An external terminal of an electronic component is provided with a lead base material and a metal thin film coating a surface of the lead base material, and an average value of a crystal size index is not less than 7, which is defined based on dimensions of a crystal particle in a direction perpendicular to the lead base material surface and in a direction parallel thereto, taken on a cut surface of the metal thin film defined by a given plane cutting the metal thin film in a direction perpendicular to the lead base material surface. Such constitution provides an electronic component having an external terminal coated with a metal thin film of a simple structure constituted of Sn or a Sn-based and substantially Pb-free alloy, formed by plating on a surface of a lead base material.
|
7. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material and including at least a first layer constituted of a material substantially Pb-free and predominantly composed of tin, wherein said first layer in said metal thin film has an amorphous structure.
0. 29. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material, said metal thin film being composed only of a first layer constituted of a material substantially Pb-free and predominantly composed of tin,
wherein said first layer in said metal thin film has an amorphous structure.
0. 38. An electronic component, comprising:
an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film covering a surface of said lead base material,
wherein said metal thin film has a first layer made of a material substantially Pb-free;
wherein said first layer is made of a material predominantly composed of tin; and
wherein said first layer in said metal thin film has an amorphous structure.
0. 24. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material and including a first layer constituted of a material substantially Pb-free and predominantly composed of tin,
wherein said lead base material comprises a plated layer underlying said first layer on which said first layer is formed, and
wherein said first layer in said metal thin film has an amorphous structure.
5. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material and including at least a first layer constituted of a material substantially Pb-free and predominantly composed of tin, wherein said first layer is formed by plating, and a total extended length of a crystal particle boundary of said first layer is not more than 300 μm per 1000 μm2 of observation area, on a cut surface parallel to a surface of said lead base material.
0. 28. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material, said metal thin film being composed only of a first layer constituted of a material substantially Pb-free and predominantly composed of tin,
wherein said first layer is formed by plating, and a total extended length of a crystal particle boundary of said first layer is not more than 300 μm per 1000 μm2 of observation area, on a cut surface parallel to a surface of said lead base material.
0. 37. An electronic component, comprising:
an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film covering a surface of said lead base material,
wherein said metal thin film has a first layer made of a material substantially Pb-free;
wherein said first layer is made of a material predominantly composed of tin;
wherein said first layer is formed by plating;
wherein a total extended length of a crystal particle boundary of said first layer is less than or equal to 300 μm per 1000 μm2 of observation area; and
wherein said observation area is a cut surface parallel to said surface of said lead base material.
0. 23. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material and including a first layer constituted of a material substantially Pb-free and predominantly composed of tin,
wherein said lead base material comprises a plated layer underlying said first layer on which said first layer is formed, and
wherein said first layer is formed by plating, and a total extended length of a crystal particle boundary of said first layer is not more than 300 μm per 1000 μm2 of observation area, on a cut surface parallel to a surface of said lead base material.
0. 19. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material and including a first layer constituted of a material substantially Pb-free and predominantly composed of tin,
wherein said first layer is formed by plating, and a total extended length of a crystal particle boundary of said first layer is not more than 300 μm per 1000 μm2 of observation area, on a cut surface parallel to a surface of said lead base material, and
wherein said first layer is composed of a crystal particle arranged in a single layer on said surface of said lead base material.
0. 33. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material and including a first layer constituted of a material substantially Pb-free and predominantly composed of tin,
wherein said first layer is formed by plating, and a total extended length of a crystal particle boundary of said first layer is not more than 300 μm per 1000 μm2 of observation area, on a cut surface parallel to a surface of said lead base material, and
wherein said first layer is composed of a plurality of columnar crystal particles arranged in a single layer on said surface of said lead base material.
3. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material and including at least a first layer constituted of a material substantially Pb-free and predominantly composed of tin,
wherein an average value of Xh/Xv is not less than 4, where Xv and Xh respectively represent dimensions of a crystal particle constituting said first layer in a direction perpendicular to said lead base material surface and in a direction parallel thereto, taken on a cut surface of said first layer defined by a given plane cutting said first layer in a direction perpendicular to said lead base material surface.
0. 27. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material, said metal thin film being composed only of a first layer constituted of a material substantially Pb-free and predominantly composed of tin,
wherein an average value of Xh/Xv is not less than 4, where Xv and Xh respectively represent dimensions of a crystal particle constituting said first layer in a direction perpendicular to said lead base material surface and in a direction parallel thereto, taken on a cut surface of said first layer defined by a given plane cutting said first layer in a direction perpendicular to said lead base material surface.
1. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material and including at least a first layer constituted of a material substantially Pb-free and predominantly composed of tin,
wherein an average value of a crystal size index is not less than 7 when said crystal size index is defined as (a+b)/2, where a and b respectively represent dimensions in μm of a crystal particle constituting said first layer in a direction perpendicular to said lead base material surface and in a direction parallel thereto, taken on a cut surface of said first layer defined by a given plane cutting said first layer in a direction perpendicular to said lead base material surface.
0. 20. A method of manufacturing an electronic component comprising an external terminal, including a lead base material constituted of a predetermined metal material and a metal thin film coating a surface of said lead base material, said metal thin film including a first layer constituted of a material substantially Pb-free and predominantly composed of tin, said first layer being composed of a plurality of crystal particles arranged in a single layer on said surface of said lead base material, and said first layer being formed by an electrolytic plating process,
wherein said electrolytic plating process for forming said first layer includes an initial plating step of supplying a current having a current density not greater than 1 A/dm2 during an initial stage of a predetermined duration of time.
0. 34. A method of manufacturing an electronic component comprising an external terminal, including a lead base material constituted of a predetermined metal material and a metal thin film coating a surface of said lead base material, said metal thin film including a first layer constituted of a material substantially Pb-free and predominantly composed of tin, said first layer being composed of a plurality of columnar crystal particles arranged in a single layer on said surface of said lead base material, and said first layer being formed by an electrolytic plating process,
wherein said electrolytic plating process for forming said first layer includes an initial plating step of supplying a current having a current density not greater than 1 A/dm2 during an initial stage of a predetermined duration of time.
0. 42. A method of manufacturing an electronic component comprising an external terminal, including a lead base material constituted of a predetermined metal material and a metal thin film covering a surface of said lead base material, said metal thin film having a first layer made of a material substantially Pb-free and made of a material predominantly composed of tin, said first layer is composed of a plurality of crystal particles arranged in a single layer on said surface of said lead base material, and said first layer being formed by an electrolytic plating process,
wherein said electrolytic plating process for forming said first layer includes an initial plating step of supplying a current having a current density less than or equal to 1 A/dm2 during an initial stage of a predetermined duration of time.
0. 30. A method of manufacturing an electronic component comprising an external terminal, including a lead base material constituted of a predetermined metal material and a metal thin film coating a surface of said lead base material, said metal thin film being composed only of a first layer constituted of a material substantially Pb-free and predominantly composed of tin, said first layer being composed of a plurality of crystal particles arranged in a single layer on said surface of said lead base material, and said first layer being formed by an electrolytic plating process,
wherein said electrolytic plating process for forming said first layer includes an initial plating step of supplying a current having a current density not greater than 1 A/dm2 during an initial stage of a predetermined duration of time.
0. 26. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material, said metal thin film being composed only of a first layer constituted of a material substantially Pb-free and predominantly composed of tin,
wherein an average value of a crystal size index is not less than 7 when said crystal size index is defined as (a+b)/2, where a and b respectively represent dimensions in μm of a crystal particle constituting said first layer in a direction perpendicular to said lead base material surface and in a direction parallel thereto, taken on a cut surface of said first layer defined by a given plane cutting said first layer in a direction perpendicular to said lead base material surface.
0. 41. An electronic component, comprising:
an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film covering a surface of said lead base material,
wherein said metal thin film has a first layer made of a material substantially Pb-free;
wherein said first layer is made of a material predominantly composed of tin;
wherein said first layer is formed by plating;
wherein a total extended length of a crystal particle boundary of said first layer is less than or equal to 300 μm per 1000 μm2 of observation area;
wherein said observation area is a cut surface parallel to said surface of said lead base material; and
wherein said first layer is composed of a plurality of crystal particles arranged in a single layer on said surface of said lead base material.
0. 22. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material and including a first layer constituted of a material substantially Pb-free and predominantly composed of tin,
wherein said lead base material comprises a plated layer underlying said first layer on which said first layer is formed, and
wherein an average value of Xh/Xv is not less than 4, where Xv and Xh respectively represent dimensions of a crystal particle constituting said first layer in a direction perpendicular to said lead base material surface and in a direction parallel thereto, taken on a cut surface of said first layer defined by a given plane cutting said first layer in a direction perpendicular to said lead base material surface.
0. 18. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material and including a first layer constituted of a material substantially Pb-free and predominantly composed of tin,
wherein an average value of Xh/Xv is not less than 4, where Xv and Xh respectively represent dimensions of a crystal particle constituting said first layer in a direction perpendicular to said lead base material surface and in a direction parallel thereto, taken on a cut surface of said first layer defined by a given plane cutting said first layer in a direction perpendicular to said lead base material surface, and
wherein said first layer is composed of a plurality of the crystal particle arranged in a single layer on said surface of said lead base material.
0. 21. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material and including a first layer constituted of a material substantially Pb-free and predominantly composed of tin,
wherein said lead base material comprises a plated layer underlying said first layer on which said first layer is formed, and
wherein an average value of a crystal size index is not less than 7 when said crystal size index is defined as (a+b)/2, where a and b respectively represent dimensions in μm of a crystal particle constituting said first layer in a direction perpendicular to said lead base material surface and in a direction parallel thereto, taken on a cut surface of said first layer defined by a given plane cutting said first layer in a direction perpendicular to said lead base material surface.
0. 25. A method of manufacturing an electronic component comprising an external terminal, including a lead base material constituted of a predetermined metal material and a metal thin film coating a surface of said lead base material, said metal thin film including a first layer constituted of a material substantially Pb-free and predominantly composed of tin, said first layer being composed of a plurality of crystal particles arranged in a single layer on said surface of said lead base material, and said first layer being formed by an electrolytic plating process,
wherein said lead base material comprises a plated layer underlying said first layer on which said first layer is formed, and
wherein said electrolytic plating process for forming said first layer includes an initial plating step of supplying a current having a current density not greater than 1 A/dm2 during an initial stage of a predetermined duration of time.
0. 17. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material and including a first layer constituted of a material substantially Pb-free and predominantly composed of tin,
wherein an average value of a crystal size index is not less than 7 when said crystal size index is defined as (a+b)/2, where a and b respectively represent dimensions in μm of a crystal particle constituting said first layer in a direction perpendicular to said lead base material surface and in a direction parallel thereto, taken on a cut surface of said first layer defined by a given plane cutting said first layer in a direction perpendicular to said lead base material surface, and
wherein said first layer is composed of a plurality of crystal particles arranged in a single layer on said surface of said lead base material.
0. 32. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material and including a first layer constituted of a material substantially Pb-free and predominantly composed of tin,
wherein an average value of Xh/Xv is not less than 4, where Xv and Xh respectively represent dimensions of a crystal particle constituting said first layer in a direction perpendicular to said lead base material surface and in a direction parallel thereto, taken on a cut surface of said first layer defined by a given plane cutting said first layer in a direction perpendicular to said lead base material surface,
wherein said crystal particle is comprised of a columnar structure, and
wherein said first layer is composed of a plurality of columnar crystal particles arranged in a single layer on said surface of said lead base material.
0. 36. An electronic component, comprising:
an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film covering a surface of said lead base material,
wherein said metal thin film has a first layer made of a material substantially Pb-free;
wherein said first layer is made of a material predominantly composed of tin;
wherein an average value of Xh/Xv of a crystal particle constituting said first layer is greater than or equal to 4,
wherein Xv is a size in a first direction perpendicular to said surface of said lead base material, in said crystal particle seen in a cross section of said first layer;
wherein Xh is a size in a second direction parallel to said surface of said lead base material, in said crystal particle seen in said cross section of said first layer; and
wherein said cross section of said first layer is a given surface cutting said first layer in said first direction.
0. 31. An electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of said lead base material and including a first layer constituted of a material substantially Pb-free and predominantly composed of tin,
wherein an average value of a crystal size index is not less than 7 when said crystal size index is defined as (a+b)/2, where a and b respectively represent dimensions in μm of a crystal particle constituting said first layer in a direction perpendicular to said lead base material surface and in a direction parallel thereto, taken on a cut surface of said first layer defined by a given plane cutting said first layer in a direction perpendicular to said lead base material surface,
wherein said crystal particle is comprised of a columnar structure, and
wherein said first layer is composed of a plurality of columnar crystal particles arranged in a single layer on said surface of said lead base material.
0. 35. An electronic component, comprising:
an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film covering a surface of said lead base material,
wherein said metal thin film has a first layer made of a material substantially Pb-free;
wherein said first layer is made of a material predominantly composed of tin;
wherein an average value of a crystal size index of a crystal particle constituting said first layer is greater than or equal to 7 μm,
wherein said crystal size index defines a value obtained by dividing a sum of a size in a first direction and a size in a second direction by 2, in said crystal particle seen in a cross section of said first layer;
wherein said cross section of said first layer is a given surface cutting said first layer in said first direction;
wherein said first direction is a direction, which is perpendicular to said surface of said lead base material; and
wherein said second direction is a direction, which is parallel to said surface of said lead base material.
0. 40. An electronic component, comprising:
an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film covering a surface of said lead base material,
wherein said metal thin film has a first layer made of a material substantially Pb-free;
wherein said first layer is made of a material predominantly composed of tin;
wherein an average value of Xh/Xv of a crystal particle constituting said first layer is greater than or equal to 4,
wherein Xv is a size in a first direction perpendicular to said surface of said lead base material, in said crystal particle seen in a cross section of said first layer;
wherein Xh is a size in a second direction parallel to said surface of said lead base material, in said crystal particle seen in said cross section of said first layer;
wherein said cross section of said first layer is a given surface cutting said first layer in said first direction; and
wherein said first layer is composed of a plurality of crystal particles arranged in a single layer on said surface of said lead base material.
0. 44. An electronic component, comprising:
an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film covering a surface of said lead base material,
wherein said metal thin film has a first layer made of a material substantially Pb-free;
wherein said first layer is made of a material predominantly composed of tin;
wherein an average value of Xh/Xv of a crystal particle constituting said first layer is greater than or equal to 4,
wherein Xv is a size in a first direction perpendicular to said surface of said lead base material, in said crystal particle seen in a cross section of said first layer;
wherein Xh is a size in a second direction parallel to said surface of said lead base material, in said crystal particle seen in said cross section of said first layer;
wherein said cross section of said first layer is a given surface cutting said first layer in said first direction;
wherein said first layer is composed of a plurality of crystal particles arranged in a single layer on said surface of said lead base material; and
wherein said first layer is the uppermost layer to be contacted with a solder.
0. 39. An electronic component, comprising:
an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film covering a surface of said lead base material,
wherein said metal thin film has a first layer made of a material substantially Pb-free;
wherein said first layer is made of a material predominantly composed of tin;
wherein an average value of a crystal size index of a crystal particle constituting said first layer is greater than or equal to 7 μm,
wherein said crystal size index defines a value obtained by dividing a sum of a size in a first direction and a size in a second direction by 2, in said crystal particle seen in a cross section of said first layer;
wherein said cross section of said first layer is a given surface cutting said first layer in said first direction;
wherein said first direction is a direction, which is perpendicular to said surface of said lead base material;
wherein said second direction is a direction, which is parallel to said surface of said lead base material; and
wherein said first layer is composed of a plurality of crystal particles arranged in a single layer on said surface of said lead base material.
0. 46. An electronic component, comprising:
an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film covering a surface of said lead base material,
wherein said metal thin film has a first layer made of a material substantially Pb-free;
wherein said first layer is made of a material predominantly composed of tin;
wherein an average value of Xh/Xv of a crystal particle constituting said first layer is greater than or equal to 4,
wherein Xv is a size in a first direction perpendicular to said surface of said lead base material, in said crystal particle seen in a cross section of said first layer;
wherein Xh is a size in a second direction parallel to said surface of said lead base material, in said crystal particle seen in said cross section of said first layer;
wherein said cross section of said first layer is a given surface cutting said first layer in said first direction;
wherein said first layer is composed of a plurality of crystal particles arranged in a single layer on said surface of said lead base material; and
wherein said average value of said crystal size index is obtained by continuously arranged crystal particles more than or equal to 5 particles.
0. 43. An electronic component, comprising:
an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film covering a surface of said lead base material,
wherein said metal thin film has a first layer made of a material substantially Pb-free;
wherein said first layer is made of a material predominantly composed of tin;
wherein an average value of a crystal size index of a crystal particle constituting said first layer is greater than or equal to 7 μm,
wherein said crystal size index defines a value obtained by dividing a sum of a size in a first direction and a size in a second direction by 2, in said crystal particle seen in a cross section of said first layer;
wherein said cross section of said first layer is a given surface cutting said first layer in said first direction;
wherein said first direction is a direction, which is perpendicular to said surface of said lead base material;
wherein said second direction is a direction, which is parallel to said surface of said lead base material;
wherein said first layer is composed of a plurality of crystal particles arranged in a single layer on said surface of said lead base material; and
wherein said first layer is the uppermost layer to be contacted with a solder.
0. 45. An electronic component, comprising:
an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film covering a surface of said lead base material,
wherein said metal thin film has a first layer made of a material substantially Pb-free;
wherein said first layer is made of a material predominantly composed of tin;
wherein an average value of a crystal size index of a crystal particle constituting said first layer is greater than or equal to 7 μm,
wherein said crystal size index defines a value obtained by dividing a sum of a size in a first direction and a size in a second direction by 2, in said crystal particle seen in a cross section of said first layer;
wherein said cross section of said first layer is a given surface cutting said first layer in said first direction;
wherein said first direction is a direction, which is perpendicular to said surface of said lead base material;
wherein said second direction is a direction, which is parallel to said surface of said lead base material;
wherein said first layer is composed of a plurality of crystal particles arranged in a single layer on said surface of said lead base material; and
wherein said average value of said crystal size index is obtained by continuously arranged crystal particles more than or equal to 5 particles.
2. The electronic component as recited in
4. The electronic component as recited in
6. The electronic component as recited in
8. The electronic component as recited in
9. The electronic component as recited in
10. The electronic component as recited in
11. The electronic component as recited in
12. The electronic component as recited in
13. The electronic component as recited in
0. 14. A method of manufacturing an electronic component comprising an external terminal, including a lead base material constituted of a predetermined metal material and a metal thin film coating a surface of said lead base material, said metal thin film including at least a first layer constituted of a material substantially Pb-free and predominantly composed of tin, said first layer being formed by an electrolytic plating process,
wherein said electrolytic plating process for forming said first layer includes an initial plating step of supplying a current having a current density not greater than 1 A/dm2 during an initial stage of a predetermined duration of time.
0. 15. The method as recited in
wherein said predetermined temperature in said heat treatment step is not more than a melting point of said first layer.
0. 16. The method as recited in
wherein said heat treatment step includes melting step of heating said first layer at a temperature equal to or higher than a melting point thereof for a predetermined time and gradual cooling step of gradually cooling said first layer after said melting step, and
wherein a cooling rate in said gradual cooling step is not more than 3 degree centigrade per second.
0. 47. The electronic component as recited in claim 17, wherein a thickness of said single layer is defined by a thickness of each of said crystal particles.
0. 48. The electronic component as recited in claim 18, wherein a thickness of said single layer is defined by a thickness of each of said crystal particles.
0. 49. The electronic component as recited in claim 19, wherein a thickness of said single layer is defined by a thickness of each of said crystal particles.
0. 50. The method as recited in claim 20, wherein a thickness of said single layer is defined by a thickness of each of said crystal particles.
0. 51. The electronic component as recited in claim 31, wherein a thickness of said single layer is defined by a thickness of each of said crystal particles.
0. 52. The electronic component as recited in claim 32, wherein a thickness of said single layer is defined by a thickness of each of said crystal particles.
0. 53. The electronic component as recited in claim 33, wherein a thickness of said single layer is defined by a thickness of each of said crystal particles.
0. 54. The method as recited in claim 34, wherein a thickness of said single layer is defined by a thickness of each of said crystal particles.
0. 55. The electronic component as recited in claim 39, wherein a thickness of said single layer is defined by a thickness of each of said crystal particles.
0. 56. The electronic component as recited in claim 40, wherein a thickness of said single layer is defined by a thickness of each of said crystal particles.
0. 57. The electronic component as recited in claim 41, wherein a thickness of said single layer is defined by a thickness of each of said crystal particles.
0. 58. The method as recited in claim 42, wherein a thickness of said single layer is defined by a thickness of each of said crystal particles.
0. 59. The electronic component as recited in claim 43, wherein a thickness of said single layer is defined by a thickness of each of said crystal particles.
0. 60. The electronic component as recited in claim 44, wherein a thickness of said single layer is defined by a thickness of each of said crystal particles.
0. 61. The electronic component as recited in claim 45, wherein a thickness of said single layer is defined by a thickness of each of said crystal particles.
0. 62. The electronic component as recited in claim 46, wherein a thickness of said single layer is defined by a thickness of each of said crystal particles.
|
This application is based on Japanese patent application. No.2003-319789, the content of which is incorporated hereinto by reference.
1. Field of the Invention
The present invention relates to an electronic component, and more specifically to an electronic component provided with an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of the lead base material and including at least a first layer constituted of a material substantially Pb-free and predominantly composed of tin, and to a method of manufacturing such electronic component.
2. Description of the Related Art
When implementing an electronic component such as an integrated circuit (hereinafter abbreviated as “IC”), a transistor, a resistance, a condenser and so forth on a circuit board or the like, an external terminal of the electronic component is electrically connected to a conductive electrode of the circuit board, via a low-melting solder. In this process, the external terminal of the electronic component has to have sufficient solder wettability, so as to secure desired connection reliability between the electronic component and the circuit board. For this purpose, a surface of the lead base material of the external terminal is provided with a metal thin film constituted of Sn or an Sn-based alloy mainly composed of Sn, formed in advance by a surface finishing process such as electrolytic plating.
Referring to the low-melting solder, an Sn—Pb alloy mainly containing tin (hereinafter designated by “Sn”) and an additive of lead (hereinafter designated by “Pb”) has been popularly used. Here, Sn is the main ingredient of the alloy and serves as an adhesive. Also Pb constitutes, together with Sn, a group of metals that can form a low-melting alloy, and serves to lower a melting point of the alloy and to enhance an adhesion strength thereof. Accordingly, an Sn—Pb alloy has been widely utilized in implementing an electronic component on a circuit board, because of the advantage that a melting point can be easily controlled by adjusting a ratio of those two ingredients, and that these metals are inexpensive.
Referring also to the metal thin film to be formed on a surface of a lead base material of an external terminal included in an electronic component, the metal thin film formed by plating an Sn—Pb alloy has been popularly employed. It is because of the excellent wettability with a low-melting Sn—Pb solder as well as of the inexpensive cost that an Sn—Pb alloy has been preferably employed for plating to form a metal thin film on a surface of a lead base material for an external terminal.
However, the Pb ingredient in the Sn—Pb alloy is harmful against a human body, and besides discarding a used electronic device incurs environmental pollution. Accordingly, Pb is not desirable from an environmental viewpoint. Lately, therefore, a so-called Sn-based and substantially Pb-free alloy, which excludes Pb as an ingredient for constituting a low-melting solder, has come to be popularly used when implementing an electronic component on a circuit board. In correspondence with such trend, on the part of the lead base material of the electronic component also, a Sn-based and substantially Pb (lead) free alloy has come to be widely used for plating a surface thereof, to form a metal thin film.
Here, “substantially Pb-free” means a concentration of Pb of less than 1 wt %, preferably 0.1 wt %. On the other hand, “Pb contained material” contains Pb of 5 to 10 wt %.
When plating a Sn-based and substantially Pb-free alloy on a surface of a lead base material to form a metal thin film, the key issue is maintaining a desired low-melting solder wettabillty and securing desired connection reliability, whichever metal may be adopted as an additive to Sn.
However in case where a Sn-based and substantially Pb-free alloy is plated on a surface of a lead base material to form a metal thin film, a fine metal whisker are prone to appear on a surface of an external terminal under a circumstance of practical use of the electronic component, unlike a case of forming a metal thin film by an Sn—Pb alloy. Such whisker may cause a short circuit between the external terminals, and the tendency becomes higher especially in an electronic component such as an IC in which a multitude of external terminals are led out at fine intervals from a peripheral portion of the package body. Accordingly, restraining emergence of a whisker constitutes a critical issue when forming an outer coating of a metal thin film by plating Sn or a Sn-based and substantially Pb-free alloy on a surface of a lead base material of external terminals disposed in an electronic component.
Referring to this issue, models of whisker emergence mechanism, as well as methods of restraining whisker emergence for the respective models thus far proposed will be described below.
For example, JP-A Laid Open No.2002-246208 refers to a whisker that emerges on an external terminal of a variable resistor. More specifically, the external terminal is provided with a first plated layer consisting of copper (hereinafter designated by “Cu”) formed on a surface thereof, and a second plated layer consisting of Sn of 1 to 4 μm in particle diameter, formed on the first plated layer. The cited document states that a whisker emerges after long hours of use of such variable resistor, thereby causing the variable resistor to render an unstable output.
Also, JP-A Laid Open No.2001-110666 discloses providing an Sn-plated layer consisting of fine particles not larger than 1 μm in average crystal particle diameter, on an outermost layer of an external electrode consisting of a plurality of layers, formed on a base material surface of an electronic component. More specifically, the external electrode includes a nickel (hereinafter designated by “Ni”) plated layer formed on a thick film electrode located in contact with both end portions of a ceramic base material, and an Sn-plated layer being formed on the Ni-plated layer and constituting an outermost layer of the external electrode. The Sn-plated layer is formed by electrolytic plating of Sn, such that an average crystal particle diameter becomes 1 μm or less. Such fine structure can restrain whisker emergence on the Sn-plated layer, even under a circumstance of a temperature cycle alternately repeating a high temperature and a low temperature.
Also, Ryusuke Kawanaka et al., “Role of Lead in growth suppression and growth mechanism of Tin-proper whisker”, Japanese Association for Crystal Growth, Vol. 10, No.2, pp. 148-156, Dec. 15, 1983 reports different emergence mechanisms of a whisker.
However, the method of fusing the plated particles in the Sn-plated layer according to the JP-A Laid Open No.2002-246208 includes, for example, placing internal and external terminals in a first furnace provided with an FIR heater for approx. 30 seconds for preheating up to 220 degree centigrade, and passing them through a second heating furnace provided with a burner in approx. one second, for heating up to approx. 900 degree centigrade. Treating at such a high temperature a semiconductor component provided with a resin material, which is less resistant against heat than a metal, at a position close to a terminal incurs heat degeneration of the resin component (melting, carbonization, degradation, oxidation and so on), deterioration of materials of each configuration, mechanical damage by vaporizing expansion of water in the package, irregular growth of the interfacial metal alloy layer to cause degradation in reliability of performance of the component.
Also, the JP-A Laid Open No.2001-110666 proposes forming an Sn-plated layer consisting of fine crystal particles of not larger than 1 μm in average diameter, to thereby restrain whisker emergence under a temperature cycle. However, some data have shown a contradictory result that a whisker is more prone to appear when a crystal particle diameter of the Sn-plated layer is smaller (For example, JP-A Laid Open No.1990-170996).
According to studies on the whisker emergence mechanism so far achieved, including the foregoing JP-A Laid Open No.2002-246208, JP-A Laid Open No.2001-110666. JP-A Laid Open No.1990-170996, and Ryusuke Kawanaka et al., “Role of Lead in growth suppression and growth mechanism of Tin-proper whisker”, Japanese Crystal Growth Society, Vol. 10, No.2, pp. 148-156, Dec. 15, 1983, it is generally considered that formation of an interface reaction layer and a surface oxide layer, internal compression stress in a plated layer, recrystallization, defect displacement, unmatched thermal expansion coefficient between a base material and a plated layer, a compression stress generated by a mechanical processing and so forth are promoting factors for the whisker growth.
Nevertheless, from the viewpoint of environmental protection, it is necessary to promote the use of a substantially Pb-free material for plating an outer surface of an external terminal of an electronic component. For this purpose, it is essential to restrain the whisker emergence under a circumstance of practical use, effectively and at a low cost.
As a result of intensive studies to solve the foregoing problem, the inventor has discovered a method of restraining whisker growth, based on newly established findings as described below.
Firstly, samples were prepared which included an external terminal constituted of a lead base material made of a nickel alloy containing 42% of iron (hereinafter designated by “Fe-42% Ni-alloy”) or of a metal material mainly containing copper. In the sample an outer surface of the lead base materials was plated with Sn or a Sn-based and substantially Pb-free alloy under different plating conditions, so as to form a metal thin film. These samples were subjected to a temperature cycle test and a high temperature and high humidity test etc. to examine whether or not a whisker would emerge on the metal thin film. Thereafter, the samples on which a whisker 20 has emerged on the metal thin film have been picked up, for close observation of the whisker 20 through a secondary electron microscope. As a result, it has been proven that a pattern appropriate to a coating deposited by plating remains at a tip portion of the whisker 20, and that besides an entirety of the whisker 20 is constituted of a single crystal.
This leads to an assumption that the whisker 20 is not a crystal that has newly emerged after forming the metal thin film 2, but a crystal which one of the crystal particles originally formed in the plating deposition process where the metal thin film 2 has been formed has grown in a specific direction. Accordingly, it has been concluded that a diameter of the whisker 20 has a correlation with a size of a crystal particle 3 that is considered to be the origin of the whisker growth, included in the metal thin film 2.
Also, through the observation of a process of the whisker growth, it has been assumed that Sn atoms constituting the whisker have gathered from an extensive area in the metal thin film 2 to thereby build the whisker, since a void or a variation (reduction) in thickness of the metal thin film is scarcely seen in the proximity of the position where the whisker has grown, despite a large number of Sn atoms have obviously transferred.
Further, based on these findings, it has been concluded that the emergence and growth of the whisker 20 largely depends on a size of the crystal particle 3 constituting the metal thin film 2. More specifically, with respect to an energy for the emergence and growth of the whisker, such assumption has been made that a greater driving energy is required in order that a thicker whisker emerges from a larger crystal particle, and that a thicker whisker grows shorter by an equal amount of driving energy or supply of Sn atoms.
Then the observation was carried out on the assumption that the whisker growth rate is determined by a supply amount of Sn atoms from a surrounding area, and that the transference of Sn atoms takes place according to a diffusion mechanism of Sn. And based on a characteristic of a whisker that it may rather emerge more prominently under a low temperature, an intergranular diffusion, which predominantly takes place under a low temperature, has been focused on. As a result, an assumption has been reached that a metal thin film constituted of larger crystal particles, and having a smaller crystal particle boundary in a unit volume, provides a slower whisker growth rate.
Also, based on the foregoing assumption that a whisker is nothing but one of the crystal particles formed in advance during the plating deposition process, which has grown in a specific direction, it has been concluded that a metal thin film of a amorphous structure, which does not include a crystal particle that can grow as a whisker, can naturally inhibit the whisker emergence.
Further, the prepared samples were classified into two groups in consideration of the foregoing conclusions. A first sample group consisted of a plurality of untested samples extracted out of the lots including the samples on which a whisker has emerged, while a second sample group consisted of a plurality of untested samples extracted out of the lots including the samples on which a whisker has not emerged. As a result of close observation of a metal thin film structure of these two groups, especially focusing on a crystal particle size, the following facts have been proven.
(1) A whisker has not emerged on a sample having large crystal particles in a plane parallel to a lead base material surface, on a metal thin film surface.
(2) A whisker has not emerged either on a sample having smaller crystal particles in a plane parallel to a lead base material surface, on a metal thin film surface, provided that the metal thin film is thicker.
(3) Upon evaluating a size of crystal particles utilizing a crystal size index, the definition of which will be subsequently described, an average crystal size index of the first sample group has proved to be 3 to 6, while that of the second sample group has proved to be 8 to 15.
The present invention has been conceived based on the foregoing findings, as described hereunder.
According to the present invention, there is provided an electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of the lead base material, wherein the metal thin film includes at least a first layer constituted of a material substantially Pb-free and predominantly composed of tin, and an average value of a crystal size index is not less than 7, when the crystal size index is defined as (a+b)/2, where a and b respectively represent dimensions in μm of a crystal particle constituting the first layer in a direction perpendicular to the lead base material surface and in a direction parallel thereto, taken on a cut surface of the first layer defined by a given plane cutting the first layer in a direction perpendicular to the lead base material surface.
Also, according to the present invention there is provided an electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of the lead base material, wherein the metal thin film includes at least a first layer constituted of a material substantially Pb-free and predominantly composed of tin, and an average value of Xh/Xv is not less than 4, where Xv and Xh respectively represent dimensions of a crystal particle constituting the first layer in a direction perpendicular to the lead base material surface and in a direction parallel thereto, taken on a cut surface of the first layer defined by a given plane cutting the first layer in a direction perpendicular to the lead base material surface.
Also, according to the present invention there is provided an electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of the lead base material, wherein the metal thin film includes at least a first layer constituted of a material substantially Pb-free and predominantly composed of tin, and the first layer is formed by plating.
Also, according to the present invention there is provided an electronic component comprising an external terminal including a lead base material constituted of a predetermined metal material, and a metal thin film coating a surface of the lead base material, wherein the metal thin film includes at least a first layer constituted of a material substantially Pb-free and predominantly composed of tin, and the first layer has a amorphous structure.
Such constitution permits providing a sufficiently small crystal particle boundary in a unit volume of the metal thin film, for example by increasing a diameter of the crystal particles constituting the metal thin film, when forming the metal thin film mainly containing Sn on a surface of a lead base material of an external terminal included in an electronic component. Accordingly, transference of Sn atoms, which is the cause of the whisker emergence and growth in the metal thin film, is restrained. Besides, even though a whisker should emerge, a greater amount of Sn atoms per unit length would be necessary for the whisker growth, since the whisker has a large diameter. As a result, the whisker emergence in the metal thin film is restrained, and even though the whisker should emerge, the subsequent whisker growth is restrained so that the whisker can only grow short.
The present invention prevents an accidental short circuit caused by the whisker emergence and growth, thereby permitting high-density implementation of electronic components, further resulting in upgraded reliability of the implemented components.
Now referring to the accompanying drawings, embodiments of the present invention will be described hereunder.
Firstly, the crystal size index will be described as this is one of the principal features of the present invention. Generally, a particle diameter is used to define a size of a crystal particle. However, since a crystal particle is of an irregular three-dimensional shape, it is difficult to measure a size exactly, and besides the interpretation is ambiguous. Accordingly, the inventor has established a definition of the “crystal size index” through an undermentioned process, in order to quantitatively define a size of a crystal particle constituting a metal thin film.
The crystal size index is defined as a sum of (a+b) divided by 2, where a and b respectively represent a dimension of a crystal particle in μm in a direction perpendicular to a surface of the lead base material 1 (hereinafter simply referred to as “base material surface”) and in directions parallel to the base material surface, taken on a cut surface of the metal thin film 2 defined by a (given) plane 40 cutting the metal thin film 2 in a direction perpendicular to the base material surface. As shown in
An average crystal size index is to be worked out by first observing and measuring a crystal size index of m pieces (m is an integer not fewer than 2) of crystal particles continuously aligned on a given cut surface, and then dividing a sum of the crystal size index values by m, in other words by calculating an average value of the crystal size index of the crystal particles exposed on the cut-surface. Arithmetically, the average crystal size index is obtained by the following formula, when a crystal size index of an nth crystal particle (n is an integer that satisfies 1≦n≦m) is designated by (an+bn)/2:
Now an electronic component according to a first embodiment of the present invention will be described hereunder.
In this embodiment, a resin-sealed (plastic-packaged) integral circuit (referred to “IC”) is taken up as an example of the electronic component without limiting thereto, and description will be made on an external terminal of such IC.
Referring to
According to this embodiment, the external terminal 5 of the IC 10 is provided with the metal thin film 2 which only includes the first layer, formed by plating on a surface of the lead base material 1 constituted of for example an Fe-42% Ni-alloy. The metal thin film 2 of this embodiment is constituted of an Sn—Bi alloy layer predominantly containing Sn with approx. 1.5 wt % of Bi as an additive metal and substantially Pb-free. Practically, an acidic plating solution of a composition as shown in Table 1 was selected for use as a plating bath, among the commercially available acidic plating solutions, and plating was performed with a plating current profile shown in
TABLE 1
Component
Concentration
Sn2+
18
g/L
Bi3+
0.6
g/L
Free acid
1.0N
Additive for medium-speed plating
22
mL/L
Employing a plating current profile as shown in
Also, a greater whisker restraining effect can be achieved by further increasing the crystal particle size through a subsequent heat treatment of a metal thin film constituted of large crystal particles formed according to the first embodiment. Such heat treatment may be performed in two ways; heating at a temperature equal to or lower than a melting point of the metal thin film for a long time so that the crystal particles gradually grow, or once heating to the melting point or higher of the metal thin film and then slowly solidifying the metal thin film.
Now, a whisker emergence status on the IC 10 of this embodiment, observed during accelerated tests including a high temperature and high humidity test and a temperature cycle test, will be described.
Further, this embodiment may be modified such that an average value of Xh/Xv (Xv and Xh are values in the same unit) becomes not less than 4, where Xv and Xh respectively represent dimensions of a crystal particle constituting the first layer in a direction perpendicular to a surface of the lead base material 1 and in a direction parallel thereto, taken on a cut surface of the first layer defined by a given plane cutting the first layer in a direction perpendicular to the surface of the lead base material 1. Alternatively, the metal thin film 2 may be constituted such that a total extended length of the crystal particle boundary of the first layer does not exceed 300 μm per 1000 μm2 of observation area, on a cut surface of the first layer parallel to a surface of the lead base material 1. In case where the first layer has a structure that satisfies either of these conditions, the whisker emergence and growth on the metal thin film 2 can be similarly restrained to the first embodiment.
An electronic component according to a second embodiment of the present invention will now be described hereunder.
Here, a difference of the electronic component of this embodiment from that of the first embodiment only lies in the external terminal, more specifically in a structure of the first layer in the metal thin film of the lead base material surface, and the remaining portions may be the same as the first embodiment. Accordingly, the subsequent description only refers to a structure of the first layer in the metal thin film of this embodiment. The difference from the first embodiment is that the first layer in the metal thin film has a substantially amorphous structure. Forming the first layer in an amorphous structure eliminates the continuous particle boundary, through which the Sn atoms can efficiently transfer. Therefore, even though a whisker emerges, the transference of the Sn atoms necessary for growth of the whisker is restrained, and resultantly the whisker growth is restrained.
A preferable method of forming an amorphous structure in the metal thin film by plating may include preparing a plating solution having a relatively high concentration, setting a sufficient separation between a cathode and an electrode of an object to be plated, applying a high voltage to significantly increase a deposition rate, and further turning the current on and off according to a predetermined profile.
Further, a metal thin film having an amorphous structure may also be formed in the following method, in addition to the plating method. Melted Sn or an Sn-alloy may be applied by thermal spraying to an exposed surface of the lead base material so that the Sn or Sn-alloy is rapidly cooled. In this way the lead base material can be coated with the Sn or Sn alloy thin film having an amorphous structure, thereby forming an external terminal provided with the first layer of an amorphous structure. When applying this method to the IC 10 of the foregoing embodiment, the process may preferably include mounting a semiconductor chip on a lead frame, performing a wire bonding, sealing with a resin and applying a heat shielding cover on the resin-sealed portion. Then the thermal spraying may be carried out to apply melted Sn or an Sn-alloy only to an exposed surface of the lead base material so that the Sn or Sn-alloy is rapidly cooled. As a result, the Sn or Sn-alloy thin film coating the lead base material surface obtains an amorphous structure, thereby forming an external terminal provided with the first layer of an amorphous structure. Here also, recrystallization gradually takes place in the first layer formed as above, because of heat to be applied in a subsequent process. However, crystal particles formed by such recrystallization have a different orientation and distribution from those obtained by an ordinary plating method, and the recrystallization does not result in formation of a structure that permits emergence of a whisker.
In addition, referring to a thickness of the first layer, it has been proven that a preferable thickness range is not less than 5 μm and not more than 30 μm, more preferably not less than 10 μm and not more than 25 μm.
It is to be understood that the present invention is not limited to the foregoing embodiments, but that various modifications may be made within the scope and spirit of the present invention. For example, while the above embodiments refer to a metal thin film that only includes the first layer, an underlying plated layer such as a Cu-plated layer, Ni-plated layer, or a zinc (Zn) plated layer may be provided on a surface of the lead base material, so that the first layer may be formed thereon. Alternatively, another layer such as an Au-plated layer, which restrains emergence of a whisker, may further be formed on the first layer.
Also, the first layer may be constituted substantially of pure Sn, or an Sn-based alloy predominantly composed of Sn and containing at least one out of the group consisting of Bi, Ag, Cu, indium (In) and Zn as an additive metal. In case of employing Bi as the additive metal, it is preferable that the first layer includes an Sn—Bi alloy containing not less than 0.5 wt % but not more than 4 wt % of Bi, and that an average crystal size index of such alloy is in a range of not less than 7 but not more than 20. Also, in case of employing Ag as the additive metal, it is preferable that the first layer includes an Sn—Ag alloy containing not less than 0.5 wt % but not more than 6 wt % of Ag, and that an average crystal size index of such alloy is in a range of not less than 7 but not more than 20. Further, in case of employing Cu as the additive metal, it is preferable that the first layer includes an Sn—Cu alloy containing not more than 3 wt % of Cu, and that an average crystal size index of such alloy is in a range of not less than 10 but not more than 30.
Furthermore, while an Fe-42% Ni-alloy is adopted as the material of the lead base material 1 in the foregoing embodiments, an Fe-based alloy, Cu, or a Cu-based alloy predominantly containing Cu may be employed instead.
As described above, the present invention provides an electronic component having an external terminal coated with a metal thin film of a simple structure constituted of Sn or a Sn-based and substantially Pb-free alloy, formed by plating on a surface of a lead base material. Yet such electronic component can effectively restrain emergence of a whisker on the outer plated layer under a circumstance of practical use.
Patent | Priority | Assignee | Title |
Patent | Priority | Assignee | Title |
6811672, | Jun 27 2001 | KOBE LEADMIKK CO , LTD | Method for forming plating film and electronic component having plating film formed theron by same method |
6998036, | May 30 2000 | DR -ING MAX SCHLOTTER GMBH & CO KG | Electrolyte and method for depositing tin-silver alloy layers |
20030156395, | |||
JP1984067357, | |||
JP1985238487, | |||
JP1990170996, | |||
JP1995157893, | |||
JP1998102283, | |||
JP2001040497, | |||
JP2001040498, | |||
JP2001053210, | |||
JP2001110666, | |||
JP2002124547, | |||
JP2002246208, | |||
JP2003082500, | |||
JP2003105586, | |||
JP2003129276, | |||
JP2003535222, | |||
JP2170996, |
Executed on | Assignor | Assignee | Conveyance | Frame | Reel | Doc |
Aug 30 2013 | Renesas Electronics Coporation | (assignment on the face of the patent) | / | |||
Aug 06 2015 | Renesas Electronics Corporation | Renesas Electronics Corporation | CHANGE OF ADDRESS | 044928 | /0001 |
Date | Maintenance Fee Events |
Oct 13 2016 | M1553: Payment of Maintenance Fee, 12th Year, Large Entity. |
Date | Maintenance Schedule |
Apr 26 2019 | 4 years fee payment window open |
Oct 26 2019 | 6 months grace period start (w surcharge) |
Apr 26 2020 | patent expiry (for year 4) |
Apr 26 2022 | 2 years to revive unintentionally abandoned end. (for year 4) |
Apr 26 2023 | 8 years fee payment window open |
Oct 26 2023 | 6 months grace period start (w surcharge) |
Apr 26 2024 | patent expiry (for year 8) |
Apr 26 2026 | 2 years to revive unintentionally abandoned end. (for year 8) |
Apr 26 2027 | 12 years fee payment window open |
Oct 26 2027 | 6 months grace period start (w surcharge) |
Apr 26 2028 | patent expiry (for year 12) |