An aluminosilicate glass having a composition consisting essentially of, as calculated in weight percent on an oxide basis, of 58-70% SiO2, 12-22% Al2O3, 3-15% B2O3, 2-12% CaO, 0-3% SrO, 0-3% BaO, 0-8% MgO, 10-25% MCSB (i.e., MgO+CaO+SrO+BaO), and SrO and BaO in combination being less than 3%.

Patent
   RE41127
Priority
Dec 17 1996
Filed
Jan 30 2006
Issued
Feb 16 2010
Expiry
Nov 24 2017
Assg.orig
Entity
Large
6
28
all paid
0. 24. A glass exhibiting a linear coefficient of thermal expansion over the temperature range 25-300° C. between 30-41.5×10−7/° C. and a strain point over 650° C., said glass comprising an aluminosilicate having a composition as calculated in weight percent on an oxide basis that comprises:
60.2-70% SiO2,
15-18.9% Al2O3,
3.8-15% B2O3,
0-8% MgO,
6-12% CaO, and
0-1.9% SrO.
0. 22. A glass exhibiting a density of less than 2.50 g/cm3, a linear coefficient of thermal expansion over the temperature range 0-300° C. between 30-40×10−7/° C. and a strain point over 600° C., said glass comprising an aluminosilicate having a composition as calculated in weight percent on an oxide basis that comprises:
60.5-70% SiO2,
15-18.9% Al2O3,
7.1-15% B2O3,
0-8% MgO,
6-12% CaO, and
0-1.9% SrO.
0. 30. A aluminosilicate glass which exhibits a linear coefficient of thermal expansion over the temperature range 0-300° C. between 30-40×10−7/° C. and has a composition as calculated in weight percent on an oxide basis that comprises:
58-70% SiO2,
15-18.9% Al2O3,
7.1-15% B2O3,
0-8% MgO,
6-12% CaO, and
wherein the amount, if any, of SrO, BaO, or SrO plus BaO in the glass is such that the glass exhibits a density of less than 2.50 g/cm3 and a strain point of at least 650° C.
0. 1. A substrate for a flat panel display or photovoltaic device wherein said substrate is comprised of a flat, transparent glass exhibiting a linear coefficient of thermal expansion (CTE) over the temperature range 0-300° C. between 30-40×10−7/° C. and a strain point over 600° C., said glass consisting essentially of an aluminosilicate having a composition as calculated in weight percent on an oxide basis, of 58-70% SiO2, 12-22% Al2O3, 3-15% B2O3, 2-12% CaO, 0-3% SrO, 0-3% BaO, 0-8% MgO, and SrO and BaO in combination being less than 3%.
0. 2. A substrate glass in accordance with claim 1 which is manufactured by the float process, said glass having a liquidus viscosity greater than about 50 MPa·s (500 poises).
0. 3. A substrate according to claim 2, wherein said glass has a CTE of 32-38×10−7/° C. and a strain point over 650° C.
0. 4. A substrate according to claim 3, wherein said glass has a strain point over 675° C.
0. 5. A substrate according to claim 3, wherein the combined SrO and BaO content of said glass is less than about 1 weight percent.
0. 6. A substrate according to claim 3, wherein said glass is essentially free of SrO and BaO.
0. 7. A flat panel display comprising a substrate in accordance with claim 1.
0. 8. A substrate according to claim 1, wherein said glass consists essentially of a composition, as calculated in weight percent on an oxide basis, of 58-67% SiO2, 15-20% Al2O3, 5-13% B2O3, 5-12% CaO, 0-3% SrO, 0-3% BaO, 0-8% MgO, and SrO and BaO in combination is less than 3 wt %.
0. 9. A substrate according to claim 3, wherein said glass consists essentially of a composition, as calculated in weight percent on an oxide basis, of 58-67% SiO2, 15-20% Al2O3, 5-13% B2O3, 5-12% CaO, 0-3% SrO, 0-3% BaO, 1-8% MgO, and SrO and BaO in combination is less than 3 wt %.
0. 10. A substrate according to claim 9, wherein said glass has a strain point over 675° C.
0. 11. A substrate according to claim 9, wherein the combined SrO and BaO content of said glass is less than about 1 weight percent.
0. 12. A substrate according to claim 9, wherein the glass has a weight loss less than 5.0 mg/cm2 when immersed in 5% HCl at 95° C. for one hour.
0. 13. A substrate according to claim 1, wherein said glass consists essentially of a composition, as calculated in weight percent on an oxide basis, of 58-64% SiO2, 16-19% Al2O3, greater than 6 and less than 13% B2O3, 5-11% CaO, 0-3% SrO, 0-3% BaO, 1-8% MgO, and SrO and BaO in combination being less than 3%.
14.A glass exhibiting a linear coefficient of thermal expansion (CTE) over the temperature range 0-300° C. between 30-40×10−7/° C. and a strain point over 600° C., said glass comprising an aluminosilicate having a composition as calculated in weight percent on an oxide basis, consisting essentially of 58-70% SiO2, 12-22% Al2O3, 3-15% B2O3, 2-12% CaO, 0-3% SrO, 0-3% BaO, 0-8% MgO, and SrO and BaO in combination being less than 3%.
0. 15. A glass in accordance with claim 14 which is manufactured by the float process, said glass having a liquidus viscosity greater than about 50 MPa·s (500 poises).
0. 16. A glass according to claim 14, wherein said glass has a CTE of 32-38×10−7/° C. and a strain point over 650° C.
0. 17. A glass according to claim 16, wherein said glass has a strain point over 675° C.
0. 18. A photovoltaic device comprising a substrate in accordance with claim 1.
0. 19. A substrate according to claim 14, wherein said glass consists essentially of a composition, as calculated in weight percent on an oxide basis, of 58-67% SiO2, 15-20% Al2O3, 5-13% B2O3, 5-12% CaO, 0-3% SrO, 0-3% BaO, 1-8% MgO, and SrO and BaO in combination is less than 3 wt %.
0. 20. A substrate according to claim 1, wherein MgO+CaO+SrO+BaO is 10-25 weight percent.
0. 21. A substrate according to claim 1, wherein MgO+CaO+SrO+BaO is 8.6-18.2 weight percent.
0. 23. A glass according to claim 22 wherein the glass has a strain point over 650° C.
0. 25. A glass according to claim 22, 23, or 24 wherein the glass is essentially free of intentionally added alkali metal oxide.
0. 26. A glass according to claim 22, 23, or 24 wherein the glass is manufactured by the float process.
0. 27. A substrate for a flat panel display or a photovoltaic device wherein said substrate comprises a flat, transparent glass according to claim 22, 23, or 24.
0. 28. A flat panel display comprising a substrate in accordance with claim 27.
0. 29. A photovoltaic device comprising a substrate in accordance with claim 27.
0. 31. A glass according to claim 30 wherein the glass is essentially free of intentionally added alkali metal oxide.
0. 32. A glass according to claim 30 wherein the glass is manufactured by the float process.
0. 33. A substrate for a flat panel display or a photovoltaic device wherein said substrate comprises a flat, transparent glass according to claim 30.
0. 34. A flat panel display comprising a substrate in accordance with claim 33.
0. 35. A photovoltaic device comprising a substrate in accordance with claim 33.

More than one reissue application has been filed for the reissue of U.S. Pat. No. 6,060,168. The reissue applications are application Ser. No. 10/141,286 and the present application filed May 8, 2003 now RE 38,959 which is a continuation of application Ser. No. 10/141,286.

This application claims the benefit of U.S. provisional application Ser. No. 60/033,603, filed Dec. 17, 1996.

The invention relates to a family of aluminosilicate glass compositions exhibiting physical and chemical properties suitable for flat panel display.

Liquid crystal displays (LCDs) are passive flat panel displays which depend upon external sources of light for illumination. They are manufactured as segmented displays or in one of two basic configurations. The substrate needs (other than being transparent and capable of withstanding the chemical conditions to which it is exposed during display processing) of the two matrix types vary. The first type is intrinsic matrix addressed, relying upon the threshold properties of the liquid crystal material. The second is extrinsic matrix or active matrix (AM) addressed, in which an array of diodes, metal-insulator-metal (MIM) devices, or thin film transistors (TFTs) supplies an electronic switch to each pixel. In both cases, two sheets of glass form the structure of the display. The separation between the two sheets is the critical gap dimension, of the order of 5-10 μm.

Intrinsically addressed LCD's are fabricated using metal deposition techniques, typically at temperatures ≦350° C., followed by standard metal etching procedures. As a result, the substrate requirements therefor are often the same as those for segmented displays. Soda-lime-silica glass with a barrier layer has proven to be adequate for most needs. A high performance version of intrinsically addressed LCDs, the super twisted nematic (STN) type, has an added requirement of extremely precise flatness for the purpose of holding the gap dimensions uniform.

Extrinsically addressed LCD's can be further subdivided depending upon the nature of the electrical switch located at each optical element (subpixel). Two of most popular types of extrinsically (or active matrix, AMLCD) addressed LCD's are those based on either amorphous (a-Si) or polycrystalline (poly-Si) silicon thin film transistors (TFT's).

U.S. Pat. No. 4,824,808 (Dumbaugh, Jr.) lists four desirable properties for a glass to exhibit in order to fully satisfy the needs of a substrate for extrinsically addressed LCD's:

First, that the glass be essentially free of intentionally added alkali metal oxide to avoid the possibility of alkali metal contamination of the TFT;

Second, that the glass be sufficiently chemically durable to withstand the reagents used during the manufacture of the TFT;

Third, that the expansion mismatch between the glass and the silicon present in the TFT array be maintained at a relatively low level even as processing temperatures for the substrates increase; and

Fourth, that the glass be capable of being produced in high quality thin sheet form at low cost; that is, it must not require extensive grinding and polishing to secure the necessary surface finish.

Recent improvements in the resolution of extrinsically addressed LCD's have led to the desirability of a further glass properties, namely, a high glass strain point, a low density, and a high modulus. Strain point is used as an indication of the thermal shrinkage of the glass. As can be appreciated, the lower the strain point, the greater is this thermal shrinkage. Low thermal shrinkage is desirable for precise alignment during successive photolithographic and other patterning steps during the TFT processing. Consequently, glasses having higher strain points are generally preferred for extrinsically addressed LCD's, particularly those which employ poly-Si TFT technology. Thus, there has been considerable research to develop glasses demonstrating high strain points so that thermal shrinkage is minimized during device processing. Corning Code 1737 glass, which has the highest strain point (666° C.) in the AMLCD substrate industry, is rapidly becoming an industry standard. Concurrent with their high strain points, these glasses often have high melting temperatures, e.g. on the order of 1550-1650° C. Low densities and high modulii are desired to minimize sag during thermal processing and to allow for thinner and lighter displays.

Another technology termed “chip-on-glass” (COG) has further emphasized the need for the substrate glass to closely match silicon in thermal expansion. Thus, the initial LCD devices did not have their driver chips mounted on the substrate glass. Instead, the silicon chips were mounted remotely and were connected to the LCD substrate circuitry with compliant or flexible wiring. As LCD device technology improved and as the devices became larger and required finer resolutions, these flexible mountings became unacceptable, both because of cost and of uncertain reliability. This situation led to Tape Automatic Bonding (TAB) of the silicon chips. In that process the silicon chips and electrical connections to the chips were mounted on a carrier tape, that subassembly was mounted directly on the LCD substrate, and thereafter the connection to the LCD circuitry was completed. TAB decreased cost while improving reliability and increasing the permitted density of the conductors to a pitch of approximately 200 μm—all significant factors. COG, however, provides further improvement over TAB with respect to those three factors. Hence, as the size and quality requirements of LCD devices increase, COG is demanded for those devices dependent upon the use of integrated circuit silicon chips. For that reason, the substrate glass preferably demonstrate a linear coefficient of thermal expansion closely matching that of silicon; i.e., a linear coefficient of thermal expansion (0°-300° C.) between about 32-39×10−7/° C.

It would therefore be desirable to provide a glass substrate having a CTE in the 30-40°×10−7/° C. range and a strain point greater than 650° C., more preferably greater than 675° C. A density less than 2.50 g/cm3 and a Young's modulus of greater than 11.0 Mpsi would also be desirable. It would also be desirable for the glass to be capable of being manufactured using the float process.

The present invention is directed to boro-aluminosilicate glasses having a coefficient of thermal expansion (CTE) between 30-39×10−7/° C. over the temperature range of 25°-300° C. and have a composition consisting essentially of as calculated in weight percent on an oxide basis, 58-70 SiO2, 12-22 Al2O3, 3-15 B2O3, 0-8 MgO, 2-12 CaO, 0-3 SrO, 0-3 BaO, and SrO+BaO in combination is less than 3. The glasses also preferably employ a combination of MgO, CaO, SrO+BaO (MCSB) between about 10-25 weight percent. Other oxides may include, for example, the transition metals, particularly those in period 4 (such as ZnO and TiO2), as well as Y2O3, La2O3, ZrO2, and P2O5, and those ingredients employed for fining (e.g. CaSO4, As2O3, Sb2O3, halides, and so forth). These other oxides listed above should preferably not exceed 5 wt % in total. Na2O and K2O content each is preferably kept less than 1 weight percent and more preferably the glasses of the present invention are essentially alkali-free.

More preferably the glass consists essentially of 58-67 SiO2, 15-20 Al2O3, 5-13 B2O3, 0-8 MgO, 5-12 CaO, 0-3 SrO, 0-3 BaO, and SrO and BaO in combination being less than 3.

Most preferably the glass consists essentially of 58-64 SiO2, 16-19 Al2O3, greater than 6 and less than 13 B2O3, 1-8 MgO, 5-11 CaO, 0-3 BaO, and SrO and BaO in combination being less than 3.

The glasses of the present invention exhibit a coefficient of thermal expansion (CTE) in the range of 30-39 (more preferably 31-38, and most preferably 32-38)×10−7/° C., from 25-300° C. and a high strain point (at least 650° C., preferably greater than 675° C., in order to eliminate or minimize the need for a pre-compaction annealing step. Low density (preferably less than 2.5 g/cm3, most preferably less than 2.4 g/cm3) and high Young's modulus is desirable to minimize display weight and panel sag and at the same time maximize hardness in order to improve resistance to scratching and edge defects.

The glass compositions covered in the present invention disclosure are believed to be well suited to flat glass manufacture via the float process in that they generally: 1) do not necessarily include certain oxides or elements in amounts which are known to be detrimental to the float bath, such as As, Sb, Pb, Bi, Ti; 2) are easily melted (having 200 poise isokom temperatures less than 1600° C., more preferably below 1550° C.); and 3) exhibit liquidus viscosities greater than 103 poise. Moreover, the preferred compositions contain little or no SrO or BaO oxides in order to achieve low density, high Young's modulus, high strain point, and low melting temperature. For this reason, each of the SrO and BaO content is preferably less than 3, more preferably less than 1 (and less than 2 weight percent in combination), and most preferably is essentially zero.

The present invention is concerned with improved glasses for use as flat panel display substrates. In particular, the glasses meet the various property requirements of such substrates. It is believed that glasses of the present invention are capable of being formed using the float glass manufacturing process. To provide flexibility in the melting process, and particularly to enable the production of the glasses via the float process, it is desirable that the glass have several characteristics related to melting properties. For example, a melting temperature (i.e., temperature at which the viscosity is about 20 Pa·s (200 poises)) less than or equal to about 1550° C., and more preferably less than or equal to about 1500° C. More importantly, in order to manufacture the glass via the float glass manufacturing process, it is desirable for the glass to exhibit a viscosity at the liquidus temperature which is greater than 50 MPa·s Pa·s (500 poises), more preferably greater than 100 Mpa·s Pa·s (1000 poises), and most preferably greater than about 250 Mpa·s Pa·s (2500 poises). In addition, it is desirable that the glass be capable of exhibiting a Liquidus Temperature below about 1250° C., most preferably below about 1200° C.

The preferred glasses in accordance with the present invention have a CTE in the range of 30-39×10−7/° C., more preferably 31-38×10−7/° C., and most preferably 32-38×10−7/° C. The desire for such a CTE is primarily driven by the desire to match the CTE of silicon transistor chips. The glasses of the present invention preferably have a strain point greater than 650° C., more preferably greater than 675° C. A high strain point is desired to help prevent panel distortion due to compaction/shrinkage during subsequent thermal processing. In the most preferred embodiments, the glasses exhibit a combination of desirable CTE's and strain point. For example, the most preferred glasses exhibit a CTE between 31-38×10−7/° C., in combination with a strain point greater than about 675° C.

Chemical durability generally improves as the ratio of glass formers plus intermediates to glass modifiers increases. It is desirable that glasses for present purposes have a weight loss less than about 5.0 mg/cm2, more preferably less than 2.0 mg/cm2 and most preferably less than 1.0 mg/cm2 after exposure to the 5% HCl solution at 95° C. for 20 minutes. Glasses having compositions within the following oxide ranges in weight percent are generally characterized by wt. loss values less than 5.0 mg/cm2:

SiO2 58-70
Al2O3 12-22
CaO  2-12
SrO 0-3
BaO 0-3
MgO 1-8
B2O3  3-15
MgO + CaO + SrO + BaO 10-25
SrO + BaO 0-3

The present glasses employ 58-70% by weight SiO2 as the primary glass former. Increasing SiO2 content generally improves durability, but raises the melting point. The glasses also comprise 12-22 wt % Al2O3. As the Al2O3 content increases, glass durability increases, but CTE decreases and the melting point increases. Boric oxide (B2O3) decreases melting temperature, but is generally detrimental to HCl durability, and strain point. B2O3 content is between 3 and 15 percent by weight. Generally speaking MgO and/or CaO can replace B2O3 to maintain a low CTE, density, Young's modulus and flux the melt. B2O3 tends to decrease the liquidus temperature and increase the viscosity at the liquidus. However, relatively high levels of B2O3 are detrimental to HCl durability. The role of MgO and CaO is to limit alkali mobility and flux the melt at relatively high temperatures, while at the same time enabling a high strain point and low density. MgO is limited to 8, more preferably is 1-8, and most preferably is 2-6 weight percent. SrO and BaO in combination are preferably less than 3% more preferably less than 2%, and most preferably are essentially avoided to minimize the formation of BaSO4, SrSO4, as well as to lower the density, increase the strain point, and increase the modulus of the glass.

The invention is further illustrated by the following examples, which are meant to be illustrative, and not in any way limiting, to the claimed invention. TABLE I sets forth exemplary glass compositions in weight percent, as calculated on an oxide basis from the glass batches. These example glasses were prepared by melting 1000-5000 gram batches of each glass composition at a temperature and time to result in a relatively homogeneous glass composition, e.g. at a temperature of about 1550-1600° C. for a period of about 6 to 16 hours in platinum crucibles. Also set forth are relevant glass properties for each glass composition, determined on the glasses in accordance with techniques conventional in the glass art. Thus, the linear coefficient of thermal expansion (CTE) over the temperature range 25°-300° C. expressed in terms of ×10−7/° C., and the softening point (Soft.Pt.), annealing point (Anneal.Pt.), and strain point expressed in terms of ° C. Softening point was measured using the parallel plate method, and annealing point and strain point were both measured using beam bending viscometry.

The internal liquidus temperatures (Liq. Temp.) of the glasses were measured using the standard liquidus method, which involves placing crushed glass particles in a platinum boat, placing the boat in a furnace having a region of gradient temperatures, heating the boat in an appropriate temperature region for 24 hours, and determining by means of microscopic examination the highest temperature at which crystals appear in the interior of the glass. The 200 poise temperature (in ° C.) (defined as the temperature at which the glass melt demonstrates a viscosity of 200 poises [20 Pa.s]) was calculated employing the Fulcher equation as fit to the high temperature viscosity data. Also listed is Young's modulus, shear modulus and specific modulus (Young's modulus/density), as well as Knoop hardness, which was measured using a 100 gram load.

wt %
1 2 3 4 5 A
SiO2 60.2 60.7 60.5 62.0 61.0 57.8
Al2O3 17.8 18.0 17.9 17.0 18.0 16.5
B2O3 3.8 6.5 7.1 7.1 7.1 8.5
MgO 7.6 6.1 4.3 5.8 5.8 .75
CaO 10.6 8.7 10.2 8.1 8.1 4.15
SrO 0.0 0.0 0.0 0.0 0.0 1.9
BaO 0.0 0.0 0.0 0.0 0.0 9.4
Liquidus (° C.) 1220 1240 1210 1240 1200 1090
Temperature
Soft Pt (° C.) 947 937 940 945 942 975
Anneal Pt (° C.) 739 723 728 730 730 721
Strain Pt (° C.) 692 677 681 686 683 666
CTE (×10−7/° C.) 41.5 39.5 39.0 37.3 36.5 37.8
Density (g/cm3) 2.575 2.501 2.459 2.459 2.466 2.544
Young's Modulus (Mpsi) 12.0 10.2
Shear Modulus (Mpsi) 4.8 4.1
Specific Modulus 4.9 4.0
(Mpsi · cm3/g)
Knoop Hardness (100 g) 505 460
200 Poise Temp (° C.) 1515 1625
wt %
6 7 8 9 10
SiO2 61.3 62.4 63.5 62.7 62.1
Al2O3 18.1 18.0 18.9 18.7 18.5
B2O3 7.2 7.1 8.4 8.3 8.2
MgO 7.4 5.2 3.0 2.2 2.2
CaO 6.0 7.3 6.2 6.2 6.1
SrO 0.0 0.0 0.0 1.9 0.0
BaO 0.0 0.0 0.0 0.0 2.8
Liquidus (° C.) 1240 1240 >1260 1250 >1250
Temperature
Soft Pt (° C.) 943 958 984 985 986
Anneal Pt (° C.) 736 738 754 751 748
Strain Pt (° C.) 691 691 704 700 697
CTE (×10−7/° C.) 35.8 34.3 31.0 32.7 31.0
Density (g/cm3) 2.458 2.442 2.397 2.416 2.431
wt %
11 12 13 14 15 16
SiO2 62.8 61.9 62.7 62.4 62.5 61.5
Al2O3 16.5 16.2 16.4 16.3 17.2 17.1
B2O3 11.2 11.1 12.3 12.2 11.7 12.8
MgO 0.0 0.0 0.0 0.6 0.0 0.0
CaO 9.5 8.5 8.6 6.9 8.6 8.6
SrO 0.0 0.0 0.0 1.6 0.0 0.0
BaO 0.0 2.3 0.0 0.0 0.0 0.0
Liquidus (° C.) Temperature 1160 1145 1110 1135 1170 1185
Soft Pt (° C.) 959 960 961 959 962 952
Anneal Pt (° C.) 730 724 718 711 722 714
Strain Pt (° C.) 679 671 668 661 670 663
CTE (×10−7/° C.) 34.7 34.4 34.3 32.8 33.6 34.5
Density (g/cm3) 2.389 2.419 2.370 2.381 2.377 2.371

A glass having a composition and properties as shown in Example 5 is currently regarded as representing the best mode of the invention, that is, as providing the best combination of properties for the purposes of the invention at this time. Comparative Example A set forth in Table I represents the compositions and properties of Corning Incorporated's code 1737 glass, currently one of the most popular substrates for LCD applications. Compared to code 1737 glass, Example 5 has a higher strain point (683° C. vs. 666° C. for 1737), lower density (2.45 vs. 2.54 g/cm3), lower softening point (942 vs. 975° C.), higher Young's modulus (12 vs. 10.2 Mpsi), and higher Knoop hardness (505 vs. 460 with 100 g load), yet has a 200 poise temperature of about 1516° C. (vs. 1625 for code 1737 glass), thereby potentially enabling formation of this glass at significantly lower temperatures.

Although the invention has been described in detail for the purpose of illustration, it is understood that such detail is solely for that purpose and variations can be made therein by those skilled in the art without departing from the spirit and scope of the invention which is defined by the following claims. For example, while the glass is described herein primarily as a flat panel display substrate, it may also be used in photovoltaic device applications.

Kohli, Jeffrey T.

Patent Priority Assignee Title
10347782, Aug 04 2011 Corning Incorporated Photovoltaic module package
10509307, Jul 30 2014 Corning Incorporated High contrast, glass-based, writeable/erasable front projection screens
8975199, Aug 12 2011 Corsam Technologies LLC Fusion formable alkali-free intermediate thermal expansion coefficient glass
9309139, Feb 15 2013 Corning Incorporated High volume production of display quality glass sheets having low zirconia levels
9643883, Aug 12 2011 Corsam Technologies LLC Fusion formable alkali-free intermediate thermal expansion coefficient glass
RE46337, May 30 2008 Corning Incorporated Boroalumino silicate glasses
Patent Priority Assignee Title
2961328,
4394453, Sep 08 1981 Corning Glass Works Envelopes for tungsten-halogen lamps
4634683, Oct 23 1985 Corning Glass Works Barium and/or strontium aluminosilicate crystal-containing glasses for flat panel display devices
4634684, Oct 23 1985 Corning Glass Works Strontium aluminosilicate glass substrates for flat panel display devices
4666868, Oct 23 1985 Corning Glass Works Strontium aluminosilicate glass substrates for flat panel display devices
4666869, Oct 23 1985 Corning Glass Works Barium and/or strontium aluminosilicate crystal-containing glasses for flat panel display devices
5116787, Aug 12 1991 Corning Incorporated High alumina, alkaline earth borosilicate glasses for flat panel displays
5116788, Aug 12 1991 Corning Incorporated Alkaline earth aluminoborosilicate glasses for flat panel displays
5116789, Aug 12 1991 Corning Incorporated Strontium aluminosilicate glasses for flat panel displays
5244847, Apr 26 1991 Asahi Glass Company Ltd Alkali free glass
5326730, Jan 22 1993 Corning Incorporated Barium aluminosilicate glasses
5374595, Jan 22 1993 Corning Incorporated High liquidus viscosity glasses for flat panel displays
5489558, Mar 14 1994 Corning Incorporated Glasses for flat panel display
5508237, Mar 14 1994 Corning Incorporated Flat panel display
5741746, Mar 02 1995 Corning Incorporated Glasses for display panels
6319867, Nov 30 1998 Corning Incorporated Glasses for flat panel displays
6831029, Nov 30 1998 Corning Incorporated Glasses for flat panel displays
7524784, Nov 30 1998 Corning Incorporated Glasses for flat panel displays
EP576362,
EP672629,
EP714862,
FR2675795,
JP4160030,
JP60215547,
JP61132536,
JP7277763,
WO9711919,
WO9711920,
/
Executed onAssignorAssigneeConveyanceFrameReelDoc
Jan 30 2006Corning Incorporated(assignment on the face of the patent)
Date Maintenance Fee Events
Nov 09 2011M1553: Payment of Maintenance Fee, 12th Year, Large Entity.


Date Maintenance Schedule
Feb 16 20134 years fee payment window open
Aug 16 20136 months grace period start (w surcharge)
Feb 16 2014patent expiry (for year 4)
Feb 16 20162 years to revive unintentionally abandoned end. (for year 4)
Feb 16 20178 years fee payment window open
Aug 16 20176 months grace period start (w surcharge)
Feb 16 2018patent expiry (for year 8)
Feb 16 20202 years to revive unintentionally abandoned end. (for year 8)
Feb 16 202112 years fee payment window open
Aug 16 20216 months grace period start (w surcharge)
Feb 16 2022patent expiry (for year 12)
Feb 16 20242 years to revive unintentionally abandoned end. (for year 12)