Sterically hindered cyclic amines which are substituted by a photoactivatable acyl group at the basic nitrogen atom can be deacylated by irradiation with UV light. This is advantageous if the basicity of the amines proves troublesome during application. Examples of such photoactivatable acyl groups are phenylglyoxyl, phenylacetyl or naphthylacetyl groups.

Patent
   RE33489
Priority
Aug 27 1985
Filed
Sep 25 1989
Issued
Dec 11 1990
Expiry
Sep 25 2009
Assg.orig
Entity
unknown
4
10
EXPIRED
1. A compound of formula I ##STR14## wherein m is 1, 2 or 3,
A is a r1 --CO-- or r2 --CH2 -- group, wherein
r1 is phenyl or phenyl which is substituted by halogen, C1 -C12 alkyl, C1 -C4 alkoxy or hydroxy, or is naphthyl, C1 -C12 alkoxy, cyclohexyloxy, phenoxy or benzyloxy and, if m=1, may also be a radical b,
r2 is --CN, --P(O)(OR3)2, CH3 CO-- or OR4, wherein
r3 is C1 -C4 alkyl or phenyl, and
r4 is phenyl or phenyl which is substituted by halogen or C1 -C4 alkyl, and
when m is 1,
b is a radical corresponding to the formulae ##STR15## wherein r5 is hydrogen, --OR8, ##STR16## --N(r10 r11), r6 is --OH or --OR12 and r7 is --OR12, --CN, --COOR13 or --CONH2, or r6 and r7 together are the oxo radical (═O), or r6 and r7, together with the C-atom to which they are attached, form an unsubstituted 2-spiro-1,3-dioxolane, 2-spiro-1,3-dioxane, 5-spiro-1,3-oxazolidine, 2-spiro-1,3-oxazolidine or 5-spiro-1,3-imidazolidine ring or said ring substituted by one or more identical or different members selected from C1 -C12 alkyl or the oxo radical,
r8 is C1 -C12 alkyl, benzyl, allyl or 2-cyanoethyl,
r9 is C1 -C18 alkyl, C2 -C12 alkenyl, C5 -C8 cycloalkyl, phenyl or phenyl which is substituted by halogen, C1 -C12 alkyl, C1 -C4 alkoxy or hydroxyl, or is C7 -C12 phenylalkyl, C1 -C4 alkoxy or phenoxy,
r10 is C1 -C12 alkyl, cyclohexyl, phenyl, naphthyl, or phenyl which is substituted by C1 -C4 alkyl,
r11 is C2 -C12 alkanoyl, C3 -C8 alkenoyl, benzoyl or a group of the formula ##STR17## wherein r14 and r15 are each independently of the other C1 -C8 alkoxy, phenoxy, or a group --N(r10)(r16), in which r16 is hydrogen or C1 -C12 alkyl,
r12 is C1 -C12 alkyl and r13 is C1 -C4 alkyl, and
Y is hydrogen, C1 -C12 alkyl, allyl or benzyl;
when m is 2,
b is a divalent radical corresponding to the formulae ##STR18## wherein Z is --O--, --NH-- or --NR10 --,
r17 is methylene, 1,2-ethylene, C3 -C20 polymethylene, or branched C3 -C20 alkylene, C2 -C10 alkenylene, 1,4-cyclohexylene, 1,3-cyclohexylene, cyclohexane-1,4-dimethylene, 1,3- or 1,4-phenylene, 1,4- or 1,5-naphthylene, 4,4'-diphenylene, diphenylmethane-4,4'-diyl, diphenyl oxide-4,4'-diyl or m- or p-xylene, or a radical --NR--r19 --NH--,
r18 is 1,2-ethylene, 1,2-propylene, 1,3-propylene, 1,2-butylene, 1,4-butylene, hexamethylene, 1,4-cyclohexylene or cyclohexane-1,4-dimethylene,
r19 is 1,2-ethylene, trimethylene, tetramethylene, hexamethylene, oxtamethylene, dodecamethylene, 2,2-dimethyltrimethylene, trimethyloctamethylene, 1,4-cyclohexylene, cyclohexane-1,4-dimethylene, 1,3-phenylene, 4,4'-diphenylene, diphenylmethane-4,4'-diyl, diphenyl oxide-4,4'-diyl, or m- or p-xylylene, and
r10 and r14 are as defined above;
and, when m is 3,
b is a trivalent radical corresponding to the formulae ##STR19## wherein r20 is propane-1,2,3-triyl, butane-1,2,4-triyl, benzene-1,3,5-triyl, benzene-1,2,4-triyl or naphthalene-1,4,5-triyl, r21 is a 1,3,5-triazin-2,4-triyl radical and Z is as defined above.
2. A compound according to claim 1 of formula I, wherein A is a r1 --CO-- or r2 --CH2 --group, wherein r1 is phenyl which is substituted by halogen, C1 -C12 alkyl or C1 -C4 alkoxy, or is unsubstituted naphthyl, and r2 is --CN or CH3 CO--.
3. A compound according to claim 1 of formula I, wherein A is a benzoyl group.
4. A compound according to claim 1 of formula I, wherein m is 1 or 2 and b is a group of formula II, III or IV.
5. A compound according to claim 4 of the formula ##STR20##

The present invention relates to photolytically cleavable, N-acylated sterically hindered amines and to the use thereof for stabilising polymers against light-induced damage, in particular for stabilising acid curable resins.

It is known that sterically hindered amines are effective light stabilisers for polymers. Particular importance attaches to the light protection of varnishes for producing industrial finishes of which a long service life is required, e.g. automotive finishes or machine finishes. Acid-catalysed stoving varnishes are often used for obtaining such finishes. The addition of acid curing catalysts as well as amine light stabilisers to such varnishes before curing may result in unwanted interactions of both these components. This problem can be overcome by using N-acylated piperidines as "amine light stabilisers" in accordance with the teaching of European patent application No. EP-A-52 073. These compounds are no longer basic and thus do not give rise to interactions with acid catalysts. However, the light protective action of the N-acylated piperidines is usually inferior to that of the analogous N-unsubstituted or N-alkylated piperidines. The problem was therefore to provide light stabilisers which do not undergo interaction with the acid catalyst and which induce in the cured varnish as good a light-stabilising effect as the N-unsubstituted or N-alkylated amine light stabilisers. The same consideration also applies to acid curable resins, aside from their utility as varnishes.

It has been found that this problem can be solved by using N-acylated, sterically hindered amines as light stabilisers, which amines can be cleaved by photolysis and converted into N-unsubstituted amine light stabilisers after curing the resin by irradiation. These photolytically curable amine light stabilisers are so far not known in the art and therefore had to be developed specially for this purpose.

Accordingly, the invention relates to compounds of formula I ##STR1## wherein m is 1, 2 or 3,

A is a R1 --CO-- or R2 --CH2 -- group, wherein

R1 is phenyl or phenyl which is substituted by halogen, C1 -C12 -alkyl, C1 -C4 alkoxy or hydroxy, or is naphthyl, C1 -C12 alkoxy, cyclohexyloxy, phenoxy or benzyloxy and, if m=1, may also be a radical B,

R2 is halogen, phenyl, naphthyl, --CN, --P(O)(OR3)2, --CH3 CO-- or --OR4, wherein

R3 is C1 -C4 alkyl or phenyl, and

R4 is phenyl or phenyl which is substituted by halogen or C1 -C4 alkyl, and

B is a radical of valency m of a sterically hindered cyclic amine which is attached to the A--CO-- radical through the sterically hindered nitrogen atom.

The cyclic amine radical B can be a 5-, 6- or 7-membered ring which may also contain other hetero atoms in addition to the basic nitrogen atom. However, the radical B is not an aromatic heterocyclic radical. In particular, where m=1, B may be a radical of formula ##STR2## wherein R5 is hydrogen, --OR8, ##STR3## --N(R10 R11), R6 is --OH or --OR12 and R7 is --OR12, --CN, --COOR13 or --CONH2, or R6 and R7 together are the oxo radical (═O), or R6 and R7, together with the C-atom to which they are attached, form a heterocyclic spiro ring which may be a 2-spiro-1,3-dioxolane, 2-spiro-1,3-dioxane, 5-spiro-1,3-oxazolidine, 2-spiro-1,3-oxazolidine or 5-spiro-1,3-imidazolidine ring and which may be substituted by one or more identical or different members selected from alkyl, substituted alkyl, alkylene and/or the oxo radical,

R8 is C1 -C12 alkyl, benzyl, allyl or 2-cyanoethyl,

R9 is C1 -C18 alkyl, C2 -C12 alkenyl, C5 -C8 cycloalkyl, phenyl or phenyl which is substituted by halogen, C1 -C12 alkyl, C1 -C4 alkoxy and/or hydroxyl, or is C7 -C12 phenylalkyl, C1 -C4 alkoxy or phenoxy,

R10 is C1 -C12 alkyl, cyclohexyl, phenyl, naphthyl, or phenyl which is substituted by C1 -C4 alkyl,

R11 is C2 -C12 alkanoyl, C3 -C8 alkenoyl, benzoyl or a group of the formula ##STR4## wherein R14 and R15 are each independently of the other C1 -C8 alkoxy, phenoxy, or a group --N(R10)(R16), in which R16 is hydrogen or C1 -C12 alkyl,

R12 is C1 -C12 alkyl and R13 is C1 -C4 alkyl, and

Y is hydrogen, C1 -C12 alkyl, allyl or benzyl.

Where m is 2, B may in particular be a divalent radical selected from: ##STR5## wherein Z is --O--, --NH-- or --NR10,

R17 is a divalent aliphatic, cycloaliphatic or aromatic radical of 1 to 20 carbon atoms or a radical --NH--R19 --NH--,

R18 is a divalent aliphatic or cycloaliphatic or aromatic radical of 2 to 12 carbon atoms,

R19 is a divalent aliphatic, cycloaliphatic or aromatic radical of 2 to 16 carbon atoms, and

R10 and R14 are as previously defined.

Where m=3, B may be in particular a trivalent radical of formula ##STR6## wherein R20 is a trivalent aliphatic radical of 3 to 8 carbon atoms or a trivalent aromatic radical of 6 to 10 carbon atoms, R21 is a 1,3,5-triazin-2,4,6-triyl radical, and Z is as previously defined.

Substituents defined above as alkyl may be unbranched or branched alkyl. R3 and R13 as C1 -C4 alkyl are methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl or tert-butyl. R8, R10, R12, R16 and Y as C1 -C12 alkyl may be pentyl, n-hexyl, 2-ethylbutyl, n-octyl, 2-ethyl-n-hexyl, n-nonyl, isodecyl or n-dodecyl. R9 as C1 -C18 alkyl may be tetradecyl, hexadecyl or octadecyl.

R9 as C2 -C12 alkyl may be vinyl, allyl, 2-propenyl, methallyl, 2-buten-1-yl, 2-buten-2-yl, 2-hexen-1-yl, 2-octen-1-yl or 10-un-decen-1-yl.

R9 as C5 -C6 cycloalkyl may be cyclopentyl, cyclohexyl, methylcyclohexyl or cyclooctyl. R9 as C7 -C12 phenylalkyl may be benzyl, 1- or 2-phenylethyl or 3-phenylpropyl.

R1, R4 and R9 as substituted phenyl radicals may be 4-chlorophenyl, 3-bromophenyl, 2-fluorophenyl, 4-methylphenyl, 2,4-dimethylphenyl, 4-tert-butylphenyl, 3-methoxyphenyl or 4-ethoxyphenyl. R1 and R9 may also be 4-octylphenyl, 4-dodecylphenyl, 4-hydroxyphenyl, 2-methyl-4-hydroxyphenyl or 3,5-di-(tert-butyl)-4-hydroxyphenyl.

R9, R14 and R15 as alkoxy radicals may be methoxy, ethoxy or butoxy. R14 and R15 may also be hexyloxy, octyloxy, decyloxy or dodecyloxy.

R11 as alkanoyl or alkenoyl may be acetyl, propionyl, butyroyl, hexanoyl, octanoyl, lauroyl, acryloyl, methacryloyl or crotonoyl.

R17 as a divalent aliphatic, cycloaliphatic or aromatic radical may be methylene, 1,2-ethylene or C3 -C20 polymethylene; or branched C3 -C20 alkylene such as 1,2-propylene or trimethyltetramethylene; or C2 -C10 alkenylene such as vinylene or 2-buten-1,4-ylene; or cycloalkylene such as 1,4-cyclohexylene or 1,3-cyclohexylene; or cycloalkane-dialkylene such as cyclohexane-1,4-dimethylene; or arylene such as 1,3- or 1,4-phenylene, 1,4- or 1,5-naphthylene, 4,4'-diphenylene, diphenylmethane-4,4'-diyl or diphenyl oxide-4,4'-diyl; or aralkylene such as m- or p-xylene.

R18 as a divalent aliphatic, cycloaliphatic or aromatic radical is preferably a radical of 2 to 8 carbon atoms. Examples of such radicals are 1,2-ethylene, 1,2-propylene, 1,3-propylene, 1,2-butylene, 1,4-butylene, hexamethylene, 1,4-cyclohexylene or cyclohexane-1,4-dimethylene.

R19 as a divalent aliphatic, cycloaliphatic or aromatic radical may be an unbranched or branched alkylene radical such as 1,2-ethylene, trimethylene, tetramethylene, hexamethylene, octamethylene, dodecamethylene, 2,2-dimethyltrimethylene or trimethyloctamethylene; or a cycloalkylene radical such as 1,4-cyclohexylene; or cycloalkanealkylene such as cyclohexane-1,4-dimethylene; or arylene such as 1,3-phenylene, 4,4'-diphenylene, diphenylmethane-4,4'-diyl or diphenyl oxide-4,4'-diyl; or arene-dialkylene such as m- or p-xylylene.

R20 as a trivalent aliphatic or aromatic radical may be propane-1,2,-3-triyl, butane-1,2,4-triyl, benzene-1,3,5-triyl, benzene-1,2,4-triyl or naphthalene-1,4,5-triyl.

Preferred compounds of formula I are those wherein A is a R1 --CO-- or R2 --CH2 -- group, wherein R1 is phenyl or phenyl which is substituted by halogen, C1 -C12 alkyl or C1 -C4 alkoxy, or is unsubstituted naphthyl, and R2 is phenyl, naphthyl, --CN or CH3 CO--.

Particularly preferred compounds of formula I are those wherein A is a benzoyl group or an α-naphthylmethyl group. Further preferred compounds of formula I are those wherein m is 1 or 2 and B is a group of formulae II, III or IV.

Where m=1 and A is B--CO, the compounds conform to the formula B--CO--CO--B, wherein both radicals B are attached to the --CO group through their sterically hindered nitrogen atoms.

The compounds of formula I can be prepared in principle from the N-unsubstituted amines (H)m B by reaction with the corresponding carboxylic acid chlorides A--COCl or anhydrides (A--CO)2 O. The compounds B--CO--CO--B can be prepared by reaction of 2 moles of H--B with 1 mole of oxalyl chloride. The N-unsubstituted sterically hindered cyclic amines are known compounds which have been described in a number of patent specifications, for example U.S. Pat. Nos. 3,640,928, 3,790,525 and 3,639,409.

Some of the acid chlorides A--COCl are known compounds or can be prepared from the corresponding carboxylic acids by known methods, for example by reaction with thionyl chloride. Some of the anhydrides are also known and can be prepared e.g. by the method described in J. Cabre-Castelvi et al., in Synthesis, 1981, 616.

Representative examples of individual compounds of formula I are listed below. In these compounds, ##STR7## denotes a 2,2,6,6-tetramethylpiperidine radical Ph- is a phenyl radical and Naphth- is an α-naphthyl radical. ##STR8##

The compounds of formula I are intrinsically light stabilisers for organic polymers and can be used for stabilising them without the need for irradiation. To this end they are normally incorporated in the polymers before these are processed to moulded articles. However, they can also be added during the manufacture of the polymers. The following classes of polymer are examples of polymers which are sensitive to the action of light and which can be stabilised by addition of the compounds of this invention.

1. Polymers of mono- and diolefins, for example polyethylene (uncrosslinked or crosslinked), polypropylene, polyisobutylene, polybut-1-ene, polymethylpent-1-ene, polyisoprene or polybutadiene, and polymers of cycloolefins, e.g. of cyclopentene or norbornene.

2. Mixtures of the polymers mentioned under (1), for example mixtures of polypropylene with polyethylene or with polyisobutylene.

3. Copolymers of mono- and diolefins with each other or with other vinyl monomers, for example ethylene/propylene copolymers, propylene/but-1-ene copolymers, propylene/isobutylene copolymers, ethylene/but-1-ene copolymers, propylene/butadiene copolymers, isobutylene/isoprene copolymers, ethylene/alkylacrylate copolymers, ethylene/alkylmethacrylate copolymers, ethylene/vinyl acetate copolymers, or ethylene/acrylic acid copolymers and salts thereof (isomers), as well as terpolymers of ethylene with propylene and a diene such as hexadiene, dicyclopentadiene or ethylidene norbornene.

4. Polystyrene, poly-(p-methylstyrene).

5. Copolymers of styrene or α-methylstyrene with dienes or acrylic derivatives, for example styrene/butadiene, styrene/acrylonitrile, styrene/alkylmethacrylate, styrene/acrylonitrile/methyl acrylate, mixtures of high impact strength obtained from styrene copolymers and another polymer, for example a polyacrylate, a diene polymer or an ethylene/propylene/diene terpolymer; and also block copolymers of styrene, for example styrene/butadiene/styrene, styrene/isoprene/styrene, styrene/ethylene/butylene/styrene, or styrene/ethylene/propylene/styrene.

6. Graft copolymers of styrene, e.g. styrene with polybutadiene, styrene and acrylonitrile with polybutadiene, styrene and maleic anhydride with polybutadiene, styrene and alkyl acrylates or alkyl methacrylates with polybutadiene, styrene and acrylonitrile with ethylene/propylene/diene terpolymers, styrene and acrylonitrile with polyalkylacrylates or polyalkylmethacrylates, styrene and acrylonitrile with acrylate/butadiene copolymers, and mixtures thereof with the copolymers listed under (5), known e.g. as ABS, MBS, ASA or AES polymers.

7. Halogen-containing polymers, e.g. polychloroprene, chlorinated rubber, chlorinated or chlorosulfonated polyethylene, especially polymers of halogenated vinyl compounds, e.g. polyvinyl chloride, polyvinylidene chloride, polyvinyl fluoride, polyvinylidene fluoride and their copolymers such as vinyl chloride/vinylidene chloride, vinyl chloride/vinyl acetate or vinylidene chloride/vinyl acetate polymers.

8. Polymers which are derived from α,β-unsaturated acids and their derivatives, e.g. polyacrylates and polymethacrylates, polyacrylamides and polyacrylonitriles.

9. Copolymers of the monomers listed in (8) with one another or with other unsaturated monomers, e.g. acrylonitrile/butadiene copolymers, acrylonitrile/alkylacrylate copolymers, acrylonitrile/vinyl halide copolymers, or acrylontrile/alkylmethacrylate/butadiene terpolymers.

10. Polymers which are derived from unsaturated alcohols and amines or their acyl derivatives or acetals, e.g. polyvinyl alcohol, polyvinyl acetate, polyvinyl stearate, polyvinyl benzoate, polyvinyl maleate, polyvinylbutyral, polyallyl phthalate, polyallyl melamine.

11. Homopolymers and copolymers of cyclic ethers such as polyethylene glycols, polyethylene oxide, polypropylene oxide or their copolymers with bisglycidyl ethers.

12. Polyacetals such as polyoxymethylene, and also those polyoxymethylenes which contain e.g. ethylene oxide as comonomer.

13. Polyphenyl oxides and polyphenyl sulfides and mixtures thereof with styrene polymers.

14. Polyurethanes which are derived on the one hand from polyethers, polyesters and polybutadienes containing hydroxy end groups, and from aliphatic or aromatic polyisocyanates on the other, as well as their precursors (polyisocyanates, polyols, prepolymers).

15. Polyamides and copolyamides which are derived from diamines and dicarboxylic acids and/or from aminocarboxylic acids or the corresponding lactams, such as polyamide 4, polyamide 6, polyamide 66, polyamide 610, polyamide 11, polyamide 12, poly-2,4,4-trimethylhexamethyleneterephthalamide, poly-m-phenylene-isophthalamide, and their block copolymers with polyethers, e.g. with polyethylene glycol, polypropylene glycol or polytetramethylene glycol.

16. Polyureas, polyimides and polyamide-imides.

17. Polyesters which are derived from dicarboxylic acids and diols and/or from hydroxycarboxylic acids or the corresponding lactones, e.g. polyethylene terephthalate, polybutylene, terephthalate, poly-1,4-dimethylolcyclohexane terephthalate, polyhydroxybenzoates, and also block polyether esters which are derived from hydroxyl-terminated polyethers.

18. Polycarbonates.

19. Polysulfones, polyether sulfones and polyether ketones.

20. Crosslinked polymers which are derived from aldehydes on the one hand and from phenols, ureas and melamines on the other hand, e.g. phenol/formaldehyde resins, urea/formaldehyde resins and melamine/formaldehyde resins.

21. Drying and non-drying alkyd resins.

22. Unsaturated polyester resins which are derived from copolyesters of saturated and unsaturated dicarboxylic acids with polyhydric alcohols and from vinyl compounds as crosslinking agents, and also their halogen-containing modifications of low combustibility.

23. Crosslinkable acrylic resins which are derived from substituted acrylic esters, e.g. from epoxy acrylates, urethane acrylates or polyester acrylates.

24. Alkyd resins, polyester resins and acrylate resins which are crosslinked with melamine resins, urea resins, polyisocyanates or epoxy resins.

25. Crosslinked epoxy resins which are derived from polyepoxides, e.g. bisglycidyl ethers, or from cycloaliphatic diepoxides.

26. Naturally occurring polymers such as cellulose, natural rubber and gelatin, and also chemically modified homologous derivatives thereof such as cellulose acetates, cellulose propionates and cellulose butyrates, and cellulose ethers such as methylcellulose.

The amount of stabiliser added is in general 0.01 to 5% by weight, preferably 0.03 to 1.5% by weight and, most preferably, 0.2 to 0.6% by weight, based on the polymer to be stabilised.

The polymers may also contain other known stabilisers, for example antioxidants, light stabilisers, metal deactivators, phosphites, thiodicarboxylates, salts of higher fatty acids or other co-stabilisers. Other modifiers conventionally employed in plastics technology may also be added, for example antistats, plasticizers, lubricants, flame retardants, pigments, reinforcing agents or fillers.

If the stabilised polymers are in the form of thin layers, as they are in the case of sheets, filaments, varnishes and coatings, the stabilisers of formula I can be cleaved photochemically by irradiation with shortwave light to form compounds which are unsubstituted at the sterically hindered nitrogen atom. Irradiation is preferably effected with UV light in the wavelength range from 250 to 400 nm. Suitable light sources for the irradiation are for example medium-pressure, high-pressure and low-pressure mercury lamps as well as superactinic neon tubes. At the present time a whole range of suitable devices is available, especially for continuous irradiation, in which the material to be irradiated is transported beneath the light source. The same effect is achieved when using the stabilised polymers in the open.

As mentioned at the outset, the photochemical conversion of the N-acylated stabiliser to an N-unsubstituted stabiliser is of particular importance for stabilising acid-catalysed stoving varnishes by effecting irradiation after stoving.

Acid-curable varnishes are in particular those based on a binder that contains an amine resin, e.g. an etherified, esterified or otherwise modified melamine resin, urea resin or guanidine resin. These varnishes are normally used in admixture with alkyd, polyester or acrylic resins which contain functional groups (e.g. --OH or --COOH groups) that are crosslinked by reaction with the methylol groups of the amine resins. This crosslinking is catalysed by acids. Instead of the amine resin, the varnish can also contain methylol derivatives of polycarboximides or their ethers or esters. Sulfonic acids are usually employed as acid curing catalysts, but carboxylic acids or phosphonic acids or masked sulfonic acids are also suitable.

Acid-catalysed stoving varnishes often contain mixtures of alkyd resins, polyester resins and acrylic resins with one another or with other film-forming resins. Such film-forming resins may also be self-crosslinking, for example if they are modified by methylolamide groups, in which case they do not require the addition of an amine resin or other crosslinking agent.

The stabilisers of this invention are incorporated in the varnishes before application, preferably by adding them to a solution of the stabiliser in an organic solvent. The stoving of the varnish is usually effected in the temperature range from 100°-200°C During stoving, the stabiliser must not volatilise and decompose. Not until the subsequent irradiation of the cured varnish coating does the photochemical cleavage of the stabilise occur.

For many finishes, especially automotive finishes, the two-coat method is employed at the present time. This method comprises applying first the pigmented varnish and then the clear varnish to the undercoat. The light stabiliser can be added to the clear varnish as well as to the pigmented varnish or to both coatings.

To obtain maximum light-resistance, the concurrent use of other conventional light stabilisers, e.g. UV absorbers or organic nickel compounds, can be advantageous. The concurrent use of UV absorbers of the 2-hydroxybenzophenone, 2-(2-hydroxyophenyl)benztriazole or oxanilide type, which may have a synergistic effect, is especially useful. Examples of such compounds are: 2-(2-hydroxy-3,5-di-tert-amylphenyl)benztriazole, 2-(2-hydroxy-5-tert-octylphenyl)benztriazole, 2-(2-hydroxy-3,5-di-tert-octylphenyl)benztriazole, 2,4-dihydroxybenzophenone, 2-hydroxy-4-octyloxybenzophenone, 2-hydroxy-5-dodecyloxybenzophenone, 2-ethyl-2-ethoxy-4'-tert-butyloxalanilide or 2-ethyl-2'-ethoxyoxalanilide.

When using such combinations, the sum of all light stabilisers is 0.2 to 5% by weight, preferably 0.5 to 2% by weight, based on the film-forming resin.

Further modifiers which may be present in the varnish are antioxidants, for example of the sterically hindered phenol derivative type, phosphorus compounds such as phosphites or phosphonites, plasticisers, levelling agents, thickeners, dispersants or bonding agents.

The following Examples illustrate the preparation of the compounds of this invention and the use thereof as stabilisers.

(a) 1 ml of piperidine is added to 30 g (0.2 mole) of phenylglyoxylic acid and 18.9 ml (0.26 mole) of thionyl chloride are added dropwise, with stirring, under nitrogen such that the temperature of the reaction mixture is 25°-30°C The reaction mixture is then stirred for 24 hours at 35°-40°C and concentrated by evaporation at a maximum temperature of 40°C under vacuum. The residual crude phenylglyoxylyl chloride is a yellow oil containing an insignificant amount of powdery deposit. This crude product is used without further purification for the subsequent reactions.

(b) 24.1 g (0.1 mole) of 4-hexyloxy-2,2,6,6-tetramethylpiperidine are dissolved in 100 ml of absolute methylene chloride. To this solution are added 15.2 g (0.15 mole) of absolute triethylamine and the whole solution is cooled to -10°C At this temperature a solution of 16.8 g (0.1 mole) of phenylglyoxylyl chloride in 100 ml of methylene chloride is slowly added dropwise. When this addition is complete, the reaction mixture is allowed to warm to room temperature and stirred for about 4 hours. Precipitated hydrochloride is removed by filtration and the solution is clarified by filtration over a small amount of silica gel and concentrated by evaporation, affording 28.4 g of 1-(4-hexyloxy-2,2,6,6-tetramethylpiperidino)-2-phenylethane-1,2-dione as a yellow oil (stabiliser 1).

______________________________________
Analysis: theory
C = 73.96% found C = 73.77%
H = 9.44% H = 9.20%
N = 3.75% N = 3.25%
______________________________________

Analogous reaction of phenylglyoxylyl chloride with the corresponding cyclic amines gives the following compounds:

3-dodecyl-8-(2-phenylethane-1,2-dion-1-yl)-7,7,9,9-tetramethyl-1,3,8-triaza spiro[4.5]decane-2,4-dione (stabiliser 2);

______________________________________
Analysis: theory
C = 70.82% found C = 70.46%
H = 9.02% H = 8.82%
N = 7.99% N = 7.96%
______________________________________

3-dodecyl-1,8-bis(2-phenylethane-1,2-dion-1-yl)-7,7,9,9-tetramethyl-1,3,8-t riazaspiro[4.5]decane-2,4-dione (stabiliser 3);

______________________________________
Analysis: theory
C = 71.20% found C = 68.82%
H = 7.81% H = 7.72%
N = 6.38% N = 6.19%
______________________________________

bis-[1-(2-phenylethane-1,2-dion-1-yl)-2,2,6,6-tetramethylpiperidin-4-yl]adi pate, m.p. 135°-137°C (stabiliser 4);

1-(4-benzoyloxy-2,2,6,6-tetramethylpiperidino)-2-phenylethane-1,2-dione, m.p. 122°-124°C (stabiliser 5);

1-(4-dodecyloxy-2,2,6,6-tetramethyl(piperidino)-2-phenylethane-1,2-dione in the form of a yellow oil (stabiliser 6);

______________________________________
Analysis: theory
C = 76.10% found C = 75.78%
H = 10.35% H = 10.18%
N = 3.06% N = 2.93%
______________________________________

Analogous reaction of ethyl oxalyl chloride (C2 H5 OCOCOCl) with the corresponding cyclic amines gives the following compounds:

ethyl 2-[4-hexyloxy-2,2,6,6-tetramethylpiperidino]-2-oxoacetate (stabiliser 7);

______________________________________
Analysis: theory
C = 66.82% found C = 66.80%
H = 10.33% H = 10.32%
N = 4.10% N = 4.07%
______________________________________

3-dodecyl-8-(ethoxyoxalyl)-7,7,9,9-tetramethyl-1,3,8-triazaspiro[4.5]decane -2,4-dione (stabiliser 8) of formula ##STR9## m.p. 81°-82°C ethyl 2-(4-benzoyloxy-2,2,6,6-tetramethylpiperidino)-2-oxoacetate (stabiliser 9);

______________________________________
Analysis: theory
C = 66.46% found C = 66.33%
H = 7.53% H = 7.56%
N = 3.88% N = 3.90%
______________________________________

cyclohexanespiro-2'-[1-(ethoxyoxalyl)-1,3-diazolidin-4-one]-5'-spirocyclohe xane of formula ##STR10## (stabiliser 10), m.p. 211°-213°C bis[1-(ethoxyoxalyl)-2,2,6,6-tetramethylpiperidin-4-yl]adipate (stabiliser 11), m.p. 74°-76°C

Analogous reaction with oxalyl chloride gives the following compounds:

oxalyl di(4-benzoyl-2,2,6,6-tetramethyl)piperidide ##STR11## (stabiliser 12), m.p. 211°-214°C 1,1'-oxalyl-bis(2,2-pentamethylene-5,5-pentamethylene-1,3-diazolidin-4-one ##STR12## (stabiliser 13), m.p. 192°-193°C

A 750 ml sulfonating flask is charged with 49.7 g (0.19 mole) of 4-benzoyloxy-2,2,6,6-tetramethylpiperidine and 25.4 g (0.1 mole) of phenylacetic anhydride. The mixture is heated under nitrogen to 150°C and the resultant orange melt is stirred for 6 hours at this temperature. After this time, no more starting material can be detected in a thin-layer chromatogram (in ethyl acetate as eluant). The melt is allowed to cool and then dissolved in ethyl acetate. The solution is purified through a column of silica gel and concentrated by evaporation, affording a yellow resinous product (stabiliser 14) of formula ##STR13##

______________________________________
Analysis: theory
C = 75.96% found C = 75.75%
H = 7.70% H = 7.56%
N = 3.69% N = 3.17%
______________________________________

A two-layer metallic varnish is aplied to aluminium sheets. The undercoat (20 μm) consists of an aluminum-pigmented varnish based on a polyester/cellulose acetobutyrate/melamine resin mixture. A clear varnish (40 μm) based on a hydroxylated acrylic resin (Macrynal® SM 510 N, ex Hoechst AG) and a polyisocyanate (Desmodur® N 75, ex Bayer AG) is applied as topcoat. A solution of a stabiliser listed in Table 1 in a 1:1 mixture of ethylene glycol/xylene is added to the clear varnish. For curing, the samples are heated to 80°C for 45 minutes.

The samples are subjected to solar radiation in Florida (5° south) and the surface gloss is measured at 6 month intervals in accordance with ASTM Test Method D 523. An unstabilised sample of the same varnish serves as comparison.

TABLE 1
______________________________________
20° Gloss (%) after
Stabiliser
0 6 12 18 24 months
______________________________________
none 96 84 81 59 43
1% of 2 96 87 84 78 73
2% of 2 96 84 84 80 79
2% of 3 96 87 87 81 77
______________________________________

Samples are prepared using a two-layer metallic stoving varnish comprising an undercoat (20 μm) of an aluminium-pigmented polyester/cellulose acetobutyrate/melamine resin varnish and a topcoat of a clear varnish (40 μm) based on a thermosetting acrylic resin (Viacryl® VC 373, ex Vianova) and a melamine resin (Maprenal® MF 590, ex Hoechst AG) as crosslinking agent. A stabiliser listed in Table 2 is added to the acrylic resin. The samples are stoved for 30 minutes at 130°C

The samples are exposed in a Xenotest 1200 weathering device and the 20° gloss is measured at intervals of 800 hours in accordance with DIN 67 530. The results are reported in Table 2.

TABLE 2
______________________________________
20° Gloss (%) after
Stabiliser
0 800 1600 2400 3200 4000 h
______________________________________
none 81 53 26 20 -- --
1% of 5
87 65 52 35 23 19
1% of 6
88 77 55 42 31 26
______________________________________

Noticeable cracks occur in the samples without stabiliser after 2800 hours exposure to weathering, whereas cracks do not appear in the stabilised samples until after 5200 hours exposure.

Slongo, Mario, Berner, Godwin

Patent Priority Assignee Title
6465645, Apr 17 2001 Ciba Specialty Chemicals Corporation Long chain hindered amines and compositions stabilized therewith
6699298, Apr 17 2001 Ciba Specialty Chemicals Corporation Long chain hindered amines and compositions stabilized therewith
6755875, Apr 17 2001 Ciba Specialty Chemicals Corporation Long chain hindered amines and compositions stabilized therewith
6875870, Apr 17 2001 Ciba Specialty Chemicals Corporation Long chain hindered amines and compositions stabilized therewith
Patent Priority Assignee Title
4289686, Sep 27 1978 Ciba Specialty Chemicals Corporation Tetra-alkyl piperidine derivatives as light stabilizers
4344876, Jun 21 1978 Ciba Specialty Chemicals Corporation Stabilization of acid catalyzed stoving lacquers
4517283, Dec 16 1982 H A WHITTEN & CO , P O BOX 1368, NEW YORK, NY 10008, A PARTNERSHIP Color-photographic recording material
4552885, Dec 24 1981 Ciba Specialty Chemicals Corporation Stabilized fungicide compositions
4578454, May 08 1984 Ciba Specialty Chemicals Corporation Polyaminoamides containing polyalkylpiperidine radicals
4691015, Oct 11 1983 Ciba Specialty Chemicals Corporation Hydroxylamines derived from hindered amines
4692486, Oct 16 1981 Ciba Specialty Chemicals Corporation Synergistic mixture of low-molecular and high-molecular polyalkylpiperidines
4774332, Aug 14 1984 FIRST FIDELITY BANK, NATIONAL ASSOCIATION, NEW JERSEY, EXECUTIVE TRUSTEE UNDER THE SANDOZ TRUST OF MAY 4, 1955 Piperidine containing stabilizer compounds
4780494, Apr 13 1984 FIRST FIDELITY BANK, EXECUTIVE TRUSTEE UNDER SANDOZ TRUST OF MAY 4, 1955 Stable aqueous dispersions of tetraalkylpiperidines
GB2163158,
/
Executed onAssignorAssigneeConveyanceFrameReelDoc
Sep 25 1989Ciba-Geigy Corporation(assignment on the face of the patent)
Date Maintenance Fee Events


Date Maintenance Schedule
Dec 11 19934 years fee payment window open
Jun 11 19946 months grace period start (w surcharge)
Dec 11 1994patent expiry (for year 4)
Dec 11 19962 years to revive unintentionally abandoned end. (for year 4)
Dec 11 19978 years fee payment window open
Jun 11 19986 months grace period start (w surcharge)
Dec 11 1998patent expiry (for year 8)
Dec 11 20002 years to revive unintentionally abandoned end. (for year 8)
Dec 11 200112 years fee payment window open
Jun 11 20026 months grace period start (w surcharge)
Dec 11 2002patent expiry (for year 12)
Dec 11 20042 years to revive unintentionally abandoned end. (for year 12)