A method of preparing alloy of a transition metal and lanthanide comprising the steps of alloying a transition metal, boron, at least one lower-weight lanthanide having none or few stable compounds with iron, optionally one or more higher-weight lanthanides, a glass former, and optionally the pseudo lanthanide, yttrium; forming an amorphous or nearly amorphous metastable microstructure in the alloy; and heating the amorphous alloy to form a polycrystalline, multiphase, fine-grain single-domain structure.
|
1. A method of preparing a hard magnetic polycrystalline alloy which comprise the steps of preparing an alloy represented by the formula:
(Mw Xx B1-w-x)1-y (Yv RL1-v-z)y (Mw Xx B1-w-x)1-y (Yv R'z l1-v-z)y wherein v is from 0 to 0.8, w is from about 0.7 to about 0.98; x is from 0 to about 0.15; y is from about 0.05 to about 0.25; z z is from 0 to about 0.95; M is selected from the class group consisting of iron, cobalt, an iron-cobalt alloy, an iron-manganese alloy having at least 50 atomic percent iron, an iron-cobalt-manganese alloy having at least 50 atomic percent iron and cobalt, X is an auxillary auxiliary glass former selected from the class group consisting of phosphorous, silicon, aluminum, arsenic, genmanium germanium, indinum indium, antimony, bismuth, tin and mixtures thereof, R' is a heavier-weight lanthanide selected from the group consisting of europium and lanthanides having heavier than europium and l is a lighter weight lanthanide selected from the group consisting of cerium, praseodymium, neodymium samarium, said alloy having a polycrystalline, multiphase, single-domain microstructure wherein the average crystal-grain size does not exceed 400 A Å; creating an amorphous microstructure in said alloy; and heating said alloy at a temperature from about 850 to 1200 K. in a magnetic field of at least one kOe until a polycrystalline microstructure is obtained. 2. The method of
3. The method of
4. The method of
5. The method of
6. The method of
7. The method of
8. The method of
9. The method of
10. The method of
11. The method of
12. The method of
13. The method of
14. The method of
15. The method of
16. The method of
17. The method of
21. The method of
(Mw Xx B1-w-x)-1-y (Yv R'z l1-v-z)y wherein v is from 0 to 0.8, w is from about 0.7 to about 0.98; x is from 0 to about 0.15; y is from about 0.05 to about 0.25; z is from 0 to about 0.95; M is selected from the class consisting of iron, cobalt, an iron-cobalt alloy, an iron-cobalt alloy, an iron-manganese alloy having at least 50 atomic percent iron, an iron-cobalt-manganese alloy having at least 50 atomic percent iron and cobalt, X is an auxiliary glass former selected from the class consisting of phosphorous, silicon, aluminum, arsenic, germanium, indium, antimony, bismuth, tin and mixtures thereof, R' is a heavier-weight lanthanide selected from the group consisting of europium and lanthanides heavier than europium and l is a mixture of lanthanum and an amount of a lighter weight lanthanide selected from the group consisting of praseodymium and neodymium effective to enhance the magnetic properties of said alloy, said alloy having a polycrystalline, multiphase, single-domain microstructure wherein the average crystal-grain size does not exceed 400Å; creating an amorphous microstructure in said alloy; and heating said alloy at a temperature from about 850 to 1200 K in a magnetic field of at least one kOe until a polycrystalline microstructure is obtained. |
|||||||||||||||||||||||||||||||||
This is a
(Mw Xx B1-w-x)1-y (Yv R'2 L1-x-z)y
wherein v is 0 to 0.8; w is from about 0.7 to about 0.98; x is from 0 to about 0.15; y is from about 0.05 to about 0.25; z is from 0 to about 0.95; M is selected from the class consisting of iron, cobalt, an iron-cobalt alloy, an iron-manganese alloy having at least 50 atomic percent iron, and an iron-cobalt-manganese alloy having at least 50 atomic percent iron and cobalt, X is a glass former selected from the class consisting of phosphorous, arsenic, germanium, gallium, indium, antimony, bismuth, tin, carbon, silicon, and aluminum; R' is a higher-weight lanthanide (europium or heavier), and is L is a lower-weight lanthanide selected from the group consisting of lanthanium, cerium, praseodymium, neodymium, and samarium.
The lower-weight lanthanide (L) must be present to obtain amorphicity or near amorphicity in the intermediate alloys. The lower-weight lanthanides are characterized by their ironic structure being larger than the heavier-weight lanthanides, and their reduced ability to form stable compounds with iron. In addition to promoting amorphicity in the intermediate alloys, the lanthanides appear to also promote small crystal structure in the final alloys. A transistion metal-boron-lanthanide alloy with only lanthanum is not preferred as a hard magnet because of poor magnetic properties.
Any heavier-weight lanthanide (R') can be used, but many have poor magnetic properties, are expensive, or are difficult to process. The nonpreferred lanthanides are europium, gadolinium, ytterbium, and lutetium.
Yttrium can be added for a lighter-weight lanthanide. It is often referred to a pseudo lanthanide, yttrium can be added in a relative amount (v) of up to 0.8. If it is added, the preferred relative amount is from 0.05 to 0.6.
The preferred selection of lanthanides with or without yttrium has an average molecular volume from 20.7 to 21.0 cc/mole and the most preferred combinations have a molecular volume from 20.8 to 20.95 cc/mole. In the usual case, selections involve combinations of one or more lighter-weight lanthanides with one or more heavier-weight lanthanides. Other combinations include lanthanium with one or more other lighter-weight lanthanides and yttrium with one or more lanthanides. Prelimary tests show the average molecular volume is a major factor in determining the performance of the resulting hard magnets. A substantial number of preferred alloy compositions has z from 0.2 to 0.8. If the amount of the heavier-weight lanthanide is relatively high, ie. the average molecular volume is below the preferred range, the difficulty in obtaining amorphicity can be overcome by increasing the amount of the auxiliary glass former and/or boron and carefully processing the alloy. It should be noted that these measures are successful; if, the alloy composition is within the afore-said ranges.
Iron is the preferred metal for M. Other elements and alloys can also be used, such as cobalt, iron-cobalt alloys, and iron-manganese alloys. The preferred amount of cobalt and iron is from 0.70 to 0.86 and most preferably 0.7 to 0.8. The alloys are represented as
(1) Fea Co1-a wherein a is from about 0.01 to about 0.99; and preferably from 0.7 to 0.95;
(2) Feb Mn1-b wherein b is greater than 0.5 but less than 1.0 and preferably is greater than 0.7 but less than or equal to 0.95;
(3) Fea Coe wherein (d+e) is from about 0.5 to less than about 1.0 and preferably from 0.75 to 0.95 and d is greater than e and preferably is more than two times greater than e.
The auxillary glass formers increase the amount of lanthanide which can be included without eliminating the amorphous microstructure. The most common glass formers are phosphorous, silicon, arsenic, germanium, carbon, indium, antimony, bismuth, tin, and mixtures thereof. The preferred auxillary glass formers are phosphorus, silicon, and carbon. The preferred amount of auxillary glass former which can be added is from about 0 to about 0.1.
The amounts of the lanthanide with or without yttrium is from about 0.05 to about 0.22 of the total alloy and preferably is from 0.05 to 0.20. It is possible to form alloys with a lanthanum-lanthanide amount greater than 0.15, depending on the lanthanide, the relative amounts of iron and boron, the presence of a glass former, and the processing parameters.
All the amounts in a subgroup are expressed in atomic concentrations in that subgroup and not of the alloy. Only the subscript (y) represents a portion of the total alloy. For an alloy having M representing Fe0.5 Co0.3 Mn0.2 w equaling 0.7, x equaling O, R representing neodymium, z equaling 0.5, and y equaling 0.1, then the formula for the alloy would be ((Fe0.5 Co0.3 Mn0.7 B0.3)0.9 (Nd0.5 La0.5)0.1.
The amorphous alloys from which the polycrystalline alloys are prepared can be prepared by rapidly cooling a melt having the desired composition. A cooling rate of at least about 5×104 C/sec. and preferably at least 1×106 C/sec.
Examples of techniques for cooling thin sections include ejecting molten alloy onto a rapidly rotating inert surface, e.g., a highly polished copper wheel, ejecting molten alloy between two counterrotating rollers, vapor deposition or electrolytic deposition on a cold surface. The preferred technique is ejecting the molten alloy onto the surface of a polished, copper wheel rotating at a rate of at least 200 rpm.
The polycrystalline alloys of this invention are prepared from the above amorphous alloys by heating the alloys in an inert atmosphere at a temperature from about 850 to about 1200 K. and preferably from 950 to 1050K. until the desired microstructure is obtained. The preferred inert atmosphere is a vacuum or argon with or without a getter, such as tantalum. The alloys can be cooled at any rate and by any method. Of course, the preferred method is to let the alloy cool to room temperature by removing the heat from the alloy. The maximum average grain size is about 400 A and preferably is from 100 to 200 A.
The alloy is magnetized either by cooling the alloy after preparation in a magnetic field of at least one kOe, preferably of at least three kOe and most preferably at least 15 kOe or by applying a magnetic field of at least about 25 kOe and preferably of at least 30 kOe after the alloy is cooled. The length of exposure to the magnetic field depends on the strength of the field and the size of the sample. It can be empirically determined by routine experimentation.
To better illustrate the present invention the following examples are given by way of demonstration and are not meant to limit this disclosure or the claims to follow in any manner.
Amorphous alloys, from which the examples were prepared, were prepared by weighing out appropriate amounts of the elemental constituents having a nominal purity of at least 99.9 at %. The constituents were then melted together in an electric arc furnace under an atmosphere of purified Ar. Each ingot was turned and remelted repeatedly to ensure homogeneity.
A portion of each homogenized ingot was placed in a quartz crucible having a diameter of 10-11 mm. and a small orifice at the end of approximate diameter 0.35 mm. The quartz tube was flushed with Ar gas to prevent oxidation during heating. The ingot was then heated to the melting point by an induction furnace, then ejected onto a rapidly rotating copper wheel by raising the Ar pressure to about 8 psi. The copper wheel was ten inches in diameter and rotated at an approximate speed of 2500 RPM. The surface of the wheel was polished by using 600 grit emery paper for the final finish. The resulting ribbons were approximately 1 mm in width and 15 microns in thickness.
The morphous alloys are prepared in the manner described in U.S. Pat. No. 4,374,665 which is herein incorporated by reference.
A ribbon (8-10mg) of one of the amorphous alloys prepared by the previous method was wrapped in Tc foil, was sealed in an evacuated 3 cc quart tube tube sealed and heated by means of a heating coil to 925K. in 16 hours in a magnetic field of 1.4 kOe. Free-standing the quartz tube cooled the sample to room temperature. After cool down the ribbon was taken out for measurement of the intrinsic coercive force.
The coercive force was measured using a vibrating sample magnetometer. The magnetic field was first applied parallel to the spontaneous moment, then raised to 15 k Oe. The moment was then measured as a function of applied field as the field was reduced, then reversed to the maximum field of the magnet, then brought back up again. The intrinsic coercive force is the reverse field required to reduce the magnetization to zero on the initial reversal. The results, along with the alloy composition are summarized in Table I.
| TABLE I |
| ______________________________________ |
| Alloy Intrinsic Coercive Force (Oe) |
| ______________________________________ |
| (Co.74 Fe.06 B.20).94 Sm.01 |
| 930 |
| (Co.74 Fe.06 B.20).95 Sm.02 La.03 |
| 1120 |
| (Fe.82 B.18).95 Tb.03 La.02 |
| 3000 |
| (Co.74 Fe.06 B.20).94 Sn.03 La.03 |
| 1670 |
| (Fe.82 B.18).9 Tb.05 La.05 |
| 8500 |
| (Fe.82 B.18).9 Sm.05 La.05 |
| 600 |
| (Fe.85 B.15).9 Tb.05 La.05 |
| 9400 |
| (Fe.88 B.12).9 Tb.05 La.05 |
| 9600 |
| (Fe.82 B.18).9 Tb.06 La.04 |
| 8400 |
| ______________________________________ |
Samples of polycrystalline hard magnetic alloys were prepared by two other methods.
A ribbon (4-6 mg) of Fe0.82 B0.18)0.9 Tb0.05 prepared by the previous method was placed inside a partially flattened thin-wall tantalum tube of about 1 mm. diameter. The tantalum tube was folded into a length of about 4 mm. The folded tantalum with the ribbon inside was sealed into one end of an evacuated quartz tube. The purpose of the tantalum was to protect the ribbon from oxidation and prevent a reaction with gases relased during heat. The tube was heated to some specific temperature for one hour, then cooled to room temperature in a small magnetic field of about 2 kOe. Upon cooling, the ribbon was tested as before. The ribbon was then heated to a temperature 25 K. higher than before, treated for one hour, then cooled and measured again. This was continued until 1100 K. was reached. The results are presented in FIG. 1. The intrinsic coercive force rises to about 8.5 kOe at an anneal temperature of 925 K., then drops rapidly at higher temperatures. The coercive force depended mainly on the highest anneal temperature rather than the detailed history of the process. For example, a 16 hour anneal at 925 K. gave a magnetization loop essentially the same the above sample.
In FIG. 2 a typical magnetization curve taken at 300 K. on Fe0.82 B0.18)0.9 Tb0.05 La0.05 heat treated for 16 hours at 925 K. in a magnetic field of about two kOe is presented. The slight offset in the curve is due to a field cooling effect and disappears upon a few cycles of the field. For this alloy an intrinsic coercive force of 9 kOe, is achieved more or less independent of the details of the anneal. The one hour step anneal procedure, for example, yields an almost identical result when the maximum anneal temperature is 925 K. The shape of the magnetization curve clearly reflects the multiphase character of the sample. The amount of high coercive force phase varies somewhat from sample to sample and appears to be more sensitive to the Fe/B ratio than to the quenching procedures.
A small ribbon (4-6mg) of (Fe0.82 B0.18)0.9 Tb0.25 La0.05 prepared by the previous method, was placed inside a 50 c.c. quartz tube evacuated dynamically by a diffusion pump. The tube was placed in a furnace at 1200 K. for 0.5 to 1.5 minutes. Upon cooling the ribbon was placed in magnetic field 20 kOe for thirty minutes. The intrinsic force was measured as before. A two-minute anneal at 1200 K. produced an alloy with a lower intrinsic force, indicating that a longer heating at the high temperature causes unfavorable grain growth.
The procedure of example 1 was repeated exactly for the following alloy: Feb.833 B0.042 Nd0.125.
A ribbon (8-10 mg) of the amorphous alloy prepared by the previous method was wrapped in tantalum foil, sealed in an evacuated 3 mm-diameter quartz tube and heated by means of a heating coil to 923 K. in 16 hours in a magnetic field of 1.4 kOe. Free-standing the quartz tube cooled the sample to room temperature. After cool-down the ribbon was taken out for measurement of the intrinsic coerive force.
The procedure of example 3 was repeated except that this magnetic field was 15 kOe.
It is clear from these data that the proposed procedure can produce potentially useful coercive behavior from a wide class of rare earth containing amorphous alloys, particularly those with La, which in a number of cases is required to make the initial alloy amorphous by melt.
Obviously many modifications and variations of the present invention are possible in light of the above teachings. It is therefore to be understood that within the scope of the appended claims the invention may be practiced otherwise than as specifically described.
| Patent | Priority | Assignee | Title |
| 6125912, | Feb 02 1998 | Battelle Energy Alliance, LLC | Advanced neutron absorber materials |
| 6332933, | Dec 31 1997 | SANTOKU CORPORATION | Iron-rare earth-boron-refractory metal magnetic nanocomposites |
| 6352599, | Jul 13 1998 | SANTOKU CORPORATION | High performance iron-rare earth-boron-refractory-cobalt nanocomposite |
| 7785428, | Nov 09 2000 | Battelle Energy Alliance, LLC | Method of forming a hardened surface on a substrate |
| 8097095, | Nov 09 2000 | Battelle Energy Alliance, LLC | Hardfacing material |
| Patent | Priority | Assignee | Title |
| 3982971, | Feb 21 1974 | Shin-Etsu Chemical Co., Ltd | Rare earth-containing permanent magnets |
| 4065330, | Sep 26 1974 | The Foundation: The Research Institute of Electric and Magnetic Alloys | Wear-resistant high-permeability alloy |
| 4222770, | Mar 31 1978 | Agency of Industrial Science & Technology; Ministry of International Trade & Industry | Alloy for occlusion of hydrogen |
| 4402770, | Oct 23 1981 | The United States of America as represented by the Secretary of the Navy; UNITED STATES OF AMERICA AS REPRESENTED BY THE SECRETARY OF THE NAVY, | Hard magnetic alloys of a transition metal and lanthanide |
| 4851058, | Sep 03 1982 | MAGNEQUENCH INTERNATIONAL, INC | High energy product rare earth-iron magnet alloys |
| JP5641345, | |||
| JP5672153, | |||
| JP58123853, |
| Executed on | Assignor | Assignee | Conveyance | Frame | Reel | Doc |
| Jan 31 1989 | The United States of America as represented by the Secretary of the Navy | (assignment on the face of the patent) | / |
| Date | Maintenance Fee Events |
| Aug 06 1996 | M185: Payment of Maintenance Fee, 12th Year, Large Entity. |
| Date | Maintenance Schedule |
| Jul 27 1996 | 4 years fee payment window open |
| Jan 27 1997 | 6 months grace period start (w surcharge) |
| Jul 27 1997 | patent expiry (for year 4) |
| Jul 27 1999 | 2 years to revive unintentionally abandoned end. (for year 4) |
| Jul 27 2000 | 8 years fee payment window open |
| Jan 27 2001 | 6 months grace period start (w surcharge) |
| Jul 27 2001 | patent expiry (for year 8) |
| Jul 27 2003 | 2 years to revive unintentionally abandoned end. (for year 8) |
| Jul 27 2004 | 12 years fee payment window open |
| Jan 27 2005 | 6 months grace period start (w surcharge) |
| Jul 27 2005 | patent expiry (for year 12) |
| Jul 27 2007 | 2 years to revive unintentionally abandoned end. (for year 12) |