A light guide having a non-light emitting portion made up of multiple layers of first and second substantially non-absorptive longitudinally specular light reflector materials. The index of refraction of each layer differs from the indices of refraction of the immediately adjacent layers, such that the layers collectively have high longitudinally specular reflectivity. The light guide also has a light emitting portion made of prism light guide wall material. A substantially non-absorptive light scattering mechanism is positioned within the non-light emitting portion in opposition to the light emitting portion.

Patent
   RE37594
Priority
Mar 22 1996
Filed
Aug 11 1999
Issued
Mar 19 2002
Expiry
Mar 22 2016
Assg.orig
Entity
Large
30
90
all paid
0. 23. A light guide, comprising in cross-section:
(a) a non-light emitting portion comprising layers of first and second substantially non-absorptive polymers, said first and second polymers differing in composition such that said layers collectively have high longitudinally specular reflectivity; and,
(b) a light emitting portion comprising prism light guide wall material.
0. 22. A light guide, comprising in cross-section:
(a) a non-light emitting portion comprising multiple layers, each one of said layers having a selected index of refraction which differs from the indices of refraction of layers immediately adjacent said one of said layers, such that said multiple layers collectively have high longitudinally specular reflectivity; and,
(b) a light emitting portion comprising prism light guide wall material.
0. 24. A light guide, comprising in cross-section:
(a) a non-light emitting portion comprising multiple layers, each one of said layers having a stress induced birefringence such that said multiple layers are birefringent over a range of uniaxial to biaxial orientation of said layers and such that said multiple layers collectively have high longitudinally specular reflectivity; and,
(b) a light emitting portion comprising prism light guide wall material.
8. A light guide, comprising in cross-section:
(a) a non-light emitting portion comprising layers of first and second substantially non-absorptive polymers, said first and second polymers differing in composition such that said layers collectively have high longitudinally specular reflectivity;
(b) a light emitting portion comprising prism light guide wall material; and,
(c) a substantially non-absorptive light scattering means positioned within said non-light emitting portion in opposition to said light emitting portion.
0. 25. A light guide, comprising in cross-section:
(a) a non-light emitting portion comprising multiple layers, each one of said layers having a stress induced birefringence such that said multiple layers are birefringent over a range of uniaxial to biaxial orientation of said layers and such that said multiple layers collectively have high longitudinally specular reflectivity;
(b) a light emitting portion comprising prism light guide wall material; and,
(c) a substantially non-absorptive light scattering means positioned within said non-light emitting portion in opposition to said light emitting portion.
1. A light guide, comprising in cross-section:
(a) a non-light emitting portion comprising multiple layers of:
(i) a first substantially non-absorptive longitudinally specular light reflector;
(ii) a second substantially non-absorptive longitudinally specular light reflector;
each one of said layers having a selected index of refraction which differs from the indices of refraction of layers immediately adjacent said one of said layers, such that said multiple layers collectively have high longitudinally specular reflectivity;
(b) a light emitting portion comprising prism light guide wall material; and,
(c) a substantially non-absorptive light scattering means positioned within said non-light emitting portion in opposition to said light emitting portion.
15. A light guide, comprising in cross-section:
(a) a non-light emitting portion comprising multiple layers of:
(i) a first substantially non-absorptive longitudinally specular light reflector;
(ii) a second substantially non-absorptive longitudinally specular light reflector;
each one of said layers having a stress induced birefringence such that said multiple layers are birefringent over a range of uniaxial to biaxial orientation of said layers and such that said multiple layers collectively have high longitudinally specular reflectivity;
(b) a light emitting portion comprising prism light guide wall material; and,
(c) a substantially non-absorptive light scattering means positioned within said non-light emitting portion in opposition to said light emitting portion.
2. A light guide as defined in claim 1, wherein:
(a) said light guide cross-section is substantially constant along said light guide; and,
(b) said light scattering means has a width which increases as a function of length along said light guide.
3. A light guide as defined in claim 1, wherein:
(a) said light guide cross-section decreases as a function of length along said light guide; and,
(b) said light scattering means has a width which increases as a function of length along said light guide.
4. A light guide as defined in claim 1, further comprising a lens positioned outside said light emitting portion, said lens characterized by:
(a) low light absorption; and,
(b) light transmissivity which varies as a function of one or more of:
(i) wavelength;
(ii) polarization; and,
(iii) angle.
5. A light guide as defined in claim 1, further comprising an opaque cover surrounding and bonded to said non-light emitting portion.
6. A light guide as defined in claim 1, wherein said light scattering means comprises a non-absorptive, single textured air-polymer interface bonded to said non-light emitting portion by a non-absorptive adhesive.
7. A light guide as defined in claim 1, wherein each of said layers has a thickness of no more than 0.5 microns.
9. A light guide as defined in claim 8, wherein:
(a) said light guide cross-section is substantially constant along said light guide; and,
(b) said light scattering means has a width which increases as a function of length along said light guide.
10. A light guide as defined in claim 8, wherein:
(a) said light guide cross-section decreases as a function of length along said light guide; and,
(b) said light scattering means has a width which increases as a function of length along said light guide.
11. A light guide as defined in claim 8, further comprising a lens positioned outside said light emitting portion, said lens characterized by:
(a) low light absorption; and,
(b) light transmissivity which varies as a function of one or more of:
(i) wavelength;
(ii) polarization; and,
(iii) angle.
12. A light guide as defined in claim 8, further comprising an opaque cover surrounding and bonded to said non-light emitting portion.
13. A light guide as defined in claim 8, wherein said light scattering means comprises a non-absorptive, single textured air-polymer interface bonded to said non-light emitting portion by a non-absorptive adhesive.
14. A light guide as defined in claim 8, wherein each of said layers has a thickness of no more than 0.5 microns.
16. A light guide as defined in claim 15, wherein:
(a) said light guide cross-section is substantially constant along said light guide; and,
(b) said light scattering means has a width which increases as a function of length along said light guide.
17. A light guide as defined in claim 15, wherein:
(a) said light guide cross-section decreases as a function of length along said light guide; and,
(b) said light scattering means has a width which increases creases as a function of length along said light guide.
18. A light guide as defined in claim 15, further comprising a lens positioned outside said light emitting portion, said lens characterized by:
(a) low light absorption; and,
(b) light transmissivity which varies as a function of one or more of:
(i) wavelength;
(ii) polarization; and,
(iii) angle.
19. A light guide as defined in claim 15, further comprising an opaque cover surrounding and bonded to said non-light emitting portion.
20. A light guide as defined in claim 15, wherein said light scattering means comprises a non-absorptive, single textured air-polymer interface bonded to said non-light emitting portion by a non-absorptive adhesive.
21. A light guide as defined in claim 15, wherein each of said layers has a thickness of no more than 0.5 microns.

This application is directed to a light guide in which a highly reflective multilayer optical film is used to obtain efficient, uniform emission of diffuse light.

The prior art has evolved a variety of light guides which are capable of distributing light along the light guide for controlled emission at one or more regions remote from the light source. U.S. Pat. No. 4,750,798 exemplifies one such prior art light guide.

Such prior art light guides have predominantly reflective interior surfaces. Accordingly, light rays entering one end of the guide are reflected by the guide's inner walls as the rays proceed to the other end of the guide. In many lighting applications, the light guide is designed to "leak" light in a controlled manner, such that the amount of light emitted from the guide per unit length is acceptably uniform along the entire length of the guide, or along the entire length of each of the light guide's light emitting regions.

U.S. Pat. No. 4,984,144 (Cobb, Jr. et al) discloses a prismatic refractive optical lighting film (hereafter "prism light guide wall material") available from 3M, Inc. as "optical lighting film" under product nos. 2300 or 2301, which has been used to form a variety of prior art light guides. A common objective of such prior art guides is to distribute light from a point source over an area, to efficiently uniformly illuminate the area. Generally, the objective is to maximize the efficiency with which light is distributed along and emitted from the guide, while minimizing glare. Light guides formed of prism light guide wall material can emit light uniformly and diffusely over large areas with low glare relative to the level of illumination. Such guides are fabricated relatively easily and inexpensively, fulfilling a useful role.

In popular types of such prior art light guides the prism light guide wall material typically forms a tubular conduit. An extraction mechanism is provided inside the conduit. Light rays which enter the conduit from a light source are ordinarily internally reflected by the wall material and guided along the conduit. But, certain light rays which encounter the extraction mechanism are reflected in such a way that they are able to escape through the prism light guide wall material. However, light guides of this type are relatively inefficient in extracting diffuse light from the guide. This is because the light rays are typically reflected a number of times by a reflective cover outside the prism light guide wall material before they are emitted from the desired light emitting portion of the guide. In light guides constructed with currently available materials, each such reflection results in an absorption loss of about 5% to 10%. The net result is that about 25% of the available light is lost to absorption, instead of being emitted from the guide. In other words, the extraction efficiency of prior art light guides formed of prism light guide wall material is only about 75%.

The extraction efficiency of a light guide formed of prism light guide wall material can be improved by using an alternative technique to extract light from the guide. In particular, instead of providing an extraction mechanism inside the prism light guide wall material, a number of holes are provided in the wall material over the region from which light is to be extracted from the guide, or the wall material is otherwise modified in that region. With this design, light rays which escape from the light guide generally undergo fewer reflections before escaping, so the overall extraction efficiency is higher. Typically, only about 5% of the extracted light is lost to absorption, so the extraction efficiency is about 95%, which compares favourably to the 75% value in the previous example. A further advantage is that in some cases it is desirable that the escaping light be highly directional, as in the illumination of very high narrow architectural spaces. Such directionality is readily achieved with this alternative extraction technique.

Despite the advantages of the foregoing alternative extraction technique it has not become popular, for two reasons. First, light guides constructed in accordance with this technique are generally considered to be less visually attractive. For example, the light emitting surface is perceived as having a non-uniform distribution of light intensity, and as being too bright in some places. Second, it is much more difficult to design and manufacture light guides which employ the alternative extraction technique. Prototyping such designs typically involves an iterative procedure in which a substantial amount of valuable prism light guide wall material is unavoidably destroyed. Manufacturing such designs requires complex patterning technology to yield the optimal distribution of extraction effect over the surface of the prism light guide wall material.

The present invention overcomes the foregoing problems by exploiting the properties of newly discovered multilayer optical film materials.

In accordance with the preferred embodiment, the invention provides a light guide having a non-light emitting portion made up of multiple layers of first and second substantially non-absorptive longitudinally specular light reflector materials. The index of refraction of each layer differs from the indices of refraction of the immediately adjacent layers, such that the layers collectively have high longitudinally specular reflectivity. The light guide also has a light emitting portion comprising prism light guide wall material. A substantially non-absorptive light scattering mechanism is positioned within the non-light emitting portion in opposition to the light emitting portion.

The multiple-layered materials which make up the non-light emitting portion of the light guide may alternatively be such that each layer has a stress induced birefringence, with the layers collectively being birefringent over a range of uniaxial to biaxial orientation of the layers and having a collectively high longitudinally specular reflectivity. As another alternative, the layered materials may be first and second substantially non-absorptive polymers which differ in composition such that the layers collectively have high longitudinally specular reflectivity.

The light guide's cross-section can be substantially constant, or its cross-section may decrease along the guide. In either case, the width of the light scattering mechanism may be increased as a function of length along the light guide.

Advantageously, a low absorption lens may be positioned outside the light guide's light emitting portion. The light transmissivity characteristic of the lens may vary as a function of wavelength, polarization, angle, or a combination thereof.

FIG. 1 is a schematic cross-sectional illustration of a prior art light guide formed of prism light guide wall material and containing a light extraction mechanism.

FIG. 2 is a schematic cross-sectional illustration of a prior art light guide formed of prism light guide wall material in which a number of holes are provided in the wall material over the region from which light is to be extracted.

FIG. 3 is a schematic oblique perspective illustration, on a greatly magnified scale, of two layers of a multilayer optical film material.

FIG. 4 is a schematic oblique perspective illustration, on a greatly magnified scale, of several layers of a multilayer optical film material formed by alternating layers of at least two different materials.

FIGS. 5 and 6 are schematic cross-sectional illustrations of light guides formed of multilayer optical film material in accordance with the invention.

Prior Art Background

FIG. 1 is a schematic cross section of a typical prior art light guide 10 formed of prism light guide wall material. An outer cover having an upper, typically opaque portion 12 and a lower translucent portion 14 protects internal components of light guide 10. A white reflective film 16 is provided immediately inside opaque cover portion 12 to reflect light propagated along guide 10 which would otherwise strike opaque cover portion 12. A tubular conduit 18 formed of prism light guide wall material is provided inside film 16, to guide light emitted from a light source (not shown) longitudinally along light guide 10. A section of white extractor film 20 is provided inside conduit 18, near the top portion thereof. Extractor film 20 scatters light rays reflected onto it, causing them to escape through conduit 18 for emission through translucent cover portion 14.

In general, the width of extractor film 20 varies as a function of distance along light guide 10, in order to yield a light output which is reasonably uniform along the length of guide 10, notwithstanding the fact that the amount of light inside conduit 18 changes substantially as a function of distance along guide 10. Persons skilled in the art are readily able to customize the width variation of extractor film 20 for a particular light guide in order to attain the desired uniform light output.

The dimensions of the light guide components illustrated in FIG. 1 may vary significantly from one application to another in order to accommodate design objectives such as the desired length of guide 10, the nature of the light source, and the desired light output pattern. The guide's cross-sectional shape need not be round; a variety of shapes such as ovals and rectangles are commonly used.

The following general description characterizes all such light guides formed of prism light guide wall material, of which FIG. 1 is exemplary. Light entering one end of conduit 18 is guided toward the opposed end, where the light encounters an end mirror (not shown) which reflects the light back toward its source. As the light is guided to the end mirror and back, almost all of the light escapes from guide 10, due to the scattering effect of extractor film 20. More particularly, each light ray is internally reflected by conduit 18 until the ray encounters extractor 20. Most rays incident upon extractor 20 are scattered in directions to which conduit 18 is substantially transparent, allowing such rays to escape through conduit 18. As explained above, light guides of this type are relatively inefficient in extracting diffuse light from the guide, due to absorption losses which occur as the light rays undergo multiple reflections against white reflective film 16 prior to emission from guide 10.

FIG. 2 illustrates the aforementioned prior art technique for improving the extraction efficiency of a light guide formed of prism light guide wall material. As in the case of light guide 10, light guide 22 (FIG. 2) has a protective outer cover with an upper opaque portion 24 and a lower translucent portion 26; a white reflective film 28; and a tubular conduit 30 formed of prism light guide wall material. A series of light extraction holes 32 are provided in conduit 30 over the region from which light is to be extracted from guide 22. Light rays which escape from guide 22 through holes 32 generally undergo fewer internal reflections before escaping, so the extraction efficiency of guide 22 is generally better than that of guide 10, as explained above.

Multilayer Optical Film

In order to assist those skilled in the art in understanding the benefits attainable by constructing a light guide with a multilayer optical film a brief explanation of such films is now provided. The advantages, characteristics and manufacturing of such films are most completely described in U.S. patent application Ser. No. 08/402,041 filed Mar. 10, 1995 titled "Optical Film", which is incorporated herein by reference. Multilayer optical film is useful, for example, as highly efficient mirrors and/or polarizers. A relatively brief description of the properties and characteristics of multilayer optical film is presented below, followed by a description of an illustrative embodiment of a light guide employing multilayer optical film in accordance with the present invention.

FIG. 3 shows two layers of a multilayer stack 100, and indicates the three dimensional indices of refraction for each layer. The indices of refraction for each layer are η1x, η1y, and η1z for layer 102, and η2x, η2y, and η2z for layer 104. The relationships between the indices of refraction in each film layer to each other and to those of the other layers in the film stack determine the reflectance behaviour of the multilayer stack at any angle of incidence, from any azimuthal direction. The principles and design considerations described in U.S. patent application Ser. No. 08/402,041 can be applied to create multilayer stacks having the desired optical effects for a wide variety of circumstances and applications. The indices of refraction of the layers in the multilayer stack can be manipulated and tailored to produce the desired optical properties.

An exemplary multilayer optical film of the present invention as illustrated in FIG. 4 includes a multilayer stack 100 having alternating layers of at least two materials A and B. At least one of the materials, material A for example, has the property of stress induced birefringence, such that the index of refraction of the material is affected by the stretching process in the direction that the film is stretched. Before stretching, both materials may have the same index of refraction. Stretching the stack in the x-direction, for example, increases the index of refraction of material A in the stretch direction. This uniaxial (one directional) stretching results in a refractive index difference between layers (Δηx) in the stretch direction. This refractive index difference between layers will cause light polarized in the plane defined by the stretch direction (i.e., the x-z plane) to be reflected. If there is no stretching in the y-direction, there is no refractive index difference in the y-direction (i.e., Δηy=0) and thus light polarized in the y-z plane is transmitted. Stretching in one direction thus results in a multilayer reflecting polarizer.

If the film is biaxially stretched, i.e., stretched in both the x and y directions, a refractive index difference in both directions is created. Thus, light polarized in both the x-z and the y-z planes is reflected. Thus a biaxially stretch multilayer stack acts as mirror. By stretching the multilayer stack over a range of uniaxial to biaxial orientation, a film is created with a range of reflectivities for differently oriented plane-polarized incident light. The multilayer stack can thus be made useful as reflective polarizers, mirrors, or partial mirrors, depending upon the desired end-use application.

To achieve high off-axis reflectivity as well as high reflectivity for light at normal incidence, it has been found that the relationship of the refractive index difference in the z-direction (i.e., Δηz) is very important. Ideally, for both mirrors and polarizers, a z-index match (i.e., the condition Δηz=0) ensures high off angle reflectivity (for both polarizations in the case of mirrors, and for the reflection polarization in the case of polarizers). However, for those polarizers where an exact z-index match is not possible, the y-index difference can be manipulated to ensure that off-angle reflectivity is maximized. In this case, the sign of the y-index difference preferably matches the sign of the z-index difference.

Multilayer optical films as used in conjunction with the present invention exhibit relatively low absorption of incident light, as well as high reflectivity for off axis as well as normal light rays as described above. Multilayer optical films constructed according to the present invention exhibit a Brewster angle (the angle at which reflectance goes to zero for light incident at any of the layer interfaces) which is very large or is nonexistent. In contrast, known multilayer polymer films exhibit relatively small Brewster angles at layer interfaces, resulting in transmission of light and/or undesirable iridescence. The multilayer optical films according to the present invention, however, allow for the construction of mirrors and polarizers whose reflectivity for p polarized light decrease slowly with angle of incidence, are independent of angle of incidence, or increase with angle of incidence away from the normal. As a result, multilayer stacks having high reflectivity for both s and p polarized light over a wide bandwidth, and over a wide range of angles can be achieved.

Referring again to FIG. 4, the multilayer stack 100 can include tens, hundreds or thousands of layers, and each layer can be made from any of a number of different materials. The characteristics which determine the choice of materials for a particular stack depend upon the desired optical performance of the stack. The stack can contain as many materials as there are layers in the stack. For ease of manufacture, preferred optical thin film stacks contain only a few different materials.

The preferred multilayer stack is comprised of low/high index pairs of film layers, wherein each low/high index pair of layers has a combined optical thickness of ½ the centre wavelength of the band it is designed to reflect. Stacks of such films are commonly referred to as quarterwave stacks. For multilayer optical films concerned with the visible and the near infrared wavelengths, a quarterwave stack design results in each of the layers in the multilayer stack having an average thickness of not more than 0.5 microns.

In those applications where reflective films (e.g. mirrors) are desired, the desired average transmission for light of each polarization and plane of incidence generally depends upon the intended use of the reflective film. One way to produce a multilayer mirror film is to biaxially stretch a multilayer stack which contains a birefringent material as the high index layer of the low/high index pair. For a high efficiency reflective film, average transmission along each stretch direction at normal incidence over the visible spectrum (400-700 nm) is desirably less than 10% (reflectance greater than 90%), preferably less than 5% (reflectance greater than 95%), more preferably less than 2% (reflectance greater than 98%), and even more preferably less than 1%(reflectance greater than 99%). The average transmission at 60 degrees from the normal from 400-700 nm is desirably less than 20% (reflectance greater than 80%), preferably less than 10% (reflectance greater than 90%), more preferably less than 5% (reflectance greater than 95%), and even more preferably less than 2% (reflectance greater than 98%), and even more preferably less than 1% (reflectance greater than 99%).

In addition, asymmetric reflectance films may be desirable for certain applications. In that case, average transmission along one stretch direction may be desirably less than, for example, 50%, while the average transmission along the other stretch direction may be desirably less than, for example 20%, over a bandwidth of, for example, the visible spectrum (400-700 nm), or over the visible spectrum and into the near infrared (e.g., 400-850 nm).

Multilayer optical films can also be designed to operate as reflective polarizers. One way to produce a multilayer reflective polarizer is to uniaxially stretch a multilayer stack. The resulting reflective polarizers have high reflectivity for light with its plane of polarization parallel to one axis(in the stretch direction) for a broad range of angles of incidence, and simultaneously have low reflectivity and high transmissivity for light with its plane of polarization parallel to the other axis (in the non-stretch direction) for a broad range of angles of incidence. By controlling the three indices of refraction of each film, ηx, ηy and ηz, the desired polarizer behaviour can be obtained.

For many applications, the ideal reflecting polarizer has high reflectance along one axis (the so-called extinction axis) and zero reflectance along the other (the so-called transmission axis), at all angles of incidence. For the transmission axis of a polarizer, it is generally desirable to maximize transmission of light polarized in the direction of the transmission axis over the bandwidth of interest and also over the range of angles of interest.

The average transmission at normal incidence for a polarizer in the transmission axis across the visible spectrum (400-700 nm for a bandwidth of 300 nm) is desirably at least 50%, preferably at least 70%, more preferably at least 85%, and even more preferably at least 90%. The average transmission at 60 degrees from the normal (measured along the transmission axis for p-polarized light) for a polarizer from 400-700 nm is desirably at least 50%, preferably at least 70%, more preferably at least 80%, and even more preferably at least 90%.

The average transmission for a multilayer reflective polarizer at normal incidence for light polarized in the direction of the extinction axis across the visible spectrum (400-700 nm for a bandwidth of 300 nm) is desirably at less than 50%, preferably less than 30%, more preferably less than 15%, and even more preferably less than 5%. The average transmission at 60 degrees from the normal (measured along the transmission axis for p-polarized light) for a polarizer for light polarized in the direction of the extinction axis from 400-700 nm is desirably less than 50%, preferably less than 30%, more preferably less than 15%, and even more preferably less than 5%.

For certain applications, high reflectivity for p-polarized light with its plane of polarization parallel to the transmission axis at off normal angles are preferred. The average reflectivity for light polarized along the transmission axis should be more than 20% at an angle of at least 20 degrees from the normal.

In addition, although reflective polarizing films and asymmetric reflective films are discussed separately herein, it should be understood that two or more of such films could be provided to reflect substantially all light incident on them (provided they are properly oriented with respect to each other to do so). This construction is typically desired when the multilayer optical film is used as a reflector in a backlight system according to the present invention.

If some reflectivity occurs along the transmission axis, the efficiency of the polarizer at off-normal angles may be reduced. If the reflectivity along the transmission axis is different for various wavelengths, colour may be introduced into the transmitted light. One way to measure the colour is to determine the root mean square (RMS) value of the transmissivity at a selected angle or angles over the wavelength range of interest. The % RMS colour, CRMS, can be determined according to the equation: C RMS = ∫ λ 1 λ 2 ⁢ ( ( T - T _ ) 2 ) 1 / 2 ⁢ ⅆ λ T _

where the range λ1 to λ2 is the wavelength range, or bandwidth, of interest, T is the transmissivity along the transmission axis, and {overscore (T)} is the average transmissivity along the transmission axis in the wavelength range of interest. For applications where a low colour polarizer is desirable, the % RMS colour should be less than 10%, preferably less than 8%, more preferably less than 3.5%, and even more preferably less than 2% at an angle of at least 30 degrees from the normal, preferably at least 45 degrees from the normal, and even more preferably at least 60 degrees from the normal.

Preferably, a reflective polarizer combines the desired % RMS colour along the transmission axis for the particular application with the desired amount of reflectivity along the extinction axis across the bandwidth of interest. For polarizers having a bandwidth in the visible range (400-700 nm, or a bandwidth of 300 nm), average transmission along the extinction axis at normal incidence is desirably less than 40%, more desirably less than 25% preferably less than 15%, more preferably less than 5% and even more preferably less than 3%.

Materials Selection and Processing

With the design considerations described in the above mentioned U.S. patent application Ser. No. 08/402,041, one of ordinary skill will readily appreciate that a wide variety of materials can be used to form multilayer reflective films or polarizers according to the invention when processed under conditions selected to yield the desired refractive index relationships. The desired refractive index relationships can be achieved in a variety of ways, including stretching during or after film formation (e.g., in the case of organic polymers), extruding (e.g., in the case of liquid crystalline materials), or coating. In addition, it is preferred that the two materials have similar rheological properties (e.g., melt viscosities) such that they can be co extruded. A detailed description of the materials selection and processing conditions can be found in the above mentioned U.S. patent application Ser. No. 08/402,041, which is incorporated herein by reference.

Light Guides Incorporating Multilayer Optical Film

Currently available prism light guide wall materials are about 98% reflective for incident light rays falling within the material's acceptance angular range, and are highly transmissive for incident light rays falling outside that range. By contrast, multilayer optical film material can be made with higher reflectivity than the best currently available prism light guide wall materials, and in a manner which maintains such higher reflectivity for all incident light angles. Accordingly, multilayer optical film is well suited as a substitute for prism light guide wall material in forming tubular conduits for guiding light from one place to another, provided there is no need to emit light from the conduit.

Multilayer optical film can also be used to form light guides from which light can be efficiently extracted. Consider first FIG. 5, which depicts a light guide 34 formed of multilayer optical film in accordance with one possible embodiment of the present invention. Light guide 34 is similar to the FIG. 2 light guide 22, except that prism light guide wall material conduit 30 is replaced by tubular conduit 36 formed of multilayer optical film. White reflector film 28 is not required in guide 34, because virtually no light escapes through the highly reflective multilayer optical film 36 toward opaque cover portion 38. Light extraction holes 40 are provided in multilayer optical film conduit 36 over the region from which light is to be extracted through translucent cover 41.

Although guide 34 affords superior extraction efficiency, it is still subject to some of the basic problems which affect guide 22. In particular, extraction holes 40 detract from the outward appearance of guide 34; and, it is difficult to design and manufacture guide 34 with the required size and/or pattern of extraction holes 40 (which must vary as a function of distance along guide 34 in a manner unique to each specific design). Past experience with light guides embodying the FIG. 2 design therefore suggests that the FIG. 5 design would not be very successful.

Now consider FIG. 6, which depicts a light guide 42 formed of multilayer optical film in accordance with another (and preferred) embodiment of the present invention. Light guide 42 is similar to the FIG. 1 light guide 10, except that prism light guide wall material conduit 18 is replaced by a hybrid tubular conduit 44 which is formed of multilayer optical film in the region adjacent opaque cover portion 46 and formed of prism light guide wall material 48 in the region adjacent translucent cover portion 50. A section of white extractor film 52 is provided inside conduit 44, near the top portion thereof, to scatter light rays toward prism light guide wall material 48 at angles outside the angular range within which material 48 reflects incident light rays internally within guide 42. Such scattered rays accordingly escape through prism light guide wall material 48 and are emitted through translucent cover portion 50. White reflector film is not required in guide 42, because virtually no light escapes through the highly reflective multilayer optical film 44 toward opaque cover portion 46.

Light guide 42 retains all the advantages of light guide 10, while substantially reducing the problem of extraction efficiency loss, since multilayer optical film 44 reflects light along guide 42 with very low absorption loss. A further advantage is that multilayer optical film 44 can be bonded to opaque cover portion 46. For example, multilayer optical film 44 could be supplied bonded to a sheet metal substrate which could then be formed into the desired light guide shape, with the sheet metal constituting opaque cover portion 46.

Another advantage to such use of multilayer optical film technology is that the maximum aspect ratio of guide 42 will be somewhat increased, due to the higher reflectivity of multilayer optical film 44. Further, the quality of the collimation of the light source is less critical, because multilayer optical film 44 has a wider acceptance angle range.

An important characteristic of multiple layer optical film utilized in a light guide embodying the present invention is that the film be a longitudinally specular light reflector. As used herein, the term "longitudinally specular light reflector" means a material for which the z components of the unit direction vectors of the incident and reflected light rays are substantially the same, where the z direction is parallel to the surface of the material and is the longest direction of the light guide. Those skilled in the art will appreciate that a material which is "longitudinally specular" is not necessarily "specular"; but, that all "specular" materials are also necessarily "longitudinally specular". This distinction is important, as in some cases there may be advantages to the use of longitudinally specular materials which are not specular, such that they cause transverse scattering or some other modification of the transverse motion of the light rays as they travel down the guide. Materials which are "specular" reflect light rays by reversing only the unit direction vector of the incident light ray which is normal to the surface of the reflecting material, with the incident ray's other unit direction vectors remaining unchanged. Materials which are "longitudinally specular" reflect light rays such that only the unit direction vector of the incident light ray which is parallel to the surface of the reflecting material is unchanged, with the possibility that the incident ray's other unit direction vectors may be scattered.

Improved Light Extraction Materials

State of the art materials used to form extractor films 20, 52 absorb about 5% to 10% of the light incident upon them. In particular, absorption losses occur when light is initially scattered by the extractor, with additional absorption losses occurring if the scattered light does not immediately escape from the light guide but is internally reflected such that it is subsequently again scattered by the extractor. The latter effect becomes more significant as distance increases from the light source, since the extractor's width may necessarily be quite large at such distances.

Although this problem has always been present, previously there has not been much motivation to solve it, because it did not have much impact on overall efficiency of the light guide, having regard to the absorption losses of the prism light guide wall material used to form the light guide itself. But, with the introduction of highly reflective multilayer optical film technology, the problem becomes much more significant.

Using the best currently available material (which is about 5% absorptive) to form extractor 52, the extraction efficiency of light guide 42 is about 85%. If extractor 52 is 99.5% reflective, the extraction efficiency rises to 95%. Thus, use of a very high efficiency extractor with multilayer optical film technology makes it possible to combine the outwardly perceptible aesthetic quality of light guide 10 (FIG. 1) with the highly efficient light guide 22 (FIG. 2).

Extractor 52 need not be highly reflective itself, because it can be mounted on the internal surface of highly reflective multilayer optical film 44. Extractor 52 need only be capable of scattering incident light, which can be achieved with a single textured air-polymer interface. All that is required is that the polymer and the mounting adhesive be quite non-absorptive. It is also desirable that the material used to form extractor 52 be easily handled and easily cut by hand and by electronic cutting equipment.

Typically, the cross-section of light guide 42 is substantially constant along the guide. Because the available light decreases as a function of length along light guide 42, extractor 52 is tapered by increasing its width as a function of length along guide 42 in the direction away from the light source. Alternatively, or additionally, the cross-sectional area of the guide itself may be tapered as a function of length along the guide.

A key feature of the invention is that light guide 42 constitutes an optical cavity of high net reflectivity. In particular, if light rays are directed into the light emitting portion of the guide, a very high fraction of those rays will be re-emitted, in stark contrast to previous light guide designs. This feature can be put to advantage by positioning a specialized film "lens" 54 outside light emitting cover portion 50 to distribute the emitted light in a preferred way. The lens preferably has a low light absorption characteristic; and, a light transmissivity characteristic which varies as a function of wavelength, polarization, angle or some combination thereof. In this way the reflected light is recycled by light guide 42 and reused rather than being lost to absorption as in prior art guides.

As will be apparent to those skilled in the art in the light of the foregoing disclosure, many alterations and modifications are possible in the practice of this invention without departing from the spirit or scope thereof. Accordingly, the scope of the invention is to be construed in accordance with the substance defined by the following claims.

Whitehead, Lorne A.

Patent Priority Assignee Title
7064740, Nov 09 2001 Sharp Kabushiki Kaisha Backlit display with improved dynamic range
7164284, Dec 18 2003 Sharp Kabushiki Kaisha Dynamic gamma for a liquid crystal display
7342592, Jun 14 2004 Sharp Kabushiki Kaisha System for reducing crosstalk
7499017, Nov 09 2001 Sharp Kabushiki Kaisha Backlit display with improved dynamic range
7505018, May 04 2004 Sharp Kabushiki Kaisha Liquid crystal display with reduced black level insertion
7505027, Nov 09 2001 Sharp Kabushiki Kaisha Backlit display with improved dynamic range
7505028, Nov 09 2001 Sharp Kabushiki Kaisha Backlit display with improved dynamic range
7525528, Nov 16 2004 Sharp Kabushiki Kaisha Technique that preserves specular highlights
7532192, May 04 2004 Sharp Kabushiki Kaisha Liquid crystal display with filtered black point
7556836, Sep 03 2004 Solae, LLC High protein snack product
7573457, Oct 26 2004 Sharp Kabushiki Kaisha Liquid crystal display backlight with scaling
7602369, May 04 2004 Sharp Kabushiki Kaisha Liquid crystal display with colored backlight
7612757, May 04 2004 Sharp Kabushiki Kaisha Liquid crystal display with modulated black point
7623105, Nov 21 2003 Sharp Kabushiki Kaisha Liquid crystal display with adaptive color
7675500, Oct 28 2004 Sharp Kabushiki Kaisha Liquid crystal display backlight with variable amplitude LED
7714830, Oct 30 2004 Sharp Kabushiki Kaisha Liquid crystal display backlight with level change
7737936, Oct 28 2004 Sharp Kabushiki Kaisha Liquid crystal display backlight with modulation
7777714, May 04 2004 Sharp Kabushiki Kaisha Liquid crystal display with adaptive width
7853094, Jan 24 2006 Sharp Kabushiki Kaisha Color enhancement technique using skin color detection
7872631, Apr 05 2004 Sharp Kabushiki Kaisha Liquid crystal display with temporal black point
7898519, Feb 17 2005 Sharp Kabushiki Kaisha Method for overdriving a backlit display
8050511, Nov 16 2004 Sharp Kabushiki Kaisha High dynamic range images from low dynamic range images
8050512, Nov 16 2004 Sharp Kabushiki Kaisha High dynamic range images from low dynamic range images
8121401, Jan 24 2006 Sharp Kabushiki Kaisha Method for reducing enhancement of artifacts and noise in image color enhancement
8378955, Nov 09 2001 Sharp Kabushiki Kaisha Liquid crystal display backlight with filtering
8395577, May 04 2004 Sharp Kabushiki Kaisha Liquid crystal display with illumination control
8400396, May 04 2004 Sharp Kabushiki Kaisha Liquid crystal display with modulation for colored backlight
8712289, Oct 12 2007 Fuji Xerox Co., Ltd. Light irradiation element, image forming structure, and image forming apparatus
8941580, Nov 30 2006 Sharp Kabushiki Kaisha Liquid crystal display with area adaptive backlight
9143657, Jan 24 2006 Sharp Kabushiki Kaisha Color enhancement technique using skin color detection
Patent Priority Assignee Title
3535016,
3610729,
3647612,
3711176,
3759647,
3773882,
3801429,
4094947, Sep 03 1976 The Dow Chemical Company Multilayer coextrusion process for producing selective reflectivity
4105293, Aug 25 1976 Lighting installation based on light guide
4260220, Jun 15 1979 BRITISH COLUMBIA, UNIVERSITY OF Prism light guide having surfaces which are in octature
4310584, Dec 26 1979 The Mearl Corporation Multilayer light-reflecting film
4335421, Mar 17 1980 HUEY COMPANY, THE Light fixture, light aperture and method of uniformly illuminating an optically diffusive viewing area
4337759, Oct 10 1979 TIR TECHNOLOGIES, INC Radiant energy concentration by optical total internal reflection
4446305, Mar 02 1981 Polaroid Corporation Optical device including birefringent polymer
4520189, Mar 02 1981 Polaroid Corporation Optical device including birefringent aromatic amino carboxylic acid polymer
4521588, Mar 02 1981 Polaroid Corporation Optical device including birefringent polyhydrazide polymer
4525413, Mar 02 1981 Polaroid Corporation Optical device including birefringent polymer
4540623, Oct 14 1983 3M Innovative Properties Company Coextruded multi-layered articles
4615579, Aug 29 1983 BRITISH COLUMBIA, UNIVERSITY OF Prism light guide luminaire
4750798, Aug 29 1983 BRITISH COLUMBIA, UNIVERSITY OF Prism light guide luminaire
4755921, Apr 02 1986 Minnesota Mining and Manufacturing Company Lens
4787708, May 08 1987 Minnesota Mining and Manufacturing Company Apparatus for continuously controlled emission of light from prism light guide
4791540, May 26 1987 Minnesota Mining and Manufacturing Company Light fixture providing normalized output
4799137, Mar 24 1987 Minnesota Mining and Manufacturing Company Reflective film
4805984, Nov 21 1985 3M Innovative Properties Company Totally internally reflecting light conduit
4813765, Sep 20 1985 Device for changing directions of light rays
4834495, May 08 1987 Minnesota Mining and Manufacturing Company Collapsible light pipe
4850665, Feb 20 1987 MINNESOTA MINING AND MANUFACTURING COMPANY, A DE CORP Method and apparatus for controlled emission of light from prism light guide
4874228, Mar 24 1987 Minnesota Mining and Manufacturing Company; MINNESOTA MINING AND MANUFACTURING COMPANY, A CORP OF DE Back-lit display
4906070, Nov 21 1985 3M Innovative Properties Company Totally internally reflecting thin, flexible film
4937134, Apr 17 1989 3M Innovative Properties Company Elastomeric optical interference films
4937716, May 05 1988 Minnesota Mining and Manufacturing Company Illuminating device having non-absorptive variable transmissivity cover
4984144, May 08 1987 Minnesota Mining and Manufacturing Company High aspect ratio light fixture and film for use therein
4989125, May 10 1988 Minnesota Mining and Manufacturing Company; MINNESOTA MINING AND MANUFACTURING COMPANY, A CORP OF DE Reflector using fresnel-type structures having a plurality of active faces
4996632, Oct 07 1988 LUMINATOR HOLDING, LLC, A NEW YORK LIMITED LIABILITY COMPANY Multi-color illuminating system
5016143, Oct 07 1988 LUMINATOR HOLDING, LLC, A NEW YORK LIMITED LIABILITY COMPANY Illuminating system
5043850, Jan 10 1990 Minnesota Mining and Manufacturing Company Direction dependent line light source
5089318, Oct 31 1989 ENGELHARD CORPORATION, A CORPORATION OF NEW JERSEY Iridescent film with thermoplastic elastomeric components
5094788, Dec 21 1990 3M Innovative Properties Company Interfacial surface generator
5094793, Dec 21 1990 DOW CHEMICAL COMPANY, THE A CORPORATION OF DELAWARE Methods and apparatus for generating interfacial surfaces
5095210, Apr 06 1990 3M Innovative Properties Company Multilayer film indicator for determining the integrity or authenticity of an item and process for using same
5103337, Jul 24 1990 3M Innovative Properties Company Infrared reflective optical interference film
5122905, Jun 20 1989 3M Innovative Properties Company Relective polymeric body
5122906, Jun 20 1989 3M Innovative Properties Company Thick/very thin multilayer reflective polymeric body
5126880, Dec 18 1990 3M Innovative Properties Company Polymeric reflective bodies with multiple layer types
5149578, Dec 26 1989 3M Innovative Properties Company Multilayer film for tamper indication by use of optical interference reflection
5186530, Nov 22 1991 Minnesota Mining and Manufacturing Company Lighting structure having variable transmissivity internal light guide illumination
5202074, Dec 26 1989 The Dow Chemical Company Method for producing injection molded multilayer articles
5217794, Jan 22 1991 3M Innovative Properties Company Lamellar polymeric body
5219217, Oct 07 1988 LUMINATOR HOLDING, LLC, A NEW YORK LIMITED LIABILITY COMPANY Illuminating system
5233465, May 27 1992 3M Innovative Properties Company Visibly transparent infrared reflecting film with color masking
5234729, Feb 27 1992 3M Innovative Properties Company Multilayer polymeric reflective bodies for decorative and security applications
5243506, Jun 17 1991 Minnesota Mining and Manufacturing Company High aspect ratio light emitter having high uniformity and directionality
5269995, Oct 02 1992 3M Innovative Properties Company Coextrusion of multilayer articles using protective boundary layers and apparatus therefor
5278694, Jan 11 1990 3M Innovative Properties Company Optically dissimilar composition for polymeric reflective bodies
5309544, Mar 31 1992 Minnesota Mining and Manufacturing Company; MINNESOTA MINING AND MANUFACTURING COMPANY, A CORP OF DE Light pipe having optimized cross-section
5316703, Jan 22 1991 3M Innovative Properties Company Method of producing a lamellar polymeric body
5339198, Oct 16 1992 3M Innovative Properties Company All-polymeric cold mirror
5339382, Feb 23 1993 Minnesota Mining and Manufacturing Company Prism light guide luminaire with efficient directional output
5360659, May 24 1993 3M Innovative Properties Company Two component infrared reflecting film
5389324, Jun 07 1993 3M Innovative Properties Company Layer thickness gradient control in multilayer polymeric bodies
5424119, Feb 04 1994 JDS Uniphase Corporation Polymeric sheet having oriented multilayer interference thin film flakes therein, product using the same and method
5448404, Oct 29 1992 3M Innovative Properties Company Formable reflective multilayer body
5451449, May 11 1994 ENGELHARD CORPORATION, A CORPORATION OF NEW JERSEY Colored iridescent film
5481445, Feb 15 1994 ALP LIGHTING & CEILING PRODUCTS, INC Transflection reflector having controlled reflected and transmitted light distribution
5481637, Nov 02 1994 The University of British Columbia Hollow light guide for diffuse light
5486949, Jun 20 1989 3M Innovative Properties Company Birefringent interference polarizer
5540978, Feb 25 1992 3M Innovative Properties Company All-polymeric ultraviolet light reflecting film
5552927, Oct 16 1992 The Dow Chemical Company All-polymeric cold mirror
5568316, Oct 29 1992 3M Innovative Properties Company Formable reflective multilayer body
5661839, Mar 22 1996 The University of British Columbia Light guide employing multilayer optical film
CA1327286,
EP167721,
EP355727,
EP62751,
EP426636,
EP469732,
EP514223,
GB2196100,
GB713529,
JP5288910,
JP611607,
RE34605, Dec 11 1992 3M Innovative Properties Company Infrared reflective optical interference film
WO9109719,
WO9517303,
WO9517691,
WO9517692,
WO9517699,
WO9004132,
WO9517303,
/
Executed onAssignorAssigneeConveyanceFrameReelDoc
Aug 11 1999The University of British Columbia(assignment on the face of the patent)
Date Maintenance Fee Events
Nov 19 2004M1552: Payment of Maintenance Fee, 8th Year, Large Entity.
Dec 19 2008M1553: Payment of Maintenance Fee, 12th Year, Large Entity.


Date Maintenance Schedule
Mar 19 20054 years fee payment window open
Sep 19 20056 months grace period start (w surcharge)
Mar 19 2006patent expiry (for year 4)
Mar 19 20082 years to revive unintentionally abandoned end. (for year 4)
Mar 19 20098 years fee payment window open
Sep 19 20096 months grace period start (w surcharge)
Mar 19 2010patent expiry (for year 8)
Mar 19 20122 years to revive unintentionally abandoned end. (for year 8)
Mar 19 201312 years fee payment window open
Sep 19 20136 months grace period start (w surcharge)
Mar 19 2014patent expiry (for year 12)
Mar 19 20162 years to revive unintentionally abandoned end. (for year 12)