A composition comprising (a) at least one oxidized polycationic polyheteroaromatic compound and (b) at least one polyanion of a film-forming thermoplastic polymer containing sulfated alcohol groups ##STR1## in repeating structural units. The composition has high electrical conductivity and good mechanical properties, especially after drawing at temperatures below the melt/decomposition temperature. The material may be used as electrodes, electrically conductive filaments or components for electromagnetic screening.

Patent
   RE34514
Priority
Sep 09 1988
Filed
Apr 27 1992
Issued
Jan 18 1994
Expiry
Apr 27 2012
Assg.orig
Entity
Large
4
13
EXPIRED
1. A An electrically conductive polymer composition comprising
(a) at least one oxidized polycationic polymer and at least one polyanionic polymer, wherein the polycationic polymer is prepared by electropolymerizing, in a solution with the polyanionic polymer, a monomer selected from the group consisting of aniline, a 3-C1 -C12 alkyl-substituted aniline and a polyheteroaromatic compound which has 5- or 6-membered rings containing 1-3 heteroatoms selected from the group consisting of --O--, --S-- and --N---, which rings are either unsubstituted or substituted on the carbon atoms with C1 -C16 alkyl or at least one oxidized polycationic aniline or a 3-C1 -C12 alkyl-substituted oxidized polycationic aniline; and
(b) at least one polyanion of the polyanionic polymer is a film-forming thermoplastic polymer containing sulfated alcohol groups ##STR43## in repeating structural units, having a glass transition temperature of -100 to +350°C and a tensile strength of 5 mpa to 1000 mpa, the polyanionic polymer being selected from the group consisting of polyesters, polyester amides, polyurethanes, polyamides, polycarbonates, polyimides obtained from hydroxyl-containing monomers, saponified polymers of vinyl esters and ethers, hydroxylated polybutadiene, polyisoprene or polychloroprene, polyacrylates or polymethacrylates containing hydroxyl groups in the ester moiety, polysiloxanes containing hydroxyalkyl groups or reduced polyketones, polyadducts of glycidyl compounds containing on average more than one epoxy group with a diol, and copolymers thereof.
2. A composition according claim 1, wherein the polyheteroaromatic compound is formed from 5- or 6-membered rings which contain 1 to 3 hetero atoms selected from the group consisting of O, S and N, and the carbon atoms of which are unsubstituted or substituted by C1 -C16 alkyl.
3. A composition according to claim 2, wherein the 5- 6-membered ring is selected from the group consisting of pyrrole, thiophene, furan, 2,2'-bipyrrole, 2,2'-bithiophene, 2,2'-bifurane, thiazole, oxazole, thiadiazole and imidazole.
4. A composition according to claim 2, wherein the polyheteroaromatic compound is formed from a pyrrole of formula ##STR44## wherein R1 and R2 are each independently of the other hydrogen or C1 -C6 alkyl.
5. A composition according to claim 1, which contains 0.1 to 0.5 structural units containing sulfated alcohol groups ##STR45## per structural unit of the polyheteroaromatic compound.
6. A composition according to claim 5, which contains 0.2 to 0.4 structural units containing sulfated alcohol groups.
7. A composition according to claim 1, wherein the thermoplastic polymer containing sulfated alcohol groups ##STR46## salt form has a Tg of -100 to +350°C, and M⊕ is an alkali metal cation or an ammonium cation.
8. A composition according to claim 7, wherein the Tg if -50° to +250°C
9. A composition according to claim 1, wherein the ratio of free alcohol groups to sulfated alcohol group ##STR47## in the thermoplastic polymer is 50:1 to 1:50.
10. A composition according to claim 9, wherein the ratio is 10:1 to 1:10.
11. A composition according to claim 1, wherein the thermoplastic polyanionic polymer is an at least partially sulfated polyadduct of a) a glycidyl compound containing on average more than one epoxy group and b) a diol which contains ##STR48## groups in the polymer chain.
12. A composition according to claim 11, wherein the polyadduct contains
a) 100 to 5 mol % of identical or different structural units of formula I ##STR49## and b) 95 to 9 mol % of identical or different structural units of formula II ##STR50## based on said polyadduct in which formulae (I) and (II) above R3 and R4 are each independently of the other the radical of a diol containing aliphatic or aromatic diol groups which radical is diminished by two hydroxyl groups, and R' is hydrogen, C1 -C20 alkyl, C1 -C20 acyl or aminocarbonyl which is substituted by a C1 -C20 hydrocarbon atom.
13. A composition according to claim 12. wherein R3 and R4 are each independently of the other a radical of formula III ##STR51## wherein X is a direct bond, C1 -C4 alkylene, C2 -C12 alkylidene, C5 -C8 cycloalkylidene, --O--, --S--, --SO--, SO2 --, --CO--, --CO2, --N(C1 -C4 alkyl) or --Si(CH3)2, R5 and R6 are each independently of the other hydrogen, halogen, C1 -C4 alkyl, or C1 -C4 alkoxy, and x is 1 or 2 and y is 0 or 1.
14. A composition according to claim 12, wherein R3 and R4 are the radical ##STR52##
15. A composition according to claim 1, wherein the thermoplastic polyanionic polymer is an at least partially sulfated homopolymer or copolymer of acrylates or methacrylates containing a ##STR53## group in the ester moiety.
16. A composition according to claim 15, wherein the polyanionic polymer contains
a) 100 to 5 mol % of identical or different structural units of formula IV ##STR54## and b) 95 to 0 mol % of identical or different structural units of formula V ##STR55## based on said the polyanionic polymer, in which formulae (IV) and (V) R7 is hydrogen or methyl, R8 is linear or branched C2 -C18 -alkylene, poly(C2 -C6 oxaalkylene) containing 2 to 6 oxaalkylene units, C5 -C8 cycloalkylene, phenylene, benzylene or xylylene or is the group ##STR56## Y is --O--, ##STR57## or --N(C1 -C4 alkyl) and R12 is C1 -C18 alkyl, C5 -C7 -cycloalkyl, (C1 -C12 alkyl)-C5 -C7 cycloalkyl, phenyl, (C1 -C12 alkyl)phenyl, benzyl or (C1 -C12 alkyl)benzyl, R9 is hydrogen, C1 -C6 alkyl, --COOR12 or --COO⊖, R10 is hydrogen, fluoro, chloro, cyano or C1 -C6 alkyl, and R11 is hydrogen, fluoro chloro, cyano, R12 is --O--, C1 -C12 alkyl, --COO⊖, --COOR12, --COOR8 --OH, --OCO--R12 or phenyl, where R9 and R12 have the given meanings.
17. A composition according to claim 16, wherein the polymer contains structural units of formula IV in which R7 is hydrogen or CH3, and R8 is linear or branched C2 -C6 alkylene, cyclopentylene or cyclohexylene, and structural units of formula V wherein R9 is hydrogen, R10 is hydrogen or methyl, and R11 is --COOR12 or --COOR8 --OH.
18. A composition as set forth in claim 1 wherein said polymer is a copolymer containing moieties which are residues of saponified vinyl esters or ethers, acrylates or methacrylates containing hydroxyl groups in the ester moiety, or hydroxylated butadiene, isoprene or chloroprene; wherein the monomer has been further copolymerized with a different comonomer selected from the group consisting of acrylonitrile, olefins, diolefins, vinyl chloride, vinylidene chloride, vinyl fluoride, vinylidene fluoride, styrene, α-methylstyrene, maleic anhydride, maleimide, vinyl ethers and vinyl esters.
19. A composition as set forth in claim 1 wherein the polyimide contains residues from hydrogenated ketotetracarboxylic acids.

This application is a reissue of Ser. No. 07/401,352 filed Aug. 31, 1989 now U.S. Pat. No. 5,061,401.

The present invention relates to a composition comprising (a) at least one oxidised polycationic polyheteroaromatic compound and (b) at least one polyanion of a film-forming thermoplastic polymer containing sulfated alcohol groups ##STR2## in repeating structural units, to a process for the preparation of said composition, to a method of increasing the electrical conductivity of said composition and to the use of the composition as electrically conductive material.

It is known to obtain electrically conductive salts of polycationic polyheteroaromatic compounds by electrochemical polymerisation of heteroaromatic compounds, especially pyrrole, in the presence of nonnucleophilic anions. The mechanical properties of such salts of polyheteroaromatic compounds, which are normally deposited as film on anodes, are insufficient for many applications.

To improve the mechanical properties it has been proposed to use compositions of doped polyheteroaromatic compounds in non-conductive polymers. Reference is made in this connection to the following publications: Synthetic Metals, 22 (1987), 145-156; J. of Polym. Science: P.C.E., 23 (1985), 1687-1698, Bull. Chem. Soc. Jpn., 60, 3315-3320 (1987) and European patent application 0 191 726. To avoid the concurrent use of dopants, the concurrent use of non-nucleophilic anions in the electrochemical polymerisation has been proposed, for example polystyrene sulfonates, polyvinyl sulfonates (q.v. for example European patent specification 0 129 070 and U.S. Pat. No. 4 552 927) or latices (q.v. Synthetic Metals, 15 (1986), 175-182).

Porous compositions of polypyrrole with, for example, alkylsulfates are disclosed in German Offenlegungsschrift 3 402 133. It is mentioned that sulfates containing polymeric radicals can also be used. A film-forming composition of polypyrrole and a chlorosulfonated polyvinyl alcohol is disclosed in GB patent specification 2 124 635. Although the dry film has good conductivity, it is described as tough but brittle, and hence does not have sufficient mechanical strength.

There is a need to provide electrically conductive polymer compositions which can be processed by methods of thermoplastic processing, for example compression moulding or stretch forming, and which have good mechanical properties such as good tensile and flexural strength. It would also be useful if the electrical conductivity and the mechanical properties could be substantially improved by such a processing method.

In one of its aspects, the invention relates to a composition comprising

a) at least one polyheteroaromatic compound or an aniline in oxidised, polycationic form, and

b) at least one polyanion of a film-forming thermoplastic polymer containing sulfated alcoholic groups ##STR3## in repeating structural units.

Polyheteroaromatic compounds will be understood within the scope of this invention as meaning homopolymers and copolymers which contain repeating heteroaromatic structural units. They may be high molecular or also oligomeric, provided they are solid at room temperature and are able to form films. Preferred polyheteroaromatic compounds are those of 5- to 6-membered rings which contain 1 to 3 hetero atoms, preferably 1 hetero atom, selected from the group consisting of --O--, --S--and --N--, and the carbon atoms of which are unsubstituted or substituted by C1 -C16 alkyl, preferably C1 -C12 alkyl. Preferably two carbon atoms are not substituted, so as to be able to carry out the electrochemical polymerisation. The 5- or 6-membered ring is preferably selected from the group consisting of pyrrole, thiophene, furan, 2,2'-bipyrrole, 2,2'-bithiophene, 2,2'-bifurane, thiazole, oxazole, thiadiazole and imidazole.

Especially preferred is the polyheteroaromatic compound of a pyrrole of formula ##STR4## wherein R2 and R2 are each independently of the other hydrogen or C1 -C16 alkyl. R1 and R2 may be C1 -C12 alkyl, for example methyl or ethyl, and are preferably hydrogen. The NH-- group of the pyrrole may be substituted by C1 -C12 alkyl, preferably C1 -C6 alkyl.

Anilines may be aniline itself and aniline which is substituted in 3-position by C1 -C12 alkyl, preferably C1 -C6 alkyl.

The composition of this invention contains, in each structural unit of the polyheteroaromatic compound, preferably 0.1 to 0.5, most preferably 0.2 to 0.4, structural units containing sulfated alcohol groups ##STR5##

The thermoplastic polymer eligible for use in the composition of this invention containing sulfated alcoholic groups ##STR6## in salt form preferably has a glass transition temperature of -100° to +350°C, more particularly -50° to +250°C, measured by differential scanning calorimetry. (DCS).

The tensile strength of these thermoplastic polymers is preferably not less than 5 MPa, especially not less than 20 MPa, determined according to DIN 53 455. Depending on the nature of the polymer, the tensile strength can be up to 1000 MPa, preferably up to 500 MPa and, most preferably, up to 300 MPa. The sulfated alcohol groups in salt form may be, for example, alkali metal and ammonium salts, which are hereinafter described for the polymers.

The ratio of free alcoholic groups to sulfated alcohol groups ##STR7## in the thermoplastic polymer can be, for example, from 50:1 to 1:50, preferably from 10:1 to 1:10.

The sulfated alcohol groups may be present in the terminal position as secondary ##STR8## groups in the polymer backbone or as primary --CH2 --O--SO3.crclbar. groups in side-chains of the polymer, or in the central position as secondary ##STR9## groups or as tertiary ##STR10## groups.

The thermoplastic polymers may be derived from polymers or mixtures thereof which contain different hydroxyl groups, for example polyesters, polyester amides, polyurethanes, polyamides, polycarbonates and polyimides obtained from hydroxyl-containing monomers, saponified polymers of vinyl esters or ethers, hydroxylated polyolefins such as polybutadiene, polyisoprene or chloroprene, polyacrylates or polymethacrylates containing hydroxyl groups in the ester moiety, polysiloxanes containing hydroxyalkyl groups or reduced polyketones or copolymers thereof; as well as copolymers of vinyl alcohol, acrylates or methacrylates or diolefins with comonomers such as acrylonitrile, olefins, diolefins, vinyl chloride, vinylidene chloride, vinyl fluoride, vinylidene fluoride, styrene, α-methylstyrene, maleic anhydride, maleimide, vinyl ethers and vinyl esters.

The sulfated thermoplastic polymers are preferably derived from polymers selected from the group consisting of polyadducts of glycidyl compounds containing on average more than one epoxy group with a diol; homopolymers and copolymers of hydroxyalkyl acrylates and methacrylates; homopolymers and copolymers of butadiene, isoprene and chloroprene whose double bonds are hydroxylated; polyimides of hydrogenated ketotetracarboxylic acids, especially benzophenonetetracarboxylic acids; hydroxyalkyl polysiloxanes; and polyesters, polyamides, polyurethanes and polyimides from C4 -C12 -alkenylenediols or C4 -C12 alkenylenediamines whose double bond is hydroxylated.

The thermoplastic polymer may be, for example, an at least partially sulfated polyadduct of a) a glycidyl compound containing on average more than one epoxy group and b) a diol which contains ##STR11## groups in the polymer chain.

The polyadducts are preferably derived from glycidyl compounds containing on average two epoxy groups in the molecule.

Particularly suitable glycidyl compounds are those containing two glycidyl, β-methylglycidyl or 2,3-epoxycyclopentyl groups attached to a hetero atom (for example a sulfur atom, preferably an oxygen or a nitrogen atom). Such compounds are in particular: bis(2,3-epoxycyclopentyl)ethers; diglycidyl ethers of polyhydric aliphatic alcohols such as 1,4-butanediol, or polyalkylene glycols such as polypropylene glycols; diglycidyl ethers of cycloaliphatic polyols such as 2,2-bis(4-hydroxycyclohexyl)propane; diglycidyl ethers of polyhydric phenols such as resorcinol, bis(hydroxyphenyl)methane, 2,2-bis(p-hydroxyphenyl)propane (diomethane), 2,2-bis(4'-hydroxy-3',5'-dibromophenyl)propane, 1,3-bis(p-hydroxyphenyl)ethane; bis(β-methylglycidyl)ethers of the above-mentioned dihydric alcohols or dihydric phenols, diglycidyl esters of dicarboxylic acids such as phthalic acid, terephthalic acid, Δ4 -tetrahydrophthalic acid and hexahydrophthalic acid; N,N-diglycidyl derivatives of primary amines and amides and heterocyclic nitrogen bases containing two nitrogen atoms, and N,N'-diglycidyl derivatives of disecondary diamides and diamines such as N,N-diglycidylaniline, N,N-diglycidyltoluidine, N,N-diglycidyl-p-aminophenylmethyl ether, N,N'-dimethyl-N,N'-diglycidyl bis(p-aminophenyl)methane; N',N"-diglycidyl-N-phenylisocyanurate; N,N'-diglycidylethyleneurea; N,N'-diglycidyl-5,5-dimethylhydantoin, N,N'-diglycidyl-5-isopropylhydantoin, N,N-methylene-bis(N',N'-diglycidyl-5,5-dimethylhydantoin), 1,3-bis(N-glycidyl-5,5-dimethylhydantoin)-2-hydroxypropane; N,N'-diglycidyl-5,5-dimethyl-6-isopropyl-5,6-dihydrouracil.

The glycidyl compounds can be reacted with aliphatic, cycloaliphatic or aromatic diols to the preferred polyadducts, in which reaction a secondary alcohol group is formed at the glycidyl group e can be sulfated.

The glycidyl compounds can also be reacted with primary aliphatic, cycloaliphatic or aromatic monoamines (for example aniline, toluidine, C1 -C12 alkylamines, C2 -C12 hydroxyalkylamines), aliphatic, cycloaliphatic or aromatic dicarboxylic acids (for example maleic acid, adipic acid, trimethyladipic acid, sebacic acid, azelaic acid, succininic acid, dodecylsuccinic acid, phthalic acid, terephthalic acid, Δ4 -tetrahydrophthalic acid, hexahydrophthalic acid, 4-methylhexahydrophthalic acid, 3,6-endomethylene-Δ4 -tetrahydrophthalic acid, 4-methyl-3,6-endomethylene-Δ4 -tetrahydrophthalic acid), or with aliphatic, cycloaliphatic, heterocyclic or aromatic di-secondary amines or di-secondary carboxamides (for example N,N'-dimethylethylenediamine, N,N'-dimethylpropylene-1,3-diamine, N,N'-dimethylhexamethylenediamine, N,N'-dicyclohexylhexamethylenediamine, N,N',N"-trimethyldiethylenetriamine, N,N'-diethylpropylene-1,3-diamine, N-methyl-3,5,5-trimethyl-3-(methylaminomethyl)cyclohexylamine, N,N'-dimethylated or -N,N'-diethylated aromatic diamines, for example m- or p-phenylenediamine, bis(4-aminophenyl)methane or -sulfone, 2,2-bis(4-aminophenyl)propane, N,N-dimethyl-m-xylylenediamine, as well as ethyleneurea, 5,5-dimethylhydantoin, 5-isopropylhydantoin, N,N-methylenebis-5,5-dimethylhydantoin, 1,3-bis(5,5-dimethyl)-2-hydroxypropane, 5,5-dimethyl-6-isopropyl-5,6-dihydrouracil), by polyaddition to give linear polyadducts.

A preferred composition of this invention is one in which the polyadduct contains

a) 100 to 5 mol % of identical or different structural units of formula I ##STR12## and

b) 95 to 0 mol % of the identical or different structural units of formula II ##STR13## based on said polyadduct, in which formulae (I) and (II) above R3 and R4 are each independently of the other the radical of a diol containing aliphatic or aromatic diol groups, which radical is diminished by two hydroxyl groups, and R' is hydrogen, C1 -C20 alkyl, C1 -C20 acyl or aminocarbonyl which is N-substituted by a C1 -C20 hydrocarbon radical.

Preferably the polyadduct contains 90 to 20 mol %, preferably 30 to 80 mol %, of structural units of formula I, and 80 to 10 mol %, preferably 70 to 20 mol %, of structural units of formula II.

In a preferred embodiment of the invention, R3 and R4 are identical radicals. R3 and R4 as a radical having aliphatic diol groups contains preferably 2 to 12, most preferably 2 to 8 carbon atoms. The hydroxyl groups may be attached to open-chain or cyclic aliphatic radicals. A suitable aliphatic radical is typically linear or branched C2 -C12 -alkylene, C3 -C8 cycloalkylene, C1 -C4 alkyl-C6 --C8 cycloalkyl, cyclohexylmethylene or cyclohexyldimethylene. Illustrative examples of such radicals are ethylene, 1,2- or 1,3-propylene, 1,2-, 1,3- or 1,4-butylene, 1,2-, 1,3-, 1,4- or 1,5-pentylene, 1,2-, 1,3-, 1,4-, 1,5 or 1,6-hexylene, heptylene, octylene, nonylene, decylene, undecylene, dodecylene, 1,3-cyclopentylene, 1,3-or 1,4-cyclohexylene, 2-methyl-1,4-cyclohexylene and cyclohexyl-1,4-dimethylene.

The aromatic diol groups of the diols used for the polyadducts are preferably phenolic groups. The diol radicals carrying phenolic groups contain preferably 6 to 30, most preferably to 6 to 20, carbon atoms. A preferred embodiment of the invention relates to compositions wherein R3 and R4 are each independently of the other a radical of formula III ##STR14## wherein X is a direct bond, C1 -C4 alkylene, C2 -C12 alkylidene, C5 -C8 cycloalkylidene, --O--, --S--, --SO--, SO2 --, --CO--, --CO2 --, --N(C1 -C4 alkyl) or --Si(CH3)2, R5 and R6 are each independently of the other hydrogen, halogen, C1 -C4 alkyl, or C1 -C4 alkoxy, and x is 1 or 2 and y is 0 or 1.

X is preferably a direct bond, methylene, ethylene, C2 -C6 alkylidene. cyclohexylidene or cyclopentylidene, --O--or --S--. R5 and R6 are preferably hydrogen or methyl, and Y is preferably 1.

Preferably R3 and R4 are the radical ##STR15## A further preferred composition of the invention is one in which the thermoplastic polymer is an at least partially sulfated homopolymer or copolymer of acrylates or methacrylates containing a ##STR16## group in the ester moiety. A preferred composition of this type is one in which the polymer contains

a) 100 to 5 mol % of identical or different structural units of formula Iv ##STR17## and

b) 95 to 9 mol % of identical or different structural units of formula V ##STR18## based on said polymer, in which formulae (IV) and (v) R7 is hydrogen or methyl, R8 is linear or branched C2 -C18 -alkylene, poly(C2 -C6 oxaalkylene) containing 2 to 6 oxaalkylene units, C5 -C8 cycloalkylene, phenylene, benzylene or xylylene or is the group ##STR19## Y is --O--, ##STR20## or --N(C1 -C4 alkyl), and R12 is C1 -C18 alkyl, C5 -C7 -cycloalkyl, C1 -C12 alkyl)-C5 -C7,cycloalkyl, phenyl, (C1 -C12 alkyl)phenyl, benzyl or (C1 -C12 alkyl)benzyl, R9 is hydrogen, C1 -C6 alkyl, --COOR12 or --COO.crclbar., R10 is hydrogen, fluoro, chloro, cyano or C1 -C6 alkyl, and R11 is hydrogen, fluoro chloro, cyano, R12 is --O--, C1 -C12 alkyl, --COO.crclbar., --COOR12, --COOR8 --OH, --OCO--R12 or phenyl, where R8 and R12 have the given meanings.

Preferably the polymer contains 90 to 20 mol %, most preferably 80 to 30 mol %, of structural units of formula IV, and 80 to 10 mol %, most preferably 70 to 20 mol %, of structural units of formula V.

R8 as alkylene contains preferably 2 to 12, more particularly 2 to 8 and, most preferably, 2 to 6, carbon atoms. Illustrative examples of such groups are ethylene and the isomers of propylene, butylene, pentylene, hexylene, heptylene, octylene, nonylene, decylene, undecylene, dodecylene, tetradecylene, hexadecylene, and octadecylene. Preferred groups are ethylene, 1,2- and 1,3-propylene, 1,2-, 1,3- and 1,4-butylene, 1,2-, 1,3-, 1,4-and 1,5-pentylene, and 1,2-, 1,3-, 1,4-, 1,5- and 1,6-hexylene. R8 as poly(oxaalkylene) preferably contains 2 to 4 oxaalkylene units and preferably 2 to 4, most preferably 2 or 3, carbon atoms in the alkylene moiety.

R8 as cycloalkylene is preferably cyclopentylene or cyclohexylene.

Polymers in which R8 is the group ##STR21## are reaction products of glycidyl esters of poly- or copoly(meth)acrylic acid with a compound R12 -Y-H which contains active hydrogen.

Y is preferably --O-- ode ##STR22## R12 may be linear or branched alkyl of 1 to 18, preferably 1 to 12 most preferably, 1 to 6, carbon atoms. R12 as cycloalkyl is preferably cyclopentyl or cyclohexyl. Where R12 is (C1 -C12 alkyl)cycloalkyl, the cycloalkyl moiety is preferably cyclopentyl or cyclohexyl, and the alkyl moiety may be linear or branched and contains preferably 1 to 6, most preferably 1 to 4, carbon atoms. Where R12 is alkylphenyl or alkylbenzyl, the alkyl moiety may be linear or branched and contains preferably 1 to 6, most preferably 1 to 4, carbon atoms.

R9 is preferably hydrogen. R9 as alkyl is preferably methyl or ethyl. Where R9 is --COOR12, R12 is preferably C1 -C12 alkyl, most preferably C1 -C6 alkyl.

R10 as alkyl is preferably C1 -C4 alkyl, typically methyl, ethyl, n-propyl and n-butyl. R10 is preferably hydrogen, chloro or C1 -C4 alkyl.

Where R11 is the group R12 --O--, R12 is preferably C1 -C12 alkyl, preferably C1 -C6 alkyl. An alkyl group R11 preferably contains 1 to 6, most preferably 1 to 4, carbon atoms. Where R11 is the group --COOR12, R12 is preferably C1 -C12 alkyl, most preferably C1 -C6 alkyl, cyclopentyl or cyclohexyl. Where R11 is the group --OCO--R12, R12 is preferably C1 -C12 alkyl, most preferably C1 -C6 alkyl, phenyl or benzyl.

Where R11 is the group --COOR8 --OH, R8 has the preferred meanings assigned to it previously.

In a preferred embodiment of the invention, R9 is hydrogen, fluoro, chloro, methyl or ethyl, and R11 is fluoro, chloro, cyano, C1 -C4 alkyl, C1 -C6 alkoxy, --COO--C1 -C6 alkyl, --COO--R8 --OH, --OCC--C1 -C6 alkyl or phenyl.

R' as C1 -C20 alkyl may be linear or branched. R' as acyl may be C1 -C20 -alkyl--CO--, C5 -C8 -cycloalkyl--CO--, C1 -C15 -alkyl-C5 -C8 -cycloalkyl--CO, C5 -C8 -cycloalkyl-CH2 --O--, C1 -C14 -alkyl-C5 -C8 -cycloalkyl--CH2 CO, phenyl--CO, benzyl--CO, C1 -C14 -alkylphenyl--CO-- or C1 -C14 alkylbenzyl--CO. The hydrocarbon radical radical in the aminocarbonyl may be C1 -C20 --alkyl--, C5 -C8 --cycloalkyl, C1 -C15 -alkyl--C5 -C8 -cycloalkyl--, C5 -C8 --cycloalkyl--CH2 --, C1 -C14 -alkyl-C5 -C8 -cycloalkyl--CH2 --, phenyl, benzyl, C1 -C14 -alkylphenyl or C1 -C14 alkylphenyl or C1 -C14 alkylbenzyl. R' is preferably hydrogen.

Particularly preferred compositions are those wherein the polymer contains structural units of formula IV in which R7 is hydrogen or CH3, and R8 is linear or branched C2 -C6 alkylene, cyclopentylene or cyclohexylene, and structural units of formula V wherein R9 is hydrogen, R10 is hydrogen or methyl, and R11 is --COOR12 or --COOR8 --OH.

A further preferred embodiment of the invention relates to compositions wherein the thermoplastic polymer is an at least partially sulfated polyvinyl alcohol or polyvinyl alcohol copolymer containing ##STR23## groups. Preferably the composition contains polyvinyl alcohol copolymers.

Preferred compositions are those wherein the copolymer contains

a) 90 to 5 mol % of structural units of formula VI ##STR24## and

b) 95 to 10 mol % of identical or different structural units of formula V ##STR25## in which formulae (VI) and (V) R9, R10 and R11 have the meanings assigned to them above.

Preferably the copolymer contains 70 to 10 mol %, most preferably 60 to 20 mol %, of structural units of formula IV, and 30 to 90 mol %, most preferably 40 to 80 mol %, of structural units of formula V.

In formula V, R9, R10 and R11 have the preferred meanings previously assigned to them.

Especially preferred compositions are those wherein R9 and R10 are hydrogen and R11 is --OCOR12, wherein R12 is C1 -C18 alkyl, C5 -C7 -cycloalkyl, (C1 -C12 alkyl)C5 -C7 cycloalkyl, phenyl, benzyl, (C1 -C12 alkyl)phenyl or (C1 -C12 alkyl)benzyl.

The polyanions of component b) in the compositions of this invention ar derived from polymeric salts which are known or obtainable by methods which are known per se. These salts are film-forming thermoplastic polymers containing sulfated alcohol groups --C--O--SO3.crclbar. M.sym. in repeating structural units, in which M.sym. is an alkali metal cation or ammonium cation.

The sulfated alcohol groups may be present as secondary ##STR26## groups in the polymer backbone, or in terminal position as primary --CH2 --SO3.crclbar. M.sym. groups in side-chains of the polymer, or in central position as secondary ##STR27## groups or as tertiary ##STR28## groups.

The glass transition temperature of the polymers can be from -100 to +350°C, preferably from -50° to +250°C, measured by the DSC. The tensile strength is preferably not less than 5 MPa, most preferably 10 MPa, determined in accordance with DIN 53 455. Depending on the nature of the polymer, the tensile strength may be up to 1000 MPa, preferably up to 500 MPa and, most preferably, up to 300 MPa.

The degree of polymerisation of the polymers may be, for example, from 5 to 10 000, preferably from 10 to 5 000 and, most preferably, from 10 to 1000.

Preferred polymers are those wherein the ratio of free alcohol groups to sulfated alcohol groups in the polymer is from 50:1 to 1:50, preferably from 10:1 to 1:10.

The ammonium cation may be NH4.sym., a protonated primary, secondary or tertiary amine, or quaternary ammonium or pyridinium. The primary amine may contain 1 to 18 carbon atoms, preferably 1 to 12 and, most preferably, 1 to 6, carbon atoms, the secondary amine may contain 2 to 24 carbon atoms, preferably 2 to 12 and, most preferably 2 to 8, carbon atoms, the tertiary amine may contain 3 to 30 carbon atoms, preferably 3 to 18 and, most preferably 3 to 12, carbon atoms, and the quaternary ammonium may contain 4 to 36 carbon atoms, preferably 4 to 24 and, most preferably 4 to 18, carbon atoms.

Preferred polymers are those wherein M.sym. is Li.sym., Na.sym. or K.sym., or is R13 R14 R15 R16 N.sym., wherein R13, R14, R15 and R16 are each independently of one another hydrogen, unsubstituted or hydroxyl-substituted C1 -C18 -alkyl, phenyl, (C1 -C12 alkyl)phenyl, (C1 -C12 alkyl)benzyl, C5 -C7 -cycloalkyl, (C1 -C12 -alkyl)-C5 -C7 -cycloalkyl, or R13 und R14, when taken together, are tetramethyhlene, pentamethylene or 3-oxapentylene, and R15 and R16 have the above meanings. A preferred embodiment of the invention relates to polymers wherein at least one of R13 to R16 is not hydrogen.

Alkyl groups R13 to R16 may be linear or branched and contain preferably 1 to 12, most preferably 1 to 6, carbon atoms. Illustrative of such groups are methyl, ethyl, n- and isopropyl, n-butyl, isobutyl and tert-butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, dodecyl, tetradecyl, hexadecyl and octadecyl.

Hydroxyalkyl groups R13 to R16 may be linear or branched and contain preferably 2 to 18, more particularly 1 to 12 and, most preferably, 2 to 6, carbon atoms. Typical examples are 2-hydroxyeth-1-yl, 1- or 2-hydroxyprop-3-yl, 1-hydroxybut-4-yl and 1-hydroxyhex-6-yl.

Exemplary of alkylphenyl and alkylbenzyl are methylphenyl, dimethylphenyl, ethylphenyl, n- or isopropylphenyl, n-, iso- or tert-butylphenyl, hexylphenyl, octylphenyl, decylphenyl, dodecylphenyl and suitably alkylated benzyl radicals

R13 to R16 as cycloalkyl are preferably cyclopentyl or cyclohexyl.

R13 to R16 as alkylcycloalkyl are preferably (C1 -C12 -alkyl)cyclopentyl or (C1 -C12 alkyl)cyclohexyl.

Most preferably, R13 to R16 are C1 -C6 -alkyl.

The polymers may be derived from different hydroxyl group containing polymers, for example polyesters, polyester amides, polyurethanes, polyamides, polycarbonates and polyimides obtained from hydroxyl group containing monomers, saponified polymers of vinyl esters or ethers, hydroxylated polydiolefins such as polybutadiene, polyisoprene or choroprene, polyacrylates or polymethacrylates containing hydroxyalkyl groups in the ester moiety, polysiloxanes containing hydroxyalkyl groups or reduced polyketones or copolymers thereof; and also copolymers of vinyl alcohol, acrylates or methacrylates or diolefins with comonomers, for example acrylonitrile, olefins, diolefins, vinyl chloride, vinylidene chloride, vinyl fluoride, vinylidene fluoride, styrene, α-methylstyrene, maleic anhydride, maleimide, vinyl ethers and vinyl esters.

Such polymers are known or can be prepared by commonly known methods. Depending on the nature of the polymer and of the process conditions, hydroxyl groups in the monomers employed are protected by customary protective groups.

In a preferred embodiment of the invention, the polymers are an at least partially sulfated polyadduct of a) a glycidyl compound containing on average more than one epoxy group and (b) a diol which contains ##STR29## groups in the polymer chain. Preferred polyadducts are previously mentioned herein. Such polymers are disclosed in U.S. Pat. No. 3 402 221.

Preferred polyadducts are those wherein the polyadduct contains a) 100 to 5 mol % of identical or different structural units of formula I ##STR30## and

b) 95 to 0 mol % of identical or different structural units of formula II ##STR31## based on the polyglycidyl ether, in which formulae (I) and (II) above R3 and R4 are each independently of the other the radical of a diol containing aliphatic or aromatic diol groups, which radical is diminished by two hydroxyl groups, and R' is hydrogen, C1 -C20 alkyl, C1 -C20 acyl or aminocarbonyl which is N-substituted by a C1 -C20 hydrocarbon radical.

Especially preferred polyadducts are those wherein R3 and R4 are each independently of the other a radical of formula III ##STR32## wherein X is a direct bond, C1 -C4 alkylene, C2 -C12 alkylidene, C5 -C8 cycloalkylidene, --O--, --S--, --SO--, SO2 --, --CO--, --CO2 --, --N(C1 -C4 alkyl) or --Si(CH3)2, R5 and R6 are each independently of the other hydrogen, halogen, C1 -C4 alkyl, or C1 -C4 alkoxy, and x is 1 or 2 and y is 0 or 1.

Preferably R3 and R4 are the radical ##STR33## R3, R4, R5, R6, X, y and x have the preferred meanings previously assigned to them, and the preferred content of structural units is likewise as previously indicated.

A further preferred embodiment of the invention relates to those polymers in which the thermoplastic polymer is an at least partially sulfated homopolymer or copolymer of acrylates or methacrylates containing a ##STR34## group in the ester moiety. Such polymers are disclosed, for example, in U.S. Pat. No. 4 341 647 and 4 288 427.

Especially preferred polymers are those wherein the polymer contains

a) 100 to 5 mol % of identical or different structural units of formula IV ##STR35## and

b) 95 to 0 mol % of identical or different structural units of formula V ##STR36## based on said polymer, in which formulae (IV) and (V) R7 is hydrogen or methyl, R9 is linear or branched C2 -C18 -alkylene, poly(C2 -C6 oxaalkylene) containing 2 to 6 oxaalkylene units, C5 -C6 cycloalkylene, phenylene, benzylene or xylylene or is the group ##STR37## Y is --O--, ##STR38## or --N(C1 -C4 alkyl), and R12 is C1 -C18 alkyl, C5 -C7 cycloalkyl, (C1 -C12 alkyl)-C5 -C7 cycloalkyl, phenyl, (C1 -C12 alkyl)phenyl, benzyl or (C1 -C12 alkyl)benzyl, R9 is hydrogen, C1 -C6 alkyl, --COOR12 or --COO.crclbar., R10 is hydrogen, fluoro, chloro, cyano or C1 -C6 alkyl, and R11 is hydrogen, fluoro chloro, cyano, R12 is --O--, C1 -C12 alkyl, --COO.crclbar., --COOR12, --COOR8 --OH, OCO--R12 or phenyl, where R8 and R12 have the given meanings.

Particularly preferred polymers are those wherein the polymer contains structural units of formula IV in which R7 is hydrogen or CH3, and R8 is linear or branched C2 -C6 alkylene, cyclopentylene or cyclohexylene, and structural units of formula V wherein R9 is hydrogen, R10 is hydrogen or methyl, and R11 is --COOR12 or --COOR8 --OH.

R7 to R12 and Y have the preferred meanings previously assigned to them, and the preferred content of structural units is likewise as previously indicated.

Another embodiment of the invention relates to polymers wherein the thermoplastic polymer is an at least partially sulfated polyvinyl alcohol or sulfated polyvinyl alcohol copolymer containing ##STR39## groups. Preferably the composition contains polyvinyl alcohol copolymers.

Preferred copolymers are those wherein the copolymer contains

a) 90 to 5 mol % of structural units of formula VI ##STR40## and

b) 95 to 10 mol % of identical or different structural units of formula V ##STR41## in which formulae (VI) and (V) R9, R10 and R11 have the meanings assigned to them above.

Particularly preferred copolymers are those wherein R9 and R10 are hydrogen and R11 is --OCOR12, wherein R12 is C1 -C18 alkyl, C5 -C7 -cycloalkyl, (C1 -C12 alkyl)C5 -C7 cycloalkyl, phenyl, benzyl, (C1 -C12 alkyl)phenyl or (C1 -C12 alkyl)benzyl.

R9 to R12 have the preferred meanings previously assigned to them, and the preferred content of structural units is likewise as previously indicated.

Polysiloxanes containing sulfated and hydroxyalkyl groups in salt form are disclosed in JP-A-180690.

Polyimides containing hydroxyl groups are obtainable, for example, from ketotetracarboxylic acids by hydrogenating the keto group prior to the polyimide formation. Thus, for example, benzophenone-3,4-carboxylic acid anhydride can be converted into bis(benzene-3,4-carboxylic acid anhydride) methanol or the acids or esters thereof.

Sulfated hydroxyl group containing polyesters, polyamides, polyimides and polyurethanes eligible for use in the practice of this invention may be prepared by first preparing corresponding unsaturated polymers from unsaturated monomers, for example unsaturated dicarboxylic acids like maleic acid or fumaric acid, or from alkenylenediols or alkenylenediamines, for example from 1,4-but-2-ene-diol or 1,4-but-2-ene-diamine. The double bonds in the polymers can then be epoxidised--as also in polybutadiene, polyisoprene or chloroprene - with peracids, and the epoxide ring subsequently opened, for example by hydrolysis. The hydroxyl groups can then be sulfated (q.v. for example M. L. Hallensleben in Houben Weyl, Vol. E20, page 1994 et seq.).

The thermoplastic polymers eligible for use in the practice of this invention can be obtained in known manner by reacting a thermoplastic, film-forming polymer which contains alcohol groups ##STR42## in repeating structural units, in an inert solvent, with SO3, subsequently neutralising the reaction mixture with an alkali metal base or ammonium base, and isolating the polymer.

The process is known per se. The SO3 can be introduced, for example in gaseous form, into the reaction solution. It is preferred to use a pyridine/SO3 complex which is commercially available.

Suitable inert solvents are preferably polar aprotic solvents, the choice of solvent depending principally on the solubility of the hydroxyl group containing polymer. The solvents may be used singly or as a mixture of at least two solvents. Illustrative of suitable solvents are: ethers such as dibutyl ether, tetrahydrofuran, dioxan, methylene glycol, dimethylethylene glycol, dimethyl diethylene glycol, diethyl diethylene glycol, dimethyl triethylene glycol, halogenated hydrocarbons such as methylene chloride, chloroform, 1,2-dichloroethane, 1,1,1-trichloroethane, 1,1,2,2-tetrachloroethane, and lactones such as γ-butyrolactone, o-valerolactone and pivalolactone, carboxamides and lactams such as N,N-dimethylformamide, N,N-diethylformamide, N,N-dimethylacetamide, N-methyl-γ-butyrolactam, N-methyl-ε-caprolactam, N-methylpyrrolidone, N-acetylpyrrolidone, tetramethylurea, hexamethylphosphoramide, sulfoxides such as dimethyl sulfoxide, sulfones such as dimethyl sulfone, diethyl sulfone, trimethyl sulfone, tetramethylene sulfone, N-methylpyrrolidine, N-methylpiperidine, N-methylmorpholine, substituted benzenes such as benzonitrile, chlorobenzene, o-dichlorobenzene, 1,2-trichlorobenzene and nitrobenzene.

The reaction temperature is, for example, in the range from 20° to 150°C, preferably from 40° to 100°C The reaction time is ca. 5 to 10 hours. Upon completion of the reaction, the reaction mixture is neutralised, when SO3 is gaseous form is used, with an aqueous solution of an alkali metal base or ammonium hydroxide, or with an aqueous or organic solution of an amine hydroxide. When amine/SO3 complexes are used, for example a pyridine/SO3 complex, the corresponding ammonium salts are formed, which can be directly used in the electrochemical process. It is also possible to replace the ammonium groups in said salts by stronger bases. The salts of the sulfated polymers are usually precipitated with water. The polymer is then isolated by filtration, and can be purified by washing with water or an organic non-solvent and thereafter dried.

Polyolefins can also be prepared by, for example, radical polymerisation of acrylates and methacrylates containing --O--SO3 M.sym. radicals in the ester moiety, without or together with olefin comonomers.

The eligible salts of sulfated hydroxyl group containing polymers also have thermoplastic properties. Compared with the starting polymers, their glass transition temperature is substantially unchanged and they are distinguished by their mechanical properties, for example by high tensile and flexural strength and high flexibility. They are highly suitable polyanions for electrically conductive polycations of polyheteroaromatic compounds.

Such compositions are prepared in a manner known per se by electrochemically polymerising, in an aqueous, aqueous-organic or organic solution, a heteroaromatic compound or an aniline, in the presence of a sulfated polymer salt, and subsequently removing the composition from the anode. The composition is normally deposited as a film which, depending on the duration of the electrolysis and on the current density, may have a thickness of, for example, 1 to 500 μm or 10 to 300 μm.

The electrolysis can be carried out potentiostatically or galvanostatically. Suitable anode materials are, for example, metals (titanium, nickel, platinum, steel) or ITO glass. The current density can be, for example, from 0.5 to 20 mA/cm2, preferably from 1 to 5 mA/cm2.

The concentration of sulfated polymer salt can be from 0.05 to 1 mol/l, preferably from 0.01 to 0.5 mol/l, based on the reaction mixture. The concentration of hetero atoms or aniline can be 0.01 to 10% by volume, preferably 0.1 to 5% by volume, based on the volume of the reaction mixture.

Suitable organic solvents are electrochemically inert and, for example, protic or aprotic and polar. Suitable solvents are those listed above. Preferred solvents are carbonates, especially propylene carbonate.

Examples of further suitable solvents are acetonitrile, methylene chloride, propionitrile, nitromethane, and alkanols and water.

A preferred embodiment of the process comprises carrying out the polymerisation in an organic solvent, M.sym. being an ammonium cation having at least one organic group. M.sym. is in this connection preferably R13 R14 R15 R16 N.sym., wherein R13 to R16 are each independently of one another unsubstituted or hydroxyl-substituted C1 -C18 alkyl, phenyl, (C1 -C12 -alkyl)phenyl, (C1 -C12 -alkyl)benzyl, C5 -C7 -cycloalkyl, (C1 -C12 -alkyl)-C5 -C7 -cycloalkyl or R13 and R14, when taken together, are tetramethylene, pentamethylene or 3-oxapentylene, and R15 and R16 are as previously defined above. More particularly, R13 to R16 are C1 -C6 -alkyl, for example methyl, ethyl, n-propyl and, preferably, n-butyl.

The electrochemical polymerisation can also be carried out in water or aqueous-organic solution. The concurrent use of buffers is expedient. Suitable buffers are typically alkylammonium phosphates contatining 1 to 3, preferably 2 or 3, alkyl groups in the ammonium moiety, which alkyl groups may contain 1 to 6, preferably 1 to 4, carbon atoms. Examples of suitable buffers are trimethylammonium phosphate, triethylammonium phosphate, tri-n-propylammonium phosphate and tri-n-butylammonium phosphate. Suitable buffers are also cation exchangers in their protonated form.

It is also possible to add to the reaction mixture further substances which deposit concurrently on the anode, for example anionic plasticisers or anionic dyes.

Upon termination of the electrolysis, the compositions of the invention can be removed or peeled off from the anode in the form of films and purified by washing with solvents. The films can be cut to filaments.

The compositions of this invention have high conductivities which are usually above 0.1 S/cm. They further have valuable mechanical properties such as high toughness, tensile strength, flexural strength and flexibility. Surprisingly, it has been found that the compositions of this invention have low glass transition temperatures, so that even where polyanion concentration is low, processing by thermoplastic moulding methods is possible without loss of electrical conductivity.

The compositions of this invention can be used, for example, as electrical conductors, electrodes, cathodes for batteries, electromagnetic screening materials, electrically conductive filaments, sensors, antistatic packing material, or conductive sealing material.

It has also surprisingly been found that the compositions of this invention can be processed by methods for thermoplastic polymers, for example by moulding methods and, especially, by drawing methods (deep drawing) below the melting and decomposition temperatures, preferably in the range of the glass transition temperatures. Besides an increase in mechanical strength, an appreciable, for example an up to five-fold, increase in the electrical conductivity in the direction of drawing has surprisingly been found.

A further object of the invention is a process for increasing the electrical conductivity in a film or in filaments of the novel composition, which comprises drawing said film or filaments below the melting or decomposition temperature, preferably in the range of the glass transition temperature.

Drawing is preferably carried out at a temperature which is in the range of 20°C below or above the glass transition temperature.

Utilities for the drawn material have been mentioned above in connection with non-drawn material. These utilities constitute a further object of the invention.

The following Examples illustrate the invention in more detail. The glass transition temperature (Tg) is determined by differential scanning calorimetry (DSC). The conductivity is determined by the four-point method. The tensile strength is determined in accordance with DIN 53 455.

PAC EXAMPLE A1

Sulfated polyadduct of bisphenol A diglycidyl ether and bisphenol A (sulfation of all OH groups)

28.4 g of polyadduct having an average molecular weight of 26 800 (degree of polymerisation ca. 100) are dissolved at 50°C in 150 ml of dimethyl formamide (DMF). To this solution are added 17.5 g of sulfur trioxide/pyridine complex in 20 ml of DMF. After 5 hours, the reaction mixture is cooled to 5°C and a solution of 88 g of (n-C4 H9)4 N.sym. OH.crclbar. ×30 H2 O in 100 ml of DMF is added. The reaction mixture is poured into water and the precipitated polymer salt is isolated by filtration, washed with water and dried. Yield: 50 g (83 % of theory) of polymer salt with a Tg of 87°C

Sulfated linear polyadduct of bisphenol A diglycidyl ether and bisphenol A (sulfation of every third OH group)

28.4 g of polyadduct according to Example 1 in 100 ml of DMF, 5.3 g of sulfur trioxide/pyridine complex and 29.3 g of (n-C4 H9)4 N.sym. OH.crclbar. ×30 H2 O in 50 ml of DMF are reacted and worked up as described in Example 1. Yield: 28.6 g (73 % of theory) of polymer salt with a Tg of 99°C

Sulfated linear polyadduct of bisphenol A diglycidyl ether and bisphenol A (sulfation of every fifth OH group) 284 g of polyadduct according to Example 1 in 400 ml of DMF, 33.4 g of sulfur trioxide/pyridine complex and 160 g of (n-C4 H9)4 N.beta. OH.crclbar. ×30 H2 O in 100 ml of DMF are reacted and worked up as described in Example 1. Yield: 89 % of theory) of polymer salt with a Tg of 101.5°C

Copolymer (10:1) of methyl methacrylate and 3-sulfatopropylmethacrylate tetrabutylammonium salt

43.3 g of a copolymer (10:1) of methyl methacrylate and 3-hydroxypropyl methacrylate are dissolved at 50°C in 300 ml of DMF. To this solution are added 7.26 g of sulfur trioxide/pyridine complex. After 5 hours, the reaction mixture is cooled to 5°C and neutralised with tetrabutylammonium hydroxide 30-hydrate in 30 ml of DMF. The reaction mixture is poured into water and the precipitated product is isolated by filtration and dried, affording 45.3 g (80.3 % of theory) of polymer salt with a Tg of 127.6°C The melting point is 193°C

Copolymer (1:1) of methyl methacrylate (MMA) and 3-sulfatopropylmethacrylate tetrabutylammonium salt

45 g of a 1:1 copolymer of MMA and 3-hydroxypropyl methacrylate are dissolved at 50°C in 300 ml of DMF. To this solution are added 33.96 g of sulfur trioxide/pyridine complex. After 5 hours, the reaction mixture is cooled to 5°C and neutralised with tetrabutylammonium hydroxide 30-hydrate (170 g in 200 ml of DMF). The reaction solution is poured into water and the precipitate is isolated by filtration and dried, affording 87 g (81.3 % theory) of polymer salt with a Tg of 84.6° C.

Copolymer of 2-tetrabutylammoniumsulfatoethyl methacrylate/methylmethacrylate (1:2)

20 g (44.3 mmol) of 2-tetrabutylammonium sulfatoethyl methacrylate and 8.87 g (88.69 mmol) of methyl methacrylate are dissolved in 100 ml of acetonitrile and the solution is deaerated. After addition of 30 mg of azoisobutyronitrile, the reaction solution is stirred for 36 hours at 60°C and then concentrated to dryness under vacuum. The residue is taken up in water, the solution is filtered, and the residue is lyophilised, Yield: 20.8 g (72 % theory) of copolymer with a Tg of 85.4°C

Sulfated polybutadienes

Epoxidisation (every 4th alkene group) 57.5 g (1 mol) of cis-polybutadiene (Aldrich) are dissolved in 1000 ml of chloroform. To this solution are slowly added dropwise 43 g (0.25 mol) of 3-chloroperbenzoic acid in 500 ml of chloroform. After stirring for 12 hours, the solution is poured into methanol and the precipitated polymer is isolated by filtration and washed repeatedly with methanol.

Hydrolysis of the epoxy groups

The still moist polymer is dissolved in 1000 ml of tetrahydrofuran (THF). To this solution are slowly added 54.3 ml of 36 % HCl. After 12 hours, the reaction solution is poured into methanol and the precipitated polymer is washed repeatedly with methanol and dried under vacuum at 40°C

Sulfation

The dry polymer is dissolved in 500 ml of DMF and to this solution are added 39.75 g (0.25 mol) of pyridine/sulfur trioxide complex. After a reaction time of 5 hours, the reaction solution is neutralised with 46.25 g (0.25 mol) of tributylamine at ca. 10°C The solution is poured into water and the precipitated polymer is treated repeatedly for some time with water and subsequently dried under a high vacuum. Yield: 110 g (85 % of theory, based on polybutadiene).

______________________________________
Elemental analysis:
% C % H % N % O % S % Cl
______________________________________
cal.: 64.5 7.54 2.69 12.28 6.15 6.8
found.:
64.1 7.7 2.7 12.5 5.9 6.5
______________________________________

Tg=-46.1°C; m/(n+m): 0.25.

EXAMPLES A8 und A9

Polymers with different degrees of epoxidation and sulfation are prepared in similar manner:

______________________________________
Composition of the copolymer:
n: number of butadiene units
m: number of sulfated butadiene units
Example m/(n + m) Tg/°C.
______________________________________
A8 0.16 -48.3
A9 0.11 -56.7
______________________________________

Copolymer of MMA and 10-hydroxydecyl methacrylate

12 6 g (0.126mol) of MMA and 7.38 g (0.03 mol) of 10-hydroxydecyl methacrylate are dissolved in 40 ml of THF. The solution is then warmed to 55°C Over a period of 3 hours, a solution of 50 ml of azoisobutyronitrile in 10 ml of THF is added dropwise and, after 20 hours at 55°C, the reaction solution is poured into methanol/water to precipitate the copolymer. Yield: 17 g (85% of theory). Rel. visc.: 0.59 dl/g (in chloroform).

Sulfation

15 g (0.0223 mol, based on the copolymer compositions) of the above copolymer are dissolved at 50°C in 100 ml of DMF and to this solution are added 4.086 g (0.0257 mol) of sulfur trioxide/pyridine complex. After 2 hours, the reaction solution is neutralised with 6.11 ml (0.0257 mol) of tributylamine at a temperature below 10°C The solution is poured into water and the precipitated polymer is isolated by filtration and dried at 50°C under vacuum. Yield: 18.5 g (98.3 % of theory). Tg: 148.2°C

______________________________________
Elemental analysis:
% C % H % N % O % S % H2 O
______________________________________
cal.: 60.36 9.44 1.71 24.5 3.92 1.1
found.:
60.2 9.4 2.2 25.3 3.1 1.1
______________________________________

Copolymer of MMA and 4-hydroxybutyl methacrylate.

The polymer is prepared in accordance with Example 10. Tg: 153.5°C

______________________________________
Elemental analysis:
% C % H % N % O % S % H2 O
______________________________________
cal.: 56.7 8.9 1.89 28.1 4.3 2.4
found.:
56.6 8.8 2.5 27.8 3.9 2.0
______________________________________
m/(n + m) = 0.25
m: number of MMA units
n: number of sulfated hydroxybutyl methacrylate units.

Sulfated polymides

Synthesis of the tetracarboxylic acid component (TCC)

0.62 mol of benzophenone-3,4-dianhydride are heated to the boil in 500 ml of methanol until a clear solution forms. After cooling to room temperature, the keto groups is reduced with hydrogen under normal pressure (catalyst: 1 g of 5 % Pd/C). The catalyst is separated and the solution is concentrated to dryness. The resultant mixture consisting of bis[3-carboxy-4-(carbomethoxy)phenyl]methanol and two further isomers is isolated in a yield of 82 % (197.8 g)

Polymerisation

1 mol of TCC (mixture of isomers) and 1 mol of diamine (DA) are added, under nitrogen, to N-methylpyrrolidone such that a 20 % solution is formed. This solution is heated to 180°C over 1 hour and kept, with stirring, for 10 hours at this temperature. After cooling, the polymer is precipitated by pouring the solution into water.

______________________________________
Amine component (DA) Tg/°C.
______________________________________
(a) bis(4-amino-3-methyl-5-
302
ethylphenyl)methane
(b) diaminodurol 340 (Tm)
(c) diaminononane 105
(c) 1,3-bis(di-n-propylamine)-
82.4
tetramethyl disiloxane
______________________________________

Sulfation of the polyimides

0.1 mol of polyimide is dissolved in 100 ml of DMF and to the solution is added 0.12 mol of sulfur trioxide/pyridine complex. After stirring for 5 hours, the reaction solution is cooled to room temperature and neutralised with 0.12 mol of tributylamine. The solution is poured into water to precipitate the polymer, which is isolated, washed copiously with water, and dried under vacuum.

______________________________________
Example polymer with DA Tg/°C.
______________________________________
A12 a 290
A13 b 328 (Tm)
A14 c 100
A15 d 49.3
______________________________________
Tm melt temperature
PAC EXAMPLE B1

6 g of polymer according to Example A1 and 5 ml of pyrrole are dissolved in 200 ml of propylene carbonate. The solution is blanketed with nitrogen for 10 minutes and transferred to an electrolysis cell. At a current density of 2 mA/cm2, a ca. 200 μm thick film deposits on to the anode over 2 hours. This film is removed from the electrode mechanically. extracted first with ethanol and then with acetonitrile, and dried under vacuum. The conductivity is 8.7 S/cm. The glass transition temperature (Tg) is 95°C After drawing the film by 100 % at 95°C, the conductivity increases to 47.5 S/cm.

12 g of a copolymer according to Example A4 and 5 ml of pyrrole are dissolved in 200 ml of propylene carbonate and the solution is transferred to an electrolysis cell. In accordance with Example 7, a 290 μm thick film is obtained. The conductivity of the film is 0.75 s/cm. The Tg is 230°C

6.4 g of a copolymer according to Example A5 are dissolved in 200 ml of propylene carbonate. The solution is blanked with nitrogen for 10 minutes and transferred to an electrolysis cell. In accordance with Example 7, a 218 pm thick film is obtained. The conductivity of the film is 8.07 S/cm. After drawing the film by ca. 30%, the conductivity increases to 16.5 S/cm. The glass transition temperature is 205°C

23 g of partially sulfated polymer according to Example A2, 5.8 g of a mixture of phosphoric acid and tributylamine (pH=3.4), 12 ml of pyrrole and 4 ml of water are dissolved in 300 ml of propylene carbonate. The solution is saturated with nitrogen and transferred to an electrolysis cell fitted with a rotating Ni anode (A=30 cm2) and a fine steel cathode. After 1 hour and 7 minutes, a 150 μm thick film is deposited at a current density of 2 mA/cm2. After extraction with acetonitrile and vacuum drying, the yield is 353 g. The conductivity is 15.9 S/cm. The glass transition temperature is 110.5°C By drawing at 100° C., the conductivity changes in the direction of drawing as follows:

______________________________________
Drawing in % 1c
Conductivity in S/cm
______________________________________
0 15.9
20 25.3
40 29.4
85 33.1
______________________________________

18 g of polymer according to Example A1, 2 g of 2,2'-bithiophene, 2.1 g of a mixture of phosphoric acid and tetrabutylammonium hydroxide (pH=3.4) are dissolved in 300 ml of propylene carbonate and the solution is transferred, under nitrogen, to an electrolysis cell. After 1 hour, a 115 μm thick film deposits on to the Ni anode. The conductivity of the film is 5.5·10-3 S/cm. The Tg is 107°C

11.8 g of partially sulfated polybutadiene according to Example A7 are dissolved in 200 ml of propylene and, after addition of 10 ml of pyrrole, transferred to the already described electrolysis cell. At a current density of 2 mA/cm2, a 0.088 cm thick film deposits over the course of 2 hours. The conductivity of the film is 12.5 S/cm. After drawing at room temperature by the factor of 2.11, the conductivity increases in the direction of drawing to 126 S/cm. The elongation at break of this film is ca. 211 %, the modulus of elasticity is 387 MPa. Analogous experiments with polybutadienes according to Examples A8 and A9 give films with conductivities (undrawn) in the range of 8-14 S/cm.

A solution of 5.77 g of the copolymer according to Example A11 and 10 ml of pyrrole in 200 ml of propylene carbonate is reacted electrochemically as described in Example B6. After an electrolysis time of 1 hour, a 0.012 pm thick film is obtained. The conductivity is 3.7 S/cm. The film can be shaped at temperatures of ca. 150°C

A solution of 6.44 s of the copolymer according to Example A10 and 10 ml of pyrrole is reacted electrochemically as described in Example B6. After an electrolysis time of 1 hour, a 0.013 cm thick film is obtained. The conductivity is 4.6 S/cm. The film can be shaped at temperatures of ca. 150°C

16.7 g of the sulfated polyimide according to Example A12 are dissolved in 200 ml of propylene carbonate and 10 ml of pyrrole are added to the solution. After an electrolysis time of 53 minutes (200 As, a 0.006 cm thick film is obtained in accordance with Example B6. The conductivity is 3.9 S/cm.

7.16 g of the sulfated polyimide according to claim A13 are dissolved in 200 ml of propylene carbonate (0.05 molar) and to the solution are added 10 ml of pyrrole. In accordance with Example B6, a 0.01 cm thick film with a conductivity of 0.32 S/cm is obtained at a charging density of 200 As.

7.66 of the sulfated polyimide according to Example A14 are dissolved in 200 ml of propylene carbonate (0.05 molar, and to the solution are added 10 ml of pyrrole. In accordance with Example B6, a 0.009 cm thick film with a conductivity of 0.7 S/cm is obtained at a charging density of 200 As.

8 g of the sulfated polyimide according to Example A15 are dissolved in 200 ml of propylene carbonate (0.05 molar) and to the solution are added 10 ml of pyrrole. In accordance with Example B6, a 0.0095 cm thick film with a conductivity of 8 S/cm is obtained at a charging density of 200 As.

Wernet, Wolfgang, Stoffer, Jean

Patent Priority Assignee Title
5753774, Dec 18 1996 Witco Corporation Functional group terminated polymers containing sulfonate group via sulfonation of ethylenically unsaturated polymers
6166165, Dec 18 1996 CK Witco Corporation Polyurethane synthesis from functional group terminated polymers containing sulfonate groups
7683109, Sep 22 2004 Shin-Etsu Polymer Co., Ltd. Conductive composition and production method thereof, antistatic coating material, antistatic coating, antistatic film, optical filter, and optical information recording medium, and capacitors and production method thereof
7916455, Sep 22 2004 Shin-Etsu Polymer Co., Ltd. Conductive composition and production method thereof, antistatic coating material, antistatic coating, antistatic film, optical filter, and optical information recording medium, and capacitors and production method thereof
Patent Priority Assignee Title
4552927, Sep 09 1983 Rockwell International Corporation Conducting organic polymer based on polypyrrole
4806271, Feb 11 1987 BOARD OF TRUSTEES OF THE UNIVERSITY OF PENNSYLVANIA, THE A CORPORATION OF PENNSYLVANIA Preparation of base-type conducting polymers
4869979, Aug 10 1987 Nitto Electric Industrial Co., Ltd. Conducting organic polymer battery
4929389, Feb 12 1988 University of California Water-soluble conductive polymers
4933106, Nov 27 1986 Showa Denko Kabushiki Kaisha Highly conductive polymer composition and process for producing the same
5002699, Dec 29 1988 Honeywell INC Electrically conducting polymers and complexes
5068060, Aug 07 1986 Allied-Signal Inc. Neutral and electrically conductive poly(heterocyclic vinylenes) and processes for preparing same
5130054, Apr 02 1984 Senshin Capital, LLC Processable conductive polymers
DE3402133,
EP129070,
EP191726,
GB2124635,
JP63135453,
//
Executed onAssignorAssigneeConveyanceFrameReelDoc
Apr 27 1992Ciba-Geigy Corporation(assignment on the face of the patent)
Apr 06 1995Ciba-Geigy CorporationJAPAT LTD ASSIGNMENT OF ASSIGNORS INTEREST SEE DOCUMENT FOR DETAILS 0074380063 pdf
Date Maintenance Fee Events
Apr 05 1995M183: Payment of Maintenance Fee, 4th Year, Large Entity.


Date Maintenance Schedule
Jan 18 19974 years fee payment window open
Jul 18 19976 months grace period start (w surcharge)
Jan 18 1998patent expiry (for year 4)
Jan 18 20002 years to revive unintentionally abandoned end. (for year 4)
Jan 18 20018 years fee payment window open
Jul 18 20016 months grace period start (w surcharge)
Jan 18 2002patent expiry (for year 8)
Jan 18 20042 years to revive unintentionally abandoned end. (for year 8)
Jan 18 200512 years fee payment window open
Jul 18 20056 months grace period start (w surcharge)
Jan 18 2006patent expiry (for year 12)
Jan 18 20082 years to revive unintentionally abandoned end. (for year 12)