As there is disclosed a cemented carbide body comprising WC with an average grain size of <10 μm in a binder phase. In the cemented carbide body the WC grains can be classified in at least two groups in which a group of smaller grains has a maximum grain size amax and a group of larger grains has a minimum grain size bmin and each group contains at least 10 % of the total amount of WC grains. According to the invention bmin−amax>0.5 μm and the difference in grain size within each group is >1 μm.
|
1. A method of making a cemented carbide body comprising wet mixing without milling of at least two different WC-powders with deagglomerated powders of other carbides and a binder metal such that the WC-powers WC-powders are coated with the binder phase, said WC-grains being deagglomerated before and after being coated with binder metal, the grains of the WC-powder being classified in at least two groups in which a group of smaller grains has a maximum grain size amax and a group of larger grains has a minimum grain size bmin, each group containing at least 10% of the total amount of WC grains wherein bmin−amax>0.5 mm μm, the variation in grain size within each group being >1 μm, drying said mixture, pressing to a desired shape and sintering said pressed bodies.
2. The method of
3. The method of
4. The method of
5. The method of
6. The method of
0. 7. The method of
0. 8. The method of
0. 9. The method of
0. 10. The method of
0. 11. The method of
0. 12. The method of
0. 13. The method of
0. 14. The method of
|
|||||||||||||||||||||
The sintered inserts according to the invention are used coated or uncoated, preferably coated by MTCVD, conventional CVD or PVD, with or without Al2O3. In particular, multilayer coatings comprising TiCxNvOz with columnar grains followed by a layer of α-Al2O3, κ-Al2O3 or a mixture of α- and κ-Al2O3, have shown good results. In another preferred embodiment, the coating described above is completed with a TiN-layer which can be brushed or used without brushing.
According to the method of the present invention, a cemented carbide body is made comprising wet mixing without milling of at least two different WC-powders with deagglomerated powders of other carbides, generally TiC, TaC and/or NbC, binder metal and pressing agent, dried preferably by spray drying, pressed to inserts and sintered. The grains of the WC-powder are classified in at least two groups in which a group of smaller grains has a maximum grain size amax and a group of larger grains has a minimum grain size bmin each group containing at least 10% of the total amount of WC grains wherein bmin−amax>0.5 μm and the variation in grain size within each group is >1 μm. Preferably, prior to mixing, the WC grains are carefully deagglomerated before and after being coated with binder metal.
Particularly according to the method of the present invention, WC-powders with two narrow grain size distributions of 0-1.5 μm and 2.5-6.0 μm respectively and a weight ratio of fine WC particles (0-1.5 μm) to coarse WC particles (2.5-6.0 μm) in the range of 0.25-4.0, preferably 0.5-2.0 are wet mixed without milling with other carbides generally TiC, TaC and/or NbC, binder metal and pressing agent, dried preferably by spray drying, pressed to inserts and sintered.
It is essential according to the invention that the mixing takes place without milling, i.e., there should be no change in grain size or grain size distribution as a result of the mixing.
In a preferred embodiment, the hard constituents, at least those with narrow grain size distributions, are after careful deagglomeration coated with binder metal using methods disclosed in U.S. Pat. No. 5,505,902 or 5,529,804. In such case, the cemented carbide powder according to the invention is preferably of Co-coated WC+Co-binder, with or without additions of the cubic carbides such as TiC, TaC, NbC, (Ti,W)C, (Ta,Nb)C, (Ti,Ta,Nb)C, (W,Ta,Nb)C, and (W,Ti,Ta,Nb)C coated or uncoated, preferably uncoated, possibly with further additions of Co-powder in order to obtain the desired final composition.
The invention is additionally illustrated in connection with the following Examples which are to be considered as illustrative of the present invention. It should be understood however, that the invention is not limited to the specific details of the Examples.
A. Cemented carbide tool inserts of the type SEMN 1204 AZ, an insert for milling, with the composition in addition to WC of 8.4 wt % Co, 1.13 wt % TaC and 0.38 wt % NbC were produced according to the invention. Cobalt coated WC, WC-6 wt-% Co, prepared in accordance with U.S. Pat. No. 5,505,902 was carefully deagglomerated in a laboratory jetmill equipment, mixed with additional amounts of Co and deagglomerated uncoated (Ta,Nb)C and TaC powders to obtain the desired material composition. The coated WC-particles consisted of 50 wt % with an average grain size of 3.5 μm and 50 wt % with 1.2 μm average grain size, giving a bimodal grain size distribution. The mixing was carried out in an ethanol and water solution (0.25 l fluid per kg cemented carbide powder) for 2 hours in a laboratory mixer and the batch size was 10 kg. Furthermore, 2 weight-% lubricant, was added to the slurry. The carbon content was adjusted with carbon black to a binder phase alloyed with W corresponding to a CW-ratio of 0.89. After spray drying, the inserts were pressed and sintered according to standard practise and dense structures with no porosity were obtained.
Before coating a negative chamfer with an angle of 20 degrees was ground around the whole insert.
The inserts were coated with a 0.5 μm equiaxed TiCN-layer (with a high nitrogen content corresponding to an estimated C/N-ratio of 0.05) followed by a 4 μm thick TiCN-layer with columnar grains by using the MTCVD-technique (temperature 885-850° C. and CH3CN as the carbon and nitrogen sources). In subsequent steps during the same coating cycle, a 1.0 μm thick layer of Al2O3 was deposited using a temperature 970° C. and a concentration of H2S dopant of 0.4% as disclosed in EP-A-523 021. A thin (0.3 μm) layer of TiN was deposited on top according to known CVD-technique. XRD-measurement showed that the Al2O3-layer consisted of 100% κ-phase.
The coated inserts were brushed by a nylon straw brush containing SiC grains. Examination of the brushed inserts in a light microscope showed that the thin TiN-layer had been brushed away only along the cutting edge leaving there a smooth Al2O3-layer surface.
Coating thickness measurements on cross sectioned brush samples showed no reduction of the coating along the edge line except for the outer TiN-layer that was removed.
B. Cemented carbide tool inserts of the type SEMN 1204 AZ, an insert for milling, with the composition 9.1 wt % Co, 1.23 wt % TaC and 0.30 wt % NbC and the rest WC with unimodal distribution and an average grain size of 1.2 μm were produced in the following way. Cobalt coated WC, WC-6 weight-% Co, prepared in accordance with U.S. Pat. No. 5,505,902 was carefully deagglomerated in a laboratory jetmill equipment, mixed with additional amounts of Co and deagglomerated uncoated (Ta,Nb)C and TaC powders to obtain the desired material composition. The mixing was carried out in an ethanol and water solution (0.25 l fluid per kg cemented carbide powder) for 2 hours in a laboratory mixer and the batch size was 10 kg. Furthermore, 2 weight-% lubricant, was added to the slurry. The carbon content was adjusted with carbon black to a binder phase highly alloyed with W corresponding to a CW-ratio of 0.89. After spray drying, the inserts were pressed and sintered according to standard practise and dense structures with no porosity were obtained.
Before coating a negative chamfer with an angle of 20 degrees was ground around the whole of each insert.
The inserts were coated in the same coating batch as the inserts A above.
The coated inserts were brushed by a nylon straw brush containing SiC grains. Examination of the brushbed inserts in a light microscope showed that the thin TiN-layer had been brushed away only along the cutting edge leaving there a smooth Al2O3-layer surface.
Coating thickness measurements on cross sectioned brushed samples showed no reduction of the coating along the edge line except for the outer TiN-layer that was removed.
C. Cemented carbide tool inserts of the type SEMN 1204 AZ with the same chemical composition, average grain size of WC, CW-ratio, chamfering, CVD-coating and brushing respectively as the insert B above but produced from powder manufactured with conventional ball milling techniques were used as reference for comparison with the test specimens according to above.
Inserts from A, B and C were compared in a wet milling test in a rather highly alloyed steel (HB=310). Two parallel bars each of a thickness of 35 mm were centrally positioned relative the cutter body (diameter 100 mm ), and the bars were placed with an air gap of 10 mm between them.
The cutting data were:
Evaluated tool life expressed as cutting length of variant A according to the invention was 8200 mm and for variant B 6900 mm and finally for the standard variant C only 6100 mm. In this test the insert according to the invention with a bimodal WC grain size distribution, variant A, obtained the best result.
A. Inserts from the same batch as insert A in Example 1 above and
B. Inserts from the same batch as insert B in Example 1 above and
C. Inserts from the same batch as insert C in Example 1 above
were compared in a wet milling test in a low alloyed steel (SS 1650, HB=180). Two parallel bars each of a thickness 30 mm were centrally positioned relative the cutter body (diameter 100 mm). The bars were placed with an air gap of 10 mm between them.
The cutting data were:
Evaluated tool life expressed as cutting length of variant A according to the invention was 4800 mm and for variant B, 4200 mm and finally for the standard variant C only 3600 mm. In this test the insert according to the invention with a bimodal WC grain size distribution, variant A, performed best.
The principles, preferred embodiments and modes of operation of the present invention have been described in the foregoing specification. The invention is intended to be protected herein, however, is not to be construed as limited to the particular forms disclosed, since these are to be regarded as illustrative rather than restrictive. Variations and changes may be made by those skilled in the art without departing from the spirit of the invention.
Ostlund, Ake, Waldenstrom, Mats, Alm, Ove
| Patent | Priority | Assignee | Title |
| Patent | Priority | Assignee | Title |
| 5505751, | May 28 1987 | Kennametal Inc. | Cutting tool |
| 5505902, | Mar 29 1994 | Sandvik Intellectual Property Aktiebolag | Method of making metal composite materials |
| 5529804, | Mar 31 1994 | Sandvik Intellectual Property Aktiebolag | Method of making metal composite powders |
| 5593474, | Aug 04 1988 | Smith International, Inc. | Composite cemented carbide |
| 5624766, | Aug 16 1993 | Sumitomo Electric Industries, Ltd. | Cemented carbide and coated cemented carbide for cutting tool |
| 5674564, | Jun 25 1991 | Sandvik Intellectual Property Aktiebolag | Alumina-coated sintered body |
| 5773735, | Nov 20 1996 | The Dow Chemical Company | Dense fine grained monotungsten carbide-transition metal cemented carbide body and preparation thereof |
| Executed on | Assignor | Assignee | Conveyance | Frame | Reel | Doc |
| Jul 08 1997 | Sandvik Intellectual Property Aktiebolag | (assignment on the face of the patent) | / |
| Date | Maintenance Fee Events |
| Sep 05 2012 | M1553: Payment of Maintenance Fee, 12th Year, Large Entity. |
| Date | Maintenance Schedule |
| Sep 07 2013 | 4 years fee payment window open |
| Mar 07 2014 | 6 months grace period start (w surcharge) |
| Sep 07 2014 | patent expiry (for year 4) |
| Sep 07 2016 | 2 years to revive unintentionally abandoned end. (for year 4) |
| Sep 07 2017 | 8 years fee payment window open |
| Mar 07 2018 | 6 months grace period start (w surcharge) |
| Sep 07 2018 | patent expiry (for year 8) |
| Sep 07 2020 | 2 years to revive unintentionally abandoned end. (for year 8) |
| Sep 07 2021 | 12 years fee payment window open |
| Mar 07 2022 | 6 months grace period start (w surcharge) |
| Sep 07 2022 | patent expiry (for year 12) |
| Sep 07 2024 | 2 years to revive unintentionally abandoned end. (for year 12) |