A catheter guide wire is provided for guiding a catheter into a body cavity such as a blood vessel. The base material constituting the wire is made of an elastic alloy wire and subjected to a heat treatment such that its flexibility is sequentially increased from its proximal to distal end portions. A thermoplastic resin or/and a coil spring can be applied to at least the distal end portion of the wire base material. A method of manufacturing the catheter guide wire is also provided. The method is characterized in that the leading end side of the base material is divided into a plurality of areas and subjected to a heat treatment by changing the heat treatment temperature and the time conditions in units of the areas so that the flexibility of the base material is sequentially increased from the proximal to distal end portions of the leading end side.
|
3. A method of making a catheter guide wire for guiding a catheter, said method comprising:
forming a wire member comprising a superelastic Ni-Ti alloy wire as a base material, said base material having a proximal end portion and a leading end side; dividing said leading end side of said base material into a plurality of areas along the length thereof and a distal end portion, said plurality of areas comprising an intermediate portion between said proximal and distal end portions; and subjecting only said intermediate portion and said distal end portion to a primary heat treatment at a temperature of 400° to 500°C for about two hours, and thereafter subjecting only said distal end portion to a secondary heat treatment at a temperature of about 200°C for about 24 hours, whereby said proximal end portion is not heat treated after cold rolling, such that, after said primary and secondary heat treatments, flexibility of the guide wire is increased from said proximal end portion to said distal end portion thereof.
1. A method of making a catheter guide wire for guiding a catheter, said method comprising:
forming a wire member comprising a superelastic Ni-Ti alloy wire as a base material, said base material having a proximal end portion and a leading end side; dividing said leading end side of said base material into a plurality of areas along the length thereof and a distal end portion, said plurality of areas comprising an intermediate portion between said proximal and distal end portions; and subjecting only said intermediate portion and said distal end portion to a primary heat treatment at a temperature of 400° to 500°C for about two hours, and then subjecting only said distal end portion to a secondary heat treatment at a temperature of about 200°C for about 24 hours, whereby said proximal end portion is not heat treated after cold rolling, such that said distal end portion, after said primary and secondary heat treatments, has a yield stress of approximately 5 to 7 kg/mm2, and at least one of said areas at said intermediate portion, after said heat treatment, has a yield stress of approximately 11 to 12 kg/mm2.
5. A process for forming a guide wire for a catheter, said guide wire having a proximal end and a distal end, comprising:
forming a Ni-Ti alloy wire; cold rolling said Ni-Ti alloy wire; forming said distal end portion and said proximal end portion of said guide wire, said distal end portion having a diameter that is less than a diameter of said proximal end portion; and subsequently heat treating said distal end portion of said guide wire so as to make said distal end portion more flexible than said proximal end portion. 6. A process for forming a guide wire for a catheter, said guide wire having a proximal end and a distal end, comprising: forming a Ni-Ti alloy wire; cold rolling said Ni-Ti alloy wire; forming said distal end portion and said proximal end portion of said guide wire, said distal end portion having a diameter that is less than a diameter of said proximal end portion; subsequently heat treating said distal end portion of said guide wire so as to make said distal end portion more flexible than said proximal end portion; and forming a thermoplastic resin layer on said guide wire. 7. A process for forming a guide wire for a catheter, said guide wire having a proximal end and a distal end, comprising: forming a Ni-Ti alloy wire; cold rolling said Ni-Ti alloy wire; forming said distal end portion and said proximal end portion of said guide wire, said distal end portion having a diameter that is less than a diameter of said proximal end portion; subsequently heat treating said distal end portion of said guide wire so as to make said distal end portion more flexible than said proximal end portion; and mounting a coil spring around at least a portion of said guide wire.
8. A process for forming a guide wire for a catheter, said guide wire having a proximal end and a distal end, comprising: forming a Ni-Ti alloy wire; cold rolling said Ni-Ti alloy wire; forming said distal end portion and said proximal end portion of said guide wire, said distal end portion having a diameter that is less than a diameter of said proximal end portion; subsequently heat treating said distal end portion of said guide wire so as to make said distal end portion more flexible than said proximal end portion; forming a thermoplastic resin layer on said guide wire; and mounting a coil spring around at least a portion of said guide wire. 2. A method according to
4. A method according to
|
|||||||||||||||||||||||||||||
This application is a division of application Ser. No. 07/657,895, filed Feb. 19, 1991, now abandoned, which is a continuation of Ser. No. 07/381,391 filed Jul. 5, 1989, now abandoned. This application is a continuation of application Ser. No. 08/671,972, filed Jun. 28, 1996, now abandoned, which is a continuation of application Ser. No. 08/357,570, filed Dec. 15, 1994 now abandoned, which is a Reissue of U.S. Pat. No. 5,171,383, issued Dec. 15, 1992, which is a divisional of application Ser. No. 07/657,895, filed Feb. 19, 1991, abandoned, which is a continuation of application Ser. No. 07/381,391, filed Jul. 5, 1989, now abandoned.
The present invention relates to a catheter guide wire for guiding a clinical or testing catheter to a predetermined portion of a body cavity such as a blood vessel, a digestive tract, and a windpipe and holding it therein, and a method of manufacturing the same.
When a catheter is to be guided to a branching peripheral portion of a blood vessel or the like, first, a guide wire must be guided to a target portion. In this case, since a target portion is generally thin and thus tends to be easily damaged, the distal end portion of the guide wire must be flexible so that it will not damage a blood vessel wall, will follow the shape of the blood vessel well even if the blood vessel is curved, and can be inserted in a complex branching blood vessel. Meanwhile, the proximal end portion of the guide wire must have torque transmitting performance so that a manual operation performed at the proximal end portion is transmitted to the distal end portion. Thus, the proximal end portion of the guide wire must have comparatively high rigidity.
According to a conventional catheter guide wire having the above characteristics, a coil guide wire is made of a stainless steel wire or a piano wire, or a guide wire is made of a plastic monofilament. In each of these guide wires, its sectional area is decreased from its proximal to distal end portion, and the guide wire forms a main portion having relatively high rigidity and a relatively flexible distal end portion.
However, plastic deformation can easily occur in these conventional guide wires, and some manual operation can kink the guide wires. A kinked portion becomes an obstacle during introduction of a catheter, thus rendering smooth introduction operation of a catheter impossible as well as greatly degrading its torque transmitting performance.
A catheter guide wire free from such kinking deformation uses a very elastic alloy (e.g., Ni-Ti alloy) as a core member (see Japanese Patent Disclosure (Kokai) No. 60-63066).
A guide wire using a very elastic alloy is flexible and can restore its original shape after it is deformed to a considerable degree (strain of about 8%). Therefore, such a guide wire cannot be easily broken during operation and will not easily attain a bending tendency. However, such guide wire has a high elasticity at its distal end portion and is thus infavorable in terms of flexibility. Then the diameter of its proximal end portion is 0.5 mm or less, the rigidity is insufficient and the torque transmitting performance is poor.
The present invention has been made in view of the above situation and has as its object to provide a catheter guide wire wherein its distal end portion is very flexible, buckling deformation is difficult to occur, and its proximal end portion is very rigid, thus having a good torque transmitting performance to the distal end portion, and a method of manufacturing the same.
In order to solve the above problems, according to the present invention, a wire member made of an elastic alloy, and preferably a very elastic alloy, is used as a core member of a catheter guide wire and subjected to a heat treatment by changing the treatment conditions along its longitudinal direction, so that the rigidity at its proximal end portion becomes comparatively high, the flexibility at its distal end portion is increased, and kinking deformation will not easily occur in its distal end portion.
More specifically, according to the present invention, there is provided a catheter guide wire having leading and trailing end sides, characterized in that the guide wire comprises a wire member made of an elastic alloy member, at least the leading end side thereof has an outer diameter equal to or smaller than a minimum inner diameter of a catheter, and the wire member is subjected to a heat treatment so that its flexibility is sequentially increased from a proximal to distal end portion of the leading end side thereof.
Note that the catheter guide wire can be fabricated by using as a core member a wire member made of an elastic alloy member subjected to the heat treatment described above and forming a cover layer of a thermoplastic resin on the core member.
The core member preferably uses a very elastic alloy such as an Ni-Ti alloy, a Cu-Zn-Al alloy, a Cu-Al-Ni alloy, and an Fe-Mn alloy. The core member is preferably tapered such that a diameter at its distal end portion is smaller than that at its proximal end portion. A contrast medium such as a tungsten powder can be added to the thermoplastic resin layer.
A flexible coil spring having an outer diameter equal to or smaller than a minimum inner diameter of the catheter can be mounted to surround at least the distal end portion of the wire member.
In this case, the coil spring is preferably made of a material having a high X-ray impermeability in order to allow an X-ray photographing to be easily confirmed. Therefore, the presence of the coil spring is advantageous in giving a sufficient thickness in an X-ray image without badly affecting the flexibility of the guide wire.
As a result, the coil spring is made of a material selected from a group consisting of stainless steel, platinum, a platinum alloy and a palladium alloy, and preferably has a thickness of 0.01 to 0.15 mm, more preferably 0.05 to 0.1 mm.
Furthermore, according to the present invention, there is provided a method of manufacturing a catheter guide wire fabricated by using an elastic alloy wire as a base material, characterized in that a leading end side of the base material is divided into a plurality of areas, and a heat treatment is performed by changing the temperatures and time in units of the areas so that the flexibility of the base material is sequentially increased from the proximal to distal end portion of the leading end side.
In a conventional catheter guide wire, a diameter at a proximal end portion of a wire member made of an elastic alloy or a very elastic alloy is merely increased, and a diameter at its distal end portion is relatively decreased, thereby making the proximal end portion rigid and the distal end portion flexible. Unlike such a conventional catheter guide wire, according to the present invention, a wire member is subjected to a heat treatment by sequentially changing the confunction along its longitudinal direction. As a result, the physical characteristics of the wire member can be set in an ideal state as a catheter guide wire.
FIG. 1 is a sectional view of a catheter guide wire according to an embodiment of the present invention;
FIG. 2 is a graph of strain-stress curves of the core member of the guide wire according to the embodiment of the present invention; and
FIGS. 3 and 4 respectively represent a sectional view of a catheter guide wire on which a coil spring is mounted according to another embodiment of the present invention.
Preferred embodiments of the present invention will be described with reference to the accompanying drawings.
FIG. 1 is a sectional view of a catheter guide wire taken along the longitudinal direction according to an embodiment of the present invention. Referring to FIG. 1, reference numeral 1 denotes a core member; and 2, a thermoplastic resin layer entirely covering core member 1.
Core member 1 is a wire member made of an elastic alloy wire such as a piano wire, and preferably a very elastic alloy such as an Ni-Ti alloy. Core member 1 can have a uniform diameter of 0.2 to 0.4 mm, or can be tapered toward its distal end such that the diameter at its proximal end portion is 0.2 to 0.4 mm and the diameter at its distal end portion is 0.01 to 0.1 mm. In this specification, a very elastic alloy is defined as an alloy whose recoverable elastic strain is as large as several % to more than ten % and whose stress level does not exceed a predetermined value even if the strain is increased. The very elastic alloy generally comprises an Ni-Ti, Cu-Zn-Al, Cu-Al-Ni, or Fe-Mn alloy. If an Ni-Ti alloy is employed, it preferably contains 49 to 58 atm. % of Ni and a balance of Ti, and more preferably 49 to 51 atm. % of Ni and a balance of Ti. If a Cu-Zn-Al alloy is employed, it preferably contains 38.5 to 41.5 wt. % of Zn, 1 to 10 wt. % of ADP, and a balance of Cu. If a Cu-Al-Ni alloy is employed, it preferably contains 14 to 14.5 wt. % of Al, 3 to 4.5 wt. % of Ni, and a balance of Cu. If an Fe-Mn alloy is employed, it preferably contains 28 to 32 wt. % of Mn, 6 wt. % of Si, and a balance of Fe. A heat treatment is performed by changing the treatment conditions. As a result, the guide wire can have the following physical characteristics in its areas (1) to (III) as shown in FIG. 1.
(1) Proximal end portion (I)
When the guide wire is guided from, e.g., a straight great blood vessel (e.g., a descending aorta) to an arteriole (e.g., a coronary artery), proximal end a comparatively small number of bent portions. Proximal and portion (I) has a comparatively high rigidity and is difficult to deform. Therefore, forward/backward movement and rotation externally applied to the catheter can be easily transmitted to the distal end portion (II--III) through a blood vessel retaining an introducer (not shown).
(2) Intermediate portion (II)
Intermediate portion (II) has an elasticity so that it can easily follow a blood vessel curve of a comparatively large curve and can return to its initial shape when deformation caused by the curve is removed. Although it is flexible, intermediate portion (II) hardly attains a bending tendency and is difficult to break.
(3) Distal end portion (III)
When distal end portion (III) is inserted in a small, curved blood vessel, it can easily follow the blood vessel shape due to its flexibility, and thus will not damage the blood vessel wall. When a blood vessel has phatologic factor such as arteriosclerosis, the flexibility of distal end portion (III) is important.
Thermoplastic resin layer 2 is provided as needed in order to protect the inner surface of the blood vessel, to prevent formation of thrombus on an outer surface of the guide wire during operation of the guide wire, and not to form a difference in outer diameter between the proxital end portion and the distal end portion. For example, saturated aliphatic polyether urethane is used to form layer 2. A contrast medium can be mixed in the thermoplastic resin in advance in order to increase the contrast of the guide wire through X-ray photographing. For example, 40 to 600 parts by weight (with respect to 100 parts by weight of thermoplastic resin) of a tungsten powder can be mixed as the contrast medium. Note that saturated aliphatic polyether polyurethane is favorable for compounding of tungsten.
FIG. 2 shows the physical characteristics (strain-stress curve) at the respective portions of the core member of the present invention after a heat treatment. A heat treatment can be performed in an atmosphere of an inert gas (Ar or He), vacuum (×10-2 Torr or less) or outer atmosphere. Although a heat treatment can be performed in an outer atmosphere, it is preferably performed in a vacuum in view of embrittlement of the material, and more preferably in an inert gas. The values in FIG. 2 are obtained by cutting the core member sample into 70-mm long pieces starting from its distal end and subjecting the respective samples to a tension test.
Core member: Ni-Ti alloy wire (diameter: 0.4 mm) (49 atm. % of Ni and a balance of Ti)
Heat treatment conditions:
| ______________________________________ |
| Tension |
| Area of Test |
| Guide Wire |
| Heat Treatment Conditions |
| Sample No. |
| ______________________________________ |
| Distal end |
| About 2 hrs. at 400 to 500°C |
| (1) (2) |
| portion (III) |
| and about 24 hrs. at 200°C |
| (in outer atmosphere) |
| Intermediate |
| About 2 hrs. at 400 to 500°C |
| (3) (4) (5) |
| portion (II) |
| (in outer atmosphere) |
| Proximal end |
| No heat treatment after |
| (6) |
| portion (I) |
| cold rolling |
| ______________________________________ |
The physical characteristics at the respective portions of core member 1 are not limited to those shown in FIG. 2 and can be arbitrarily adjusted and selected in accordance with specific applications.
FIG. 3 is a partial sectional view of a catheter guide wire according to another embodiment of the present invention. Thermoplastic resin layer 2 is formed on the entire surface of core member 1 in the same manner as in FIG. 1, and coil spring 3 having a thickness of 0.08 mm is mounted on an outer surface of resin layer 2 excluding its leading and trailing end faces. Note that coil spring 3 may be provided at only the distal end portion of the guide wire. The outer diameter of the guide wire may be conveniently selected to conform with the inner diameter of a blood vessel to be inserted. Generally, however, the outer diameter of the guide wire may be selected within a range of from 0.2 to 2.0 mm.
When coil spring 3 is applied on resin layer 2 in this manner, the physical characteristics of the guide wire are as flexible at its distal end portion as shown in FIG. 1 and highly resistive to buckling deformation due to the high flexibility of the coil spring 3, relatively high in rigidity at its proximal end portion and excellent in X-ray photographing.
Coil spring 3 can be provided to directly surround core member 1 without intervening thermoplastic resin layer 2.
FIG. 4 shows an example of such a structure of the guide wire, wherein the coil spring 3 is directly wound around the outer wall of core member 1, with its distal and proximal end portions being fixed to core member 1 through a soldering material 4 made for example of Sn-Ag (96:4) alloy.
As described above, according to the catheter guide wire of the present invention, a wire member made of an elastic alloy is used as a core member and subjected to a heat treatment by sequentially changing the treatment conditions along its longitudinal direction. As a result, the proximal end portion of the guide wire has predetermined rigidity required in accordance with its application, and its distal end portion has predetermined flexibility.
The guide wire as proposed by this invention is useful for guiding a clinical or testing catheter to a predetermined portion of a body cavity such as blood vessel, a digestive tract and a windpipe, and holding it therein for a period of time.
Sugiyama, Yoshiaki, Sagae, Kyuta
| Patent | Priority | Assignee | Title |
| 10258773, | Apr 23 2007 | CARDIOGUIDANCE BIOMEDICAL, LLC | Guidewire with adjustable stiffness |
| 10967153, | Feb 08 2007 | C. R. Bard, Inc. | Shape memory medical device and methods of use |
| 6280539, | Dec 18 1990 | ABBOTT CARDIOVASCULAR SYSTEMS INC | Superelastic guiding member |
| 6582536, | Apr 24 2000 | Biotran Corporation Inc. | Process for producing steerable sheath catheters |
| 6790170, | Nov 08 2000 | Theragenics Corporation | Radioactive source wire and dual lumen catheter system for brachytherapy |
| 7163550, | Mar 26 2003 | Boston Scientific Scimed, Inc | Method for manufacturing medical devices from linear elastic materials while maintaining linear elastic properties |
| 7244319, | Dec 18 1990 | ABBOTT CARDIOVASCULAR SYSTEMS INC | Superelastic guiding member |
| 7455737, | Aug 25 2003 | Boston Scientific Scimed, Inc | Selective treatment of linear elastic materials to produce localized areas of superelasticity |
| 7637875, | Dec 28 2006 | Terumo Kabushiki Kaisha | Guide wire |
| 7641622, | Feb 09 2007 | Terumo Kabushiki Kaisha | Guide wire |
| 7665212, | Feb 23 2005 | Ultradent Products, Inc. | Methods for manufacturing endodontic instruments |
| 7743505, | Feb 23 2005 | Ultradent Products, Inc. | Methods for manufacturing endodontic instruments from powdered metals |
| 7744545, | Dec 28 2006 | Terumo Kabushiki Kaisha | Guide wire |
| 7753859, | May 11 2007 | Terumo Kabushiki Kaisha | Guide wire |
| 7762962, | Jan 12 2007 | Terumo Kabushiki Kaisha | Intermediate member, and a medical device and guide wire including such an intermediate member |
| 7780611, | May 01 2003 | Boston Scientific Scimed, Inc | Medical instrument with controlled torque transmission |
| 7896820, | Dec 26 2006 | Terumo Kabushiki Kaisha | Guide wire |
| 7918011, | Dec 27 2000 | Abbott Cardiovascular Systems, Inc. | Method for providing radiopaque nitinol alloys for medical devices |
| 7938843, | Nov 02 2000 | ABBOTT CARDIOVASCULAR SYSTEMS INC | Devices configured from heat shaped, strain hardened nickel-titanium |
| 7942892, | May 01 2003 | ABBOTT CARDIOVASCULAR SYSTEMS INC | Radiopaque nitinol embolic protection frame |
| 7976648, | Nov 02 2000 | ABBOTT CARDIOVASCULAR SYSTEMS INC | Heat treatment for cold worked nitinol to impart a shape setting capability without eventually developing stress-induced martensite |
| 8002909, | Jan 08 2003 | Boston Scientific Scimed, Inc. | Medical devices |
| 8128580, | Mar 29 2007 | Terumo Kabushiki Kaisha | Guide wire |
| 8172774, | Mar 23 2007 | Terumo Kabushiki Kaisha | Guide wire |
| 8206837, | Jan 12 2007 | Terumo Kabushiki Kaisha | Interventional medical device |
| 8292829, | May 01 2003 | Boston Scientific Scimed, Inc. | Medical instrument with controlled torque transmission |
| 8485992, | May 27 2003 | Boston Scientific Scimed, Inc. | Medical device having segmented construction |
| 8728010, | Aug 24 2006 | Boston Scientific Scimed, Inc. | Elongate medical device including deformable distal end |
| 8758268, | Feb 08 2007 | C R BARD, INC | Shape memory medical device and methods of use |
| 8845552, | May 01 2003 | Boston Scientific Scimed, Inc. | Medical instrument with controlled torque transmission |
| 8900216, | Jul 26 2006 | Johan Willem Pieter Marsman | Facilitation of antegrade insertion of a guidewire into the superficial femoral artery |
| 9387308, | Apr 23 2007 | CARDIOGUIDANCE BIOMEDICAL, LLC | Guidewire with adjustable stiffness |
| 9387309, | Apr 23 2007 | CARDIOGUIDANCE BIOMEDICAL, LLC | Guidewire with adjustable stiffness |
| 9498603, | Apr 23 2007 | CARDIOGUIDANCE BIOMEDICAL, LLC | Guidewire with adjustable stiffness |
| Patent | Priority | Assignee | Title |
| 3521620, | |||
| 3789841, | |||
| 3906938, | |||
| 4037324, | Jun 02 1972 | The University of Iowa Research Foundation | Method and system for orthodontic moving of teeth |
| 4144057, | Aug 26 1976 | MEMRY CORPORATION DELAWARE CORPORATION | Shape memory alloys |
| 4484955, | Dec 12 1983 | Shape memory material and method of treating same | |
| 4654092, | Nov 15 1983 | MEMRY CORPORATION DELAWARE CORPORATION | Nickel-titanium-base shape-memory alloy composite structure |
| 4665906, | Oct 14 1983 | Medtronic, Inc | Medical devices incorporating sim alloy elements |
| 4748986, | Dec 12 1983 | Advanced Cardiovascular Systems, Inc. | Floppy guide wire with opaque tip |
| 4813434, | Feb 17 1987 | MEDTRONIC VERSAFLEX, INC | Steerable guidewire with deflectable tip |
| 4925445, | Sep 16 1983 | Terumo Corporation | Guide wire for catheter |
| 4935068, | Jan 23 1989 | Memry Corporation | Method of treating a sample of an alloy |
| 4943326, | Oct 23 1987 | FURUKAWA ELECTRIC CO , LTD , THE; YAMAGUCHI PEARL, CO , LTD | Ornament and method of manufacturing the same |
| 4984581, | Oct 12 1988 | EV3 INC | Flexible guide having two-way shape memory alloy |
| 5069226, | Apr 28 1989 | NEC Tokin Corporation | Catheter guidewire with pseudo elastic shape memory alloy |
| 5190546, | Oct 14 1983 | Medtronic, Inc | Medical devices incorporating SIM alloy elements |
| 5230348, | Oct 12 1990 | DYMEC CO , LTD | Guide wire for a catheter |
| 5238004, | Apr 10 1990 | Boston Scientific Scimed, Inc | High elongation linear elastic guidewire |
| 5341818, | Dec 22 1992 | ABBOTT CARDIOVASCULAR SYSTEMS INC | Guidewire with superelastic distal portion |
| 5637089, | Dec 18 1990 | ABBOTT CARDIOVASCULAR SYSTEMS INC | Superelastic guiding member |
| EP13604, | |||
| EP141006, | |||
| EP161066, | |||
| JP59048643, | |||
| JP59219443, | |||
| JP60063066, | |||
| JP60138547, | |||
| JP61106173, | |||
| WO85011444, |
| Executed on | Assignor | Assignee | Conveyance | Frame | Reel | Doc |
| Oct 16 1997 | Terumo Kabushiki Kaisha | (assignment on the face of the patent) | / |
| Date | Maintenance Fee Events |
| Jun 05 2000 | M184: Payment of Maintenance Fee, 8th Year, Large Entity. |
| May 12 2004 | M1553: Payment of Maintenance Fee, 12th Year, Large Entity. |
| Date | Maintenance Schedule |
| Mar 28 2003 | 4 years fee payment window open |
| Sep 28 2003 | 6 months grace period start (w surcharge) |
| Mar 28 2004 | patent expiry (for year 4) |
| Mar 28 2006 | 2 years to revive unintentionally abandoned end. (for year 4) |
| Mar 28 2007 | 8 years fee payment window open |
| Sep 28 2007 | 6 months grace period start (w surcharge) |
| Mar 28 2008 | patent expiry (for year 8) |
| Mar 28 2010 | 2 years to revive unintentionally abandoned end. (for year 8) |
| Mar 28 2011 | 12 years fee payment window open |
| Sep 28 2011 | 6 months grace period start (w surcharge) |
| Mar 28 2012 | patent expiry (for year 12) |
| Mar 28 2014 | 2 years to revive unintentionally abandoned end. (for year 12) |