A dry etching method in which a plasma of an etching gas is generated and a magnetic material is dry-etched using a mask material made of a non-organic material, wherein an alcohol having at least one hydroxyl group is used as the etching gas. The alcohol used as the etching gas has one hydroxyl group such as an alcohol selected from the group including methanol (CH3OH), ethanol (C2H5OH) and propanol (C3H7OH).
|
1. A dry etching method comprising generating a plasma of an etching gas and dry-etching a magnetic material using a mask material made of comprising a non-organic material, wherein the etching gas is selected from the group consisting of: an alcohol having at least one hydroxyl group is used as the etching gas ; a ketone of formula RCOR′, wherein R or R′ is an alkyl group; and an alkane.
2. The dry etching method according to
3. The dry etching method according to
4. The dry etching method according to
5. The dry etching method according to
6. The dry etching method according to
0. 7. The dry etching method according to
8. The dry etching method according to
9. The dry etching method according to
10. The dry etching method according to
11. The dry etching method according to
12. The dry etching method according to
13. The dry etching method according to
14. The dry etching method according to
15. The dry etching method according to
16. The dry etching method according to
0. 17. The dry etching method according to
0. 18. The dry etching method according to
0. 19. The dry etching method according to
0. 20. A tunneling magnetoresistance device (TMR) manufacturing method comprising:
forming a TMR comprising a pair of ferromagnetic layers comprising a free layer and a pinned layer sandwiching an insulating layer and an antiferromagnetic layer on the pinned layer on a surface thereof opposite to the insulating layer employing the dry etching process of
0. 21. A magnetic random access memory (MRAM) device manufacturing method comprising the dry etching method as defined in
0. 22. A magnetic random access memory (MRAM) device manufacturing method comprising forming a magnetic random access memory comprising a pinned layer, a free layer and an insulating layer therebetween, wherein the free layer is provided by the dry etching method of
0. 23. The dry etching method according to
0. 24. The dry etching method according to
0. 25. The dry etching method according to
|
The present application claims priority of JP 2003-201254, filed in Japan on Jul. 24, 2003, the entire contents of which is incorporated hereby reference. This application is a reissue of U.S. Pat. No. 7,060,194 B2, which issued from application Ser. No. 10/897,127 filed Jul. 23, 2004.
1. Field of the Invention
The present invention relates to a embodiments. More particularly, the present invention relates to a embodiments useful for micro fabricating of a thin magnetic film such as the thin film of FeNi, CoFe, FeMn, CoPt or the like.
2. Description of the Background Art
MRAM (Magnetic Random Access Memory) is an integrated magnetic memory, and in these days, MRAM has attracted attention as a memory, which is rewritable without limit, and having a packing density of components as high as DRAM and a speed performance as high as SRAM. On the other hand, a thin film magnetic head, a magnetic sensor and the like constituting a magnetoresistive device such as GMR (giant magnetoresistance) and TMR (tunneling magnetoresistance) have been developed with rapid progress.
In an etching process for a magnetic material, ion milling has been well adopted. But, when using ion milling in an etching process for a magnetic material, there has been problems. For example, one problem is a difficulty of selectivity relative to masks made of various kinds of material.
With respect to a processed shape, when using ion milling in an etching process for a magnetic material, a profile of material to be etched has tapered tails. This is also a problem.
The before described problems are caused by the reason that ion milling is a physical spattering etching.
Therefore, the ion milling is not suitable for production of MRAM with a large capacity for which an especially micro fabrication technique is required. And, in these days, if the ion milling is used for producing a large area substrate such as the substrate having 300 mm in diameter, it is difficult to process with good uniformity and with good product yield.
Recently, instead of the ion milling which involves the before described problems, techniques having been fostered in the semiconductor industry is introduced into etching process for a magnetic material.
Among the techniques having been fostered in the semiconductor industry, RIE (Reactive Ion Etching) is expected as a technique which can be used in an etching process for a magnetic material. RIE (Reactive Ion Etching) is excellent in micro fabricating property, and can secure uniformity on a large area substrate such as the substrate having 300 mm in diameter.
However the RIE technique is used widely in the semiconductor industry, if it is used in an etching process for a magnetic material, it is difficult to process magnetic materials such as FeNi, CoFe, CoPt and the like without etching residue and deposition onto a sidewall, since the RIE is generally poor in reactivity on magnetic materials such as FeNi, CoFe, CoPt and the like.
In a case where the RIE technique is employed in etching process of the before described magnetic material, a chlorine gas (Cl2 or the like) has been adopted as an etching gas. If a chlorine gas (Cl2 or the like) is used, however, there is a problem of after-corrosion and a necessity arises for removing remaining chlorine component, attached to a surface layer of a substrate, after the etching. Furthermore, another necessity has arisen for any resistance to corrosion on an RIE apparatus itself against a chlorine gas (Cl2 or the like), which is corrosive gas.
In the current state of the RIE technique to be applied to the before described magnetic materials, an effort has been directed to establish a new reaction system with no need for an aftercorrosion treatment.
Japanese Patent Application Laid-Open (JP-A) No. 8-253881 proposed a gas mixture obtained by adding carbon monoxide (CO) gas to a nitrogen-containing compound such as gases of ammonia (NH3), amines or the like as an etching gas for a magnetic materials. This gas mixture proposed in JP-A-8-253881 is hereinafter referred to as a NH3+CO gas.
Even in the before described NH3+CO gas is used as the etching gas for the before described magnetic material, however, there has been a problem to be solved as described below.
1. It is necessary to provide any facilities for performing an exhaust treatment in an RIE apparatus, since NH3 and CO are toxic.
2. In a construction of TMR, which determines a basic performance of MRAM and a magnetoresistive device, ferromagnetic layers such as CoFe or the like, from which a pinned layer and a free layer sandwiching an insulating layer made of Al2O3 or the like are made, are ferromagnetic thin films with a small thickness in the range of from 1 to 5 nm. In a case where a NH3+CO gas is used as an etching gas, etching damage is given to the before described extremely thin ferromagnetic layers to degrade magnetic characteristic thereof. So that, it is afraid that an adverse influence would be exerted to device characteristics of MRAM and a magnetoresistive device.
In accordance with miniaturization of MRAM, a magnetoresistive device and the like, a proportion of a side surface (sidewall) of the material (FeNi, CoFe or the like) to be etched relative to all of the device in an RIE treatment has been increased. Therefore, when a NH3+CO gas is used as an etching gas for the magnetic materials, it becomes difficult to neglect the degradation of a magnetic characteristic due to etching damage on a side surface (sidewall) of the material (FeNi, CoFe or the like) to be etched.
It is an object of the present invention to provide a embodiments which can reduce etching damage degrading a magnetic characteristic of the magnetic material, wherein in a case where a magnetic material is etched using a non-organic material as a mask material, an after-corrosion treatment and any resistance to corrosion for an etching apparatus are unnecessary.
In order to achieve the object, in one embodiment of a dry etching method according to the present invention, a plasma of an etching gas is generated and a magnetic material is dry-etched using a mask material made of a non-organic material, wherein an alcohol having at least one hydroxyl group is used as the etching gas.
In the before described embodiment of the present invention, the alcohol used as the etching gas may have one hydroxyl group.
In each of the before described embodiments of the present invention, an alcohol selected from the group consisting of methanol (CH3OH), ethanol (C2H5OH) and propanol (C3H7OH) may be used as the etching gas.
In each of the before described embodiments of the present invention, a mask material may be made of a non-organic material. The mask material may comprise a single layer film or a laminated layer film made of anyone selected from the group consisting of Ta, Ti, Al and Si or the mask material may comprise a single layer film or a laminated layer film made of an oxide or a nitride of anyone selected from the group consisting of Ta, Ti, Al and Si.
For example, a single layer film or a laminated layer film made of anyone selected from the group consisting of Ta, Ti, Al and Si, each of which is an elemental metal, can be used as the before described mask material.
Also, a single layer film or a laminated layer film made of Ta oxide, Ti oxide, Al oxides such as Al2O3 and Si oxides such as SiO2, TaN, TiN, AlN, SiN and the like, which are oxides or nitrides of Ta, Ti, Al and Si respectively can be used as the before described mask material.
In the before described embodiments of the present invention, either of an elemental metal belonging to the iron group in the Group VIII, or a material essentially composed of such an elemental metal can be used as the magnetic materials to be etched.
That is to say, a dry etching method of the present invention can be applied for etching the magnetic materials such as a single layer film or a laminated layer film of Fe—Ni alloy, Co—Fe alloy, Fe—Mn alloy, Co—Pt alloy, Ni—Fe—Cr alloy, Co—Cr alloy, Co—Pt alloy, Co—Cr—Pt alloy, Co—Pd alloy and Co—Fe—B alloy, for example.
In the before described embodiments of the present invention, a temperature of a magnetic material to be etched is preferably maintained at 250° C. or lower. This is because unnecessary thermal damage is not given to a magnetic film, which has an extremely small thickness, and according to this reason, more preferable temperature of a magnetic material to be etched is in the range of from 20 to 100° C.
Also, in the before described embodiments of the present invention, a vacuum degree at which the etching is performed is desirably in the range of from 0.1 to 10 Pa. This is because anisotropy in the dry etching within the before described pressure range can be well reflected in pattern processing due to formation of a high density plasma.
Further, in the before described embodiments of the present invention, an etching gas can be added with oxygen gas, water and an inert gas as an added gas. The gases can be added either alone or in any combination of two or more selected from the group including oxygen gas, water and an inert gas. The oxygen gas and water are desirably added at respective content of not more than 25% relative to the etching gas and the inert gas is desirably added at a content of not more than 90% relative to the etching gas. Examples of the inert gases that can be used include Ar, Ne, Xe, Kr and the like.
Addition of the before described added gas or gases in the before described ranges relative to an etching gas is advantageous in that a selectivity relative to a mask increases. Excess of the upper limit of addition unpreferably decreases an etching rate or a selectivity ratio relative to a mask.
According to the experiments conducted by the present inventors, such a dry etching method is able to improve an etching speed and a selectivity ratio as compared with the before described conventional technique, in which a magnetic material is etched by using the RIE technique with adopting the NH3+CO gas and proposed as a technique which can be processed without conducting an after-corrosion treatment. Especially, in a case of etching on CoFe, the etching speed is increased 50% or more larger than the conventional technique.
The reason why such a dry etching method can exert such an excellent effect is inferred that an H radical, ions such as H+ and OH− generated in a plasma from alcohol having at least one hydroxyl group used as an etching gas: for example in a case where CH3OH is used as an etching gas, an active CH3 radical and an active H radical or ions such as CH3+, H+ and OH− generated in a plasma react with a magnetic material such as Fe—Ni, Co—Fe, Fe—Mn, Co—Pt, Ni—Fe—Cr, Co—Cr, Co—Pt, Co—Cr—Pt, Co—Pd, Co—Fe—B or the like, and perform the etching.
Also, according to experiments of the present inventors, the etching method can reduce etching damage, which degrading magnetic characteristic, to a level half as high as in the before described conventional method, in which a magnetic material is etched by using the RIE technique with adopting the NH3+CO gas and proposed as a technique which can be processed without conducting an after-corrosion treatment.
According to an embodiment of the present invention, since the dry etching method does not use corrosive NH3 and the like as an etching gas, it is not necessary to apply the after-corrosion treatment after the etching. And it is not necessary to give particular consideration to a resistance against corrosion to be equipped in the etching apparatus. In addition, according to a dry etching method of the present invention, it is not necessary to provide any facilities to be used for exhaust treatment, since none of toxic etching gas such as CO or NH3 is used.
According to another embodiment of the present invention, when a magnetic material is etched with a non-organic material as a mask, it is not necessary to apply the after-corrosion treatment after the etching as well as it is not necessary to give particular consideration to a resistance against corrosion to be equipped in the etching apparatus. In addition, according to an embodiment of the present invention, it is not necessary to provide any facilities to be used for exhaust treatment.
According to an embodiment of the present invention, when a magnetic material is etched with a non-organic material as a mask, it can reduce etching damage which degrading magnetic characteristic.
Therefore, according to the present invention, it is possible to provide a embodiments useful for micro fabricating a magnetic thin film made of a single layer film or a laminated layer film of a Fe—Ni alloy, Co—Fe alloy, Fe—Mn alloy, Co—Pt alloy, Ni—Fe—Cr alloy, Co—Cr alloy, Co—Pt alloy, Co—Cr—Pt alloy, Co—Pd alloy or Co—Fe—B alloy.
FIGS. 2(a) to 2(d) are views showing one example of a process in a case where a TMR device is etched using an embodiment of the present invention, wherein FIG. 2(a) is a schematic sectional view prior to the start of the process, FIG. 2(b) is a schematic sectional view in a state where a Ta film has been etched with PR as a mask, FIG. 2(c) is a schematic sectional view in a state where a magnetic film has been etched with a Ta mask, and FIG. 2(d) is a schematic sectional view in a state where etching is progressed as far as a free layer and stopped by an Al2O3 layer; and
Description will be given of a case where a TMR device shown in FIG. 2(a) is etched using methanol (CH3OH) as an etching gas with Ta as a mask material by using an etching apparatus equipped with an ICP (Inductive Coupled Plasma) plasma source as shown in FIG. 1.
FIG. 2(a) shows an example of basic structure of the TMR device.
A structure characterizing a TMR device is shown in FIG. 2(a) and described as follows.
Said structure includes two ferromagnetic layers made of CoFe called a free layer (a layer above the Al2O3 layer) and a pinned layer (a layer below the Al2O3 layer) sandwiching the Al2O3 film. The Al2O3 film is an insulating layer with a film thickness of 1 nm. A film thickness of the free layer is 5 nm and a film thickness of the pinned layer is 5 nm. An antiferromagnetic layer made of PtMn is arranged below the pinned layer, and has a film thickness of 15 nm.
A basic principle and workings of the TMR device are known, and they are not subject matter of the present invention, so that the description of them are omitted.
A Ta film was etched on a TMR device with a structure shown in FIG. 2(a) using CF4 gas with PR as a mask, thereby forming Ta film, as shown in FIG. 2(b), to be used as a mask for etching magnetic layers (PtMn and CoFe) including Al2O3, which is an insulating film. This process is conducted as follows.
A vacuum container 2 shown in
A gas introduction system 3 is activated to introduce an etching gas (CF4) at a predetermined flow rate into the vacuum container 2 from a cylinder not shown in
The introduced etching gas diffuses by way of the vacuum container 2 into a dielectric wall container 11. On this occasion, a plasma source 1 is activated.
The plasma source 1 comprises dielectric wall container 11, antenna 12, plasma high frequency power supply 13, and electromagnet 14.
The dielectric wall container 11 is connected airtightly to the vacuum container 2 so as to communicate between the both spaces therein.
The antenna 12 shown in
The plasma high frequency power supply 13 is connected to the antenna 12 through a matching unit not shown and through a transmission line 15, and generates a high frequency power (source power) to be supplied to the antenna 12.
The electromagnet 14 generates a predetermined magnetic field in the dielectric wall container 11.
When a high frequency generated by the plasma high frequency power supply 13 is supplied to the antenna 12 through the transmission line 15, a current flows in the single turn antenna 12, with the result that a plasma is generated in the interior of the dielectric wall container 11.
A large number of sidewall magnets 22 are disposed on the outer sidewall of the vacuum container 2 in a circumferential direction. The magnetic poles, facing the sidewall of the vacuum container 2, of the respective sidewall magnets 22 adjacent to one another are different from one another. Thereby, a cusp magnetic field is formed along the inner surface of the sidewall of the vacuum container 2 in a circumferential direction. The plasma is thus prevented from diffusing toward the inner surface of the sidewall of the vacuum container 2.
In this situation, a bias high frequency power supply 5 is activated to give a self-bias voltage which is a negative DC voltage to the wafer 9, which is an objective in an etching treatment, to thereby control an ion incident energy directed to the surface of the wafer 9 from the plasma.
The plasma generated as described above diffuses from the dielectric wall container 11 into the vacuum container 2 and reaches close to the surface of the wafer 9. In this situation, the surface of the wafer 9 is etched.
The before described etching process using CF4 gas on the Ta film with a PR mask is performed under the following conditions.
Flow rate of the etching gas (CF4): 326 mg/min (50 sccm)
Source power: 500 W
Bias power: 70 W
Pressure in the vacuum container 2: 0.8 Pa Temperature of the substrate holder 4: 40° C.
Then, methanol (CH3OH) is used as an etching gas to etch a magnetic film shown in FIG. 2(b) with Ta formed in the before described process as a mask material.
This process is also performed using the etching apparatus equipped with the ICP plasma source shown FIG. 1. The process of introducing CF4 gas as an etching gas into the vacuum container 2 by activating a gas introduction system (not shown) in the before described process is changed to the process of introducing an etching gas (CH3OH) at a predetermined flow rate into the vacuum container 2 from a cylinder 31 in which methanol (CH3OH) gas is stored (shown in
Two cases were compared with each other as to an etching characteristic such as an etching speed and a selectivity ratio.
One case (example of the present invention) where according to the embodiment of the present invention, methanol (CH3OH) is used as the etching gas to etch a magnetic film with Ta formed in a process similar to the process described above as a mask material.
And the other case (comparative example) where the NH3+CO gas is used as the etching gas to etch a magnetic film with the Ta formed in a process similar to the process described above as a mask material.
Magnetic films etched with Ta as a mask material in the both comparison tests are CoFe film and NiFe film.
Both comparison tests are conducted under the following conditions, respectively.
Conditions for the embodiment of the present invention.
Flow rate of the etching gas (CH3OH gas): 18.75 mg/min (15 sccm)
Source power: 1000 W
Bias power: 800 W
Pressure in the vacuum container 2: 0.4 Pa
Temperature of the substrate holder 4: 40° C.
Conditions for the comparative example.
Flow rate of the etching gas (NH3+CO gas):
NH3 gas: 57.0 mg/min (75 sccm)
CO gas: 31.25 mg/min (25 sccm)
Source power: 1000 W
Bias power: 1200 W
Pressure in the vacuum container 2: 0.8 Pa
Temperature of the substrate holder 4: 40° C.
Results of the before described comparison tests are as shown in the following table.
TABLE 1
Methanol
Evaluation items
(CH3OH)
NH3 + CO gas
Etching speeds (nm/min)
CoFe
34.8
21.1
NiFe
32.1
29.3
Selectivity ratios (relative to Al2O3)
CoFe
5.5
3.5
NiFe
5.1
4.8
The results of the comparison tests show that, according to an embodiment of a dry etching method of the present invention, the etching speed and selectivity ratio are larger than in the case of the conventional embodiments using the NH3+CO gas as the etching gas, especially, the etching speed in the case of CoFe can be increased by 50% or more.
As shown in the table 1, according to the embodiment of the present invention, the selectivity ratio relative to Al2O3 can be higher.
There is a step as one of a fabrication process for MRAM in which as shown in FIG. 2(d), etching is advanced as far as the free layer and stopped at the Al2O3 layer.
As shown in the table 1, a selectivity ratio relative to Al2O3 is high according to the method of the present invention.
So that, the method of the present invention is advantageous for fabrication process of MRAM, in which a step where etching is advanced as far as the free layer and then stopped at the Al2O3 layer is included.
Comparative study is made between etching damages in magnetic characteristic in a case where an etching treatment is made according to a dry etching embodiment of the present invention and in a case where an etching treatment is made with the NH3+CO gas.
The apparatus shown in
To be more detailed, magnetic thin films (CoFe and NiFe) with the same physical and chemical characteristics, in which all the films have the same thickness, so saturation magnetization thereof is the same, are prepared and subjected to an etching treatment of the embodiment of the present invention using methanol as an etching gas for an arbitrary time, and to another etching treatment using the NH3+CO gas as an etching gas for an arbitrary time. For both cases, saturation magnetization of specimens after each kind of etching is measured with a vibrating sample magnetometer (VSM).
The etching, followed by the measurement, is repeated on each material (a magnetic thin film: CoFe and NiFe) three or more times during each material (a magnetic thin film: CoFe and NiFe) to be etched is remained, and graphs are prepared that shows relationships between an etching time and saturation magnetization after each etching.
Since an etching amount (in this case, measured with a thickness) is generally proportional to an etching time, plotting of an etching time using the abscissa relative to saturation magnetization to which the coordinate is assigned results in a straight line when being connected on the graph, in which an amount of saturation magnetization decreases monotonously.
This straight line is extrapolated to a point where an etching time=0, thereby obtaining a decrease in saturation magnetization immediately after the etching relative to that prior to the etching.
Results are compared with actual saturation magnetization prior to etching to obtain a decrease in saturation magnetization as an etching damage degrading magnetic characteristic, and furthermore, the results are compared between decreases in saturation magnetization amounts in a case where methanol (CH3OH) is used as an etching gas according to the embodiment of the present invention and in a case where the NH3+CO gas is used as an etching gas.
In the example of the embodiment of the present invention, a CoFe thin film and a NiFe thin film, instead of a TMR device, are individually etched according to the before described embodiment of the present invention using the apparatus shown in
In a case where the NH3+CO gas is used (comparative example), in the apparatus shown in
That is, the process of introducing an etching gas (CH3OH) at a predetermined flow rate into the vacuum container 2 from a cylinder 31 in which methanol (CH3OH) gas is stored(shown in
Both processes in Comparison Test Example 2 are conducted under the respective following conditions.
Conditions for the embodiment of the present invention.
Flow rate of the etching gas (CH3OH gas): 18.75 mg/min (15 sccm),
Source power: 1000 W
Bias power: 200 W
Pressure in the vacuum container 2: 0.4 Pa
Temperature of the substrate holder 4: 40° C.
Conditions for the comparative example.
Flow rate of the etching gas (NH3+CO gas):
NH3 gas: 57.0 mg/min (75 sccm)
CO gas: 31.25 mg/min (25 sccm)
Source power: 1500 W
Bias power: 300 W
Pressure in the vacuum container 2: 0.6 Pa
Temperature of the substrate holder 4: 40° C.
In results of comparison in etching damage obtained from a change in saturation magnetization after etching on the materials (NiFe and CoFe) to be etched, it is found that decrease in saturation magnetization in a case where the NH3+CO gas is used is larger than in a case where CH3OH gas is used by about 1.6 times for NiFe and about 5.4 times for CoFe regardless of lower etching speed. That is, according to an embodiment of the present invention, it is confirmed that etching damage, which degrading a magnetic characteristic, is greatly decreased.
Although the ICP plasma apparatus equipped with a single turn antenna shown in
In the embodiment of the present invention, in a case where a magnetic material is etched with a non-organic material as a mask material, a structure of a TMR device is not limited to the structure shown in FIGS. 2(a)˜2(d) even if the magnetic material is processed into the TMR device.
In the before described embodiments of the present invention, description is given of a case where methanol is used as an etching gas, there can be used any of ketones expressed by a chemical formula RCOR′, wherein R or R′ is an alkyl group, for example, vaporizable ketones such as methyl ethyl ketone, isopropyl methyl ketone, methyl propyl ketone and the like. Any of hydrocarbons having a methyl group can be used in addition to methane, such as ethane, propane and butane.
Although the preferred embodiments and comparison test examples of the present invention are described above using the attached drawings, the present invention is not limited to the before described embodiments, and it can be altered or modified to various modes without departing from the technical scope construed based on the appended claims.
Kodaira, Yoshimitsu, Hiromi, Taichi
Patent | Priority | Assignee | Title |
10134605, | Jul 11 2013 | Lam Research Corporation | Dual chamber plasma etcher with ion accelerator |
10224221, | Apr 05 2013 | Lam Research Corporation | Internal plasma grid for semiconductor fabrication |
10388491, | Oct 31 2011 | Canon Anelva Corporation | Ion beam etching method of magnetic film and ion beam etching apparatus |
10685815, | Aug 25 2009 | Canon Anelva Corporation | Plasma processing apparatus and device manufacturing method |
11171021, | Apr 05 2013 | Lam Research Corporation | Internal plasma grid for semiconductor fabrication |
11276816, | Jun 20 2018 | HITACHI HIGH-TECH CORPORATION | Method of manufacturing magnetic tunnel junction and magnetic tunnel junction |
11678583, | Jun 20 2018 | HITACHI HIGH-TECH CORPORATION | Method of manufacturing magnetic tunnel junction and magnetic tunnel junction |
8298430, | Oct 25 2007 | TDK Corporation | Method of etching magnetoresistive film by using a plurality of metal hard masks |
8914970, | Apr 23 2013 | Western Digital Technologies, INC | Method for making a tunneling magnetoresistive (TMR) sensor |
9017526, | Jul 08 2013 | Lam Research Corporation | Ion beam etching system |
9039911, | Aug 27 2012 | Lam Research Corporation | Plasma-enhanced etching in an augmented plasma processing system |
9147581, | Jul 11 2013 | Lam Research Corporation | Dual chamber plasma etcher with ion accelerator |
9230819, | Apr 05 2013 | Lam Research Corporation | Internal plasma grid applications for semiconductor fabrication in context of ion-ion plasma processing |
9245761, | Apr 05 2013 | Lam Research Corporation | Internal plasma grid for semiconductor fabrication |
9257295, | Jul 08 2013 | Lam Research Corporation | Ion beam etching system |
9418859, | Aug 27 2012 | Lam Research Corporation | Plasma-enhanced etching in an augmented plasma processing system |
9431269, | Jul 11 2013 | Lam Research Corporation | Dual chamber plasma etcher with ion accelerator |
9601688, | Aug 25 2011 | Canon Anelva Corporation | Method of manufacturing magnetoresistive element and method of processing magnetoresistive film |
9633846, | Apr 05 2013 | Lam Research Corporation | Internal plasma grid applications for semiconductor fabrication |
9685299, | Dec 27 2011 | Canon Anelva Corporation | Substrate processing apparatus, etching method of metal film, and manufacturing method of magnetoresistive effect element |
9793126, | Aug 04 2010 | Lam Research Corporation | Ion to neutral control for wafer processing with dual plasma source reactor |
Patent | Priority | Assignee | Title |
4687543, | Feb 21 1986 | MOTOROLA, INC , A DE CORP | Selective plasma etching during formation of integrated circuitry |
5171411, | May 21 1991 | The BOC Group, Inc. | Rotating cylindrical magnetron structure with self supporting zinc alloy target |
5409738, | Nov 21 1990 | Hitachi Global Storage Technologies Japan, Ltd | Recording medium |
5425844, | Jun 23 1993 | Kabushiki Kaisha Toshiba | Method of making layer containing magnetic material |
6238582, | Mar 30 1999 | Veeco Instruments, Inc. | Reactive ion beam etching method and a thin film head fabricated using the method |
6794297, | Aug 10 2001 | OKI SEMICONDUCTOR CO , LTD | Method for etching an antireflective coating and for fabricating a semiconductor device |
6821907, | Mar 06 2002 | Applied Materials, Inc | Etching methods for a magnetic memory cell stack |
6825156, | Jun 06 2002 | EKC TECHNOLOGY, INC | Semiconductor process residue removal composition and process |
20020096493, | |||
20030038106, | |||
20030052079, | |||
20030170998, | |||
20040222185, | |||
JP8253881, |
Executed on | Assignor | Assignee | Conveyance | Frame | Reel | Doc |
Jun 12 2008 | Canon Anelva Corporation | (assignment on the face of the patent) | / | |||
Jun 13 2008 | Anelva Corporation | Canon Anelva Corporation | CHANGE OF NAME SEE DOCUMENT FOR DETAILS | 021093 | /0012 |
Date | Maintenance Fee Events |
Nov 12 2009 | M1551: Payment of Maintenance Fee, 4th Year, Large Entity. |
May 03 2010 | ASPN: Payor Number Assigned. |
Nov 13 2013 | M1552: Payment of Maintenance Fee, 8th Year, Large Entity. |
Nov 30 2017 | M1553: Payment of Maintenance Fee, 12th Year, Large Entity. |
Date | Maintenance Schedule |
Nov 10 2012 | 4 years fee payment window open |
May 10 2013 | 6 months grace period start (w surcharge) |
Nov 10 2013 | patent expiry (for year 4) |
Nov 10 2015 | 2 years to revive unintentionally abandoned end. (for year 4) |
Nov 10 2016 | 8 years fee payment window open |
May 10 2017 | 6 months grace period start (w surcharge) |
Nov 10 2017 | patent expiry (for year 8) |
Nov 10 2019 | 2 years to revive unintentionally abandoned end. (for year 8) |
Nov 10 2020 | 12 years fee payment window open |
May 10 2021 | 6 months grace period start (w surcharge) |
Nov 10 2021 | patent expiry (for year 12) |
Nov 10 2023 | 2 years to revive unintentionally abandoned end. (for year 12) |