A coated turning insert particularly useful for turning in stainless steel is disclosed. The insert is characterized by a WC—Co-based cemented carbide substrate having a highly w-alloyed Co-binder phase and a coating including an inner layer of ticxNyOz with columnar grains followed by a layer of fine-grained, κ-Al2O3 and a top layer of TiN. The layers are deposited by using CVD methods.
|
1. A cutting tool insert particularly for turning of steel comprising a cemented carbide body and a coating wherein said cemented carbide body contains WC, 6-15 wt-% Co and 0.2-1.8 wt % cubic carbides of Ti, Ta and/or Nb and a highly w-alloyed binder phase with a CW-ratio of 0.78-0.93 and said coating comprises
a first (innermost) layer of ticxNyOz with a thickness of <1.5 μm, and with equiaxed grains with size <0.5 μm
a second layer of ticxNyOz with a thickness of 2-5 μm with columnar grains with an average diameter of <5 μm and
an outer layer of a smooth, fine-grained (0.5-2 μm) κ-Al2O3 with a thickness of 0.5-6 μm.
4. A method of making an insert for turning comprising a cemented carbide body and a coating wherein a WC—Co-based cemented carbide body with a highly w-alloyed binder phase with a CW-ratio of 0.78-0.93 is coated with
a first (innermost) layer of ticxNyOz with x+y+z=1, with a thickness of 0.1-1.5 μm, with equiaxed grains with size <0.5 μm using known CVD-methods
a second layer of ticxNyOz with x+y+z=1, with a thickness of 2-8 μm with columnar grains with a diameter of about <5 μm deposited by MTCVD-technique, using acetonitrile as the carbon and nitrogen source for forming the layer in a preferred temperature range of 850-900° C. and
a layer of a smooth κ-Al2O3 with a thickness of 0.5-6 μm.
2. The cutting tool inset of
3. The cutting tool insert of
5. The method of
7. The method of
8. The method of
9. The cutting tool insert of
10. The cutting tool insert of
11. The method of
12. The method of
0. 15. The cutting tool of
0. 16. The cutting tool of
0. 17. The cutting tool of
0. 18. The cutting tool of
0. 19. The method of
|
The present application is a reissue of U.S. Pat. No. 6,200,671 B1, which is a national stage application of PCT/SE96/01578 filed on Nov. 29, 1996, and which claims the benefit of priority to Swedish Application No. 9504304-8 filed Nov. 30, 1995 and to Swedish Application No. 9602413-8 filed Jun. 17, 1996.
The present invention relates to a coated cutting tool (cemented carbide insert) particularly useful for wet turning of toughness-demanding stainless steel components like square bars, flanges and tubes, with raw surfaces such as cast skin, forged skin, hot or cold rolled skin or pre-machined surfaces.
When turning stainless steels with cemented carbide tools, the cutting edge is worn according to different wear mechanisms, such as adhesive wear, chemical wear, abrasive wear and by edge chipping caused by cracks formed along the cutting edge, the so-called comb cracks.
Different cutting conditions require different properties of the cutting insert. For example, when cutting in steels with raw surface zones, a coated cemented carbide insert must consist of a tough carbide and have very good coating adhesion. When turning in stainless steels, the adhesive wear is generally the dominating wear type.
Measures can be taken to improve the cutting performance with respect to a specific wear type. However, very often such action will have a negative effect on other wear properties.
So far it has been very difficult to improve all tool properties simultaneously. Commercial cemented carbide grades have therefore been optimised with respect to one or few of the wear types and hence to specific application areas.
Swedish patent application 9503056-5 which corresponds to U.S. Ser. No. 08/703,965, herein incorporated by reference, discloses a coated cutting insert particularly useful for turning in hot and cold forged low alloyed steel components. The inserts is characterised by a cemented carbide substrate consisting of Co—WC and cubic carbides having a 15-35 μm thick surface zone depleted from cubic carbides, a coating including a layer of TiCxNyOz with columnar grains, a layer of smooth, fine grained κ-Al2O3, and preferably an outer layer of TiN.
Swedish patent application 09/077,360 9504304-8 which corresponds to U.S. Ser. No. 09/077,360 filed concurrently herewith discloses a coated cutting insert particularly useful for wet and dry milling of low and medium alloyed steels. The insert is characterised by a cemented carbide substrate consisting of Co—WC and cubic carbides, a coating including a layer of TiCxNyOz with columnar grains, a layer of smooth, fine grained κ-Al2O3 and preferably an outer layer of TiN.
It has now been found that combinations of the substrates and coatings described in the above patent applications give rise to excellent cutting performance in stainless steels turning. A cemented carbide substrate with a cubic carbide depleted surface zone combined with a coating in accordance with patent application, 9503056-5, which corresponds to U.S. Ser. No. 08/703,965, has been found to be especially suitable for high speed turning in easy stainless steel, such as turning of machineability improved 304L. In more difficult work piece materials such as 316-Ti, and in operations with a high degree of thermal cycling such as turning of square bars a straight WC—Co substrate of the type described in patent application 09,077,360 950304-8 which corresponds to U.S. Ser. No. 09/077,360 filed concurrently herewith, has been found the most suitable.
It is an object of this invention to avoid or alleviate the problems of the prior art.
It is further an object of this invention to provide a coated cutting tool particularly useful for wet turning of toughness-demanding stainless steel components.
In one aspect of the invention there is provided a cutting tool insert particularly for turning of steel comprising a cemented carbide body and a coating wherein said cemented carbide body contains WC, 6-15 wt-% Co and 0.2-1.8 wt.-% cubic carbides of Ti, Ta and/or Nb and a highly W-alloyed binder phase with a CW-ratio of 0.78-0.93 and said coating comprises
In another aspect of the invention there is provided a method of making an insert for turning comprising a cemented carbide body and a coating wherein a WC—Co-based cemented carbide body with a highly W-alloyed binder phase with a CW-ratio of 0.78-0.93 is coated with
A turning tool insert according to the invention useful for turning of steel consists of a cemented carbide substrate with a highly W-alloyed binder phase and with a well-balanced chemical composition and grain size of the WC, a columnar TiCxNyOz-layer, a κ-Al2O3-layer, a TiN-layer and optionally followed by smoothening the cutting edges by brushing the edges with, e.g., a SiC-based brush.
The cobalt binder phase is highly alloyed with W. The content of W in the binder phase can be expressed as the CW-ratio=Ms/(wt % Co 0.0161) CW-ratio=Ms/(wt % Co 0.0161), where Ms is the measured saturation magnetization of the cemented carbide substrate in kA/m hAm2/kg and wt % Co is the weight percentage of Co in the cemented carbide. The CW-value is a function of the W content in the Co binder phase. A low CW-value corresponds to a high W-content in the binder phase. According to the present invention, improved cutting performance is achieved if the cemented carbide substrate has a CW-ratio of 0.78-0.93.
According to the present invention, a turning tool insert particularly useful for difficult stainless steel turning is provided with a cemented carbide substrate with a composition of 6-15 wt % Co, preferably 9-12 wt % Co, most preferably 10-11 wt % Co, 0.2-1.8 wt % cubic carbides, preferably 0.4-1.8 wt % cubic carbides, most preferably 0.5-1.7 wt % cubic carbides of the metals Ta, Nb and Ti and balance WC. The cemented carbide may also contain other carbides from elements from group IVb, Vb or VIb of the periodic table. The content of Ti is preferably on a level corresponding to a technical impurity. The preferred average grains size of the WC depend on the binder phase content. At the preferred composition of 10-11 wt-% Co, the preferred grain size is 1.5-2 μm, most preferably about 1.7 μm. The CW-ratio shall be 0.78-0.93, preferably 0.80-0.91, and most preferably 0.82-0.90. The cemented carbide may contain small amounts, <1 volume %, of η-phase (M6C), without any detrimental effect. From the CW-value it follows that no free graphite is allowed in the cemented carbide substrate according to the present embodiment.
The coating comprises
According to the method of the invention, a WC-Co-based, cemented carbide substrate is made with a highly W-alloyed binder phase with a CW-ratio of 0.78-0.93, preferably 0.80-0.91, and most preferably 0.82-0.90, a content of cubic carbides of 0.2-1.8 wt %, preferably 0.4-1.8 wt %, most preferably 0.5-1.7 wt % of the metals Ta, Nb and Ti, with 6-15 wt % Co, preferably 9-12 wt % Co, most preferably 10-11 wt % Co, at which Co-content, the WC grain size 1.5-2 μm, most preferably about 1.7 μm. The body is coated with:
The invention is additionally illustrated in connection with the following Examples which are to be considered as illustrative of the present invention. It should be understood, however, that the invention is not limited to the specific details of the Examples.
A. A cemented carbide turning tool insert in style CNMG120408-MM with the composition 10.5 wt-% Co 1.16 wt-% Ta, 0.28 wt-% Nb and balance WC, with a binder phase highly alloyed with W corresponding to a CW-ratio of 0.87, was coated with an innermost 0.5 μm equiaxed TiCN-layer with a high nitrogen content, corresponding to an estimated C/N ratio of 0.05, followed by a 4.3 μm thick layer of columnar TICN deposited using MT-CVD technique. In subsequent steps during the same coating process, a 1.1 μm layer of Al2O3 consisting of pure κ-phase according to procedure disclosed in EP-A-523 021 which corresponds to U.S. Pat. No. 5,674,564, was used. A thin, 0.5 μm, TiN layer was deposited, during the same cycle, on top of the Al2O3-layer. The coated insert was brushed by a SiC-containing nylon straw brush after coating, removing the outer TiN layer on the edge.
B. A cemented carbide turning tool insert in style CNMG120408-MM with the composition of 7.5 wt-% Co, 1.8 wt-% TiC, 3.0 wt-% TaC, 0.4 wt-% NbC, balance WC and a CW-ratio of 0.88. The cemented carbide had a surface zone, about 25 μm thick, depleted from cubic carbides. The insert was coated with an innermost 0.5 μm equiaxed TiCN-layer with a high nitrogen content, corresponding to an estimated C/N ratio of 0.05, followed by a 7.2 μm thick layer of columnar TICN deposited using MT-CVD technique. In subsequent steps during the same coating process, a 1.2 μm layer of Al2O3 consisting of pure κ-phase according to procedure disclosed in EP-A-523 021 which corresponds to U.S. Pat. No. 5,674,564, was used. A thin, 0.5 μm, TiN layer was deposited, during the same cycle, on top of the Al2O3-layer. The coated insert was brushed by a SiC-containing nylon straw brush after coating, removing the outer TiN layer on the edge.
C. A competitive cemented carbide turning tool insert in style CNMG120408 from an external leading cemented carbide producer was selected for comparison in a turning test. The carbide had a composition of 9.0 wt-% Co, 0.2 wt-% TiC, 1.7 wt-% TaC, 0.2 wt-% NbC, balance WC and a CW-ratio of 0.90. The insert had a coating consisting of 1.0 μm TiC, 0.8 μm TiN, 1.0 μm TiC and, outermost, 0.8 μm TiN. Examination in light optical microscope revealed no edge treatment subsequent to coating.
D. A competitive cemented carbide turning tool insert in style CNMG120408 from an external leading cemented carbide producer was selected for comparison in a turning test. The cemented carbide had a composition of 5.9 wt-% Co, 3.1 wt-% TiC, 5.6 wt-% TaC, 0.1 wt-% NbC, balance WC and a CW-ratio of 0.95. The cemented carbide had a surface zone, about 30 μm thick, which was enriched in Co content. The insert had a coating consisting of 5.3 μm TiC, 3.6 μm TiCN, outermost, 2.0 μm TiN. Examination in light optical microscope revealed no edge treatment subsequent to coating.
E. A competitive cemented carbide turning tool insert in style CNMG120408 from an external leading cemented carbide producer was selected for comparison in a turning test. The carbide had a composition of 8.9 wt-% Co, balance WC and a CW-ratio of 0.84. The insert had a coating consisting with 1.9 μm TiC, 1.2 μTiN, 1.5 μm Al2O3 laminated with 3 0.1 μm tick layers of TiN, and, outermost, 0.8 μn TiN. Examination in light optical microscope revealed no edge treatment subsequent to coating.
F. A competitive cemented carbide turning tool insert in style CNMG120408 from an external leading cemented carbide producer was selected for comparison in a turning test. The carbide had a composition of 5.4 wt-% Co, 2.7 wt-% TiC, 3.5 wt-% TaC, 2.3 wt-% NbC, balance WC and a CW-ratio of 0.94. The cemented carbide had a surface zone, about 40 μm thick, which was enriched in Co content. The insert had a coating consisting of 5.3 μm TiC, 3.6 μm TiCN, outermost, 2.0 μm TiN. Examination in light optical microscope revealed no edge treatment subsequent to coating.
Inserts from A, B, C, D, E and F were compared in facing of a bar, diameter 180, with two, opposite, flat sides (thickness 120 mm) in 4LR60 material. Feed 0.25 mm/rev, speed 180 m/min and depth of cut 2.0 mm.
The wear mechanism in this test is chipping of the edge. The inserts with gradient substrate (B, E and F) looked good after three cuts but broke suddenly after about four.
Insert
Number of cuts
A (acc. to invent.)
15
B (outside invention)
5
C (external grade)
9
D (external grade)
9
E (external grade)
4
F (external grade)
4
Inserts A, and B from above were selected for a turning test, longitudinal and facing in machineability improved AISI304L stainless steel.
Cutting speed was 250 m/min, feed 0.3 mm/rev and depth of cut 2 mm. Cutting time 1 minute/cycle.
The wear mechanism was plastic deformation.
Insert
Number of cycles
B (outside invention)
7
A (acc. to invent.)
4
G. Inserts in geometry TNMG160408-MM with composition and coating according to A above.
H. Inserts in geometry TNMG160408-MM with composition and coating according to B above.
I. Inserts in geometry TNMG160408 with composition and coating according to C above.
The inserts G, H and I were tested in longitudinal, dry, turning of a shaft in duplex stainless steel.
Feed 0.3 mm/rev, speed 140 m/min and depth of cut 2 mm. Total cutting time per component was 12 minutes.
Insert G and I got plastic deformation whereas insert H got some notch wear.
Two edges of insert G were worn out to produce one component whereas one edge of insert H completed one component and four edges were required to finalise one component using insert I.
Insert
Number of edges/component
H (outside invention)
1
G (acc. to invent.)
2
I (external grade)
4
Inserts A and E from above were selected for a turning test, mainly facing, in a cover rotorcase made in cast AISI316 stainless steel. The cutting was interrupted due to component design.
Cutting speed was 180 m/min, feed 0.2 mm/rev and depth of cut 0-2 mm (irregular shape of casting). Cutting time 10.5 minutes/component.
The wear mechanism was a combination of edge chiping and plastic deformation.
Insert
Number of components
A (acc. to invent.)
2
E (external grade)
1
Inserts according to A, B, C and D were selected for a turning test. Internal turning of AISI304 stainless steel valve substrate. Cutting speed was 130 m/min and feed 0.4 mm/rev. The stability was poor due to the boring bar.
The wear was chipping of the edge for inserts D and B whereas inserts A and C got plastic deformation.
Insert
Number of components
A (acc. to invent.)
9
D (external grade)
7
C (external grade)
5
B (outside invention)
2
Inserts A and C from above were selected for a turning test, roughing of a square bar in AISI316Ti stainless steel. The cutting was interrupted due to component design.
Cutting speed was 142 m/min, feed 0.2 mm/rev, depth of cut 4 mm. and cutting time 0.13 minutes/component.
The wear was chipping of the edge.
Insert
Number of components
A (acc. to invent.)
25
C (external grade)
15
The principles, preferred embodiments and modes of operation of the present invention have been described in the foregoing specification. The invention which is intended to be protected herein, however, is not to be construed as limited to the particular forms disclosed, since these are to be regarded as illustrative rather than restrictive. Variations and changes may be made by those skilled in the art without departing from the spirit of the invention.
Ljungberg, Björn, Östlund, Åke, Gustafson, Per, Lindskog, Per
Patent | Priority | Assignee | Title |
10837104, | Aug 29 2015 | Kyocera Corporation | Coated tool |
Patent | Priority | Assignee | Title |
4610931, | Mar 27 1981 | Kennametal Inc. | Preferentially binder enriched cemented carbide bodies and method of manufacture |
4643620, | May 27 1983 | Sumitomo Electric Industries, Ltd. | Coated hard metal tool |
5137774, | Jul 13 1989 | SECO TOOLS AB | Multi-oxide coated carbide body and method of producing the same |
5162147, | Jul 13 1989 | SECO TOOLS AB, A CORP OF SWEDEN | Kappa-alumina oxide coated carbide body and method of producing the same |
5372873, | Oct 22 1992 | Mitsubishi Materials Corporation | Multilayer coated hard alloy cutting tool |
5451469, | Dec 18 1992 | Sandvik Intellectual Property Aktiebolag | Cemented carbide with binder phase enriched surface zone |
5545490, | Jun 21 1994 | Mitsubishi Materials Corporation | Surface coated cutting tool |
5549980, | Feb 21 1992 | Sandvik Intellectual Property Aktiebolag | Cemented carbide with binder phase enriched surface zone |
5576093, | Oct 22 1992 | Mitsubishi Materials Corporation | Multilayer coated hard alloy cutting tool |
5652045, | Oct 20 1994 | Mitsubishi Materials Corporation | Coated tungsten carbide-based cemented carbide blade member |
5674464, | Jul 13 1992 | European Economic Community | Desulphurization of waste gases |
5786069, | Aug 28 1996 | Sandvik Intellectual Property Aktiebolag | Coated turning insert |
5915162, | May 31 1993 | Sumitomo Electric Industries, Ltd. | Coated cutting tool and a process for the production of the same |
5920760, | May 31 1994 | Mitsubishi Materials Corporation | Coated hard alloy blade member |
EP653499, | |||
EP685572, | |||
EP686707, | |||
EP693574, | |||
EP709484, |
Executed on | Assignor | Assignee | Conveyance | Frame | Reel | Doc |
Nov 29 1996 | Sandvik Intellectual Property AB | (assignment on the face of the patent) | / |
Date | Maintenance Fee Events |
Sep 03 2008 | M1552: Payment of Maintenance Fee, 8th Year, Large Entity. |
Aug 15 2012 | M1553: Payment of Maintenance Fee, 12th Year, Large Entity. |
Date | Maintenance Schedule |
Jan 08 2011 | 4 years fee payment window open |
Jul 08 2011 | 6 months grace period start (w surcharge) |
Jan 08 2012 | patent expiry (for year 4) |
Jan 08 2014 | 2 years to revive unintentionally abandoned end. (for year 4) |
Jan 08 2015 | 8 years fee payment window open |
Jul 08 2015 | 6 months grace period start (w surcharge) |
Jan 08 2016 | patent expiry (for year 8) |
Jan 08 2018 | 2 years to revive unintentionally abandoned end. (for year 8) |
Jan 08 2019 | 12 years fee payment window open |
Jul 08 2019 | 6 months grace period start (w surcharge) |
Jan 08 2020 | patent expiry (for year 12) |
Jan 08 2022 | 2 years to revive unintentionally abandoned end. (for year 12) |