5 to 0.6 microns on the inner surface of the face plate of a monochromatic cathode ray tube and then dried. After uniformly exposing the resulting film to light, a powder of white phosphor having a particle size of about 7 to 8 microns and consisting of a mixture of zinc sulfide-silver, zinc sulfide-copper, and aluminam was sprayed to a thickness of about 15 to 20 microns, and excess powder was removed with compressed air. After the assembly was left standstill stationary for two minutes, a fine powder of isobuthyl isobutyl methacrylate resin having a particle size of about 0.05 microns was applied to a thickness of about 5 microns and the resulting film was then developed. Thereafter, the face plate was heated to 85°C to fuse together the particles of the resin for forming a continuous film acting as a filming layer on the phosphor film, followed by predetermined steps to obtain a fluorescent screen.

It should be understood that the foregoing examples show only few examples of the method of this invention for preparing a fluorescent screen of a multilayer construction, and that various types of fluorescent screens can be prepared by adjusting the quantity of the sticky liquid by varying the quantity of the applied photosensitive sticky substance and the quantity of exposure light, or by changing the combination of the powdery substances. For example, the filming layer described in Example 3 can also be applied following the steps described in Examples 1 and 2.

As described above, according to the method of manufacturing a fluorescent screen of a cathode ray tube of this invention, a film of photosensitive sticky substance is exposed to light to render it sticky, then powders of various substances are applied to the sticky film, and excess powders are removed to develope. After the sticky liquid has oozed out to the surface of the film, another powder is applied again and then developed. In this manner, a multilayer fluorescent screen having any desired number of layers and consisting of different materials can readily be prepared until the sticky liquid does not ooze out any more.

Claims

1. A method of manufacturing a fluorescent screen of a cathode ray tube comprising the steps of:

forming a film of photosensitive sticky substance that exhibits stickiness when exposed to light on an inner surface of a face plate of said tube;

exposing said film to light to render portions thereof sticky;

applying a powdery substance onto said film to cause said powdery substance to adhere to said portions of the film rendered sticky;

removing excess powder to form a film pattern of said powdery substance;

causing the substance responsible for stickiness to ooze out onto said film pattern;

applying another powdery substance onto said film pattern; and

removing an excess of said another powdery substance, thus forming said fluorescent screen.

2. The method according to claim 1 wherein said photosensitive sticky substance comprises a compolymer of a complex salt of diazonium salt and zinc chloride.

3. The method according to claim 1 wherein said film of photosensitive sticky substance has a thickness of about 0.5 to 0.8 microns.

4. The method according to claim 1 wherein said powdery substance comprises powders a powder of phosphors of one of three colors of green, blue and red.

5. The method according to claim 1 4 wherein said another powdery substance comprises a powder of graphite silica.

6. The method according to claim 5 which further comprises the step of applying a powder of white substance onto a film of graphite to form a reflection layer a phosphor of a second of said three colors.

7. The method according to claim 1 6 wherein said a second another powdery substance comprises comprising a powder of silica is applied to said phosphor of said second color.

8. A method according to claim 1 wherein said powdery substance comprises a powder of graphite and said another powdery substance comprises a powder of titanium oxide.

9. The method according to claim 1 wherein said powdery substance is a powder of a phosphor and said another powdery substance comprises an isobutyl methacrylate resin.