Excellent films of a high Tc superconductor are easily produced on metal coated substrates at a temperature below 700°C These metal buffer films are made of Pt, Au, Ag, Pd, Ni or Ti. The film superconductivity is significantly improved by the metal buffer layer. Since it is easy to form this metal coating on a substrate, the invention can increase the potential number of usable substrates such as fibers, amorphous solids or semiconductors.
|
1. A superconductor comprising an A--b--cu oxide film deposited on a metal film formed on a substrate, said A--b--cu oxide containing elements A and b and cu and O, the molar ratio of said elements A and b and cu being in a range of ##EQU4## wherein the element A is one element selected from Tl, Bi, Pb, Y and lanthanum series elements (atomic number: 57-71), and the element b is one element selected from the Group IIa elements; and said metal film being a transition metal element selected from Pt, Au, Ag, Pd, Ni and Ti the composition A--b--cu--O of said oxide film being in the form of layered perovskite-like structure.
2. A superconductor according to
multi-layer structure.3. A superconductor according to claim 1 comprising an A--b--cu oxide film deposited on a metal film formed on a substrate, said A--b--cu oxide containing elements A and b and cu and O, the molar ratio of said elements A and b and cu being in a range of ##EQU5## wherein the element A is one element selected from Tl, Bi, Pb, Y and lanthanum series elements (atomic number: 57-71), and the element b is one element selected from the Group IIa elements; and said metal film being a transition metal element selected from Pt, Au, Ag, Pd, Ni and Ti, and the composition A--b--cu--O of said oxide film being in the form of layered perovskite structure, wherein the a surface of said substrate is coated with a glass film selected from the group consisting of quartz glass, high silica glass, borosilicate glass, soda-lime glass and oxynitride glass and wherein the glass film is positioned between the substrate and the metal film. 4. A superconductor according to
5. A superconductor according to
6. A superconductor according to
crystal (100) plane or (110) plane MgO substrate.7. A superconductor according to claim 3, using a single crystal R plane sapphire substrate. A superconductor according to claim 3, using a single crystal C plane sapphire substrate. 9. A superconductor according to claim 3, using a single crystal A plane sapphire substrate. 10. A superconductor according to claim 2 3, using a single crystal (111) plane spinel substrate. 11. A superconductor according to claim 3, using a single crystal (110) plane spinel substrate. 12. A superconductor according to claim 3, using a single crystal (100) plane spinel substrate.
13. A superconductor according to
plane or (110) plane strontium titanate substrate.14. A superconductor according to claim 1 comprising an A--b--cu oxide film deposited on a metal film formed on a substrate, said A--b--cu oxide containing elements A and b and cu and O, the molar ratio of said elements A and b and cu being in a range of ##EQU6## wherein the element A is one element selected from Tl, Bi, Pb, Y and lanthanum series elements (atomic number: 57-71), and the element b is one element selected from the Group IIa elements; and said metal film being a transition metal element selected from Pt, Au, Ag, Pd, Ni and Ti, and the composition A--b--cu--O of said oxide film being in the form of layered perovskite structure, using a fiber substance substrate wherein the fiber is selected from the group consisting of glass fiber, carbon fiber, quartz fiber and heat resistant metal alloy fibers. 15. A superconductor according to claim 14, wherein the fiber substrate is made of glass fiber, carbon fiber or a heat-resistant metal alloy fiber such as the fiber of Nb, Ti, Ta, stainless steel or the like. 16. A superconductor according to
17. An article comprising:
(a) a substrate (b) a noble metal buffer layer selected from the group consisting of silver and gold formed on said substrate (c) a high temperature superconductor layer consisting of Y--Ba--cu--O formed on said buffer layer.
18. An article comprising:
(a) a substrate (b) a metal buffer layer selected from the group consisting of nickel, palladium, platinum, gold, silver and titanium formed on said substrate (c) a high temperature superconductor layer consisting of a high temperature superconducting layer formed on said buffer
layer. The superconductor according to |
|||||||||||||||||||||||||||
This invention relates to a superconductor, more particularly to a compound film superconductor.
A-15 type binary (two-element) compounds such as niobium nitride (NbN) and niobium germanide (Nb3 Ge) had been known as high Tc superconductors, but the superconducting transition temperature of these materials was only about 24° K. at highest. Perovskite type ternary (three-element) compounds have been expected to show higher transition temperatures, and a Ba═La═Cu--O high-Tc-superconductor has been proposed (J. B. Bendorz and K. A. Muller, Zetschrift Fur Physik B-Condensed Matter, 64, 189-193, 1986).
Recently it was reported that Y═Ba═Cu--O type compounds could form superconductors with even higher transition temperatures than those of prior ones (M. K. Wu et al, Physical Review Letters, Vol. 58, No. 9, 908-910, 1987).
The superconducting mechanism of the Y═Ba--Cu--O type materials is not yet definitely known, but there is a possibility that these materials could have respectively transition temperatures higher than the temperature of liquid nitrogen and it is expected that such compounds would show more useful properties than the conventional binary compounds as high-Tc-superconductors.
More recently, as superconductive materials with higher transition temperatures, Bi═Si--Ca--Cu--O system (H. Maeda et al, Japanese Journal of Applied Physics, 27, 1988, L298) and Tl--Ba--Ca--Cu--O Systems (Z. Z. Sheng et al, Nature, 332, 1988, L139) have been discovered, both of which have transition temperatures higher than 120° K.
However, with the present technical level, these oxide superconductive materials can only be produced by a sintering process, so that these supercondutive materials are available only in the form of powders or blocks of ceramics. In the practical applications of these types of materials, it is strongly desired that they are made into a film or wire. It has been, however, very difficult with the conventional technique to obtain a desired film or wire from these materials because of the poor reproducibility and a lack of reliability of their superconductive properties when they are made into a film or wire.
The present inventors found that it is possible to form from these materials a high Tc superconductor film retaining well the characteristics of these materials by using film producing techniques such as sputtering etc. and adding a novel concept to the interface structure of the superconductor film. Based on this finding and by further incorporating unique ideas in the film substrate, the present inventors have succeeded in creating a novel superconducting film structure.
The superconductor according to this invention comprises an oxide film deposited on a metal film formed on a substrate, these oxide containing A, B and Cu and being a ternary (three-element) or quaternary (four-element) compound having an elemental ratio satisfying the following relation: ##EQU1## wherein A is at least one element selected from Tl, Bi, Sc, Y and lanthanum series elements (atomic number: 57-71), and B is at least one elements selected from Ba, Sr, Ca, Be, Mg and Group IIa elements.
The superconductor of this invention is essentially characterized in that a superconductive film is formed on a metal buffer film. The superconductive film is produced from the sputtering target which is made by breaking down its bare material into very fine powder and depositing such powdery target on a substrate, so that the composition of the formed superconductor film is essentially homogeneous as compared with the conventional sintered materials. Also, the superconductive film is homogeneously deposited and it becomes dense and flat on a metal film. Therefore, the present invention can not only realize an extraordinarily high quality superconductor but also increase the potential number of usable substrates, making it possible to obtain a film structure suitable for realizing various types of superconductor devices having superconductive films.
FIG. 1 is a sectional view showing the structure of a substrate for a superconductor as an embodiment of this invention.
FIG. 2 is a view showing the surface morphology of this superconductor as observed by SEM photography (10,000 magnifications).
FIG. 3 is a similar view to FIG. 1 of the superconductor surface when no Pt film was deposited.
FIG. 4 is a sectional view of a superconductor on a glass-coated substrate.
FIG. 5 is a sectional view showing the structure of a superconductor on an amorphous substrate.
FIG. 6 is a graph showing comparatively the current density in a film formed directly on a sapphire substrate and that in a film formed on a Pt-coated substrate.
Referring to FIG. 1, a ternary or quaternary compound film 13 is deposited, by sputtering for instance, on a metal film 12 formed on the surface of a substrate 11. Substrate 11 is designed to hold the superconductive compound film 13. This compound film 13 is formed usually at a high temperature on the order of 700°C When a ternary compound film was formed directly on substrate 11 with no buffer layer of metal film 12, the superconductive film gave a surface morphology shown in FIG. 3, that is, it became a micro-crystalline plate 20 and was in a state of being directed randomly. This film was small in superconducting critical current, high in hygroscopicity because of high vacancy rate, poor in reliability, with a roughened surface and incapable of micro-fabrication such as photoetching.
When the metal film 12 was formed at the interface between substrate 11 and a film 13 of a ternary compound such as YbaCuO, there was obtained a smooth surface state as illustrated in FIG. 2. As noted from the surface morphology, the film 13 was in a dense state in its morphology and the critical current density was improved approximately 10 times over the film of FIG. 3. The results are represented graphically in FIG. 6. The present inventors have also confirmed the enhancement of zero-resistance temperature from 73 K to 88 K and a significant improvement of film quality. Thus, the intervention of metal film 12 has produced a remarkable effect for the improvement of various superconductive properties, too.
As a result of studies on the materials of metal film 12 shown in FIG. 1, the present inventors found that Ni, Pd, Pt, Au, Ag and Ti were effective, Pt being the best choice. The similar effect was seen in use of quaternary compounds such as Bi--Ca--CuO and TlBaCaCuO. However, no desired film could be formed on a Mo, Ta, or Cu surface.
Among the substrates mentioned above, there are some on which it is difficult to form a metal film by said sputtering. In such a case, a glass coating 14 is first formed on substrate 11 and then a metal film 12 is formed thereon, followed by deposition thereon of a superconductive oxide film at a high temperature of about 700°C as shown in FIG. 4. Quartz glass, high silica glass, borosilica glass, soda-lime glass and oxynitride glass could be effectively used for such glass coating.
The present inventors also found that certain materials could be advantageously used for the substrate 11 of FIG. 1 for obtaining its best performance.
A single crystal substrate is effective for forming a highly crystalline ternary or quaternary oxide compound film 13 on the surface of metal film 12 provided on substrate 11. As a result of research on substrate materials effective for forming a superconductor comprising a ternary oxide compound film, the present inventors confirmed that single crystals of magnesium oxide (MgO), sapphire (α--al2 O3), spinel, strontium titanate (SrTiO3), silicon (Si), silicon compounds, gallium arsenide etc. are effective as substrate material. This was quite a surprising revelation. The thickness of metal film 12 is usually in the range of tens to thousands of angstroms (Å), so that it is inconceivable from conditional knowledge that the ternary compound film should be influenced by the crystallinity of the substrate therebelow.
The crystalline structure and chemical composition of the A--B--Cu--O superconductor of this invention are not yet definitely known, but the analyses show that is has an oxygen-defected perovskite structure. The present inventors confirmed that when the elemental ratio in the produced film is in the range defined by ##EQU2## a superconducting phenomenon is observed in the film through there could be slight differences in transition temperature.
In sputtering deposition, a sintered A--B--Cu--O ceramic is used as target, but in case the substrate temperature is 700°C, there is seen a tendency that the produced film becomes deficient in Cu as compared with the metal components of the target. The present inventors confirmed, however, that this can be overcome by adding about 50% excess amount of Cu in the target. From the above, it was determined that the target composition should be the one defined by ##EQU3## which falls in the optimal compositional range of the film. If the target composition is in this range, desired sputtering deposition can be accomplished not only when the target is plate-like, cylindrical or fiber-like ceramic but also when it is in the form of sintered particles or powders. In the case where the target is in a powdery form, the powder is placed in, for instance, a stainless steel dish. In case of using a fiber-like substrate, it is effective to employ glass fiber, carbon fiber or heat-resistant alloy fibers comprising niobium, titanium, tantalum, stainless steel, etc.
The present inventors confirmed that when fabricating this type of superconductor is a desired form, for example, in a cylindrical form, it is more effective to use a metal-coated substrate so-called sintered chinaware than single crystals, and they also found the most suitable chinaware materials. That is, the present inventors confirmed that alumina, magnesia, zirconia, steatite, forsterite, beryllia, spinel and the like are best suited for use as metal-coated chinaware substrate these materials are excellent in workability and fitness to the substrate 11 of the superconductive film 12. In this case, it suffices if at least the surface of the substate is composed of said chinaware material as in the case of single crystals.
As a result of more close examinations on effectiveness of these crystalline substrates, the present inventors found that there is a preferred direction for crystalline orientation of this type of crystalline substrate. It was discovered that in case of using single crystals of sapphire as substrate, it is possible to integrate the superconductive film of this invention in a silicon device of an SOS (silicon on supphire) structure by heteroepitaxially growing a (100) Si film on the R plane. The present inventors also confirmed that in the case of C plane and a plane sapphire, the integration with an SOS silicone device is possible by heteroepitaxially growing a (111) Si film on the planes.
It was further confirmed by the present inventors that in the case of a C plane sapphire single substrate, it is possible to integrate a superconductor of a laminar structure of this invention with a Group III-V semiconductor device by heteroepitaxially growing a Group III-V semiconductor film such as a (111) GaAs film, (001) GaN film, (111) GaP film, etc., on said substrate. This indicates the practical applicability of the superconductor of this invention for wiring of ultra-high-speed GaAs devices. The present inventors also confirmed that in the case of spinel single crystal substrate, it is possible to integrate the superconductor of this invention with an Si or GaAs device in the same was as in the case of sapphire single crystal substrate by heteroepitaxially growing a (100) Si film or (111) GaAs film on the substrate surface by using the (100) plane spinel.
It was further ascertained that in the case of using a (110) plane spinel substrate, integration with an Si or GaAs device is possible by effecting heteroepitaxial growth of a (110) Si film or (100) GaAs film on the substrate surface. The present inventors also disclosed that in the case of SrTiO3 singular crystal substrate, the grown superconductor film is provided with very excellent crystallinity when the (100) plane is used as substrate.
Then, a superconductor film was formed on an amorphous solid by using the buffer metal film.
Referring to FIG. 5, a compound film 13 is deposited, by sputtering for instance, on a metal film 12 formed on the surface of an amorphous substrate 15. In this case, substrate 15 serves for holding the superconductive compound film 13. This film 13 is usually deposited at a high temperature of 700°C When the compound film was deposited directly on the amorphous substrate 15 with no intervention of metal film 12, the strong adhesion to the substrate was lost and electric resistance increased excessively to destroy the superconductive properties. When metal film 12 was interposed between substrate 15 and three-element compound film, the surface assumed a dense state as shown in FIG. 2 and a good superconductive film 13 was obtained.
The present inventors also found that amorphous substances such as quartz glass, pyrex, amorphous silicon, etc., are effective for the substrate 15 of FIG. 5.
For better understanding of the subject matter of this invention, it will be described more concretely below by showing the embodiments.
By using sapphire single crystal R plane as substrate 11 and a Pt plate as target, a Pt film 12 was deposited on the substrate by DC planar magnetron sputtering as shown in FIG. 1. Deposition was carried out at a sputtering power of 300 V×30 mA by using Ar gas pressurized to 8 Pa and maintaining the substrate temperature at 250°-500°C to form a 0.1 μm thick film. This Pt film was polycrystalline. On this Pt film 12 was deposited a compound film 13 by high frequency planer magnetron sputtering using sintered ErBa2 Cu4.5O8 as target. This sputtering deposition of compound film 13 was carried out under Ar gas pressure of 0.5 Pa at a sputtering power of 150 W for a period of one hour by maintaining the substrate temperature at 700°C to form a 0.5 μm thick film.
This film showed a room-temperature resistance of 600 Ω and a superconducting transition temperature of 88 K.
Film formation on a glass coated substrate is described below with reference to FIG. 4.
Used as substrate 11 was the silicon single crystal (111) plane coated with heat-oxidized silicon to form a 1,000 A thick glass coating 14. By using a Pt plate as target, a Pt film 12 was deposited on said glass coating 14 by DC planer magnetron sputtering under the following conditions: Ar gas pressure: 8 Pa, sputtering power: 300 V×30 mA, substrate temperature: 250-500°C, film thickness: 0.1 μm. This Pt film is a polycrystal structure. On this Pt film 12 was deposited a three-element compound superconductive film 13 by high-frequency planer magnetron sputtering using a sintered ErBa2 Cu4.5 O5 target. This deposition was carried out under an Ar gas pressure of 0.5 Pa at a sputtering power of 150 W for a period of one hour by maintaining the substrate temperature at 700°C to form a 0.5 μm thick film. The thus formed superconductive film showed a room-temperature resistance of 600 Ω and a superconducting transition temperature of 88°C
Described below is another embodiment of the invention in which a superconductive film was formed on an amorphous substrate.
As shown in FIG. 5, a Pt film 12 was deposited on a quartz glass substrate 15 by DC planer magnetron sputtering using a Pt plate target. Sputtering was carried out in an 8 Pa argon gas at a sputtering power of 300 V×30 mA by maintaining the substrate temperature at 250°-600°C to form a 0.1 μm thick film. This Pt film was polycrystalline. On this Pt film was deposited a compound film 13 by high-frequency planer magnetron sputtering with a sintered ErBa2 Cu4.5 O8 target under the following conditions: Ar gas pressure: 0.5 Pa, sputtering power: 150 W, sputtering time: 2 hours, substrate temperature: 700°C, film thickness: 0.5 μm.
The thus obtained superconductive film showed a room-temperature resistance of 30 Ω and a superconducting transition temperature of 90° K.
As described above, the superconductor according to this invention is characterized in that a superconductive compound film is formed on a metal film. The superconductive compound film is formed by first breaking down the base superconductive material into a state of very fine particles, which is called "atomic state", and depositing such particulate material on a substrate, so that the composition of the formed superconductor is essentially homogeneous as compared with the conventional sintered products. Thus, a superconductor of extraordinarily high quality is realized by the present invention.
According to the present invention, as explained above, it is possible to form a superconductive film which is dense in its entire structure and also improved in critical current density. Further, the superconductive film of this invention can be integrated with various electronic devices such as Si and GaAs devices and is also appliable as a key material for various types of superconductive devices such as Josephson elements. It is to be noted particularly that there is a possibility that the transition temperature of this type of compound superconductors could be reduced to room temperature. This invention, therefore, can expand the scope of use of superconductors and thus is of high industrial value.
The present invention can increase the types of substrate usable for superconductors by incorporating a metal film and makes it possible to form such substrates a high quality superconductive film having a high critical temperature and a high critical current density. Thus, this invention greatly contributes to the realization of various types of superconductive devices.
Adachi, Hideaki, Higashino, Hidetaka, Hatta, Shinichiro, Hirochi, Kumiko
| Patent | Priority | Assignee | Title |
| 10109673, | Sep 20 2006 | SEEQC,INC | Double-masking technique for increasing fabrication yield in superconducting electronics |
| 9136457, | Sep 20 2006 | SEEQC,INC | Double-masking technique for increasing fabrication yield in superconducting electronics |
| 9595656, | Sep 20 2006 | SEEQC,INC | Double-masking technique for increasing fabrication yield in superconducting electronics |
| Patent | Priority | Assignee | Title |
| 4826808, | Mar 27 1987 | Massachusetts Institute of Technology | Preparation of superconducting oxides and oxide-metal composites |
| 4975413, | Aug 12 1987 | Amoco Corporation | Superconductor-coated carbon fiber composites |
| 5122507, | May 01 1987 | SUMITOMO ELECTRIC INDUSTRIES, LTD | Process for manufacturing a superconducting composite |
| 5168127, | Mar 20 1987 | Fujikura Ltd. | Oxide superconducting wire |
| EP284489, | |||
| EP300499, |
| Executed on | Assignor | Assignee | Conveyance | Frame | Reel | Doc |
| Mar 06 1998 | Matsushita Electric Industrial Co., Ltd. | (assignment on the face of the patent) | / |
| Date | Maintenance Fee Events |
| Feb 26 2001 | M183: Payment of Maintenance Fee, 4th Year, Large Entity. |
| Aug 23 2001 | ASPN: Payor Number Assigned. |
| Feb 01 2005 | M1552: Payment of Maintenance Fee, 8th Year, Large Entity. |
| Mar 02 2009 | REM: Maintenance Fee Reminder Mailed. |
| Aug 26 2009 | EXP: Patent Expired for Failure to Pay Maintenance Fees. |
| Date | Maintenance Schedule |
| Aug 08 2003 | 4 years fee payment window open |
| Feb 08 2004 | 6 months grace period start (w surcharge) |
| Aug 08 2004 | patent expiry (for year 4) |
| Aug 08 2006 | 2 years to revive unintentionally abandoned end. (for year 4) |
| Aug 08 2007 | 8 years fee payment window open |
| Feb 08 2008 | 6 months grace period start (w surcharge) |
| Aug 08 2008 | patent expiry (for year 8) |
| Aug 08 2010 | 2 years to revive unintentionally abandoned end. (for year 8) |
| Aug 08 2011 | 12 years fee payment window open |
| Feb 08 2012 | 6 months grace period start (w surcharge) |
| Aug 08 2012 | patent expiry (for year 12) |
| Aug 08 2014 | 2 years to revive unintentionally abandoned end. (for year 12) |