A method of both hardening and polishing a concrete surface includes the steps of first applying to the concrete surface a hardening/densifying silicate compound, allowing the compound to remain in contact with the surface for a period of time sufficient to allow it to soak into the surface of the concrete, cleaning the surface and allowing it to dry, and polishing the surface with a diluted silicate polishing compound. The polishing step includes the steps of applying to the concrete surface a diluted silicate polishing compound, mechanically polishing the concrete surface with a rotary polishing machine, using pads or disks or drums, cleaning the concrete surface, and repeating said steps with polishing pads or disks of increasingly finer grit until the surface obtains an aesthetically desirable level of shine.
|
1. A method of hardening and polishing a concrete surface comprising the steps of:
(a) applying to the concrete surface a hardening/densifying silicate compound; (b) allowing the compound to remain in contact with the surface for a period of time sufficient to allow the compound to soak into the surface of the concrete; (c) removing any puddles and allowing the surface to dry; (d) applying to the concrete surface a diluted silicate polishing compound; and (e) mechanically polishing the concrete surface with a rotating diamond abrasive disk or drum.
9. The method of polishing a concrete surface comprising the steps of:
(a) applying to the concrete surface a diluted silicate polishing compound; (b) mechanically polishing the concrete surface to which the compound has been applied with a rotating diamond-impregnated abrasive pad, disk, or drum; (c) cleaning the concrete surface; (d) applying the concrete surface more of said diluted silicate polishing compound; (e) mechanically polishing the concrete surface with a rotating diamond-impregnated polishing pad, disk, or drum having a less rough grit than was used in the previous polishing step; and (f) repeating steps (c) through (e) until, upon cleaning, the surface has the desired level of shine.
14. The method of honing and polishing a rough, irregular concrete surface comprising the steps of:
(a) cleaning the surface; (b) honing the surface with a rough grit honing disk, using water as a lubricant, so as to produce a substantially smooth, even surface. ; (c) cleaning the surface and allowing it to dry. ; (d) applying to the concrete surface a hardening/densifying silicate compound; (e) allowing the hardening/densifying silicate compound to remain in contact with the surface for a period of time sufficient to allow the silicate hardening/densifying compound to soak into the surface of the concrete; and (g) mechanically polishing the concrete surface with a rotating diamond abrasive disk or drum.
20. A method of removing and leveling soft, porous, carbonated concrete from a surface and polishing the surface, said method comprising the steps of:
(a) abrading and removing the soft surface with a coarse rotating grinder; (b) cleaning the surface and allowing it to dry; (c) applying to the concrete surface a silicate hardening/densifying compound; (d) allowing the silicate hardening/densifying compound to remain in contact with the surface for a period of time sufficient to allow the silicate hardening/densifying compound to soak into the surface of the concrete; (e) allowing the surface to dry thoroughly, removing any puddles; (f) mechanically polishing the concrete surface with a rotating diamond abrasive disk or drum; (g) cleaning the concrete surface; (h) applying to the concrete surface a diluted silicate polishing compound; (i) mechanically polishing the concrete surface with a rotating diamond polishing pad, disk or drum having a less rough grit than was used in the previous polishing step; and (j) repeating steps (f) through (h) until, upon cleaning, the surface has the desired level of shine.
2. The method as described in
3. The method as described in
4. The method as described in
5. The method as described in
6. The method as described in
0. 7. The method as described in
8. The method as described in
10. The method as described in
11. The method as described
0. 12. The method as described in
13. The method as described in
0. 15. The method described in
16. The method described in
(h) cleaning the concrete surface; (i) applying to the concrete surface a diluted silicate polishing compound; (j) mechanically polishing the concrete surface with a rotating diamond polishing pad, disk or drum having a less rough grit than was used in the previous polishing step; and (k) repeating steps (h) through (j) until, upon cleaning, the surface has the desired level of shine.
17. The method as described in
(i) abrading the surface with a coarse rotating grinder disk; and (ii) applying a chemical stripper to remove any remaining part of the coating.
0. 18. The method described in
19. The method described in claim 18 17 wherein said polishing pads, disks or drums are in a grit coarseness range of about 50 to 800.
|
1. Field of the Invention
The present invention relates to a method for polishing concrete surfaces. More particularly, the present invention relates to an improved method for polishing and repairing concrete walls, floors, and the like.
2. State of the Art
Concrete is one of the most widely used construction materials. Because of its strength, durability, ease of manufacture, ease of installation, and relatively low cost, it is frequently the material of choice for floors, walls, and the like. However, there are many instances where it is desirable to have a floor or wall surface with a pleasing high gloss finish or shine. In such cases, concrete may be overlooked in favor of other more high cost materials such as marble, stone, terrazo, etc.
There are a number of known methods of cleaning and polishing marble and stone surfaces. For example, U.S. Pat. No. 5,605,493 to Donatelli et al. discloses a fairly typical method for stone polishing including the steps of applying a solution to a stone floor, mechanically polishing with a rotary disk, and removing the slurry. Similarly, U.S. Pat. No. 5,454,751 to Wiand discloses an abrasive rotary polishing disk designed to resist damage from ridges, bumps, and other floor irregularities. These prior art devices and methods deal exclusively with stone floors of various kinds, and do not address the polishing of concrete. Moreover, while these known devices and methods anticipate the use of a liquid lubricant of some kind during polishing to create a slurry.
The use of silicates as abrasives is also well known. For example, U.S. Pat. No. 4,565,644 to Smith et al. discloses a floor cleaning and waxing composition which may include silicate abrasives, U.S. Pat. No. 5,191,002 to Davis discloses a floor care maintenance system including a floor finish stripper containing sodium metasilicate. U.S. Pat. No. 1,965,299 to Patterson discloses an abrading and polishing composition for enamels, lacquers, etc., which may include a silicate abrasive agent. U.S. Pat. No. 2,196,992 to Keller discloses a metal polish which contains sodium silicate. U.S. Pat. No. 3,540,891 to Muhler discloses a household cleaning and polishing composition containing zirconium silicate. U.S. Pat. No. 3,615,305 to Muhler discloses a dental amalgam polishing composition containing stannous silicate. U.S. Pat. No. 3,685,218 to Gamble discloses a glass polishing composition containing zirconium silicate. Notably, none of these prior art methods mention or suggest the use of silicates as a polishing compound for concrete.
It is an object of this invention to provide a method of mechanically polishing a concrete surface to obtain an aesthetically pleasing high gloss using a silicate polishing solution.
It is also an object of the present invention to provide a method of internally densifying and hardening a concrete surface using silicate based compounds.
It is another object of this invention to provide a method of honing, smoothing, and polishing a rough concrete surface using silicate based compounds.
The above and other objects are realized in a specific illustrative embodiment of a method of hardening and polishing concrete surfaces. This method includes the steps of first densifying and hardening the concrete surface by a silicate based hardening/densifying compound, allowing the hardening/densifying compound to remain in contact with surface for a period of time sufficient to allow it to soak into the surface of the concrete, cleaning the surface and allowing it to dry, secondly polishing the surface with a diluted silicate polishing compound. The surface polishing step includes applying to a concrete surface a diluted silicate polishing compound, mechanically polishing the concrete surface with a rotary, drum or disc polishing machine, cleaning the concrete surface, and then repeating the above steps with polishing pads or discs, of increasingly finer grit until the surface obtains an aesthetically desirable level of shine.
In accordance with another aspect of the invention, a rough concrete surface may be honed and polished by the steps of cleaning the surface, honing the surface with a rough grit honing disk so as to produce a smooth even surface, using water as a lubricant, cleaning the surface and allowing it to dry, applying to the concrete surface a silicate hardening/densifying compound, allowing the silicate hardening/densifying compound to remain in contact with the surface for a period of time sufficient to allow the compound to soak into the surface of the concrete, allowing the surface to dry thoroughly, removing any puddles, mechanically polishing the concrete surface, cleaning the surface, and polishing the surface with a diluted silicate polishing compound as described above.
Other objects and features of the invention will be apparent to those skilled in the art, based on the following description.
A concrete surface, such as a floor or wall, may be polished in accordance with the present invention once it has cured sufficiently. Adequate curing usually requires at least 28 days after the concrete is placed, though the time may vary depending on environmental conditions, the particular concrete mix, and whether any additives such as fast-setting admixture have been used. The general process involves first applying to the concrete a silicate-based hardening/densifying compound. This compound, in solution, is applied to the concrete surface at a suitable rate to completely wet the surface, and is allowed to remain in contact with the surface for a period of time sufficient to allow the compound to fully soak into the surface of the concrete. The excess solution is then removed and the surface allowed to thoroughly dry. Once dry, a solution of diluted silicate compound is applied to the surface to form a polishing slurry as the surface is buffed or polished using for example, a rotary polishing machine. In the preferred embodiment of the present invention, the hardneing/densifying solution is composed of water to silicate compound ration of 3 to 1, while the diluted silicate polishing compound comprises water and silicate compound in a ratio of approximately 10 to 1. Exemplary silicate compounds suitable for use in both the hardening and polishing steps include, among others, sodium silicate, zinc fluosilicate and magnesium fluosilicate. Other silicate compounds may also be used, but a preferred silicate compound is sodium silicate. Suitably rotary polishing machines are well known in the industry, and typically incorporate circular abrasive pads, or disks or drums which mount to the bottom of the machine. Suitable pads, or disks include Turbo Spiral made by VMC Technical Assistance Corporation, and may comprise diamond-impregnated abrasive disks or drums.
To adequately polish the surface following this method, it is usually required to pass over the surface with the rotary polishing machine so as to allow the rotating disk, pad or drum to contact all areas of the surface at least twice. Alternatively, three passes in alternatingly perpendicular directions may be used to obtain superior results. During polishing there should be a continuous flow of polishing compound to adequately lubricate the polishing action and impart desired shine to the surface. When the appropriate passes have been made over a given surface, the surface is cleaned; the surface may be inspected to determine whether the desired level of shine has been achieved. The surface must be dry in order to see its true shine and appearance.
If the desired level of shine has not been achieved, the above process is repeated using abrasive pads of less grit each time, and cleaning the surface between each repetition of the process. If the floor is not cleaned between each repetition of the process, excessive wear of the polishing disk will occur. As is well known in the industry, the coarseness of abrasives is indicated by numbers, with lower numbers representing coarser grit, and higher numbers representing finer grit. A typical concrete surface in good condition may be initially polished with 120 to 800 grit pads, disks or drums depending on the desired sheen. With each successive repetition of the polishing process, the grit of the pads will typically be increased by 200 each time. A satisfactorily high gloss may be obtained with pads, disks or drums of anywhere from 800 to 1800 grit, depending on one's preferred level of shine.
Alternatively, a rough or damaged concrete surface may need to be honed before the polishing process is possible. The surface must first be cleaned, then honed with a 50 or 120 grit rotary grinding disk using at least two passes. Water is used as a lubricant to produce a slurry. This process may require more passes or graduation from one grit level to another--with clenaing in between--as described above. Once the surface has become smooth and even, a silicate hardening/densifying compound (described earlier) is applied to the surface and allowed to soak into it. this compound will preferably be applied at a rate of one gallon per 40 to 200 square feet, and will be allowed to soak into the surface for approximately 30 minutes without being removed, and without additional water being used, though any puddles should be removed. The surface should be allowed to dry completely before polishing begins. The surface is then polished as described above starting with a 50 grit pad, disk or drum then stepping up to 220 or 600 grit, and so on until the desired shine is achieved, using a continuous flow of diluted slicate polishing compound (diluted 10:1 with water as described above) with each grit, and always removing the slurry between polishing stages.
An abnormally porous, soft, or carbonated, concrete surface may need to be honed before polishing is possible. In such case, the surface must first be cleaned, then honed with a 50 or 120 grit rotary grinding disk using at least two passes. Water is used as a lubricant to produce a slurry. This process may require more passes and/or graduation from one grit level to another, with cleaning in between, as described above. Once the soft surface has been removed and the remaining surface has become smooth and even, a silicate hardening/densifying compound (described earlier) is applied to the surface and allowed to soak into it. This compound is preferably applied at a rate of one gallon per 40 to 200 square feet, and is allowed to soak into the surface for approximately 30 minutes without being removed, and without additional water being use, though any puddles should be removed. The surface is allowed to dry completely before polishing begins. The surface is then polished as described above starting with a 50 grit pad, and stepping up to 440 or 600 grit, and so on until the desired shine is achieved, using a continuous flow of diluted silicate polishing compound (diluted 10:1 with water as described above) with each grit, and always removing the slurry between polishing stages.
In the manner described, a concrete surface may be hardened and polished to a high gloss finish or shine.
It is to be understood that the above-described arrangements are only illustrative of the application of the principles of the present invention. Numerous modification and alternative arrangements may be devised by those skilled in the art without departing from the spirit and scope of the present invention and the appended claims are intended to cover such modifications and arrangements.
Wetherell, Mark, Jones, Jerald W.
Patent | Priority | Assignee | Title |
10322485, | Jan 29 2010 | KAYNE SENIOR CREDIT III LOANCO, LLC, AS ADMINISTRATIVE AGENT; ADHESIVES TECHNOLOGY CORPORATION | Methods for polishing flooring surfaces |
10343254, | Feb 01 2013 | Global Polishing Systems, LLC | Concrete cutting, polishing, and coloring treatment solutions and methods |
11130209, | Jan 29 2010 | KAYNE SENIOR CREDIT III LOANCO, LLC, AS ADMINISTRATIVE AGENT; ADHESIVES TECHNOLOGY CORPORATION | Methods for providing glossy surfaces |
11471998, | Feb 01 2013 | Global Polishing Systems, LLC | Tools for polishing and refinishing concrete and methods for using the same |
7071153, | Apr 29 2004 | DIVERSEY, INC | Method of enhancing a soiled porous surface and maintenance thereof |
7255513, | Aug 16 2004 | Diamond trowel blade | |
7481602, | Aug 16 2004 | Diamond trowel blade | |
7530762, | May 26 2006 | Methods and apparatuses for surface finishing cured concrete | |
7775741, | May 26 2006 | Apparatus and method for surface finishing cured concrete | |
9073165, | Feb 01 2013 | GLOBAL POLISHING SYSTEMS LLC | Methods for grinding and polishing dried concrete using amorphous colloidal silica solution |
9662757, | Feb 01 2013 | Global Polishing Systems, LLC | Concrete cutting, polishing and coloring treatment solutions and methods |
Patent | Priority | Assignee | Title |
165898, | |||
1965299, | |||
2078289, | |||
2196992, | |||
2275272, | |||
2277203, | |||
3540891, | |||
3615305, | |||
3685218, | |||
4565644, | Jul 06 1983 | CREATIVE PRODUCTS RESOURCE, INC | Floor cleaning and waxing composition |
4699807, | Oct 07 1986 | Golden Age Furniture Finishing Products Co. | Finish restorer |
4910824, | Nov 17 1987 | Amano Corporation | Floor polisher |
5016310, | Aug 21 1989 | Tennant Company | Floor scrubber having laterally variable scrub brush position |
5026421, | Dec 09 1987 | Rhone-Poulenc Chimie | Polishing compositions based on cerium and process for the preparation thereof |
5057152, | Jun 24 1987 | UOP, DES PLAINES, ILLINOIS A NY GENERAL PARTNERSHIP; KATALISTIKS INTERNATIONAL, INC | Surface cleaner/polish compositions and a process for the preparation thereof |
5174813, | Nov 07 1991 | Dow Corning Corporation | Polish containing derivatized amine functional organosilicon compounds |
5191002, | Oct 18 1991 | Puritan/Churchill Chemical Company; PURITAN CHURCHILL CHEMICAL COMPANY | Method and compositions for a floor care maintenance system |
5203046, | Jul 22 1991 | Floor buffing machine | |
5309592, | Jun 23 1992 | XARAZ PROPERTIES LLC | Cleaning robot |
5441677, | Sep 01 1993 | Hi-Tech Floors, Inc.; HI-TECH FLOORS, INC | Method of making high gloss, hardened concrete floors |
5454751, | Mar 30 1990 | Marble, granite and stone finishing and abrasive pads therefor | |
5605493, | Apr 19 1994 | NILFISK, INC | Stone polishing apparatus and method |
6454632, | Oct 30 1998 | CURECRETE CHEMICAL COMPANY, INC | Method of hardening and polishing concrete floors, walls, and the like |
Executed on | Assignor | Assignee | Conveyance | Frame | Reel | Doc |
Jul 12 2002 | WETHERELL, MARK | CURECRETE CHEMICAL COMPANY, INC | ASSIGNMENT OF ASSIGNORS INTEREST SEE DOCUMENT FOR DETAILS | 013357 | /0023 | |
Oct 01 2002 | Curecrete Chemical Company, Inc. | (assignment on the face of the patent) | / |
Date | Maintenance Fee Events |
May 11 2004 | M2551: Payment of Maintenance Fee, 4th Yr, Small Entity. |
Jun 16 2008 | REM: Maintenance Fee Reminder Mailed. |
Aug 19 2008 | ASPN: Payor Number Assigned. |
Sep 02 2008 | M2552: Payment of Maintenance Fee, 8th Yr, Small Entity. |
Sep 02 2008 | M2555: 7.5 yr surcharge - late pmt w/in 6 mo, Small Entity. |
Jul 16 2012 | REM: Maintenance Fee Reminder Mailed. |
Nov 30 2012 | EXP: Patent Expired for Failure to Pay Maintenance Fees. |
Date | Maintenance Schedule |
Dec 23 2006 | 4 years fee payment window open |
Jun 23 2007 | 6 months grace period start (w surcharge) |
Dec 23 2007 | patent expiry (for year 4) |
Dec 23 2009 | 2 years to revive unintentionally abandoned end. (for year 4) |
Dec 23 2010 | 8 years fee payment window open |
Jun 23 2011 | 6 months grace period start (w surcharge) |
Dec 23 2011 | patent expiry (for year 8) |
Dec 23 2013 | 2 years to revive unintentionally abandoned end. (for year 8) |
Dec 23 2014 | 12 years fee payment window open |
Jun 23 2015 | 6 months grace period start (w surcharge) |
Dec 23 2015 | patent expiry (for year 12) |
Dec 23 2017 | 2 years to revive unintentionally abandoned end. (for year 12) |