A multilayer hard coating for tools for machining applications with a multilayer structure for improving the wear resistance of workpieces includes at least one (AlyCr1-y)X layer (0.2≦y≦0.7), wherein X is one of the following elements N, C, B, CN, BN, CBN, NO, CO, BO, CNO, BNO, CBNO, but preferably N or CN, and/or a (TizSi1-z) layer (0.99≧z≧0.7). The hard coating also includes at least one layer stack with one (AlCrTiSi) X mixed layer, followed by another (TizSi1-z)X layer, followed by another (AlCrTiSi) X mixed layer, followed by another (AlyCr1-y)X layer.
|
1. A method of providing a hard coating on a workpiece, comprising:
a) positioning the workpiece in a coating system adjacent at least one TiSiX TiSi target and at least one AlCrX AlCr target, each of said targets having an associated cathodic arc source, wherein X is selected from the group consisting of N, C, B, CN, BN, CBN, NO, CO, BO, CNO, BNO, and CBNO;
b) rotating the workpiece;
c) applying a biasing voltage to said workpiece; and
d) selective operating said cathodic arc sources to deposit a multilayer coating onto the workpiece, said multilayer coating comprising:
at least one layer selected from the group consisting of:
an (AlyCr1-y)X layer, wherein 0.2≦y≦0.7 and X is selected from the group consisting of N, C, B, CN, BN, CBN, NO, CO, BO, CNO, BNO, and CBNO, and a (TizSi1-z)X layer, wherein 0.99≧z≧0.7, and
at least one layer stack comprising the following layers:
one (AlCrTiSi)X mixed layer
followed by another (TizSi1-z)X layer
followed by another (AlCrTiSi)X mixed layer
followed by another (AlyCr1-y)X layer,
wherein X, y and z are as previously defined.
18. A method of providing a hard coating on a workpiece, comprising:
a) positioning the workpiece in a coating system adjacent at least one TiSiX TiSi target and at least one AlCrX AlCr target, each of said targets having an associated cathodic arc source, wherein X is selected from the group consisting of N, C, B, CN, BN, CBN, NO, CO, BO, CNO, BNO, and CBNO;
b) rotating the workpiece;
c) applying a biasing voltage to said workpiece; and
d) selective operating said cathodic arc sources to deposit a multilayer coating onto the workpiece, said multilayer coating comprising:
at least one layer selected from the group consisting of:
an (AlyCr1-y)X layer, wherein 0.2≦y≦0.7 and X is selected from the group consisting of N, C, B, CN, BN, CBN, NO, CO, BO, CNO, BNO, and CBNO, and
a (TizSi1-z)X layer, wherein 0.99≧z≧0.7, and
at least one layer stack comprising the following layers:
one (AlCrTiSi)X mixed layer
followed by another (AlyCr1-y)X layer
followed by another (AlCrTiSi)X mixed layer
followed by another (AlyCr1-y)X layer,
wherein X, y and z are as previously defined.
2. The method of
3. The method of
4. The method of
5. The method of
6. The method of
i) deposition of an AlCrX adhesive layer having a thickness of approximately 0.2 microns;
ii) operating the cathodic arc sources associated with all of said targets together to deposit a mixed AlCrX/TiSiX layer;
iii) turning off only the cathodic arc sources associated with said at least one AlCrX AlCr target to deposit a pure TiSiX layer;
iv) reactivating the cathodic arc sources associated with said at least one AlCrX AlCr target to again deposit a mixed AlCrX/TiSiX layer; and
v) turning off the cathodic arc sources associated with said at least one TiSi target to deposit a pure AlCrX layer.
7. The method of
8. The method of
9. The method of
10. The method of
11. The method of
12. The method of
AlyCr1-yN layer between 75 nm and 200 nm
TizSi1-zN layer between 50 and 150 nm
(AlCrTiSi)X mixed layer 20±10 nm.
13. The method of
14. The method of
15. The method of
16. The method of
17. The method of 1, characterized by the fact that an additional sliding layer is deposited on the hard coating.
19. The method of
21. The method of
22. The method of
X in said at least one layer is N or CN,
X in said (TizSi1-z)X layer is N or CN, and
0.95≧z≧0.85.
23. The method of
24. The method of
0. 25. The method of claim 1, said at least on AlCr target comprising one or more elements selected from the group of elements in Groups IVb, Vb, VIb of the Periodic Table of Elements.
|
This invention concerns a multilayer hard coating for tools (hard metal and high-speed steel) for machining applications—especially drilling applications.
EP 1174528 A2 describes a tool coating comprised of a series of several individual layers, wherein the first layer is composed of a nitride, carbide, carbonitride, boride, oxide, etc. of the elements Ti, Al and/or Cr, and a second layer is composed of a nitride, carbide, carbonitride, boride, oxide etc. of Si and at least one element from groups 4a, 5a and 6a of the PTE [Periodic Table of the Elements]. The advantage of this coating is that the Si in the upper layer critically improves the wear resistance and oxidation resistance. The Cr—Si-based cover layers mainly improved tool life. TiAlN, CrAlN and TiN layers are chosen for the bottom layer.
EP 1422311 A2 describes Al—Cr—(Si)—O-based hard layers that can be made as nitrides, carbide, oxide, boride, etc. For all layers, it is true that a small percentage of oxygen (1-25%) is contained in the layers. It should also be mentioned that another hard layer can be applied in the coating mentioned in the invention. Ti—Si—N Ti—B—N, BN, Cr—Si—N, etc., inter alia, are given here as examples. One advantage of the invention is the use of small quantities of oxygen or silicon and oxygen, since this results in greater hardness, improved wear resistance and high-temperature oxidation resistance.
EP 1219723 A2 introduces a Ti—Al—Cr—X-N-based coating, where X can stand for Si, B and/or C. The advantage of this coating is to improve wear-resistance compared to conventional coatings. The invention also describes a target that must be composed of at least Ti, Al and Cr.
The tools with hard coatings in the state of the art (Ti—Al—N-based coatings) have shorter tool lives than the new optimized (Al1-xCrxX)—Ti1-ySiy) X-hard coatings for X=N or CN.
The disadvantages of the state of the art are also that with Al—Cr—N coatings at high temperatures in an atmosphere of inert gas (for example, an argon atmosphere), the coating starts to decompose at around 900° C. If this heat-treatment process is carried out in an atmosphere of oxygen, the decomposition process goes into a higher temperature range. Now, if a continual cut is being considered in machining, the local temperatures are very high (sometimes over 1000° C.) in the contact area between the surface of the tool and the workpiece. If this contact surface is large enough so that no/little oxygen can have a stabilizing effect on the coating surface, the cubic CrN breaks down into hexagonal Cr2N and then at a higher temperature into metallic Cr. This coating decomposition process results in premature wear on the coating in use, which manifests as crater wear in particular.
The purpose of the invention is to prevent the disadvantages of the state of the art and especially to improve the tool life of coated tools, like chip removal tools, for example, cutting and forming tools and components for machinery and forming. It is also the problem of the invention to provide a method of cutting such coatings, especially cutting such coatings on sawn workpieces.
The invention describes a special multi-layer design for a coating to prevent the coating from disintegrating too fast (wearing out) during use. The multi-layer design prevents or at least delays the disintegration and subsequent diffusion of the Cr—N portion in the AlCrN coating at high temperatures.
An RCS-type industrial coating system from the Balzer Company is used for the deposition of the Al—Cr—(X)—N/Ti—Si—N hard layers, as described, for example, in EP 1186681 in FIGS. 3 to 6 and the Description, column 7, line 18 to column 9, line 25. For this, the cleaned workpieces, depending on their diameter, attached to two or, for diameters smaller than 50 mm, to three rotating substrate holders and two Ti—Si targets produced by fusion metallurgy and four targets made of Al—Cr—(X) alloys produced by powder metallurgy are installed in six cathode arc sources placed on the walls of the coating system. The geometry of the target layout is basically determined by the octagonal plot of the RCS system, in which two heating segments arranged opposite each other separate two groups of three segments in a row with an arc cathode. For these experiments, an SiTi target was installed in the opposite middle element of each group of three. But other target layouts are also possible to produce such layers. In principle, such layers can be deposited in each system that has at least two arc cathodes in a geometrically equivalent position, for example at the same coating height of one or more rotating substrate holders. An expert knows it is possible to further influence the thickness of the individual layers or laminates by arranging the target or setting the respective substrate movement or rotation or the angular speed of rotation of a workpiece, depending on the type of system.
Next, the workpieces are brought to a temperature of approximately 500° C. by radiational heating also placed in the system and then the surface undergoes etch cleaning by Ar ions by applying a DC bias voltage of −100 to −200 V in an Ar atmosphere at a pressure of 0.2 Pa.
After that, an Al—Cr—N adhesive layer approximately 0.2 μm thick is deposited by operating four Al—Cr sources with a capacity of 3 kW and applying a substrate bias of −50 V for a period of approximately 5 minutes. Then, a multilayer coating is purposely created, in which first 2 Ti—Si sources also with 3 kW are connected to the 4 Al—Cr sources, and they are operated together for a period of approximately 1 minute. Then the 4 Al—Cr sources are turned off and a pure Ti—Si—N coating is deposited for approximately 3 minutes. Then the 4 Al—Cr sources are connected to it again for approximately 1 minute. After that, the TiSi sources are turned off, and a pure Al—Cr—N coating is deposited for another 5 minutes. This sequence for the layer stack is followed several times during the deposition in the invention. Finally, another cover layer approximately 0.5 μm thick is applied, which was produced exclusively with the Ti—Si sources. Alternately, a thicker AlCrN cover layer can be applied here. All layers were deposited in an atmosphere of pure nitrogen at a pressure of around 3 pa and a negative substrate preliminary voltage of roughly 50 volts. Basically the process pressure in each of these steps can be set in a range from 0.5 to around 8 pa, but preferably between 0.8 and 5 Pa, whereby the atmosphere can be either pure nitrogen or a mixture of nitrogen and an inert gas, like argon, for nitride layers, or a mixture of nitrogen and a gas containing carbon, which can be mixed with an inert gas if necessary can be used for carbonitride layers. Accordingly, oxygen or a gas containing boron can be mixed in, as is known, for the deposition of layers containing oxygen or boron.
Table 1 shows the composition of the target, the crystal structure of the layer and the adhesion. Table 2 summarizes the process parameters, such as the target capacity, negative substrate preliminary voltage, process pressure and temperature.
According to the invention, workpieces are distinguished by the fact that a cubic (AlyCr1-y)X layer is deposited with X=N or CN, but preferably N, and 0.2≦y≦0.7, preferably 0.3≦y≦0.5 alternating with a cubic (TizSi1-z)X layer with X=N or CN, but preferably N, and 0.99≧z≧0.7, preferably 0.97≧z≧0.85 (see
Another way of designing the desired multilayer system, can be by periodically turning the coating sources on and off similarly to
The method in the invention is characterized by the fact that a process is chosen in order to deposit the layer stack described above. The multilayer structure is achieved by purposely turning the coating sources on and off. The multilayer substructure is maintained in addition by rotating or moving the workpieces being coated within the coating system.
Example 1 describes coatings with a defined number of layers or packets of layers, whereby a layer stack consists of a sequence of AlCrTiSiN layers followed by a layer of TiSiN, AlCrTiSiN and AlCrN. It is easy to see that compared to the layer tested in Experiment No. 1, which was deposited according to the state of the art, an improvement in tool life can be achieved with the coating in the invention. It is also clear that the optimal layer thickness of the individual layers made of AlyCr1-yN and TizSi1-zN is important for the necessary increase in tool life. This layer thickness for AlyCr1-yN is between 75 nm and 200 nm, preferably 120 nm to 170 nm, and for TizSi1-zN between 50 and 150 nm, preferably between 70 to 120 nm. In this example, these layer thicknesses were altered over the coating time so that for all experiments, a comparable layer thickness of roughly 4 μm could be achieved. For these experiments, a layer design was chosen like the one described in
Basically, completely different workpieces can be coated advantageously with these kinds of AlyCr1-yN/TizSi1-zN multilayer coatings. Examples of this are cutting tools like milling cutters, hob cutters, spherical head cutters, planar and profile cutters and drills, taps, shaving dies, reamers and indexable inserts for lathe and mill work and forming tools like stamps, dies, drawing dies, knockout cores or thread formers. Also injection-molding tools, for example for metal injection-molding alloys, synthetic resins or thermoplastics, especially injection-molding tools like those used for producing plastic molded parts or data carriers like CDs, DVDs et al., can be protected advantageously with such layers. Although better results are not always achieved by the coatings in the inventions for all applications on different tools, much higher wear resistance can be achieved, at least on certain applications and in the examples listed than with the coatings known in the past.
In addition, because of the behavior of AlyCr1-yN/TizSi1-zX multilayer coatings, which is similar in principle, an improvement in wear behavior can be expected when target compositions and coating parameters in the following layer systems are chosen so that X=N, C, B, CN, BN, CBN, NO, CO, BO, CNO, BNO and CBNO, but preferably N and CN and 0.2≦y≦0.7, preferably 0.40≦y≦0.68 and 0.99≧z≧0.7, preferably 0.95≧z≧0.85.
One way of improving the coating properties of AlyCr1-yN/TizSi1-zN multilayer coatings consists of alloying other chemical elements from one or more groups of Groups IVb, Vb and/or VIb of the Periodic Table of the Elements, or silicon. It can be especially advantageous to alloy with the layer stack of the AlyCr1-y-mMmN layer, with 0≦m≦0.25, preferably with 0≦m≦0.15. The elements for M=W, V, Mo, Nb and Si have proven particularly advantageous (see Example No. 5).
Another way of improving the properties of the layer system is to put an extra sliding layer on the layer stack or on the cover layer closing the hard coating on the outside. The sliding coating system can be made of at least one metal or a carbide of at least one metal and disperse carbon, MeC/C, whereby the metal is a metal from the Group IVb, Vb and/or VIb and/or silicon. For example, a WC/C cover layer with a hardness that can be set between 1000 and 1500 HV that has excellent intake properties is especially suitable for this. CrC/C coatings also have similar behavior with a somewhat higher friction coefficient.
With such coated deep-hole drills, after a bore hole was produced, it was possible to detect additional intake smoothness of the chip surfaces, which has only be achieved to date by expensive mechanical machining. This results in an improvement in chip transport along the chip groove and minimization of friction torque during the drilling process. Such properties are also of interest particularly for component applications with sliding, rubbing or rolling stresses, especially when there is a lack of lubrication or when they run dry, or if an uncoated counter body must be protected at the same time. Other ways of making a sealing sliding coating are metal-free diamond-like carbon coatings, or MoSx, WSx or MoSx or MoWx layers containing titanium.
The sliding layer can be applied, as mentioned, directly to the multilayer system or after another adhesive layer is applied, in order to achieve the best possible adhesion of the layer composite. The adhesive layer can be designed to be made of metal, nitride, carbide, carbonitride or as a gradient layer.
For example, WC/C or CrC/C layers can be produced, after applying a sputtered or arced Cr or Ti adhesive layer, advantageously by sputtering a WC target while adding a gas containing carbon. Here, the percentage of gas containing carbon is increased over time to achieve a larger percentage of free carbon in the layer.
The following will show advantageous applications of the invention, as examples, using different cutting operations.
Drills with Inner-Cooled HM Drill Bits of Structural
Steel
Tool:
Hard metal drill with cooling ducts
Diameter D = 6.8 mm
Workpiece:
Structural steel DIN 1.1191 (Ck45)
Drilling parameters:
Cutting speed vc = 120 m/min
Tooth feed fz = 0.2 mm/rotation
Hole depth z = 34 mm (5 × D)
Cooling:
5% emulsion
Process:
blind hole
Wear criterion:
Corner wear VB = 0.2 mm
Tool life expressed
Layer
in units of length of
thickness
path traversed**
Experiment No.
[μm]
[m]
1 AlCrN + TiSiN
3.9
54.3
2 AlCrN + 2 × layer stack 1* + TiSiN
4.2
43.9
3 AlCrN + 4 × layer stack 1* + TiSiN
3.9
65.2
4 AlCrN + 8 × layer stack 1* + TiSiN
4.0
76.2
5 AlCrN + 12 × layer stack 1* + TiSiN
4.0
54.3
6 AlCrN + 15 × layer stack 1* + TiSiN
3.9
43.9
*A (1×) coating stack corresponds to a one-time sequence of “AlCrTiSiN + TiSiN + AlCrTiSiN + AlCrN.”
**In which the width of the wear land was VB = 0.2 mm.
Example 1 shows a comparison of the tool lives of coated HM drills, in which a different number of coating stacks were applied with the same adhesive layer, namely AlCrN and a cover layer, namely TiSiN. The coating time of the TiSiN and AlCrN layers was adjusted so that in the end, the total thicknesses of the layers were comparable. An optimum total tool life was found in Experiment No. 4 with a total number of 37 layers, which shows a clear improvement over the state of the art from Experiment No. 1.
Drills with Inner-Cooled HM Drills of Structural
Steel
Tool:
Hard metal drill with cooling ducts
Diameter D = 6.8 mm
Workpiece:
Structural steel DIN 1.1191 (Ck45)
Drilling parameters:
Cutting speed vc = 120 m/min.
Tooth feed fz = 0.2 mm/rotation
Hole depth z = 34 mm (5 × D)
Cooling:
5% emulsion
Process:
Blind hole
Wear criterion:
Corner wear VB = 0.2 mm
Tool life expressed
in length of path traversed
Experiment No.
with VB = 0.2 mm in meters
6 (TiAlN/TiN multilayer)
32.3
8 (TiAlN monolayer)
32.3
9 (AlCrN monolayer)
65.9
10 AlCrN + 8 × layer stack 1* + TiSiN
76.2
Example 2 shows a comparison of the tool lives of coated HM drill bits. Here, an improvement in tool life was also able to be achieved with the AlCrN/TiSiN multilayer compared to hard coatings of TiAlN/TiN multilayer and TiAlN monolayer coatings used industrially.
Drills with Outer-Cooled HM Drill Bits of Structural
Steel
Tool:
Hard metal drill with cooling ducts
Diameter D = 6.8 mm
Workpiece:
Structural steel DIN 1.1191 (Ck45)
Drilling parameters:
Cutting speed vc = 120 m/min.
Tooth feed fz = 0.2 mm/rotation
Hole depth z = 23.8 null (3.5 × D)
Cooling:
5% emulsion
Process:
Blind hole
Wear criterion:
Corner wear VB = 0.15 mm
Tool life expressed
in length of path traversed
Experiment No.
with VB = 0.15 mm in meters
11 (TiAlN/TiN multilayer)
46.1
12 (TiAlN monolayer)
42.3
13 (AlCrN monolayer)
22.6
14 AlCrN + 8 × layer stack 1* + TiSiN
61.5
Example 3 shows a comparison of the tool lives of coated HM drill bits. Here, an improvement in tool life was also able to be achieved with the AlCrN/TiSiN multilayer compared to hard TiAlN-based coatings used industrially.
Drills with Inner-Cooled HM Drill Bits of Cast Iron
(GGG-50)
Tool:
Hard metal drill with cooling ducts
Diameter D = 6.8 mm
Workpiece:
Cast iron with spherical graphite GGG50
Drilling parameters:
Cutting speed vc = 200 m/min.
Tooth feed fz = 0.3 mm/rotation
Hole depth z = 34 mm (5 × D)
Cooling:
5% emulsion
Process:
Blind hole
Wear criterion:
Corner wear VB = 0.1 mm
Tool life expressed
in length of path traversed
Experiment No.
with VB = 0.1 mm in meters
15 (TiA1N/TiN multilayer)
57.1
16 (TiA1N monolayer)
142.8
17 (AlCrN monolayer)
185.6
18 AlCrN + 8 × layer stack 1* + TiSiN
199.9
Example 4 shows a comparison of the tool lives of coated HM drill bits. Here, an improvement in tool life was also able to be achieved with the AlCrN/TiSiN multilayer coating compared to hard layers of TiAlN/TiN multilayer coating and TiAlN monolayer coatings used industrially.
Drills with Inner-Cooled HM Drill Bits of Structural Steel
Tool:
Hard metal drill with cooling ducts
Diameter D = 6.8 mm
Workpiece:
Structural Steel DIN 1.1191 (Ck45)
Drilling parameters:
Cutting speed vc = 120 m/min.
Tooth feed fz = 0.2 mm/rotation
Hole depth z = 34 mm (5 × D)
Cooling:
5% emulsion
Process:
Blind hole
Wear criterion:
Corner wear VB = 0.2 mm
Tool life expressed
Layer
in length of path
thick-
traversed with
Al
Cr
M
ness
VB = 0.2 mm in
Experiment No.
at %
at %
at %
[μm]
meters
19 AlCrWN + 8 ×
70
28
2
3.8
65.8
layer stack 2* + TiSiN
20 AlCrWN + 8 ×
70
25
5
3.4
59.3
layer stack 2* + TiSiN
21 AlCrNbN + 8 ×
70
25
5
3.8
57.8
layer stack 2* + TiSiN
22 AlCrMoN + 8 ×
70
25
5
4.8
61.2
layer stack 2* + TiSiN
23 AlCrVN + 8 ×
70
25
5
4.2
68.0
layer stack 2* + TiSiN
24 AlCrSiN + 8 ×
70
25
5
4.0
54.4
layer stack 2* + TiSiN
*A (l×) layer stack 2* corresponds to a one-time coating sequence of “AlCrMTiSiN + TiSiN + AlCrMTiSiN + AlCrMN,” wherein M stands for one of the elements W, Nb, Mo V or Si.
Example 5 shows a comparison of the tool lives of HM drills coated according to the invention on which multilayer systems with different chemical compositions, but the same cover layer (TiSiN) were deposited. As a chemical composition, the target composition was varied, wherein Al was kept constant, and Cr was partly replaced by a third element. The process parameters for layer deposition were kept equal as in the other experiments.
Another way of producing a corresponding layer stack is when, as in
In
(Al1-a-b-cCraTibSic)X
where 0.18≦a≦0.48; 0.28≦b≦0.4; 0.004≦c≦0.12. The aluminum content is advantageously kept at over 10 at %. If other elements are added, as mentioned above, to achieve a corresponding effect, depending on the element, a minimum concentration of 0.5 to 1 atom percentage and a maximum concentration of 15% to 25% are added.
In
TABLE 1
Composition of Target
Ex-
Crystal
Target 1
Target 2
Layer
peri-
Struc-
Al
Cr
Ti at
Si at
Thickness
Ad-
ment
ture
at %
at %
M at %
%
%
[μm]
hesion
A
B1
70
30
—
85
15
4.0
HF1
B
B1
70
28
W = 2
85
15
3.8
HF1
C
B1
70
25
2 = 5
85
15
3.4
HF1
D
B1
70
25
Nb = 5
85
15
3.8
HF1
E
B1
70
25
V = 5
85
15
4.8
HF1
F
B1
70
25
Mo = 5
85
15
4.2
HF1
G
B1
70
25
Si = 5
85
15
4.0
HF1
TABLE 2
Experi-
PTargetAl—Cr—M
PTargetTi—Si
USubstrate
PN2
Temp.
ment
[kW]
[kW]
[V]
[Pa]
[° C.]
A
3
3
−50
3
500
B
3
3
−50
3
500
C
3
3
−50
3
500
D
3
3
−50
3
500
E
3
3
−50
3
500
F
3
3
−50
3
500
G
3
3
−50
3
500
Patent | Priority | Assignee | Title |
10675690, | Sep 04 2015 | OSG CORPORATION | Hard coating and hard coating-covered member |
10676810, | Sep 04 2015 | OSG CORPORATION | Hard coating and hard coating-covered member |
Patent | Priority | Assignee | Title |
6274257, | Oct 29 1999 | Ionbond, LLC | Forming members for shaping a reactive metal and methods for their fabrication |
6586122, | Jul 13 2000 | Mitsubishi Hitachi Tool Engineering, ltd | Multilayer-coated cutting tool |
6790543, | Nov 07 2001 | Hitachi Tool Engineering, Ltd. | Hard layer-coated tool |
6827976, | Apr 29 1998 | Oerlikon Trading AG, Trubbach | Method to increase wear resistance of a tool or other machine component |
7348074, | Apr 01 2005 | Oerlikon Trading AG, Trubbach | Multilayer hard coating for tools |
CA2523882, | |||
EP1174528, | |||
EP1219723, | |||
EP1422311, | |||
JP10025566, | |||
JP6322517, | |||
JP9041127, |
Executed on | Assignor | Assignee | Conveyance | Frame | Reel | Doc |
Aug 25 2010 | Oerlikon Trading AG, Trubbach | (assignment on the face of the patent) | / | |||
Dec 10 2014 | Oerlikon Trading AG, Trubbach | Oerlikon Surface Solutions AG, Trubbach | CHANGE OF NAME SEE DOCUMENT FOR DETAILS | 059795 | /0243 | |
Feb 12 2016 | Oerlikon Surface Solutions AG, Trubbach | OERLIKON SURFACE SOLUTIONS AG, PFÄFFIKON | CHANGE OF NAME SEE DOCUMENT FOR DETAILS | 059912 | /0979 |
Date | Maintenance Fee Events |
Oct 23 2013 | M1551: Payment of Maintenance Fee, 4th Year, Large Entity. |
Nov 15 2017 | M1552: Payment of Maintenance Fee, 8th Year, Large Entity. |
Nov 18 2021 | M1553: Payment of Maintenance Fee, 12th Year, Large Entity. |
Date | Maintenance Schedule |
Jun 28 2014 | 4 years fee payment window open |
Dec 28 2014 | 6 months grace period start (w surcharge) |
Jun 28 2015 | patent expiry (for year 4) |
Jun 28 2017 | 2 years to revive unintentionally abandoned end. (for year 4) |
Jun 28 2018 | 8 years fee payment window open |
Dec 28 2018 | 6 months grace period start (w surcharge) |
Jun 28 2019 | patent expiry (for year 8) |
Jun 28 2021 | 2 years to revive unintentionally abandoned end. (for year 8) |
Jun 28 2022 | 12 years fee payment window open |
Dec 28 2022 | 6 months grace period start (w surcharge) |
Jun 28 2023 | patent expiry (for year 12) |
Jun 28 2025 | 2 years to revive unintentionally abandoned end. (for year 12) |