There is disclosed a lubricating oil composition which contains from about 100 to 450 parts per million of molybdenum from a molybdenum compound which is substantially free of active sulfur and about 750 to 5,000 parts per million of a secondary diarylamine. This combination of ingredients provides improved oxidation control and friction modifier performance to the lubricating oil. The composition is particularly suited for use as a crankcase lubricant.
|
0. 50. A method for improving the antioxidancy and friction properties of a lubricant adapted for use in lubricating an internal combustion engine which method comprises including in the lubricant a molybdenum compound which is free of phosphorus and is free of active sulfur, said molybdenum compound providing about 100 to 450 parts per million of molybdenum to the lubricant and about 750 to 5000 parts per million of an oil soluble secondary diarylamine.
0. 23. A lubricating composition comprising:
a major amount of lubricating oil,
at least one oil soluble molybdenum compound that is free of phosphorus and free of active sulfur, and
at least one oil soluble secondary diarylamine,
wherein the ratio of molybdenum provided by said oil soluble molybdenum compound relative to said oil soluble secondary diarylamine is about 0.02 to 0.6 parts by weight molybdenum per part of said second diarylamine, said oil soluble molybdenum compound is present in an amount to provide about 100 to 450 parts per million of molybdenum based on the weight of said lubricating composition, provided said oil soluble secondary diarylamine is present in an amount equal to, or greater than, from about 750 ppm based on the weight of said lubricating composition.
0. 59. A lubricating composition comprising:
a major amount of lubricating oil,
at least one oil soluble molybdenum carboxylate compound that is free of phosphorus and free of active sulfur and provides about 104 to 468 ppm of molybdenum based on the weight of the lubricating composition, wherein the carboxylate anion has from 4 to 30 carbon atoms,
at least one oil soluble secondary diarylamine comprising an alkylated diphenyl amine,
wherein the ratio of molybdenum provided by said oil soluble molybdenum compound relative to said oil soluble secondary diaryl amine is about 0.02 to 0.6 parts by weight molybdenum per part of said secondary diarylamine, and provided said oil soluble secondary diarylamine is present in an amount equal to, or greater than, about 750 ppm based on the weight of said lubricating composition.
0. 71. A lubricating composition consisting essentially of:
a major amount of lubricating oil; and
an antioxidant combination that consists essentially of:
at least one oil soluble molybdenum compound that is free of phosphorus and free of active sulfur, and
at least one oil soluble secondary diarylamine,
wherein the ratio of molybdenum provided by said oil soluble molybdenum compound relative to said oil soluble secondary diarylamine is about 0.02 to 0.6 parts by weight molybdenum per part of said secondary diarylamine, said oil soluble secondary diarylamine is present in an amount of about 750 to about 5,000 parts per million of said lubricating composition, provided said oil soluble molybdenum compound is present in an amount so as to provide greater than about 100 ppm molybdenum based on the weight of said lubricating composition.
0. 22. A lubricating composition comprising:
a major amount of lubricating oil,
at least one oil soluble molybdenum compound that is free of phosphorus and free of active sulfur, and
at least one oil soluble secondary diarylamine,
wherein the ratio of molybdenum provided by said oil soluble molybdenum compound relative to said oil soluble secondary diarylamine is about 0.02 to 0.6 parts by weight molybdenum per part of said second diarylamine, said oil soluble secondary diarylamine is present in an amount of about 750 to about 5,000 parts per million of said lubricating composition, said oil soluble molybdenum compound and said secondary diaryl amine are present in an effective antioxidant amount, provided said oil soluble molybdenum compound is present in an amount so as to provide greater than about 100 ppm molybdenum based on the weight of said lubricating composition.
0. 1. A lubricating composition comprising a major amount of lubricating oil, an oil soluble molybdenum compound providing about 100 to 450 parts per million of molybdenum, said molybdenum compound selected from the group consisting of a sulfur and phosphorus free organic amide molybdenum complex and a molybdenum carboxylate wherein the carboxylate anion has from about 4 to 30 carbon atoms and about 750 to 5,000 parts per million of an oil soluble secondary diarylamine.
0. 2. The composition of
0. 3. The composition of
0. 4. The composition of
0. 5. The composition of
wherein R1 and R2 each independently represent an aryl group having from about 6 to 30 carbon atoms.
0. 6. The composition of
0. 7. A method for improving the antioxidancy and friction properties of a lubricant which comprises including in the lubricant, a molybdenum compound which provides about 100 to 450 parts per million of molybdenum said molybdenum compound selected from the group consisting of a sulfur and phosphorus free organic amide molybdenum complex and a molybdenum carboxylate wherein the carboxylate anion has from about 4 to 30 carbon atoms and about 750 to 5,000 parts per million of an oil soluble secondary diarylamine.
0. 8. The method of
wherein each of R1 and R2 is alkphenyl having from about 4 to 18 carbon atoms in each alkyl group.
0. 9. The method of
0. 10. The method of
0. 11. The method of
0. 12. The method of
0. 13. A lubricating oil concentrate prepared by dissolving a total of from about 2.5 to 90 parts by weight of an oil soluble molybdenum compound selected from the group consisting of a sulfur and phosphorus free organic amide molybdenum complex and a molybdenum carboxylate derived from an organic carboxylic acid having about 4 to 30 carbon atoms and an oil soluble secondary diarylamine dissolved in 10 to 97.5 parts of a solvent wherein the weight ratio of molybdenum to amine is from about 0.02 to 0.6 parts of molybdenum for each part of amine.
0. 14. The concentrate of
0. 15. The concentrate of
0. 16. A lubricating oil composition prepared by mixing an oil soluble molybdenum compound selected from the group consisting of a sulfur and phosphorus free organic amide molybdenum complex and a molybdenum carboxylate derived from monocarboxylic acids selected from the group consisting of aliphatic acids having about 4 to 18 carbon atoms, alicyclic acids containing from 4 to 12 carbon atoms and aromatic acids containing from 7 to 14 carbon atoms and an oil soluble secondary diaryl amine in a lubricating oil wherein the concentration of the molybdenum in the oil is from about 100 to 450 parts per million and the concentration of the amine in the oil is from about 750 to 5,000 parts per million based on said composition.
0. 17. The lubrication composition of
A. the molybdenum compound is a molybdenum carboxylate of an aliphatic acid having from 4 to 18 carbon atoms and the concentration thereof is from about 100 to 250 parts per million of the composition; and
B. the diaryl amine is of the formula:
##STR00004##
wherein R1 and R2 each independently represent an aryl group having from about 6 to 30 carbon atoms and the concentration thereof is from about 1,000 to 4,000 parts per million of the composition.
0. 18. The lubrication composition of
0. 19. A method for improving the antioxidant and friction properties of a lubricant which comprises adding to the lubricant an oil soluble molybdenum carboxylate derived from an organic carboxylic acid having from about 4 to 30 carbon atoms and wherein said molybdenum carboxylate provides about 100 to 450 parts per million of molybdenum and about 750 to 5,000 parts per million of an oil soluble secondary diarylamine.
0. 20. The method of
0. 21. The method of
wherein each of R1 and R2 is alkphenyl having from about 4 to 18 carbon atoms in each alkyl group.
0. 24. A lubricating composition according to
0. 25. A lubricating composition according to
0. 26. A lubricating composition according to
0. 27. A lubricating composition according to
0. 28. A lubricating composition according to
0. 29. A lubricating composition according to
0. 30. A lubricating composition according to
0. 31. A lubricating composition according to
0. 32. A lubricating composition according to
0. 33. A lubricating composition according to
0. 34. A lubricating composition according to
0. 35. A lubricating composition according to
0. 36. A lubricating composition according to
0. 37. A lubricating composition according to
0. 38. A lubricating composition according to
0. 39. A lubricating composition according to
0. 40. A lubricating composition according to
0. 41. A lubricating composition according to
0. 42. A lubricating composition according to
0. 43. A lubricating composition according to
0. 44. A lubricating composition according to
wherein R1 and R2 each independently represent an aryl group having from 6 to 30 carbon atoms.
0. 45. A lubricating composition according to
0. 46. A lubricating composition according to
0. 47. A lubricating composition according to
0. 48. A lubricating composition according to
0. 49. A lubricating composition according to
0. 51. A method for lubricating an engine comprising adding a lubricating composition of
0. 52. An engine lubricated according to the method of
0. 53. A lubricating composition according to
0. 54. A lubricating composition according to
0. 55. A lubricating composition according to
0. 56. A lubricating composition according to
0. 57. A lubricating composition according to
0. 58. A lubricating composition according to
0. 60. A lubricating composition according to
0. 61. A lubricating composition according to
0. 62. A lubricating composition according to
0. 63. A lubricating composition according to
0. 64. A lubricating composition according to
0. 65. A lubricating composition according to
0. 66. A lubricating composition according to
0. 67. A lubricating composition according to
0. 68. The lubricating composition according to
0. 69. A method for lubricating an internal combustion engine comprising adding a lubricating composition of
0. 70. An internal combustion engine lubricated according to the method of
0. 72. The lubricating composition according to
0. 73. The lubricating composition according to
0. 74. The lubricating composition according to
0. 75. The lubricating composition according to
0. 76. The lubricating composition comprising:
a major amount of lubricating oil,
at least one oil soluble molybdenum compound that is free of phosphorus and free of active sulfur, and
at least one oil soluble secondary diarylamine,
wherein the ratio of molybdenum provided by said oil soluble molybdenum compound relative to said oil soluble secondary diarylamine is about 0.02 to 0.6 parts by weight molybdenum per part of said secondary diarylamine, wherein said oil soluble molybdenum compound is present in an amount to provide greater than about 100 parts per million of molybdenum based on the weight of said lubricating composition, provided said oil soluble secondary diarylamine is present in an amount up to 5,000 ppm based on the weight of said lubricating composition.
|
This application 09/604,285, filed Jun. 26, 2000, is a continuation of application 09/359,770, filed Jul. 22, 1999, now U.S. Pat. No. RE 37,363 E, and each are reissues of U.S. Pat. No. 5,650,381, which issued from application Ser. No. 08/559,879, filed Nov. 20, 1995.
1. Field of the Invention
This invention relates to lubricating oil compositions, their method of preparation, and use. More specifically this invention relates to lubricating oil compositions which contain a molybdenum compound and a secondary diarylamine wherein the molybdenum compound is substantially free of active sulfur. The use of both the molybdenum and amine within certain concentrations provide improved oxidation control and friction modifier performance to lubricating oil compositions. The lubricating oil compositions of this invention are particularly useful as crankcase lubricants.
2. Description of the Related Art
Lubricating oils as used in the internal combustion engines of automobiles or trucks are subjected to a demanding environment during use. This environment results in the oil suffering oxidation which is catalyzed by the presence of impurities in the oil such as iron compounds and is also promoted by the elevated temperatures of the oil during use. This oxidation of lubrication oils during use is usually controlled to some extent by the use of antioxidant additives which may extend the useful life of the oil, particularly by reducing or preventing unacceptable viscosity increases.
We have now discovered that a combination of about 100 to 450 parts per million (ppm) of molybdenum from an oil soluble molybdenum compound which is substantially free of active sulfur and about 750 to 5,000 ppm of an oil soluble secondary diarylamine is highly effective in inhibiting oxidation in lubricant compositions and that this antioxidant performance is supplemented by improved friction modifier performance. The molybdenum acts synergistically with secondary diarylamines to provide significant improvement in oxidation control. In addition to excellent oxidation control, the molybdenum compounds also act as friction modifiers to provide substantial fuel economy performance.
Lubricant compositions containing various molybdenum compounds and aromatic amines have been used in lubricating oils. Such compositions include active sulfur or phosphorus as part of the molybdenum compound, use additional metallic additives, various amine additives which are different from those used in this invention, and/or have concentrations of molybdenum and amine which do not show the synergistic results obtained by this invention.
U.S. Pat. No. 3,285,942 of Nov. 15, 1966 to Esso discloses the preparation of glycol molybdate complexes which have utility in lubrication oils.
U.S. Pat. No. 4,394,279 of Jul. 19, 1983 to L. de Vries et al. discloses an antioxidant additive combination for lubrication oils prepared by combining (a) an active sulfur containing molybdenum compound prepared by reacting an acidic molybdenum compound, a basic nitrogen compound and carbon disulfide with (b) an aromatic amine compound.
U.S. Pat. No. 4,832,857 of May 23, 1989 to Amoco Corp discloses a process for preparation of overbased molybdenum alkaline earth metal and alkali metal dispersions for use in lubricating oil compositions.
U.S. Pat. No. 4,846,983 of Jul. 11, 1989 W. C. Ward discloses molybdenum containing hydrocarbyl dithiocarbamates prepared from primary amines that impart antiwear, antioxidant, extreme pressure, and friction properties to lubricating oils. Again, among other shortcomings, these molybdenum compounds contain substantial quantities of active sulfur.
U.S. Pat. No. 4,889,647 of Dec. 26, 1989 to R. T. Vanderbilt Co. discloses organic molybdenum complexes for use in lubrication oil compositions.
U.S. Pat. No. 5,137,647 of Aug. 11, 1992 to R. T. Vanderbilt Co. discloses molybdenum complexes for use in fuels and lubricating oil compositions.
U.S. Pat. No. 5,143,633 of Sept. 1, 1992 to Gallo et al discloses superbasic additives for lubricant oils containing an organic molybdenum complex.
WO95/07962 of Mar. 23, 1995 to A. Richie et al. discloses a crankcase lubricant composition for use in automobile or trunk engines which contains copper, molybdenum, and aromatic amines. In addition to the requirement for use of copper, this publication recites a very broad range of concentrations of amine used with the molybdenum in the examples of that publication is well outside the range which this invention has found to be synergistic. Also, many of the molybdenum compounds of this reference contain active sulphur, phosphorus, and other elements and the amines include compounds such as primary amines which were not found synergistic with the molybdenum carboxylates of this invention.
WO95/07963 of 23 Mar. 1995 to H. Shaub discloses highly sulfurized molybdenum compounds and various secondary aromatic amines having at least one aromatic group for producing a synergistic antioxidant effect when used as an antioxidant additive for lubricating oils. Again the molybdenum compounds contain active sulfur.
WO95/07966 of 23 Mar. 1995 to J. Atherton et al. discloses engine oil lubricants of various molybdenum compounds including that of some with active sulfur, certain organo-phosphorus compounds, an aminic antioxidant and a phenolic antioxidant within certain proportions.
In one aspect, this invention is directed to a lubricating composition comprising (a) a major amount of lubrication oil, (b) an oil soluble molybdenum compound substantially free of active sulfur which provides about 100 to 450 parts per million of molybdenum, and (c) about 750 to 5,000 parts per million (ppm) of an oil soluble secondary diarylamine.
In another aspect, the invention is directed to a method for improving the antioxidancy and friction properties of a lubricant by incorporating in the lubricant a molybdenum compound which is substantially free of active sulfur and a secondary diarylamine in the above described concentrations.
In still another aspect, the invention is directed to a lubrication oil concentrate comprising a solvent and a combination of from about 2.5 to 90 percent by weight of an oil soluble molybdenum compound which is substantially free of active sulfur and an oil soluble secondary diarylamine wherein the weight ratio of molybdenum from the molybdenum compound to the diarylamine in the concentration is from about 0.020 to 0.60 parts of molybdenum for each part of amine.
In yet another aspect, the invention is directed to a lubricating composition prepared by mixing 100 to 450 parts per million of oil soluble molybdenum compound substantially free of active sulfur and 750 and 5,000 parts of a secondary diaryl amine in a lubricating composition.
In a yet further aspect, the invention is directed to a lubrication oil concentrate prepared by dissolving in about 10 to 97.5 parts of a solvent a total of 2.5 to 90 parts of an oil soluble molybdenum compound substantially free of active sulfur and an oil soluble secondary diaryl amine.
In yet a still further aspect, the molybdenum compound used in the various compositions and methods of this invention is substantially free of sulfur.
The compositions of this invention have various uses as lubricants such as for automotive and trunk crankcase lubricants as well as transmission lubricants.
A key advantage of this invention is the multifunctional nature of the molybdenum/diarylamine combination and the relatively low treat levels required for a performance benefit. This additive combination provides both oxidation control and friction control to the oil. This reduces the need for supplemental oxidation protection and frictional properties and should reduce the overall cost of the entire additive package. Further cost reduction is gained by the low treat levels employed.
The molybdenum compound used in this invention can be any molybdenum compound which is soluble in the lubricant or formulated lubricant package and is substantially free of active sulfur. By “soluble” or “oil soluble” is meant that the compound is oil soluble or solubilized under normal blending conditions into the lubrication oil or concentrate thereof. “Active” sulfur is sulfur which is not fully oxidized. Active sulfur further oxidizes and becomes more acidic in the oil upon use. Illustratively, sulfur such as divalent sulfur is active sulfur whereas the sulfur in a sulfonate group is fully oxidized and thus non-active sulfur. It is preferred however that the molybdenum compound be substantially free of all sulfur. By “substantially free” we mean that the molybdenum compound contains less than about 0.5% by weight of the material in question, e.g., active sulfur which is generally an insufficient amount to add significantly to corrosion. The sulfur content of some commercially available molybdenum compounds can often have as much as about 1,000 ppm of sulfur as a contaminant and occasionally there can be as much as 2,000 ppm of the active sulfur. Such small amounts often come from contamination is processing the various ingredients involved. By “alkphenyl” or “alkaryl” we mean a phenyl or aryl group, respectively, which contains an alkyl substituent.
Oil soluble molybdenum compounds prepared from a molybdenum source such as ammonium molybdates, alkali and alkaline earth metal molybdates, molybdenum trioxide, and molybdenum acetylacetonates and an active hydrogen compound such as alcohols and polyols, primary and secondary amines and polyamines, phenols, ketones, anilines, etc. can be used in combination with the diarylamines in this invention. The following listing provides examples of some molybdenum compounds which are substantially free of active sulfur and that may be used in combination with diarylamines in this invention:
Molybdenum salts such as the carboxylates are a preferred group of molybdenum compounds. The molybdenum salts used in this invention may be completely dehydrated (complete removal of water during preparation), or partially dehydrated. They may be salts of the same anion or mixed salts, meaning that they are formed from more than one type of acid. Illustrative of suitable anions there can be mentioned chloride, carboxylate, nitrate, sulfonate, or any other anion.
The molybdenum carboxylates may be derived from any organic carboxylic acid. The molybdenum carboxylate is preferably that of a monocarboxylic acid such as that having from about 4 to 30 carbon atoms. Such acids can be hydrocarbon aliphatic, alicyclic, or aromatic carboxylic acids. Monocarboxylic acids such as those of aliphatic acids having about 4 to 18 carbon atoms are preferred, particularly those having an alkyl group of about 6 to 18 carbon atoms. The alicyclic acids may generally contain from 4 to 12 carbon atoms. The aromatic acids may generally contain one or two fused rings and contain from 7 to 14 carbon atoms wherein the carboxyl group may or may not be attached to the ring. The carboxylic acid can be a saturated or unsaturated fatty acid having from about 4 to 18 carbon atoms. Examples of some carboxylic acids that may be used m prepare the molybdenum carboxylates include: butyric acid; valeric acid; caproic acid heptanoic acid; cyclohexanecarboxylic acid; cyclodecanoic acid; naphthenic acid; phenyl acetic acid; 2-methylhexanoic acid; 2-ethylhexanoic acid; suberic acid; octanoic acid; nonanoic acid; decanoic acid; undecanoic acid; lauric acid, tridecanoic acid; myristic acid; pentadecanoic acid; palmitic acid; linolenic acid; heptadecanoic acid; stearic acid; oleic acid; nonadecanoic acid; eicosanoic acid; heneicosanoic acid; docosanoic acid; and erucic acid.
A number of methods have been reported in the literature for preparing the molybdenum carboxylates, e.g., U.S. Pat. No. 4,593,012 of Jun. 3, 1986 to Usui and U.S. Pat. No. 3,578,690 of May 11, 1971 to Becker, both of which are incorporated herein by reference in their entirety. The Usui patent describes the production of hydrocarbon soluble salts (molybdenyl carboxylates) by reaction of an ammonium molybdate with a carboxylic acid in the presence of an organic amine at specified elevated temperatures while removing water, U.S. Pat. No. 3,578,690 prepares its molybdenum carboxylates by reacting molybdenum oxide, molybdenum halide, alkali earth molybdate, alkaline earth molybdate, ammonium molybdate or mixtures of molybdenum sources with carboxylic acids at elevated temperatures and with removal of water.
The exact composition of the oil soluble molybdenum carboxylates can vary. Most of the literature refers to these compounds as molybdenum carboxylates. They have also been referred to as molybdenum carboxylate salts, molybdenyl (Mo O22+) carboxylates and molybdenyl carboxylate salts, molybdenum carboxylic acid salts, and molybdenum salts of carboxylic acids.
The concentration of the molybdenum from the molybdenum compound in the lubricant composition can vary depending upon the customer's requirements and applications. The actual amount of molybdenum added is based on the desired final molybdenum level in the lubricating composition. From about 100 to 450 parts per million of molybdenum are used in this invention based on the weight of the lubricating oil composition which may be formulated to contain additional additives and preferably about 100 to 250 parts per million of molybdenum and particularly 125 to 250 ppm are used based on the weight of the lubricating oil composition. The quantity of additive, e.g. molybdenum carboxylate to provide molybdenum, is based on the total weight of the formulated or unformulated lubricating oil composition.
The secondary diarylamines are well known antioxidants and there is no particular restriction on the type of secondary diarylamine used in the invention. Preferably, the secondary diarylamine antioxidant has the general formula:
##STR00001##
wherein R1 and R2 each independently represents a substituted or unsubstituted aryl group having from 6 to 30 carbon atoms. Illustrative of substituents for the aryl there can be mentioned aliphatic hydrocarbon groups such as alkyl having from about 1 to 20 carbon atoms, hydroxy, carboxyl or nitro, e.g., an alkaryl group having from 7 to 20 carbon atoms in the alkyl group. The aryl is preferably substituted or unsubstituted phenyl or naphthyl, particularly wherein one or both of the aryl groups are substituted with an alkyl such as one having from 4 to 18 carbon atoms. It is further preferred that both aryl groups be substituted, e.g. alkyl substituted phenyl.
The secondary diarylamines used in this invention can be of a structure other than that shown in the above formula which shows but one nitrogen atom in the molecule. Thus, the secondary diarylamine can be of a different structure provided that at least one nitrogen has 2 aryl groups attached thereto, e.g., as in the case of various diamines having a secondary nitrogen atom as well as two aryls on one of the nitrogens. The secondary diarylamines used in this invention preferably have antioxidant properties in lubricating oils, even in the absence of the molybdenum compound.
The secondary diarylamines used in this invention should be soluble in the formulated crankcase oil package. Examples of some secondary diarylamines that may be used in this invention include: diphenyl amine; various alkylated diphenylamines, 3-hydroxydiphenylamine; N-phenyl-1,2-phenylenediamine; N-phenyl-1,4-phenylenediamine; dibutyldiphenylamine; dioctyldiphenylamine; dinonyldiphenylamine; phenyl-alpha-naphthylamine; phenyl-beta-naphthylamine; diheptyldiphenylamine; and p-oriented styrenated diphenylamine.
The concentration of the secondary diarylamine in the lubricating composition can vary depending upon the customer's requirements and applications. A practical diarylamine use range in the lubricating composition is from about 750 parts per million to 5,000 parts per million (i.e. 0.075 to 0.5 wt %), preferably the concentration is from 1,000 to 4,000 parts per million (ppm) and particularly from about 1,200 to 3,000 ppm by weight. Quantities of less than 750 ppm have little or minimal effectiveness whereas quantities larger than 5,000 ppm are not economical.
Preferably, the quantity of molybdenum is relation to the quantity of the secondary amine should be within a certain ratio. The quantity of molybdenum should be about 0.020 to 0.6 parts by weight for each part by weight of the amine in the lubricating oil composition. Preferably, this ratio will be from about 0.040 to 0.40 parts of the molybdenum per part of the amine and particularly about 0.05 to 0.3 parts of the molybdenum per part of the amine. The total quantity of molybdenum and amine can be provided by one or more than one molybdenum or amine compound.
The composition of the lubricant oil can vary significantly based on the customer and specific application. In general, the oil is a formulated oil which is composed of between 75 and 95 wt % of a mineral lubrication oil, between 0 and 10 wt % of a polymeric viscosity index improver, and between about 5 and 15 wt % (weight percent) of an additive package. The additive package generally contains the following components:
The lubrication oil component of this invention may be selected from any of the synthetic or natural oils used as lubricants such as that for crankcase lubrication oils for spark-ignited and compression-ignited internal combustion engines, for example automobile and truck engines, marine, and railroad diesel engines. Synthetic base oils include alkyl esters of dicarboxylic acids, polyglycols and alcohols, poly-alpha-olefins, including polybutenes, alkyl benzenes, organic esters of phosphoric acids, and polysilicone oils.
Natural base oils include mineral lubrication oils which may vary widely as to their crude source, e.g., as to whether they are paraffinic, naphthenic, or mixed paraffinic-naphthenic.
The lubrication oil base stock conveniently has a viscosity of about 2.5 to about 15 cSt or mm2/s and preferably about 2.5 to about 11 cSt or mm2/s at 100° C.
A polymeric viscosity index improver (VII) component may be used in this invention and such component may be selected from any of the known viscosity index improvers. The function of the VII is to reduce the rate of change of viscosity with temperature, i.e. they cause minimal increase in engine oil viscosity at low temperature but considerable increase at high temperature. Examples of viscosity index improvers include polyisobutylenes, polymethacrylates, ethylene/propylene copolymers, polyacrylates, styrene/maleic ester copolymers, and hydrogenated styrene/butadiene copolymers.
In addition to the lubricant additives mentioned thus far, there is sometimes a need for other supplemental additives that perform specific functions not provided by the main components. These additional additives include, pour point depressants, corrosion inhibitors, rust inhibitors, foam inhibitors and supplemental friction modifiers.
The lubricating oil compositions of this invention can be made by adding the molybdenum additive and the secondary diarylamine additive in a lubrication oil composition. In the case of a formulated oil, the composition can also contain additional additives such as dispersants, detergents, zinc dihydrocarbyl dithiophosphates, and still additional antioxidants. The method or order of component addition is not critical. Alternatively, the combination of molybdenum and amine additives can be added to the lubrication oil as a concentrate with or without such concentrate containing the remaining additives.
The lubricating oil concentrate will comprise a solvent and from about 2.5 to 90 weight percent (wt %) and preferably 5 to 75 wt % of the combination of the molybdenum additive and amine additive of this invention. The solvent may be that of hydrocarbon oils, e.g., mineral lubrication oil or a synthetic oil. The ratio of molybdenum to amine in the concentrate composition is from about 0.02 to 0.6 parts of molybdenum per part of amine and preferably from about 0.04 to 0.4 parts of molybdenum for each part of the amine by weight. In addition to the molybdenum and amine additives of this invention, the concentrate may contain additional additives as is conventional in the art, e.g., dispersants, detergents, and zinc dihydrocarbyl dithiophosphates.
There are a number of recent trends in the petroleum additive industry that may restrict, and/or limit, the use of certain additives in formulated crankcase oils. The key trends are the move to lower phosphorus levels in the oil, the new fuel economy requirements and the move to more severe engine test conditions for qualifying oils. Such changes may show that certain currently used antioxidant additives are no longer effective in protecting the oil against oxidation. The molybdenum/diarylamine based antioxidant mixture disclosed herein provides a solution to this need. Furthermore, there is concern that phosphorus from the lubricant tends to poison catalyst used in catalytic converters, thereby preventing them from functioning to full effect. Also, active sulfur containing antioxidants, including active sulfur containing molybdenum compounds are known to cause copper corrosion. This is generally known and has been disclosed by T. Colclough in Atmospheric oxidation and Antioxidants, Volume II, chapter 1, Lubrication Oil Oxidation and Stabilization, G. Scott, editor, 1993 Elsevier Science Publishers.
The molybdenum compound in this invention is preferably substantially free of phosphorus and substantially free of active sulfur and it is particularly preferred to have the molybdenum compound substantially free of sulfur whether active or otherwise.
The following examples are illustrative of the invention and its advantageous properties. In these examples as well as elsewhere in this application, all parts and percentages are by weight unless otherwise indicated.
The following example shows the antioxidant synergism that exist,; when molybdenum naphthenate and a diphenylamine are formulated into an SAE Grade 5W-30 type motor oil. The example also shows that this antioxidant behavior is unique when compared to other metals.
A variety of oil soluble metals and one diphenylamine type antioxidant were blended into an SAE Grade 5W-30 type motor oil as shown in Table 1. The only additional antioxidant in these blends was the zinc dialkyldithiophosphate. The oxidation stability of these oils was measured by pressurized differential scanning calorimetry (PDSC) as described by J. A. Walker and W. Tsang in “Characterization of Lubrication Oils by Diffrential Scanning Calorimetry”, SAE Technical Paper Series, 801383 (Oct. 20-23, 1980). Oil samples were treated with an iron (III) acetylacetonate catalyst (55 ppm Fe) and 2 milligrams (mg) were analyzed in an open aluminum hermetic pan. The DSC cell was pressurized with 500 psi air and programmed with the following heating sequence: (1) jump from ambient to 165° C., (2) jump from 165° C. to 175° C. at 2 C/min. (3) isothermal at 175° C. The oil samples were held at 175° C. until an exothermic release of heat was observed. The exothermic release of heat marks the oxidation reaction. The time from the start of the experiment to the exothermic release of heat is called the oxidation induction time and is a measure of the oxidation stability of the oil (i.e. the longer the oxidation induction time the greater the oxidative stability of the oil). All oils are evaluated in duplicate and the results averaged. As shown in Table 1 the oil samples containing both molybdenum naphthenate and diphenylamine had the longest oxidation induction times. These oil samples also contain other metals. In order to rule out the possibility of the other metal contributing to the improved oxidative stability of the oils, the oxidation induction time data was analyzed for main and interaction effects as described by G. E. P. Box, W. G. Hunter, and J. S. Hunter in “Statistics for Experiments”, 1978, John Wiley & Sons. The results are provided in Table IA. The results show the following:
The other metals show very little effect, or a negative effect, on the oxidative stabilty of the oil. In addition, the other metals show no interaction effect, or a negative interaction effect, with the diphenylamine.
In the below Tables I and IA: Ce Nap is cesium naphthenate; Co Nap is cobalt naphthenate; Ni Oct is nickel octanoate; and Mo Nap is molybdenum naphthenate. The concentration of metallic additives is expressed in parts per million of the metal. DPA is dinonyldiphenylamine which is expressed in percent by weight, e.g. 0.1 wt % being 1,000 ppm; Induction Time is the DSC Induction Time in minutes as an average.
TABLE I
PDSC Induction Times for Motor Oil Blends
Concentration of Additives In SAE Grade 5W-30 Type Motor Oil*
Oil
Cc
Co
Ni
Mo
Process
Induction
No.
Nap
Nap
Oct
Nap
DPA
Oil Wt. %
Time
1
0
0
0
0
0.10
1.50
41.8
2
200
0
0
0
0.00
1.27
16.5
3
0
200
0
0
0.00
1.27
26.4
4
200
200
0
0
0.10
0.83
26.5
5
0
0
200
0
0.00
1.35
16.1
6
200
0
200
0
0.10
0.92
28.1
7
0
200
200
0
0.10
0.92
33.5
8
200
200
200
0
0.00
0.68
22.7
9
0
0
0
200
0.00
1.27
24.7
10
200
0
0
200
0.10
0.83
60.1
11
0
200
0
200
0.10
0.83
62.5
12
200
200
0
200
0.00
0.60
34.6
13
0
0
200
200
0.10
0.92
72.4
14
200
0
200
200
0.00
0.68
26.0
15
0
200
200
200
0.00
0.68
40.9
16
200
200
200
200
0.10
0.25
54.2
*A formulated crankcase oil containing 83.2 wt % base oil, 6.2 wt % polymeric viscosity index improver, 6.9 wt % ashless dispersant, 2.1 wt % calcium, sodium & magnesium overbased & neutral detergents, and 1.2 wt % zinc dialkyldithiophosphate.
TABLE IA
Main Effects and Interaction Effects On PDSC Oxidation Induction Time
Main Effect
Interaction Effect
Factors and Interactions
(minutes)
(minutes)
Cc Nap
−6.2
Co Nap
2.0
Ni Oct
0.1
Mo Nap
20.5
DPA
21.4
Cc Nap with Co Nap
−0.2
Cc Nap with Ni Oct
−1.8
Cc Nap with Mo Nap
−0.2
Co Nap with Ni Oct
0.2
Co Nap with Mo Nap
0.3
Ni Oct with Mo Nap
2.8
Mo Nap with DPA
9.4
Ni Oct with DPA
−0.8
Co Nap with DPA
−8.4
Cc Nap with DPA
−4.1
Molybdenum naphthenate and alkylated diphenylamine, Naugalube 680, from Uniroyal Chemical Company; were blended into an SAE Grade 5W-30 type motor oil as shown in Table II. The only additional antioxidant in these blends was the zinc dialkyldithiophosphate. The oxidation stability of these oils was measured by pressurized differential scanning calorimetry (PDSC) as described in Example 1. These oils were also subjected to the following hot oil oxidation test: Into 25 grams (g) of each motor oil was blended 0.8 g of a catalyst mixture containing 5.55 wt % iron (III) naphthenate (6 wt % Fe content) and 94.45 wt % xylenes. Dry air was blown through the oil at rates of 10 Liters (L)/hour (h) while maintaining the temperature at 160° C. for a period of 72 hours. The oil was cooled and the percent change in viscosity between the new oil and the oxidized oil was determined at 40° C. A lower percent change in viscosity for an oil is an indication of less oil degradation and thus better oxidation control by the additives. All oils were evaluated in duplicate and the results averaged. Results from the PDSC and the hot oil oxidation test are found in Table II. Both the PDSC results and the hot oil oxidation test results show that the combination of molybdenum naphthenate (Mo-Nap) and alkylated diphenylamine (N-680) provides superior oxidation control versus use of these additives separately. Note that for the samples containing a combination of molybdenum naphthenate and the diphenylamine the measured oxidation induction time values are significantly larger than the expected values. The expected values are what one would observe if there was no synergism between the molybdenum naphthenate and the diphenylamine, i.e. the additives act independently of each other. Expected values are calculated by adding the increase in induction time due to the individual additives. The much larger measured induction time values versus the expected values clearly show the molybdenum naphthenate/diphenylamine synergism. In the following Table II, the concentration of the molybdenum naphthenate is expressed in ppm of molybdenum whereas the concentration of the N-680 Amine is expressed in weight percent, i.e. 0.1 wt % is equal to 1,000 ppm. The oxidation induction time by PDSC in minutes is in the column headed as “Induction Time”. The OIT expected response in minutes is in the column under “Expected Time”; the viscosity increase from 72 hour HOOT (%) is an average of duplicate runs and is under the column headed “Viscosity Increase”.
TABLE II
Oxidative Stability of Motor Oil Blends*
by PDSC and the Hot Oil Oxidation Test
Concentration
of Additives
Process
Induc-
Oil
Mo Nap
N-680
Oil
tion
Expected
Viscosity
#
(As ppm Mo)
Wt %
Wt %
Time
Time
Increase
1
0
0.000
1.25
28.4
28.4
303.18
2
125
0.000
1.04
35.1
35.1
671.48
3
250
0.000
0.83
33.0
33.0
362.22
4
0
0.075
1.18
44.9
44.9
44.64
5
125
0.075
0.97
63.5
51.6
36.93
6
250
0.075
0.76
73.0
49.5
66.10
7
0
0.150
1.10
62.5
62.5
31.61
8
125
0.150
0.89
107.8
69.2
11.93
9
250
0.150
0.68
108.7
67.1
10.02
* A formulated crankcase oil containing 83.2 wt % base oil, 6.2 wt % polymeric viscosity index improver, 6.9 wt % ashless dispersant, 2.1 wt % calcium, sodium, and magnesium overbased and neutral detergents, and 1.2 wt % zinc dialkyldithiophosphate.
The following example shows that other classes of amines, e.g., certain substituted amines, disubstituted phenylene diamines, and alkyl amines, are not effective or minimally effective at controlling oxidation when used in combination with molybdenum carboxylates.
Molybdenum naphthenate and a variety of amines, were blended into an SAE Grade 5W-30 type motor oil (formulated crankcase oil as described in Example 2) as shown in Table III and as further described below. The only additional antioxidant in these blends was the zinc dialkyl dithiophosphate. The oxidation stability of these oils was measured by pressurized differential scanning calorimetry (PDSC) as described in Example 1. These oils were also subjected to the hot oil oxidation test described in Example 2.
Both the hot oil oxidation test results (small percentage changes in viscosity) and the PDSC test results (prolonged oxidation induction times) show that the combination of molybdenum naphthenate and alkylated diarylamines is more effective than the individual additives. Phenyl-naphthyl amines show some effectiveness when used in combination with molybdenum naphthenate. The substituted anilines, substituted phenylene diamines, and alkyl amines, were much less effective when used in combination with molybdenum naphthenate. In fact, the hot oil oxidation test results show that many of these other amines show a prodegradant effect (large percent changes in viscosity versus oil #0) when used in combination with molybdenum naphthenate.
The results of the tests of Example 3 are shown in Table III. In Table III, the first column is the test number involved. The column headed “A” shows the concentration of molybdenum naphthenate expressed in ppm of molybdenum. The remaining columns “B” through “J” show concentrations in weight percent wherein column “B” is that of dinonyl diphenylamine; column “C” is an alkylated diphenylamine trade named Naugalube 680, from Uniroyal Chemical Company; “D” is phenyl-alpha-naphthylamine; “E” is disecbutyl phenylenediamine; “F” is 4-tetradecylaniline; “G” is 2,5-di-t-butylaniline; “H” is 2,6-diisopropyl aniline; “I” is di-n-decylamine; and “J” is that of process oil. The results of these tests are shown in Table IIIA wherein for each of the numbered oil samples there is shown the results of the tests of Table III.
TABLE III
Oxidation of Motor Oils Containing Molybdenum Naphthenates and Amines
Concentration of additives in SAE Grade 5W-30 Type Motor Oil*
Oil
A
B
C
D
E
F
G
H
I
J
0
0
0.00
0.00
0.00
0.00
0.00
0.00
0.00
0.00
1.25
1
200
0.00
0.00
0.00
0.00
0.00
0.00
0.00
0.00
0.92
2
0
0.10
0.00
0.00
0.00
0.00
0.00
0.00
0.00
1.15
3
200
0.10
0.00
0.00
0.00
0.00
0.00
0.00
0.00
0.82
4
0
0.00
0.10
0.00
0.00
0.00
0.00
0.00
0.00
1.15
5
200
0.00
0.10
0.00
0.00
0.00
0.00
0.00
0.00
0.82
6
0
0.00
0.00
0.10
0.00
0.00
0.00
0.00
0.00
1.15
7
200
0.00
0.00
0.10
0.00
0.00
0.00
0.00
0.00
0.82
8
0
0.00
0.00
0.00
0.10
0.00
0.00
0.00
0.00
1.15
9
200
0.00
0.00
0.00
0.10
0.00
0.00
0.00
0.00
0.82
10
0
0.00
0.00
0.00
0.00
0.10
0.00
0.00
0.00
1.15
11
200
0.00
0.00
0.00
0.00
0.10
0.00
0.00
0.00
0.82
12
0
0.00
0.00
0.00
0.00
0.00
0.10
0.00
0.00
1.15
13
200
0.00
0.00
0.00
0.00
0.00
0.10
0.00
0.00
0.82
14
0
0.00
0.00
0.00
0.00
0.00
0.00
0.10
0.00
1.15
15
200
0.00
0.00
0.00
0.00
0.00
0.00
0.10
0.00
0.82
16
0
0.00
0.00
0.00
0.00
0.00
0.00
0.00
0.10
1.15
17
200
0.00
0.00
0.00
0.00
0.00
0.00
0.00
0.10
0.82
*A formulated crankcase oil containing 83.2 wt % base oil, 6.2 wt % polymeric viscosity index improver, 6.9 ashless dispersant, 2.1 wt % calcium, sodium and magnesium overbased & neutral detergents, and 1.2 wt % zinc dialkyldithiophosphate.
TABLE IIIA
Oxidation Induction Time
Viscosity Increase
By PDSC (min)
From 72 h HOOT (%)
Oil #
Avg From Duplicate Runs
Avg From Duplicate Runs
0
41.8
510.6
1
54.0
1650.2
2
72.9
89.3
3
111.2
59.5
4
81.8
68.9
5
102.8
48.8
6
66.8
129.1
7
74.3
102.2
8
61.3
150.6
9
62.6
417.3
10
40.8
728.1
11
41.8
1387.4
12
40.3
534.2
13
48.2
1058.8
14
34.2
463.2
15
46.2
561.7
16
39.9
305.0
17
39.7
905.8
Molybdenum octoate and alkylated diphenylamine, Naugalube 680, from Uniroyal Chemical Company, were blended into an SAE grade 5W-30 type motor oil as shown in Table IV. The only additional antioxidant in these blends was the zinc dialkyldithiophosphate. The frictional properties of these oils were measured using the High Frequency Reciprocating Rig. In this instrument 1-2 mls (milliliters) of a sample oil are placed in a temperature controlled steel pan. A steel ball attached to a moveable arm is lowered into the pan. A load of 400 g is applied to the steel ball/arm assembly. The steel/ball arm assembly is oscillated at 20 Hz over a 1 mm (millimeter) path length. As the arm is oscillated, a friction coefficient is determined every 5 seconds. The test lasts 3 minutes so approximately 30 data points are averaged m determine the friction coefficient of an oil in a given test. A reduction in the friction coefficient corresponds to improved fiction properties of the oil. Duplicate tests were performed on each oil at 70° C., 100° C., and 130° C. The average friction coefficient and standard deviation (SD) for each sample are shown in Table IV.
It can be seen from Table IV that an improvement in friction properties (lower coefficient of friction) results when the concentration of molybdenum octoate is increased in the oil. Reference oil 5 (R5) shows that a conventional antioxidant is not as effective as a friction modifier compared to molybdenum octanoate.
In Table IV: “Mo-Oct.” is molybdenum octoate; “N-680” is alkylated diphenylamine; “t-Bu” is t-butylphenols; and “PO” is process oil.
TABLE IV
Frictional Properties Of Motor Oil Blends using the High Frequency Reciprocating Rig Test
Concentration of additives in
SAE GRADE 5W-30 TYPE
MOTOR OIL
Mo-
A-
Oct
N-680
t-Bu
P.O.
FRICTION COEFFICIENT
Oil
ppm
wt %
wt %
wt %
70 C
SD
100 C
SD
130 C
SD
R1
0
0
0
0
0.117
0.001
0.116
0.001
0.116
0.001
2
204
0.125
0
0.375
0.117
0.001
0.113
0.002
0.113
0.001
3
319
0.125
0
0
0.110
0.001
0.104
0.004
0.106
0.004
4
432
0.125
0
0
0.105
0.001
0.095
0.001
0.091
0.001
R5
0
0.125
0.70
0.375
0.125
0.001
0.128
0.002
0.127
0.003
This example shows that the benefit of the molybdenum/diphenylamine combination requires using at least 100 ppm of the molybdenum. As shown in Example 6, this enhanced oxidation performance starts to break down at extremely high levels (greater than 400 ppm) of molybdenum.
Molybdenum 2-ethylhexanoate, containing 13.0 wt % molybdenum and alkylated diphenylamine. Naugalube 680, from Uniroyal Chemical Company, were blended into an SAE grade 5W-30 motor oil as shown in Table V below. The control 5W-30 motor oil contained the following additives:
Formulated Motor Oil Components
Weight %
ZDDP
1.1
Ashless dispersant
7.0
Viscosity Index Improver
7.0
Neutral & Overbased Detergents
1.4
Pour Point Depressant
0.5
Diluent Oil
83.0
The oxidative stability of these oils was measured by using the following Hot Oil Oxidation Test: Into 25 g of each motor oil was blended 0.8 g of catalyst mixture containing 5.55 wt % Iron (III) Naphthenate (6 wt % Fe content) and 94.45 wt % xylenes. Dry air was blown through the oil at a rate of 10 L/h (liters per hour) while maintaining the temperature at 160° C. for a period of 64 hours. The oil was cooled and the percent change in viscosity between the new oil and the oxidized oil was determined at 40° C. The lower percent change in viscosity for an oil is an indication of less oil degradation and thus better oxidation control by the additives. The abbreviations “% visc Incr” in Table V relates to percent viscosity increase. All oils were evaluated in duplicate and the results averaged. The results are found in Table V.
TABLE V
Oxidative Stability of Motor Oil Blends By the Hot Oil Oxidation Test
Molybdenum
Amine
2-ethyl-
% Viscosity Increase
Change
N-680
hexanoate
After 74 h
% Visc
Sample
wt %
ppm Mo
in the HOOT
Incr
0
0.15
0
70
0
1
0.15
52
69
−1
2
0.15
104
68
−2
3
0.15
156
49
−21
4
0.15
208
43
−27
5
0.15
260
46
−24
6
0.15
312
35
−35
7
0.15
364
32
−38
8
0.15
416
27
−43
9
0.15
468
23
−47
The viscosity results in the above table clearly show that at molybdenum level of 104 ppm, the molybdenum/diarylamine combination showed but a small improvement for the oxidative stability of the oil. However, at molybdenum levels greater than 104 such as 156 ppm, a significant improvement in oxidation control is seen. The largest improvement occurs between 104 ppm and 156 ppm molybdenum content.
A sample of molybdenum octoate was diluted with paraffin oil, blended at 50° C. for 1 hour and filtered using a pressure filtration apparatus. The molybdenum content of the filtered oil was determined to be 2.91 wt %
The diluted and filtered molybdenum octoate sample described above, and alkylated diphenylamine. Naugalube 680, from Uniroyal Chemical Company, were blended into an SAE grade 5W-30 type motor oil as shown in Table VI. The control 5W-30 motor oil contained the components specified in Example 5 above. The oxidative stability of these oils was measured using the Hot Oil Oxidation Test described in Example 5. All oils were evaluated in duplicate and the results averaged. The results are found in Table VI.
TABLE VI
Oxidative Stability of Motor Oil Blends By The Hot Oil Oxidation Test
Amine
% Viscosity
Change %
Sample
Wt %
PPM Mo
Increase
Viscosity
1
0.125
0
55
0
2
0.125
204
35
−20
3
0.125
318
27
−28
4
0.125
432
133
78
The viscosity results of the above Table VI clearly show that if a sufficient amount of amine is not present, a high molybdenum content becomes detrimental to the oxidative stability of the oil. In this example 0.125% amine with 318 ppm molybdenum provides good antioxidant protection. Increasing the molybdenum level to 432 ppm is not as effective as the lower concentrations to the oxidative stability of the oil (large increase in viscosity).
A series of lubrication formulations in accordance with this invention were tested in the Sequence IIIE engine test. The IIIE test uses a 231 CID (3.8 liter) Buick V-6 engine at high speed (3,000 rpm) and a very high oil temperature of 149° C. for 64 hours. This test is used to evaluate an engine oil's ability to minimize oxidation, thickening, sludge, varnish, deposits, and wear. The formulations contained 7.0 wt % viscosity index improver, 7.0 wt % ashless dispersant, 1.1 wt % ZDDP, 1.4 wt % detergents, 0.5 wt % supplemental additives, with the remainder being mineral oil. The addition of supplemental antioxidants are indicated in Table VII along with the engine test results. Hindered, mixed t-butylphenol antioxidant, referred to as “Phenolic” in Table VII below and a secondary alkylated diphenylamine, referred to as “Amine” in Table VII below disclosed for use in this invention are commercially available. Formulation A, also simply referred to in the table as “A” contained no molybdenum. The molybdenum source in formulation B, simply referred to as “B” in the table is molybdenum octoate available from Shepherd Chemical Company. The molybdenum source in formulation C, simply referred to as “C” in the table, is molybdenum 2-ethylhexanoate available from OM Group, TVTM indicates that the oils viscosity was too viscous to measure and represents a severe failing result in the IIIE engine. Some of the abbreviations used in the below Table VII are as follows: “% Vise, Inc.@ 64 h” means percent viscosity increase in 64 hours; “AE Sludge” is average engine sludge rating; “APS Varnish” is average piston skirt varnish; “ORL Deposit” is oil ring land deposit; “AC Wear” is average cam wear; MC Wear is maximum cam wear; and “L” is liters.
TABLE VII
Sequence IIIE Evaluation of
Molybdenum/Secondary Diphenylamine Antioxidants
Passing
Result
Limits
A
B
C
Phenolic Content (wt %)
0.7
0
0
Amine Content (wt %)
0.1
0.125
0.2
Molybdenum Content
0
458
115
(ppm Mo)
% Vis. Inc. @ 64 h
375 Max.
TVTM
152
300
AE Sludge
9.2 Min.
9
9.54
9.56
APS Varnish
8.9 Min.
7.96
9.1
9.38
ORL Deposit
3.5 Min.
2.53
4.38
4.8
Stuck Ring
2
2
1
AC Wear
30 Max.
7.2
7.8
6.5
MC Wear
64 Max.
15.0
12.00
11.00
Oil Consumption in Liters
5.1 Max.
4.35
3.32
3.35
The results of the above Table VII clearly show that the conventional phenolic antioxidant in Formulation A is ineffective in combination with the diphenylamine at controlling viscosity and passing the IIIE engine test. The molybdenum/diphenylamine combination in formulations B and C is very effective at both controlling viscosity and passing the engine test.
This example shows that the molybdenum carboxylate/diphenylamine combination is also effective in lubricants that do not contain additional additives. Alkylated diphenylamine, Naugalube 680, from Uniroyal Chemical Company, and molybdenum HEX-CEM, from OM Group, were blended into Petro Canada Paraflex HT100 (650N) base oil as described in Table VIII. These samples were subjected to the hot oil oxidation test described in Example 2 with the only change being that the heating period was reduced from 72 hours to 40 hours. The oils were cooled and the percent change in viscosity between the new oil and the oxidized oil was determined at 40° C. The results are shown in Table VIII below.
TABLE VIII
Hot Oil Oxidation of Unadditized Base Oil
In the Presence and Absence of Molybdenum.
Base Oil
N-680
Mo HEX-CEM
% Change Visc.
Oil #
(wt %)
(wt %)
(ppm Mo)
After 40 h
1
99.75
0.25
0
318
2
99.65
0.25
130
−2
3
99.55
0.25
260
1
It can be seen from the above Table VIII that significant improvement in oxidative stability of unadditized base oil occurs when a molybdenum carboxylate is combined with a secondary diarylamine.
The following example shows antioxidant synergism between molybdenum and a diarylamine wherein the molybdenum compound is not a carboxylate.
Molyvan 855, a sulfur and phosphorus free organic amide molybdenum complex supplied by R. T. Vanderbilt Company, Inc. (CAS Reg. No. 64742-52-5), alkylated diphenylamine Naugalube 680, from Uniroyal Chemical Company, and process oil were blended into an SAE Grade 5W-30 type motor oil as shown in Table IX below. The formulated oil used in this example was the same as that used in Example 1. The only additional antioxidant in these blends was the zinc dialkyldithiophosphate. The oxidation stability of these oils was measured by pressurized differential scanning calorimetry (PDSC) as described in Example 1. These oils were also subjected to the hot oil oxidation test described in Example 2 with the only change being that the heating period was reduced from 72 hours to 64 hours. All oils were evaluated in duplicate or triplicate and the results averaged. The results are found in Table IX below. Both the PDSC results and the hot oil oxidation test results show that the combination of the organic amide molybdenum complex and the alkylated diphenylamine provides superior oxidation control versus use of these additives separately. Note that for samples containing a combination of Molyvan 855 and alkylated diphenylamine the measured values are significantly larger than the expected values. The expected values are what one would observe if there were no synergism between the Molyvan 855 and the alkylated diphenylamine, i.e. the additives act independently of each other. The much larger measured OIT values versus the expected values clearly show the organic amide molybdenum complex/diphenylamine synergism.
TABLE IX
Molyvan 855
Process
Added
N-680
Oil
Induction
Expected
Viscosity
Wt. %
Added
Added
Time
OIT
Increase
Oil
(ppm Mo)
Wt %
Wt %
(min)
(min)
(%)
A
0
0
1.25
26.6
201
B
0
0.1
1.15
59.4
42
C
0.272 (200)
0
0.98
50.8
548
D
0.272 (200)
0.1
0.88
106.2
83.6
25
Gatto, Vincent James, Devlin, Mark Thomas
Patent | Priority | Assignee | Title |
10174272, | Jul 14 2016 | AFTON CHEMICAL CORPORATION | Dispersant viscosity index improver-containing lubricant compositions and methods of use thereof |
10179886, | May 17 2016 | AFTON CHEMICAL CORPORATION | Synergistic dispersants |
10214703, | Jul 16 2015 | AFTON CHEMICAL CORPORATION | Lubricants with zinc dialkyl dithiophosphate and their use in boosted internal combustion engines |
10280383, | Jul 16 2015 | AFTON CHEMICAL CORPORATION | Lubricants with molybdenum and their use for improving low speed pre-ignition |
10323205, | May 05 2016 | AFTON CHEMICAL CORPORATION | Lubricant compositions for reducing timing chain stretch |
10336959, | Jul 16 2015 | AFTON CHEMICAL CORPORATION | Lubricants with calcium-containing detergent and their use for improving low speed pre-ignition |
10370615, | Jan 18 2017 | AFTON CHEMICAL CORPORATION | Lubricants with calcium-containing detergents and their use for improving low-speed pre-ignition |
10377963, | Feb 25 2016 | AFTON CHEMICAL CORPORATION | Lubricants for use in boosted engines |
10421922, | Jul 16 2015 | AFTON CHEMICAL CORPORATION | Lubricants with magnesium and their use for improving low speed pre-ignition |
10443011, | Jan 18 2017 | AFTON CHEMICAL CORPORATION | Lubricants with overbased calcium and overbased magnesium detergents and method for improving low-speed pre-ignition |
10443558, | Jan 18 2017 | AFTON CHEMICAL CORPORATION | Lubricants with calcium and magnesium-containing detergents and their use for improving low-speed pre-ignition and for corrosion resistance |
10494583, | May 17 2016 | AFTON CHEMICAL CORPORATION | Synergistic dispersants |
10513668, | Oct 25 2017 | AFTON CHEMICAL CORPORATION | Dispersant viscosity index improvers to enhance wear protection in engine oils |
10550349, | Jul 16 2015 | AFTON CHEMICAL CORPORATION | Lubricants with titanium and/or tungsten and their use for improving low speed pre-ignition |
10584297, | Dec 13 2016 | AFTON CHEMICAL CORPORATION | Polyolefin-derived dispersants |
10836976, | Jul 18 2018 | AFTON CHEMICAL CORPORATION; AFTON CHEMICAL COMPANY | Polymeric viscosity modifiers for use in lubricants |
11098262, | Apr 25 2018 | AFTON CHEMICAL CORPORATION | Multifunctional branched polymers with improved low-temperature performance |
11155764, | May 05 2016 | AFTON CHEMICAL CORPORATION | Lubricants for use in boosted engines |
11214753, | Jan 03 2020 | AFTON CHEMICAL CORPORATION | Silicone functionalized viscosity index improver |
11479736, | Jun 04 2021 | AFTON CHEMICAL CORPORATION | Lubricant composition for reduced engine sludge |
11572523, | Jan 26 2022 | AFTON CHEMICAL CORPORATION | Sulfurized additives with low levels of alkyl phenols |
11608477, | Jul 31 2021 | AFTON CHEMICAL CORPORATION | Engine oil formulations for low timing chain stretch |
11753599, | Jun 04 2021 | AFTON CHEMICAL CORPORATION | Lubricating compositions for a hybrid engine |
11760953, | Apr 25 2018 | AFTON CHEMICAL CORPORATION | Multifunctional branched polymers with improved low-temperature performance |
11773343, | Nov 17 2021 | AFTON CHEMICAL CORPORATION | Engine oil formulation with improved Sequence VIII performance |
11788027, | Feb 18 2022 | AFTON CHEMICAL CORPORATION | Engine oil formulation with improved sequence VIII performance |
11851628, | Dec 21 2021 | AFTON CHEMICAL CORPORATION | Lubricating oil composition having resistance to engine deposits |
11898119, | Jan 25 2022 | AFTON CHEMICAL CORPORATION | Lubricating oil compositions with resistance to engine deposit and varnish formation |
7858565, | May 05 2006 | VANDERBILT MINERALS, LLC; VANDERBILT CHEMICALS, LLC | Antioxidant additive for lubricant compositions, comprising organotungstate |
7875579, | Mar 06 2007 | VANDERBILT MINERALS, LLC; VANDERBILT CHEMICALS, LLC | Lubricant antioxidant compositions containing a metal compound and a hindered amine |
7879777, | May 05 2006 | VANDERBILT MINERALS, LLC; VANDERBILT CHEMICALS, LLC | Antioxidant additive for lubricant compositions, comprising organotungstate, diarylamine and organomolybdenum compounds |
7935663, | Mar 06 2007 | VANDERBILT MINERALS, LLC; VANDERBILT CHEMICALS, LLC | Molybdenum compounds |
8093190, | Mar 06 2007 | VANDERBILT MINERALS, LLC; VANDERBILT CHEMICALS, LLC | Lubricant antioxidant compositions containing a metal compound and a hindered amine |
9657252, | Apr 17 2014 | AFTON CHEMICAL CORPORATION | Lubricant additives and lubricant compositions having improved frictional characteristics |
9677026, | Apr 08 2016 | AFTON CHEMICAL CORPORATION | Lubricant additives and lubricant compositions having improved frictional characteristics |
9701921, | Apr 08 2016 | AFTON CHEMICAL CORPORATION | Lubricant additives and lubricant compositions having improved frictional characteristics |
RE40595, | Nov 20 1995 | Afton Chemical Intangibles LLC | Lubricant containing molybdenum compound and secondary diarylamine |
Patent | Priority | Assignee | Title |
3285942, | |||
3578690, | |||
4095963, | Feb 17 1977 | DESMET HOLDING COMPANY | Stabilization of deodorized edible oils |
4175043, | Sep 21 1978 | Mobil Oil Corporation | Metal salts of sulfurized olefin adducts of phosphorodithioic acids and organic compositions containing same |
4330420, | May 13 1980 | Texaco Inc. | Low ash, low phosphorus motor oil formulations |
4370246, | Apr 27 1981 | Chevron Research Company | Antioxidant combinations of molybdenum complexes and aromatic amine compounds |
4394279, | Aug 07 1981 | Chevron Research Company | Antioxidant combinations of sulfur containing molybdenum complexes and aromatic amine compounds for lubricating oils |
4428848, | Nov 09 1981 | Texaco Inc. | Molybdenum derivatives and lubricants containing same |
4479883, | Jan 06 1982 | EXXON RESEARCH AND ENGINEERINC COMPANY A DE CORP | Lubricant composition with improved friction reducing properties containing a mixture of dithiocarbamates |
4593012, | Mar 09 1984 | ARCO CHEMICAL TECHNOLOGY, L P A PARTNERSHIP OF DE | Production of hydrocarbon-soluble salts of molybdenum for epoxidation of olefins |
4648985, | Nov 15 1984 | The Whitmore Manufacturing Company | Extreme pressure additives for lubricants |
4812246, | Mar 12 1987 | Idemitsu Kosan Co., Ltd. | Base oil for lubricating oil and lubricating oil composition containing said base oil |
4824611, | Dec 18 1984 | OMG AMERICAS, INC | Preparation of hydrocarbon-soluble transition metal salts of organic carboxylic acids |
4832857, | Aug 18 1988 | Ethyl Corporation | Process for the preparation of overbased molybdenum alkaline earth metal and alkali metal dispersions |
4846983, | Feb 21 1986 | The Lubrizol Corp. | Novel carbamate additives for functional fluids |
4889647, | Nov 14 1985 | R T VANDERBILT COMPANY, INC , 30 WINFIELD STREET, NORWALK, CNNECTICUT, A CORP OF NEW YORK | Organic molybdenum complexes |
5137647, | Dec 09 1991 | R T VANDERBILT COMPANY, INC A CORPORATION OF NEW YORK | Organic molybdenum complexes |
5143633, | Jun 19 1989 | Societe Nationale Elf Aquitaine | Overbased additives for lubricant oils containing a molybdenum complex, process for preparing them and compositions containing the said additives |
5232614, | Feb 23 1989 | Exxon Chemical Patents Inc. | Lubricating oil compositions and additives for use therein |
5364545, | Jul 09 1993 | EXXON RESEARCH & ENGINEERING CO | Lubricating oil composition containing friction modifier and corrosion inhibitor |
5412130, | Jun 08 1994 | VANDERBILT MINERALS, LLC; VANDERBILT CHEMICALS, LLC | Method for preparation of organic molybdenum compounds |
5605880, | Apr 30 1993 | Exxon Chemical Patents INC; Tonen Corporation | Lubricating oil composition |
5650381, | Nov 20 1995 | Afton Chemical Intangibles LLC | Lubricant containing molybdenum compound and secondary diarylamine |
5994277, | Sep 13 1993 | Exxon Chemical Patents, Inc. | Lubricating compositions with improved antioxidancy comprising added copper, a molybdenum containing compound, aromatic amine and ZDDP |
6150309, | Aug 04 1998 | Exxon Research and Engineering Co. | Lubricant formulations with dispersancy retention capability (law684) |
6174842, | Mar 30 1999 | Afton Chemical Intangibles LLC | Lubricants containing molybdenum compounds, phenates and diarylamines |
EP696636, | |||
GB2097422, | |||
JP6100880, | |||
JP7286190, | |||
RE37363, | Jul 22 1999 | Afton Chemical Intangibles LLC | Lubricant containing molybdenum compound and secondary diarylamine |
WO9507962, | |||
WO9507963, | |||
WO9507966, | |||
WO9502027, | |||
WO9507962, | |||
WO9507963, | |||
WO9507966, | |||
WO9527022, |
Executed on | Assignor | Assignee | Conveyance | Frame | Reel | Doc |
Nov 10 1995 | GATTO, VICENT J | Ethyl Corporation | ASSIGNMENT OF ASSIGNORS INTEREST SEE DOCUMENT FOR DETAILS | 011105 | /0757 | |
Nov 10 1995 | DEVLIN, MARK T | Ethyl Corporation | ASSIGNMENT OF ASSIGNORS INTEREST SEE DOCUMENT FOR DETAILS | 011105 | /0757 | |
Jun 26 2000 | Afton Chemical Intangibles LLC | (assignment on the face of the patent) | / | |||
Apr 10 2001 | Ethyl Corporation | BANK OF AMERICA, N A , AS COLLATERAL AGENT | NOTICE OF GRANT SECURITY INTEREST | 011712 | /0298 | |
Apr 30 2003 | Ethyl Corporation | CREDIT SUISSE FIRST BOSTON, CAYMAN ISLANDS BRANCH | GRANT OF PATENT SECURITY INTEREST | 014146 | /0832 | |
Apr 30 2003 | BANK OF AMERICA, N A | ETHLYL CORPORATION | RELEASE OF SECURITY INTEREST | 014146 | /0783 | |
Jun 18 2004 | Ethyl Corporation | SUNTRUST BANK, AS ADMINISTRATIVE AGENT | SECURITY INTEREST SEE DOCUMENT FOR DETAILS | 014782 | /0348 | |
Jun 30 2004 | Ethyl Corporation | Afton Chemical Intangibles LLC | ASSIGNMENT OF ASSIGNORS INTEREST SEE DOCUMENT FOR DETAILS | 016301 | /0175 | |
Dec 21 2006 | Afton Chemical Intangibles LLC | SUNTRUST BANK | SECURITY AGREEMENT | 018883 | /0902 | |
May 13 2011 | SUNTRUST BANK | Afton Chemical Intangibles LLC | RELEASE BY SECURED PARTY SEE DOCUMENT FOR DETAILS | 026761 | /0050 |
Date | Maintenance Fee Events |
Date | Maintenance Schedule |
Jan 03 2009 | 4 years fee payment window open |
Jul 03 2009 | 6 months grace period start (w surcharge) |
Jan 03 2010 | patent expiry (for year 4) |
Jan 03 2012 | 2 years to revive unintentionally abandoned end. (for year 4) |
Jan 03 2013 | 8 years fee payment window open |
Jul 03 2013 | 6 months grace period start (w surcharge) |
Jan 03 2014 | patent expiry (for year 8) |
Jan 03 2016 | 2 years to revive unintentionally abandoned end. (for year 8) |
Jan 03 2017 | 12 years fee payment window open |
Jul 03 2017 | 6 months grace period start (w surcharge) |
Jan 03 2018 | patent expiry (for year 12) |
Jan 03 2020 | 2 years to revive unintentionally abandoned end. (for year 12) |