A novel tolan derivative compound as a liquid crystal substance having a low viscosity and a good compatibility with existing liquid crystals at low temperatures in addition to a large optical anisotropy value and a high clearing point, and a liquid crystal mixture containing the above compound are provided, which compound is expressed by the formula ##STR1## wherein R1 represents an alkyl group of 1 to 10 carbon atoms, R2 represents an alkyl group of 1 to 10 carbon atoms, X represents --CH2 CH2 -- and A represents an h atom or an f atom.

Patent
   RE34264
Priority
Aug 04 1986
Filed
Oct 18 1990
Issued
May 25 1993
Expiry
Oct 18 2010
Assg.orig
Entity
Large
0
14
all paid
5. A tolan derivative compound expressed by the formula ##STR16## wherein each of R1 and R2 independently represents an alkyl group of 2 to 5 carbon atoms.
1. A tolan derivative compound expressed by the formula ##STR14## wherein R1 represents an alkyl group of 1 to 10 carbon atoms, R2 represents an alkyl group of 1 to 10 carbon atoms, X represents --CH2 CH2 -- and A represents an h atom or an f atom.
4. A liquid crystal mixture comprising at least two components at least one of which is a tolan derivative compound expressed by the formula ##STR15## wherein R1 represents an alkyl group of 1 to 10 carbon atoms, R2 represents an alkyl group of 1 to 10 carbon atoms, X represents --CH2 CH2 -- and A represents an h atom or an f atom.
2. A tolan derivative compound according to claim 1 wherein A represents h.
3. A tolan derivative compound according to claim 1 wherein said X represents --CH2 CH2 -- and said A represents f.
6. A tolan derivative compound according to claim 5 wherein R1 and R2 are the same. 7. A tolan derivative compound according to claim 5 wherein R1 and R2 each comprise an ethyl group. 8. A tolan derivative compound according to claim 5 wherein R1 and R2 each comprise a propyl group. 9. A tolan derivative compound according to claim 5 wherein R1 comprises an ethyl group and R2 comprises a propyl group. 10. A tolan derivative compound according to claim 5 wherein R1 comprises an ethyl group and R2 comprises a butyl group. 11. A tolan derivative compound according to claim 5 wherein R1 comprises a propyl group and R2 comprises an ethyl group. 12. A tolan derivative compound according to claim 5 wherein R1 comprises a propyl group and R2 comprises a butyl group.
13. A liquid crystal mixture comprising at least two components, at least one of which is a tolan derivative compound expressed by the formula ##STR17## wherein each of R1 and R2 independently represents an
alkyl group of 2 to 5 carbon atoms. 14. A liquid crystal mixture according to claim 13 wherein R1 and R2 are the same. 15. A liquid crystal mixture according to claim 13 wherein R1 and R2 each comprise an ethyl group. 16. A liquid crystal mixture according to claim 13 wherein R1 and R2 each comprise a propyl group. 17. A liquid crystal mixture according to claim 13 wherein R1 comprises an ethyl group and R2 comprises a propyl group. 18. A liquid crystal mixture according to claim 13 wherein R1 comprises an ethyl group and R2 comprises a butyl group. 19. A liquid crystal mixture according to claim 13 wherein R1 comprises a propyl group and R2 comprises an ethyl group. 20. A liquid crystal mixture according to claim 13 wherein R1 comprises a propyl group and R2 comprises a butyl group.

This application is a reissue of Ser. No. 07/079,997 filed Jul. 13, 1987, U.S. Pat. No. 4,778,620.

1. Field of the Invention

This invention relates to a tolan derivative as a novel compound and a liquid crystal mixture containing the same.

2. Description of the Related Art

Display elements having liquid crystals applied thereto make use of the electrooptical effect exhibited by liquid crystal substances, and the display modes thereof include various ones such as those of TN (Twisted Nematic) type, DS (Dynamic Scattering) type, guest-host type, DAP type, etc.

While the properties required for liquid crystal substances used vary depending on these respective modes, the following properties are required in common therewith:

a property that liquid crystal phases are exhibited within as broad a temperature range as possible and a property that the liquid crystal substances are stable to moisture, heat, light, air, etc. At present, however, there is no single compound which satisfies all of such requirements; thus there have been used liquid crystal mixtures obtained by mixing several kinds of liquid crystal compounds or mixing compound(s) similar to liquid crystal compounds with several kinds of liquid crystal compounds.

As to tolan derivatives used as a component of liquid crystal materials, compounds expressed by the following formulas (1) to (3) are disclosed in (1) French patent application laid-open No. 2,141,438, (2) Japanese patent application laid-open No. Sho 60-152427/1985 and (3) Japanese patent application laid-open No. Sho 60-204731/1985, respectively: ##STR2## wherein R3 and R4 each represent an alkyl group or an alkoxy group. ##STR3## and R and R' each represent a linear chain alkyl group.

These tolan compounds are liquid crystal materials having specific features of a large optical anisotropy value (hereinafter abbreviated to Δn) and a high clearing point.

The object of the present invention is to provide a liquid crystal substance having a low viscosity and a good compatibility with existing liquid crystals at low temperatures in addition to the above-mentioned specific features and also to enhance the degree of freeness of choice of liquid crystal materials.

The present invention resides in a tolan derivative compound expressed by the formula ##STR4## wherein R1 represents an alkyl group of 1 to 10 carbon atoms, R2 represents an alkyl group or an alkoxy group each of 1 to 10 carbon atoms, X represents --CH2 CH2 -- or a single bond and A represents an H atom or an F atom provided that A represents an F atom in the case where X represents a single bond. The present invention is also directed to a liquid crystal mixture comprising at least two components at least one of which is said tolan derivative compound.

The embodiments of the present invention include compounds expressed by the following group of formulas: ##STR5## wherein R1 and R2 are as defined above.

These compounds are liquid crystalline compounds having a slightly negative dielectric anisotropy value.

Preferred compounds among those expressed by the formula (I-a) are those wherein R1 represents ethyl, propyl, butyl or pentyl and R2 represents methyl, ethyl, propyl, butyl, pentyl, methoxy, ethoxy, propoxy, butoxy or pentyloxy in the formula (I-a).

For example, 4-(trans-4-propylcyclohexyl)-1-ethyl)-4'-ethyltolan shown in Example 1, described later, is a liquid crystal compound having a large Δn value, a very low viscosity and a braod nematic range and it can constitute a nematic liquid crystal material having various specific features well balanced.

Preferred compounds among those expressed by the formula (I-b) are those wherein R1 represents ethyl, propyl, butyl or pentyl and R2 represents ethyl, propyl, butyl or pentyl in the formula. The tolan derivatives expressed by the formula (1-a) or (1-b) are characterized in that an ethylene group is introduced into a core structure having three six-membered rings bonded linearly. It is presumed that by introducing the ethylene group, a relatively low melting point (i.e. the lower limit temperature of a mesomorphic phase) and a low viscosity have been realized in the compounds of (I-a) and (I-b). Further, it is also presumed that as to be compounds of the formula (I-b), introduction of a fluorine atom as a lateral substituent into the central phenylene ring of the compound of the formula (I-a) may have realized increase in the nematic range and decrease in the smectic range without increasing the viscosity so much as compared to the compound of the formula (I-a). The compound (I-b) is also a nematic liquid crystal having a large Δn value and a low viscosity as in the case of the compound (I-a).

Preferred compounds among those of the formula (I-c) are those wherein R1 or R2 represents ethyl, propyl, butyl or pentyl. Some compounds of the formula (I-c), wherein both R1 and R2 have a long chain alkyl group, have a high viscosity so that such compounds are for practical reasons not particularly preferred. In the compounds of the formula (I-c) the melting point and the clearing point are lowered by a fluorine substitution at a lateral position of the central phenylene ring. Further, as to compounds expressed by the formulas (I-b) and (I-c), a fluorine substitution at a lateral position of the central phenylene ring improves the compatibility of the compound with other liquid crystals at low temperatures.

The compounds of the present invention can be prepared for example according to the following preparation scheme, R1, R2, X and A therein being as defined above: ##STR6##

A substituted benzene compound expressed by the formula (II) is first reacted with a 4-substituted-phenylacetyl chloride and anhydrous aluminum chloride in carbon disulfide to obtain a ketone derivative of the formula (III), which is then reacted with a reducing agent such as lithium aluminum hydride in an anhydrous solvent such as ether or tetrahydrofuran to obtain a compound of the formula (IV). Successively this alcohol derivative is subjected to dehydration reaction in the presence of a catalyst mentioned later in an inert organic solvent under atmospheric pressure and at a reflux temperature to obtain an ethylene derivative of the formula (V). As the inert organic solvent, benzene, toluene, chloroform, carbon tetrachloride, methylene chloride, etc. are suitable, and as the catalyst, Lewis acids such as aluminum chloride, tin tetrachloride, titanium tetrachloride, etc., mineral acids such as sulfuric acid, phosphoric acid, etc., toluenesulfonic acid, etc. are usable.

Successively bromine is attached onto the ethylene derivative of the formula (V) in a solvent such as methylene chloride, ethylene chloride, carbon tetrachloride, etc. to obtain a compound of the formula (VI), which is reacted with potassium tertiary-butoxide in tetrahydrofuran solvent, followed by a series of generally known purification procedures of extraction, washing, recyrstallizatuon, etc. to obtain the objective compound of the formula (I). The reactions of the respective steps are known, but the overall reactions are novel.

The substituted benzene of the formula (II) as the starting raw material is obtained by applying a known reaction to an easily commercially available raw material. Namely, a substituted benzene of the formula (II) wherein X represents an ethylene group is obtained by reducing a ketone derivative obtained by a Friedel-Crafts reaction of a trans-4-alkylcyclohexylacetyl chloride with benzene or by coupling reaction of a trans-4-alkylcyclohexylacetyl chloride with bis(3-fluorophenyl)cadmium, while a substituted benzene of the formula (II) wherein X represents a single bond is obtained by subjecting a substituted cyclohexanol obtained by a Grignard reaction of 3-fluorophenylmagnesium bromide with a 4-alkylcyclohexanone, to a dehydration reaction and then a hydrogenation reaction.

Preferred representative examples of liquid crystal compounds used as components of the liquid crystal mixture of the present invention admixture with the compound expressed by the formula (I) are

4-substituted-phenyl 4'-substituted-benzoates,

4-substituted-phenyl 4'-substituted-cyclohexanecarboxylates,

4'-substituted-biphenyl-4-yl 4"-substituted-cyclohexanecarboxylates,

4-substituted-phenyl 4'-(4-substituted-cyclohexanecarbonyloxy)benzoates,

4-substituted-phenyl 4'-(4-substituted-cyclohexyl)benzoates,

4-substituted-cyclohexyl 4'-(4-substituted-cyclohexyl)benzoates,

4,4'-substituted-biphenyls,

4,4'-substituted-phenylcyclohexanes,

4,4"-substituted-terphenyls,

4,4"-substituted-biphenyl-4'-yl-cyclohexanes,

2-(4'-substituted-phenyl)-5-substituted-pyrimidines, etc.

Compounds having lateral substituent(s) of halogen atom(s) or cyano group(s) on the phenylene ring(s) of the above-mentioned compounds may also be used as components of the liquid crystal mixture of the present invention.

As is generally known, in a liquid crystal display element, the product of the cell thickness (d) and the optical anisotropy value (Δn) of the liquid crystal material employed must be set to a specified value in order to prevent an interference fringe on the cell surface which deteriorates the view of the display. In practice, the value of Δn×d has been set to any one of 0.5, 1.0, 1.6 or 2.2. Since the value of Δn×d is set to definite values as described above, if a liquid crystal material having a large Δn value is used, it is possible to reduce the d value. When the d value is reduced, the response time is reduced. Thus, liquid crystal materials having a large Δn value are important for preparing a liquid crystal display cell having a high response rate and no interference fringe. Further, in order to reduce the response time, a low viscosity is also necessary.

The compounds corresponding to formula (I) of the present invention are novel nematic liquid crystal compounds having a large Δn value (ca. 0.26), a high N-I transition point and further a low viscosity (ca. 16 cp at 20°C). Thus, when a compound of the formula (I) of the present invention is mixed with various mother liquid crystals, it is possible to prepare a practical liquid crystal material having a low viscosity, a large Δn value and a high N-I transition point.

The present invention will be described more concretely by way of examples, but it should not be construed to be limited thereto.

In addition, symbols C-S point, C-N point, S-N point and N-I point in the examples refer to crystalline-smectic transition point, crystalline-nematic transition point, smectic-nematic transition point and nematic-isotropic liquid transition point, respectively.

PAC 4-(Trans-4-propylcyclohexyl-1-ethyl)-4'-ethyltolan

Anhydrous aluminum chloride (27.7 g, 0.21 mol) was added to carbon disulfide (160 cc), followed by adding 4-ethylphenylacetyl chloride (31.7 g, 0.174 mol) under cooling, successively adding trans-4-propylcyclohexylethylbenzene (40 g, 0.174 mol) over about one hour, thereafter agitating the reaction mixture at room temperature for 10 hours, distilling off carbon disulfide, adding the residue to dilute hydrochloric acid aqueous solution, decomposing the resulting aluminum chloride complex with stirring for one hour, extracting the resulting raw crystals with toluene (100 cc), washing with water, drying, distilling off toluene and recrystallizing the remaining solids from ethyl acetate to obtain the following compounds (35.3 g): ##STR7##

This compound was dissolved in anhydrous tetrahydrofuran (50 cc), followed by dropwise adding the solution to a solution of lithium aluminum hydride (2.7 g, 0.07 mol) in anhydrous tetrahydrofuran (100 cc), further agitating the mixture at 0°C for one hour, thereafter adding 20 wt. % sulfuric acid (50 cc) to the reaction mixture to dissolve the inorganic substance, extracting the separated oily substance with toluene (100 cc), washing the separated toluene solution with 10% sodium hydrogen carbonate aqueous solution, further washing with water until the washing water became neutral, drying the resulting toluene solution with anhydrous sodium sulfate, adding p-toluenesulfonic acid (1.8 g), heating the mixture under reflux, removing the formed water to the outside of the system, allowing the resulting material to cool down to room temperature after completion of the reaction, washing the toluene solution with water until the washing water became neutral, drying the toluene solution with anhydrous sodium sulfate, distilling off toluene and recrystallizing the remaining solids from ethyl acetate to obtain the following compound (25 g): ##STR8##

This product exhibited liquid crystal phases and the transition points were as follows: C-S point: 143.9°C, S-N point: 151.3°C and N-I point: 197.9°C

This compound was dissolved in methylene chloride (150 cc), followed by dropwise addition of bromine (11.0 g, 0.069 mol) at room temperature and reaction of the mixture for one hour, thereafter distilling off methylene chloride and recrystallizing the remaining solids from n-heptane to obtain the following compound (24.5 g): ##STR9##

This compound was then dissolved in anhydrous tetrahydrofuran (100 cc), followed by adding potassium tertiary-butoxide (22.5 g, 0.20 mol), agitating the mixture at 40°C for 2 hours, thereafter adding water (200 cc) to the reaction mixture, extracting the separated raw crystals with toluene (100 cc), washing with water, drying, distilling off toluene and recrystallizing the remaining solids from ethyl acetate to obtain the following compound (15.0 g): ##STR10##

This compound exhibited liquid crystal phases and the transition points were as follows: C-S point: 68.7°C, S-N point: 74.1°C and N-I point: 161.8°C

Tolan derivatives obtained in the same manner as in Example 1 and their phase transition points are shown in Table 1 together with the results of Example 1.

TABLE 1
______________________________________
##STR11##
Phase transition point (°C.)
C-S point
or
Example
R1 R2 C-N point
S-N point
N-I point
______________________________________
1 n-C3 H7
C2 H5
68.7 74.1 161.8
2 C2 H5
CH3
84.3 144.1
3 C2 H5
C2 H5
69.4 141.2
4 C2 H5
n-C3 H7
66.1 149.2
5 C2 H5
n-C4 H9
59.1 62.3 137.4
6 n-C3 H7
CH3
83.6 169.1
7 n-C3 H7
n-C3 H7
67.1 77.6 166.6
8 n-C3 H7
n-C4 H9
36.4 90.0 158.8
9 n-C4 H9
CH3
85.6 (77.8) 162.3
10 n-C4 H9
C2 H5
69.5 92.7 155.7
11 n-C4 H9
n-C3 H7
65.6 94.2 161.6
12 n-C4 H9
n-C4 H9
59.8 103.1 152.5
13 n-C5 H11
CH3
91.7 (85.6) 165.3
14 n-C5 H11
C2 H5
81.5 100.4 158.0
15 n-C5 H11
n-C3 H7
67.9 112.1 165.4
16 n-C5 H11
n-C4 H9
55.2 119.9 156.3
______________________________________

In Table 1 and the succeeding Tables 2 and 3, the symbol () indicates a monotropic transition point.

Compounds shown in Table 2 were obtained from 3-(trans-4-alkylcyclohexylethyl)fluorobenzenes and 4-substituted-phenylacetyl chlorides in the same manner as in Example 1.

TABLE 2
______________________________________
##STR12##
Phase transition point (°C.)
C-S point
or
Example
R1 R2 C-N point
S-N point
N-I point
______________________________________
17 C2 H5
n-C3 H7
36.0 135.2
18 C2 H5
n-C4 H9
26.1 126.5
19 n-C3 H7
CH3
73.2 158.3
20 n-C3 H7
C2 H5
50.8 149.8
21 n-C3 H7
n-C3 H7
50.2 155.5
22 n-C3 H7
n-C4 H9
42.0 148.6
23 n-C4 H9
C2 H5
58.3 147.8
24 n-C4 H9
n-C3 H7
56.5 (43.5) 155.1
25 n-C4 H9
n-C4 H9
50.4 71.8 147.1
______________________________________

Compounds shown in Table 3 were obtained from 3-(trans-4-alkylcyclohexyl)fluorobenzenes and 4-substituted-phenylacetyl chlorides in the same manner as in Example 1.

TABLE 3
______________________________________
##STR13##
Phase transition
point (°C.)
Example R1 R2 S-N point
N-I point
______________________________________
26 n-C3 H7
CH3
103.5 198.0
27 n-C3 H7
C2 H5
78.3 191.0
28 n-C3 H7
n-C3 H7
79.1 199.3
29 n-C3 H7
n-C4 H9
50.5 187.7
30 C2 H5
C2 H5
50.6 166.9
31 C2 H5
n-C3 H7
49.8 175.8
32 C2 H5
n-C4 H9
49.3 162.1
______________________________________

A liquid crystal mixture A consisting of

______________________________________
trans-4-propyl-(4-cyanophenyl)
30% by weight.
cyclohexane
trans-4-pentyl-(4-cyanophenyl)
40% by weight.
cyclohexane
and
trans-4-heptyl-(4-cyanophenyl)
30% by weight
cyclohexane
______________________________________

has a N-I point of 52.1°C, a viscosity of 20°C of 22.4 cp and an optical anisotropy value Δn of 0.119.

When 4-(trans-4-propylcyclohexyl-1-ethyl)-4'-ethyltolan (15 parts by weight) as a compound of the present invention shown in Example 1 was added to the liquid crystal mixture A (85 parts by weight), the N-I point of the resulting liquid crystal mixture rose to 68.0°C, the viscosity at 20°C thereof lowered to 19.0 cp and the optical anisotropy value Δn thereof rose to 0.142.

Further, even when this liquid crystal mixture was allowed to stand at -30°C for 30 days, no deposition of crystal occurred.

When 2-fluoro-4-(trans-4-propylcyclohexyl-1-ethyl)-4'-ethyltolan (15 parts by weight) as a compound of the present invention shown in Example 20 was added to the liquid crystal mixture A (85 parts by weight) used in Example 33, the N-I point of the resulting liquid crystal mixture rose to 65.0°C, the viscosity at 20°C thereof lowered to 20.8 cp and the optical anisotropy value Δn rose to 0.140.

Further, even when this liquid crystal mixture was allowed to stand at -30°C for 30 days, no deposition of crystal occurred.

When 2-fluoro-4-(trans-4-propylcyclohexyl)-4'-ethyltolan (15 parts by weight) as a compound of the present invention shown in Example 27 was added to the liquid crystal mixture A (85 parts by weight) used in Example 33, the N-I point of the resulting liquid crystal mixture rose to 66.7°C, the viscosity at 20°C lowered to 21.0 cp and the optical anisotropy value Δn rose to 0.140.

Further, even when this liquid crystal mixture was allowed to stand at -30°C for 30 days, no deposition of crystal occurred.

It can be seen from these Examples that the compound of the formula (I) of the present invention can raise the N-I point of the mother liquid crystals up to a practically sufficient value, can raise the Δn thereof and yet can reduce the viscosity thereof and also is a liquid crystal material having a superior compatibility at low temperatures.

When 4-(trans-4-propylcyclohexyl)-4'-ethyltolan (15 parts by weight) as one of tolan derivatives shown in the formula (2) as a prior art was added to the liquid crystal mixture A (85 parts by weight) used in Example 33, the N-I point of the resulting liquid crystal mixture rose to 68.3°C, the viscosity at 20°C thereof was 22.8 cp and the optical anisotropy value thereof rose to 0.141, but when the mixture was allowed to stand at -30°C, deposition of crystal occurred in only one day.

When 4-(4-propylphenyl)-4'-ethyltolan (15 parts by weight) as one of tolan derivatives shown in the formula (2) as a prior art was added to the liquid crystal mixture A (85 parts by weight) used in Example 33, the N-I point of the resulting liquid crystal mixture rose to 70.3°C and the Δn thereof rose to 0.145, but the viscosity at 20°C thereof also rose to 28.0 cp. When this liquid crystal mixture was allowed to stand at -30°C, deposition of crystal occurred in only 5 hours .

Goto, Yasuyuki, Ogawa, Tetsuya

Patent Priority Assignee Title
Patent Priority Assignee Title
3925482,
4400293, Oct 29 1980 Merck Patent Gesellschaft Mit Beschrankter Haftung Liquid crystalline cyclohexylphenyl derivatives
4528114, Dec 18 1981 Merck Patent Gesellschaft Mit Beschrankter Haftung Acetylenes
4583826, Oct 19 1981 Merck Patent Gesellschaft Mit Beschrankter Haftung Phenylethanes
4705870, Jan 23 1984 Dainippon Ink and Chemicals, Inc. Tolan-type nematic liquid crystalline compounds
4705905, Jan 23 1984 Dainippon Ink and Chemicals, Inc. Tolan-type nematic liquid crystalline compounds
4713468, Jan 23 1984 Dainippon Ink and Chemicals, Inc. Tolan-type nematic liquid crystalline compounds
4726910, Jan 23 1984 Dainippon Ink and Chemicals, Inc. Tolan-type nematic liquid crystalline compounds
4788363, Jul 17 1986 Dainippon Ink and Chemicals, Inc. Nematic methyltolans
4816180, Jan 20 1987 Chisso Corporation Novel tolan type liquid crystal compound
EP84194,
FR2234261,
GB2155465,
JP63250332,
/
Executed onAssignorAssigneeConveyanceFrameReelDoc
Oct 18 1990Chisso Corporation(assignment on the face of the patent)
Date Maintenance Fee Events
Apr 05 1996M184: Payment of Maintenance Fee, 8th Year, Large Entity.
May 08 1996ASPN: Payor Number Assigned.
Apr 12 2000M185: Payment of Maintenance Fee, 12th Year, Large Entity.


Date Maintenance Schedule
May 25 19964 years fee payment window open
Nov 25 19966 months grace period start (w surcharge)
May 25 1997patent expiry (for year 4)
May 25 19992 years to revive unintentionally abandoned end. (for year 4)
May 25 20008 years fee payment window open
Nov 25 20006 months grace period start (w surcharge)
May 25 2001patent expiry (for year 8)
May 25 20032 years to revive unintentionally abandoned end. (for year 8)
May 25 200412 years fee payment window open
Nov 25 20046 months grace period start (w surcharge)
May 25 2005patent expiry (for year 12)
May 25 20072 years to revive unintentionally abandoned end. (for year 12)