The present invention is intended to provide a semiconductor optoelectric device with high luminescent efficiency and a method of manufacturing the same. The semiconductor optoelectric device 18 according to the present invention is constructed by depositing compound-semiconductor layers 13 and 14 on a monocrystalline substrate 11 of a hexagonal close-packed structure. The shape of the monocrystalline substrate 11 is a parallelogram. Individual sides of the parallelogram are parallel to a <11-20> orientation. As the monocrystalline substrate, sapphire, zinc oxide or silicon carbide may be used. As the compound-semiconductor layers, an n-type GaN layer 13 and p-type GaN layer 14 may be used.
|
1. A semiconductor optoelectric device, comprising:
a polygonal monocrystalline substrate of a hexagonal close-packed structure, oriented in <0001> axis, and having a polygonal peripheral area, individual sides of the polygonal monocrystalline substrate are substantially parallel to <11-20> axis;
compound-semiconductor layers deposited on said polygonal monocrystalline substrate; and
electrodes connected to said compound-semiconductor layers;
wherein a surface roughness of a back surface of said substrate falls within 10% of the thickness of said substrate.
2. The semiconductor optoelectric device according to
3. The semiconductor optoelectric device according to
4. The semiconductor optoelectric device according to
5. The semiconductor optoelectric device according to
0. 6. A semiconductor optoelectric device, comprising:
a polygonal monocrystalline substrate of a hexagonal close-packed structure, oriented in <0001> axis, and having a polygonal peripheral area, individual sides of said polygonal monocrystalline substrate are substantially parallel to <1-100> axis or <11-20> axis, a thickness of said polygonal monocrystalline substrate is at least half as wide as a longest side of said polygonal monocrystalline substrate, a surface roughness of a back surface of said polygonal monocrystalline substrate falls within 10% of the thickness of said polygonal monocrystalline substrate;
compound-semiconductor layers deposited on the polygonal monocrystalline substrate; and
electrodes connected to said compound-semiconductor layers.
0. 7. The semiconductor optoelectric device according to
0. 8. The semiconductor optoelectric device according to
0. 9. The semiconductor optoelectric device according to
0. 10. The semiconductor optoelectric device according to
0. 11. A semiconductor optoelectric device, comprising:
a polygonal monocrystalline substrate of a hexagonal close-packed structure, oriented in <0001> axis, and having a polygonal peripheral area, one side of said polygonal monocrystalline substrate is substantially parallel to <11-20> axis, another side of said polygonal monocrystalline substrate is substantially parallel to <1-100> axis, a thickness of said polygonal monocrystalline substrate is at least half as wide as a longest side of said polygonal monocrystalline substrate, and a surface roughness of a back surface of said polygonal monocrystalline substrate falls within 10% of the thickness of said polygonal monocrystalline substrate.
0. 12. The semiconductor optoelectric device according to
0. 13. The semiconductor optoelectric device according to
0. 14. The semiconductor optoelectric device according to
15. The semiconductor optoelectric device according to claim 11 1, wherein the shape of said polygonal monocrystalline substrate is a rectangle or a square.
16. The semiconductor optoelectric device according to
0. 17. The semiconductor optoelectric device according to
0. 18. The semiconductor optoelectric device according to
0. 19. The semiconductor optoelectric device according to claim 1, wherein
said substrate is in the shape of a parallelogram in which two sides are substantially parallel to the <11-20> axis, and the other sides are substantially parallel to the <1-100> axis.
0. 20. The semiconductor optoelectric device according to claim 1, wherein
one side of said substrate is substantially parallel to the <11-20> axis, and another side is substantially parallel to the <1-100> axis.
0. 21. The semiconductor optoelectric device according to claim 19, wherein the semiconductor optoelectric device comprises a laser diode.
0. 22. The semiconductor optoelectric device according to claim 20, wherein the semiconductor optoelectric device comprises a laser diode.
|
1. Field of the Invention
The present invention relates to a semiconductor optoelectric device and a method of manufacturing the same.
2. Description of the Related Art
Semiconductor optoelectric devices such as light emitting diodes (LED) and laser diodes (LD) are usually manufactured as follows. The deposition layers, such as GaAs, InGaP, GaAlAs, were grown in an epitaxial growth system on a substrate made of GaAs or GaP having a zinc blend structure by metal organic chemical vapor deposition (MOCVD) or molecular beam epitaxial growth (MBE) or both. The substrate thus obtained is cut into chips, thereby obtaining semiconductor optoelectric devices.
The substrate on which semiconductor layers are deposited is cleaved after scribe lines are provided on the substrate by use of a needle scriber. Since the substrate having a zinc blende structure possesses a natural cleavage line of cutting in a <110> orientation, it can be easily cut into chips along the scribe lines extending in the <110> orientation.
Recently, as a material for a semiconductor optoelectric device emitting at a short-wavelength including blue light, gallium nitride based materials represented by GaN has attracted attention. When the gallium nitride based material is used in manufacturing a semiconductor optoelectric device, a sapphire substrate is usually employed. The sapphire substrate is diced by a disc cutter or cut after the scribing lines are provided. The resultant semiconductor chips are usually a square or rectangular.
However, sapphire having a hexagonal close-packed structure does not distinctly have such a natural cleavage line as the zinc blende structure has. Therefore, an excessive force must be applied to dice or cut the sapphire substrate along the scribe lines, unlike in the case of the substrate having a zinc blende structure. The excessive force applied to the sapphire substrate imposes an undesirable influence on performance of the semiconductor optoelectric devices, lowering the yield of the diode. For example, the excessive force degrades crystallizable of the epitaxial layers on sapphire substrate, ultimately decreasing the luminescence efficiency. Attempts have been made to manufacture a laser diode by using a sapphire substrate. However, they failed, since it was not possible to cleave the sapphire substrate into chips in mirror-like flat planes, a requisite feature for manufacturing a laser diode. Accordingly, it still remains difficult to produce laser diodes from the hexagonal close-packed structure crystalline substrate.
On the other hand, a compound-semiconductor made of a group II-VI element such as ZnSe has attracted attention as a material for a visual-light emitting diode. This is because it has a bandgap equal to or more than the energy corresponding to visible-light, blue or green wavelength. The group II-VI compound-semiconductor is advantageous since it has an wavelength in a short wavelength range covering blue to ultraviolet, unlike a compound-semiconductor of a group III-V element (GaAlAs or InGaAlP) employed in conventional laser diodes and LEDs, has an operating wavelength range on the longer wavelength side of green. Furthermore, the group II-VI compound-semiconductor is also advantageous since it can achieve the same results as those of conventional semiconductor optical devices such as, small, light, low-voltage operational ability and high reliability. By virtue of these advantages, the group II-VI compound-semiconductor is expected to be used in a high-density optical disk and a full-color display of an open-air message board.
As a blue-green light emitting diode using the group II-VI element such as ZnSe, a current-injection type laser diode is known to be operated at room temperature. As is reported in OKUYAMA et al., Electronics Letters Vol. 29, No. 16, pp. 1488-1489 (1993), the group II-VI compound-semiconductor such as ZnSe grain on a GaAs substrate in accordance with the MBE (molecular beam epitaxial growth) method, the blue-green laser diode is formed.
However, no practical laser diode capable of being operated at a low voltage and having a long-life and high luminescence efficiency, have been achieved. This is because,
(a) It is difficult to make the II-VI family compound-semiconductor lattice-match with a substrate made of a different family type such as GaAs, unlike the III-V family compound-semiconductor;
(b) It is difficult to control the growth of a semiconductor layer on a substrate. As a result, many defects develop in the semiconductor layers, particularly, near the interface with a substrate, then a carrier concentration is low; and
(c) The defects are generated by the current application.
The present invention was made with the view toward overcoming the aforementioned problems such as low luminescence efficiency, low yield, and no applicability to a laser diode, accompanied by conventional semiconductor optoelectric devices employing a sapphire substrate.
An object of the present invention is to provide a semiconductor optoelectric device having a high luminescence efficiency and to provide a method of manufacturing the same. Another object of the present invention is to provide a laser diode using a sapphire substrate.
The semiconductor optoelectric device of the present invention comprises:
a polygonal monocrystalline substrate of a hexagonal close-packed structure, oriented in <0001> axis, and having a polygonal peripheral area, individual sides of said polygonal monocrystalline substrate are substantially parallel to a <11-20> axis;
compound-semiconductor layers deposited on the polygonal monocrystalline substrate; and
electrodes connected to the compound-semiconductor layers.
According to a preferable embodiment of the semiconductor optoelectric device of the present invention, the polygonal monocrystalline substrate is a parallelogram.
Furthermore, the semiconductor optoelectric device of the present invention comprises:
a polygonal monocrystalline substrate of a hexagonal close-packed structure, oriented in <0001> axis, and having a polygonal peripheral area, one side of said polygonal monocrystalline substrate is substantially parallel to <11-20> axis, another side of said polygonal monocrystalline substrate is substantially parallel to <1-100> axis, a longest side of said polygonal monocrystalline substrate is at least twice as long as a thickness of the polygonal monocrystalline substrate, and a surface roughness of a back surface of said polygonal monocrystalline substrate falls within 10% of the thickness of said polygonal monocrystalline substrate;
compound-semiconductor layers deposited on the monocrystalline substrate oriented; and
electrodes connected to the compound-semiconductor layers.
According to another preferable embodiment of the present invention, the polygonal monocrystalline substrate is a rectangle or square.
The hexagonal close-packed structure monocrystalline substrate may be made of sapphire, zinc oxide, silicon carbide and the like. The compound-semiconductor may be made of an element selected from the group consisting of a lanthanide series element, an actinide series element, In, Ga, Al, B, Tl, Y and Sc, in coupled with an element selected from the group consisting of N, As, P, Sb and Bi.
According to a still another preferable embodiment of the semiconductor optoelectric device of the present invention, the compound-semiconductor is a hexagonal close-packed structure.
According to a further preferable embodiment of the semiconductor optoelectric device, one of the compound-semiconductor layers is a hexagonal close-packed structure containing nitrogen.
The method of manufacturing the semiconductor optoelectric device of the present invention comprises the steps of:
depositing compound-semiconductor layers on a hexagonal close-packed structure monocrystalline substrate oriented in <0001> axis;
connecting electrodes to the compound-semiconductor layers; and
cutting the monocrystalline substrate provided with the compound-semiconductor layers into polygonal chips individual sides of which are substantially parallel to a <11-20> orientation.
Furthermore, the method of manufacturing the semiconductor optoelectric device of the present invention comprises the steps of:
preparing the hexagonal close-packed structure monocrystalline substrate oriented in <0001> axis such that the surface roughness of a back surface of the monocrystalline substrate falls within 10% of the thickness thereof;
depositing compound-semiconductor layers on the hexagonal close-packed structure monocrystalline substrate;
connecting electrodes to the compound-semiconductor layers; and
cutting the monocrystalline substrate provided with the compound-semiconductor layers into polygonal chips such that
a side is substantially parallel to a <11-20> orientation;
another side is substantially parallel to a <1-100> orientation; and
the longest side is at least twice as long as the thickness of the monocrystalline substrate.
Moreover, the semiconductor optoelectric device of the present invention comprises:
a substrate;
semiconductor layers deposited on the substrate; and
electrode connected to at least one of the semiconductor layers, wherein,
the substrate has an opening extending from the back surface of the substrate into the semiconductor layer;
an area of the smallest horizontal cross section of the opening provided to the substrate is smaller than that of the opening provided to the semiconductor layer; and
the electrodes are formed so as to be contact with the semiconductor layer through the opening of the substrate.
In
According to the present invention, the semiconductor optoelectric device are obtained by cutting the hexagonal close-packed structure monocrystalline substrate into polygonal chips in such a way that individual sides of the polygonal chips are parallel to the <11-20> orientation. In this manner, the monocrystalline substrate can be desirably cut without the application of an excessive force. This is because the hexagonal close-packed structure crystalline has a characteristic natural cleavage line of cutting along the <11-20> orientation. This fact was found by the present inventors. As a result, a physical influence due to the cutting, such as crystallizability degradation, can be reduced and a luminescent efficiency is improved. In addition, preferable advantages such as improvement in the yield and a long life, will be offered to the semiconductor optoelectric device.
The laser diodes obtained by the application of the method of the present invention will have flatter cleaved planes than before and generate desirable laser oscillation.
Besides the aforementioned advantages, the present invention entails the following advantages.
In the case of manufacturing a semiconductor optoelectric device, light emitting from the upper surface of the compound-semiconductor layers, the present invention contributes to minimizing a light-emitting area occupied by electrodes since the electrodes can be provided in the vicinity of vertices having an interior angle of 60°.
In the case of an LED of edge emission type, the present invention contributes to improving light output therefrom, namely, external quantum efficiency. This is because the total side length, which is responsible for light emission, of the polygonal compound semiconductor layers of the present invention is longer than that of a square and a rectangular one, assuming that they have the same surface area.
Most desirably, the polygon is a parallelogram, however, an equilateral triangle or a polygon the interior angles of which are a multiple of 60° may be used. Even if each side of the polygon is off the <11-20> orientation by ±3° or less, the monocrystalline substrate can be desirably cleaved.
According to the findings by the present inventors, if the thickness of the monocrystalline substrate and the surface roughness of the back surface thereof satisfy predetermined conditions, the hexagonal close-packed structure monocrystalline substrate can be also cleaved well in the <1-100> orientation. To describe more specifically, if the thickness of the monocrystalline substrate is less than half of the longest side of the polygon chips and if the back surface of the monocrystalline substrate is polished in such a way that the surface roughness of the back surface falls within 10% of the substrate thickness, the substrate can be cleaved well along the <1-100> orientation.
As shown in
Average roughness Rz of 10 points arbitrarily chosen from the back surface of the monocrystalline substrate is desirably 10 μm or less. More desirably, the average roughness Ra along the center line of the back surface of the monocrystalline substrate is 10 μm or less. When a laser diode is manufactured by setting Ra at 10 μm or less, the laser threshold (Jth) of generating laser oscillation can be drastically lowered, as shown in
Such surface roughness corresponds with that of the back surface of the monocrystalline substrate polished so as to have a light permeability of 50% or more when a light of 500 nm in wavelength is applied.
The polishing of the back surface offers not only an advantage of the cleavage along the <11-20> and <1-100> orientations but also another advantages. One of the advantages, which is observed in the case of a laser diode, is that light reflected from the substrate has decreased. As a result, a laser oscillation mode becomes stable. In the case of an LED, since the smooth and flat cleaved plane reduces light scattering and light absorption with the aid of the polished back-surface, light output will be maintained at the same level even if a small chip is used.
The invention set forth in claim 25 is concerned with a structure of a semiconductor optoelectric device comprising compound-semiconductor layers deposited on a predetermined chemical compound substrate, both of which belongs to a different chemical family. More specifically, the invention relates to the semiconductor optoelectric device comprising a chemical compound substrate made of a III-V family such as GaAs and compound-semiconductor layers of a II-VI family, such as ZnSe, grown on the substrate. However, such a semiconductor optoelectric device has a problem with putting into practice since lattice matching is hardly attained between the substrate and the semiconductor layers.
The present inventors devised an opening extending from the back surface of a substrate to the semiconductor layer of such a semiconductor optoelectric device and then an electrode is provided through the opening so as to be contact to the semiconductor layer. As a result, they found that such a construction ensures an improvement in a luminescence efficiency and high reliability, low-voltage operation and high-temperature operation. When the opening is provided, the semiconductor layers may be partially removed.
When many defects, which are produced by the different lattice constant between the substrate and the semiconductor layers, are present in semiconductor layers near the interface with a substrate, if the opening is formed, the defects can be effectively removed. As a result, an electrode can be directly provided on a defect-free crystalline portion of the semiconductor layers. In the semiconductor optoelectric device thus constructed, since a current is not flow through the area near the interface with the substrate having many defects, the reliability will be improved and operating voltage can be reduced. Moreover, defects will not be generated by current application. If an electrode having a low heat-resistance is used, the semiconductor optoelectric device obtained will be improved in temperature characteristics besides high reliability, low operation voltage, and high operation temperature. Since an electrode is formed directly in the semiconductor layer, a current is not dispersed in the substrate. This structure of the semiconductor optoelectric device can therefore serves as a current-flow confinement structure.
The processes of manufacturing an LED according to a first embodiment of the present invention are shown in
In the first place, a 100 μm-thick substrate 11 made of sapphire is prepared, as shown in
Thereafter, on the SiO2 layer 15, a photoresist (not shown) is coated. To the photoresist is applied a parallelogram pattern having a missing portion in the vicinity of one of two vertices having the interior angle of 60° (shown in
Afterward, a photoresist (not shown) is coated, another pattern is applied having a missing portion in the vicinity of the other vertex having an interior angle of 60° diagonally positioned to the vertex mentioned above. After the photoresist is exposed to light and developed, an exposed portion of the layer 15 is removed by etching using hydrofluoric acid. As a result, the upper portion of the p-type GaN layer 14 is partially exposed, as shown in
On the LEDs 18 aligned on the substrate, scribe lines are provided by a needle-scriber along parallelogram patterns formed on the aligned LEDs 18, as shown in
Examples of the LED 18 mounting are shown in
The LED of the present invention shown in this embodiment can be cut by one/tenth of force required for conventional LED using a sapphire substrate. As a result, the substrate cleavage imposes no physical influence on LED. In other words, the degree of crystallization is not lowered, with the result that the LED will be improved in an luminescent efficiency.
Since the electrodes are formed near vertices having an interior angle of 60°, the ratio of the area occupied by the electrodes relative to the upper surface area of the p-type GaN layer 14 responsible for light-emission is low in the LED of the present invention, compared to conventional LEDs having electrodes near vertices having an interior angle of 90°. Therefore, a light output of the LED is improved.
By virtue of the advantages mentioned above, the LED of the present invention described in this embodiment is improved in brightness by 30% or more, in life by 50% or more, and in yield by 90% or more. It should be noted that as the yield of the conventional LED is about 50%.
A second embodiment of the LED according to the present invention is shown in
A third embodiment of the LED according to the present invention is shown in
In Embodiment 3, the same advantages as in Embodiment 1 were successfully obtained.
A first embodiment of the laser diode according to the present invention is shown in
As shown in
Hitherto, attempts have been made to manufacture laser diodes by using a sapphire substrate. However, the chips obtained by cutting along scribe lines were difficult to generate laser oscillation. In contrast, the laser diode of this embodiment was confirmed to generate laser oscillation at a threshold of 20 mA.
A second embodiment of the laser diode according to the present invention is shown in
As shown in
The laser diode of Embodiment 5 is improved in an optical confinement and current confinement, compared to the laser diode of Embodiment 4. As a result, it was confirmed to generate laser oscillation at a threshold 10 mA or less.
A fourth embodiment of the LED according to the present invention is shown in
As shown in
From the portion in the vicinity of one of the two vertices (an interior angle of 60°) of the parallelogram thus formed, the layers 55 and 54 are removed. The resultant exposed layer 53 is etched half in depth. On the layer 55, an AuNi electrode 56 is provided. On the layer 53, an AlTi electrode 57 is provided as shown in
The LED of this embodiment is improved over the conventional LED, in the light output of the LED by 100% or more and in the life by 100%.
A fifth embodiment of the LED according to the present invention is shown in
As shown in
On the upper surface of the layer 65, an electrode 66 is provided in an X-letter form corresponding to the diagonal lines of the parallelogram. On the lower surface of the SiC substrate 61, an AlTi electrode 67 is provided.
Since etching is not required, unlike the LED of Embodiment 6, the LED of this embodiment can be manufactured in fewer steps. The LED of this embodiment was capable of emitting light in the same amount and had the same life as that of the LED in embodiment 6.
A third embodiment of the laser diode according to the present invention is shown in
As shown in
On the upper surface of the layer 75, an AuNi electrode zone 76 is provided near the center. On the upper surface of the layer 75 excluding the portion on which an electrode 76 is provided, a SiO2 layer 78 is formed. On the other hand, on the lower surface of a SiC substrate 71, an AlTi electrode 77 is provided.
Since etching of the compound-semiconductor layers is not required, unlike the laser diodes of Embodiments 4 and 5, the LED of this embodiment is manufactured in fewer steps. The laser diode of this embodiment can generate laser oscillation at the same threshold as in Embodiment 4.
In the foregoing, we explained various embodiments of semiconductor optoelectric devices obtained by cutting the substrate along the <11-20> orientation. The aforementioned embodiments can be applied to the case where a substrate is cut along the <1-100> orientation.
Basic advantages of the present invention can be obtained by cutting a substrate in the <11-20> (or <1-100> orientation). Therefore, the shape of the semiconductor optoelectric devices is not always a parallelogram and may be an equilateral triangle, trapezoid, equilateral hexagon, and other polygons.
If the scribe line is deviated from the <11-20> orientation by an angle within ±3°, an excessively large force may not be required for cutting the substrate. As long as the deviation of the scribe line falls within the range, a substrate can be cut by such a scribing method.
If the chips are cut along scribe lines which are slightly off the <11-20> orientation, the “off-direction” can be corrected by etching the cleaved plane of the chips using phosphoric acid. As a result, the flat and vertically-cleaved planes can be obtained. Instead of the phosphoric acid etching, dry-etching may be employed using chlorine and boron chloride.
In place of the MOCVD method employed in the embodiments mentioned above, a CVD method and an MBE (molecular beam epitaxial growth) method may be employed.
The substrate preferably has a thickness of 30 to 500 μm, more preferably, 40-150 μm. This is because the substrate will be easily fractured if the thickness is less than 30 μm, and a large cleaving force will be required if the thickness is larger than 500 μm. As the result, the performance of the semiconductor optoelectric devices will be adversely affected.
Hereinbelow, we will describe embodiments of semiconductor optoelectric devices one side of which is cut along the <11-20> orientation and the other side of which is cut in the <1-100> orientation. In these cases, a rectangular semiconductor optoelectric devices are resulted.
As is shown in
After the mask of the SiO2 film is removed, a SiO2 film 87 is formed over the upper surface of the layer 82 thus exposed, the side plane of semiconductor layers 86 to 83 which are exposed by etching, and the upper surface of the layer 86. In the SiO2 film 87, opening zones are formed in parallel with the <1-100> orientation. Consequently, portions of the layers 82 and 86 are partially exposed. On the exposed layer 86 and the exposed layer 82, an Al/Ni electrode 88 and an Au/Pt/Ti electrode 89 are respectively provided.
Afterwards, the back surface of the sapphire substrate 81 is polished by diamond to form a mirror plane. The mirror plane can be prepared by wet etching using an acid (, or alkali, or dry etching such as RIE, or RIBE). The substrate having a mirror plane on the back side is then carefully cleaved into flat-plate chips of 1 mm×500 μm so as to have a length of 1 mm parallel to the opening zone, that is, in the <1-100> orientation.
The laser diode thus obtained showed a threshold of laser oscillation which is a half of that of the conventional laser diode.
A fifth embodiment of the laser diode according to the present invention is shown in
As shown in
Afterwards, the back surface of the sapphire substrate 91 is polished by diamond to form a mirror plane. To the layer 96 exposed in the opening zone, an Al/Ni electrode 98 is provided. To the mirror plane on the back side of the substrate 91, an Au/Ti electrode 99 is provided.
In the same manner as in Embodiment 9, the substrate 91 is carefully cleaved into flat-plate chips of 1 mm×500 μm so as to have a length of 1 mm parallel to the opening zone, that is, in the <1-100> orientation.
The laser diode thus obtained showed a threshold of laser oscillation which is a half of that of the conventional laser diode.
A sixth embodiment of the laser diode according to the present invention is shown in
As shown in
Again, the SiO2 film 107 is formed and then patterning is applied in the same manner as above. As a result, an opening zone is obtained along the <1-100> orientation, in which the layer 106 is partially exposed. To the exposed layers 106 and 102, an Al/Ni electrode 108 and an Au/Pt/Ti electrode 109 are respectively provided.
Afterwards, the back surface of the sapphire substrate 101 is polished along the boarder of chip patterns by diamond as shown in
The laser diode thus obtained showed a threshold current which is a half of that of the laser diode to which no back-surface polishing is applied.
A seventh embodiment of the laser diode according to the present invention is shown in
As shown in
Afterwards, the back surface of the sapphire substrate 201 is polished along the boarder of chip patterns by diamond. In this manner a mirror plane is formed. The mirror plane can be obtained by the wet etching using an acid (, or alkali, or the dry etching such as RIE, or RIBE).
Subsequently, using the SiO2 film as a mask, an opening zone 201a extending from the central back surface of the substrate to the layer 202 is formed. To the layer 206 exposed on the upper side, an Al/Ni electrode 208 is provided. To the layer 202 exposed to the bottom side by way of the opening 201a, an Al/Ti electrode 209 is provided.
The substrate is carefully cleaved into flat-plate chips of 1 mm×500 μm so as to have a length of 1 mm parallel to the opening zone, that is, in the <1-100> orientation, in the same manner as in Embodiment 9. In this case, if the chips are formed so as to have a length of 1 mm in the orientation of <11-20> the same effects can be obtained.
The laser diode thus obtained showed a threshold of laser oscillation which is a quarter of that of the conventional laser diode.
Hereinbelow, we will describe an embodiment recited in claim 25 of the present invention.
An eighth embodiment of the laser diode according to the present invention is shown in
As shown in
On the upper clad layer 304, a p-type current-blocking layer 305 (thickness: 1 μm, doping carrier concentration: 1E18 cm−3) are formed. In the layer 305 is formed an opening 305a in which the layer 304 is exposed. On the current blocking layer 305, an n-type ZnSe layer 306 (thickness: 3 μm, a doping carrier concentration: 1E18 cm−3) is formed so as to be contact with the upper clad layer 304 through the opening 305a. On the layer 306, an n-type ZnSe capping layer 307 (thickness: 500 μm, doping carrier concentration: 1E19 cm−3) is formed. Furthermore, over the entire layer 307, an n-electrode 308 is provided. The electrode 308 is formed by laying a Ti layer (10 nm), Pt (50 nm) layer, and Au layer (300 nm), sequentially.
From the bottom surface of the substrate 301 into the layer 302, a slot-form opening 309 is provided as shown in
To explain the manufacturing steps of the aforementioned structure more specifically, the laser diode is formed as follows: in the first place, to clean a surface of the substrate 301, the temperature of a wafer is raised up to about 550° C. to 650° C. for 5 minutes under a vacuum of 1E-8 Torr or less. By this process, contaminants present on the surface, such as an oxide film, can be removed. The removal of the contaminants was confirmed by the RHEED observation.
Thereafter, layers 302, 303, 304 to 305 are sequentially grown by the MBE method applied at 300° C. Nitrogen is used as a p-type dopant and chlorine as an n-type dopant. Then, a wafer is taken out from an MBE growing furnace and subjected to photolithography and etching in a bromine-series solution. Through this step, an opening 305a is formed extending from the layer 305 to the layer 304.
Afterwards, the resultant wafer is placed in the MBE growth furnace, layers 306 and 307 are formed at 250° C. After the wafer is taken out from the furnace, again, the n-electrode 308 is formed over the entire surface of the wafer. After Au is vapor-deposited onto the back surface of the GaAs substrate 301, the wafer is adhered on a glass plate by applying wax on the n-electrode 308 side. Then, the vapor-deposited Au is etched by means of photography in couple with a KI-series etching solution to prepare a mask for forming a slot-form opening 309. Using the mask, the GaAs substrate is etched by use of an etching solution containing NaOH and H2O2 in a ratio of 5 to 1. Since the etch rate to ZnSe is slow, etching stops at the ZnSe lower clad layer 302. After the layer 302 is partially etched by use of a bromine-series etching solution, CuSe is allowed to grow in an aqueous solution to form the CuSe electrode 310. Finally the Pd/Au electrode 311 is formed.
The laser diode thus constructed as shown in
As is apparent from the above results, by providing an opening extending from the back surface of the substrate to the ZnSe lower clad layer, continuous wave operation, which is difficult in the prior art, is successfully attained at room temperature. In addition, laser oscillation can be made at the temperature ensuring sufficient reliability. Actually, it is confirmed that the continuous wave operation of the laser diode for 10,000 hours or more can be made at an operation temperature of 70° C., under an operation power of 5 mW.
The sufficient reliability is attained for the reason that the opening extending from the back surface of the substrate to the semiconductor layer is provided to the semiconductor optoelectric device comprising the substrate made of a III-V family compound-semiconductor and semiconductor layers made of a II-VI family compound-semiconductor. This is because
(a) defects present in the semiconductor layers near the interface with the substrate are removed;
(b) factors affecting to degrade properties are eliminated by forming electrodes so as to be directly contact we semiconductor layers; and
(c) The generation of defects is suppressed in the semiconductor layers near the interface with the substrate, in comparison with a case where a current indirectly flows into the semiconductor layers via the substrate. Consequently, the defects are prevented from being extended into a light-emitting portion.
Since a current density is improved by virtue of a current confinement structure obtained in the semiconductor optoelectric device according to the present invention, operation can be carried out under low voltage. Furthermore, since a current does not flow into the edge surface of the semiconductor layers, degradation of the edge surface is lowered. In addition, since the presence of metal used as electrodes contributes to a good heat radiation element, the semiconductor optoelectric device can efficiently and effectively radiate heat.
A ninth embodiment of the laser diode according to the present invention is shown in
As shown in a cross-sectional view (
On the upper clad layer 405, an n-type ZnSSe current-blocking layer 406 (thickness: 1 μm, doping carrier concentration: 1E18 cm−3) is formed. In the layer 406, an opening 406a is provided in which the upper clad layer 405 is partially exposed. On the layer 406 and in the opening 406a, a p-type ZnSSe layer 407 (thickness: 3 μm, dopting carrier concentration: 1E18 cm−3) is formed so as to be contact with the layer 405. On the layer 407, a p-type ZnSSe cap layer 408 (thickness: 500 nm, doping carrier concentration: 1E19 cm−3) is formed. Further, over the entire surface of the cap layer 408, a p-electrode is provided. The p-electrode is formed by laying a Pd (50 nm) layer and an Au (300 nm) layer one on top of the other.
To the substrate 401 is provided an opening 410 of a slot form which extends from the back surface of the substrate 401 into a lower portion of the layer 403 through the layer 402. Since the opening 410 is formed, the layer 402 and the lower portion of the layer 403 are partially removed.
An etch rate to the layers 402 and 403 is higher than that to the substrate 401. As a result, the horizontal cross-sectional area of the opening 410 in the layer 402 is larger than that of the opening in the layer 401.
On the back surface of the layer 401 including the inner surface of the opening 410, an n-type electrode 411 is formed. The n-type electrode is formed by laying an In layer (10 nm) and an Au layer (300 nm) sequentially on the layer 403.
In the laser diode thus constructed, good properties were obtained in the same way as in Embodiment 13.
As is described in the above, by providing the opening such that the horizontal cross sectional area of the opening formed in the semiconductor layers contact with the substrate is larger that of the opening 410 formed in the substrate 401, electrodes can be tightly connected to the semiconductor body. For example, when element In is employed as an electrode, interior stress generated in the cooling step after the In is deposited and heated, is successfully absorbed by the larger opening of the semiconductor layers. As a result, element In tightly adheres on the surface of the semiconductor layers. On the other hand, since the In electrode layer is not deposited on the side walls of the buffer layer 402 and the lower clad layer 403 formed by etching, it is advantageous that a leak current path is not formed extending to the interface with the substrate.
In the foregoing, embodiments of laser diode recited in claim 25 have been explained referring to
Yamamoto, Masahiro, Ishikawa, Masayuki, Saito, Shinji, Nishikawa, Yukie, Fujimoto, Hidetoshi, Rennie, John, Kokubun, Yoshihiro
Patent | Priority | Assignee | Title |
Patent | Priority | Assignee | Title |
3589936, | |||
3816906, | |||
4542397, | Apr 12 1984 | Xerox Corporation | Self aligning small scale integrated circuit semiconductor chips to form large area arrays |
5006908, | Feb 13 1989 | Nippon Telegraph and Telephone Corporation | Epitaxial Wurtzite growth structure for semiconductor light-emitting device |
5122845, | Mar 01 1989 | Toyoda Gosei Co., Ltd.; Nagoya University and Research Development Corporation of Japan | Substrate for growing gallium nitride compound-semiconductor device and light emitting diode |
5341024, | Jul 17 1992 | Bell Semiconductor, LLC | Method of increasing the layout efficiency of dies on a wafer, and increasing the ratio of I/O area to active area per die |
5585648, | Feb 03 1995 | Cree, Inc | High brightness electroluminescent device, emitting in the green to ultraviolet spectrum, and method of making the same |
5587593, | Apr 20 1994 | TOYODA GOSEI CO , LTD ; Research Development Corporation of Japan | Light-emitting semiconductor device using group III nitrogen compound |
JP2291147, | |||
JP49134271, | |||
JP5166923, | |||
JP6283758, | |||
JP63249114, | |||
JP8153931, |
Executed on | Assignor | Assignee | Conveyance | Frame | Reel | Doc |
Oct 11 2011 | Kabushiki Kaisha Toshiba | (assignment on the face of the patent) | / |
Date | Maintenance Fee Events |
Date | Maintenance Schedule |
May 14 2016 | 4 years fee payment window open |
Nov 14 2016 | 6 months grace period start (w surcharge) |
May 14 2017 | patent expiry (for year 4) |
May 14 2019 | 2 years to revive unintentionally abandoned end. (for year 4) |
May 14 2020 | 8 years fee payment window open |
Nov 14 2020 | 6 months grace period start (w surcharge) |
May 14 2021 | patent expiry (for year 8) |
May 14 2023 | 2 years to revive unintentionally abandoned end. (for year 8) |
May 14 2024 | 12 years fee payment window open |
Nov 14 2024 | 6 months grace period start (w surcharge) |
May 14 2025 | patent expiry (for year 12) |
May 14 2027 | 2 years to revive unintentionally abandoned end. (for year 12) |