The present invention provides a flexible two component polyurethane and method for producing the polyurethane. The cured polyurethane is flexible, durable and weather resistant. The polyurethane is suitable for use as a protective layer on various substrates. The flexible polyurethane is the reaction product of solvent-free reaction components. The first component includes one or more polyols, optionally, one or more diols, and a catalyst. The second component includes a primary aliphatic isocyante crosslinker.
|
1. An article comprising:
a) a substrate selected from polymeric material, wood, fabric, reinforced polymers, metal, reflective sheeting, and a combination thereof, wherein the polymeric material or the polymer of the reinforced polymer comprises a polyvinyl chloride, polyester, acrylic polymer, polycarbonate, polyurethane, polyethylene acrylic acid copolymer, or polyvinyl acetate; and
b) a clear polyurethane applied as a protective layer on a first surface of said substrate, said polyurethane is a reaction product of,
i) a first component comprising one or more polyols having an equivalent weight in the range from about 28 to about 3000, optionally one or more diols having an equivalent weight in the range from about 30 to about 4000, and a catalyst; and
ii) a second component comprising at least 50 weight percent of a primary polyisocyanate having a functionality of at least three, and wherein the first and second components together are solvent free, and wherein any isocyanate source in the clear protective polyurethane layer consists of the primary polyisocyanate.
18. An article comprising:
a) a substrate having a first surface, said substrate selected from polymeric material, wood, fabric, reinforced polymers, metal, reflective sheeting, and a combination thereof, wherein the polymeric material or the polymer of the reinforced polymer comprises a polyvinyl chloride, polyester, acrylic polymer, polycarbonate, polyurethane, polyethylene acrylic acid copolymer, or polyvinyl acetate;
b) indicia on at least a portion of the first surface of the substrate; and
c) a clear polyurethane applied as a protective layer over the indicia and any exposed portions of the first surface of said substrate, wherein the polyurethane is a reaction product of:
i) a first component comprising one or more polyols having an equivalent weight in the range from about 28 to about 3000, optionally one or more diols having an equivalent weight in the range from about 30 to about 4000, and a catalyst; and
ii) a second component comprising at least 50 weight percent of a primary polyisocyanate having a functionality of at least three, and wherein the first and second components together are solvent free;
wherein the first and second components form a solvent-free admixture having an NCO:OH ratio of about 0.75 to about 1.25, and wherein any isocyanate source in the clear protective polyurethane layer consists of the polyisocyanate component.
14. An article comprising:
a) a substrate selected from polymeric material, wood, fabric, reinforced polymers, metal, reflective sheeting, and a combination thereof, wherein the polymeric material or the polymer of the reinforced polymer comprises a polyvinyl chloride, polyester, acrylic polymer, polycarbonate, polyurethane, polyethylene acrylic acid copolymer, or polyvinyl acetate; and
b) a clear protective polyurethane layer on directly contacting a first surface of the substrate, wherein the clear protective polyurethane layer contains primary aliphatic isocyanate crosslinking, and wherein about 25% or more of the total crosslink density is contributed by a polyisocyanate components component having a functionality of at least three, said clear protective polyurethane layer exhibiting at least one property selected from the group consisting of a flexural modulus of 1.0×108 1.0×108 pascals or less, a storage modulus of 1.0×108 1.0×108 pascals or less, a shore A hardness of less than 94, a hoffman scratch-hardness test result of 2 or less, and a color shift, in accordance with heat aging test ASTM D2244-79, within 1 delta E, wherein the clear protective polyurethane layer comprises a polyester polyurethane, polycarbonate polyurethane, polyacrylate polyurethane, polyalkylene polyurethane, polyether polyurethane, or a combination thereof and wherein any isocyanate source in the clear protective polyurethane layer consists of the polyisocyanate component.
2. An article as recited in
3. An article as recited in
5. An article as recited in
6. An article as recited in
7. An article as recited in
8. An article as recited in
9. An article as recited in
10. An article as recited in
11. An article as recited in
12. An article as recited in
13. An article as recited in
15. An article as recited in
(i) a first component comprising one or more polyols having an equivalent weight in the range from about 28 to about 3000, optionally one or more diols having an equivalent weight in the range from about 30 to about 4000, and a catalyst; and
(ii) a second component comprising at least 50 weight percent of a primary polyisocyanate having a functionality of at least three, and wherein the first and second components together are solvent free.
16. An article as recited in
17. An article as recited in
19. An article as recited in
0. 20. An article comprising:
a) a substrate selected from polymeric material, wood, fabric, reinforced polymers, metal, reflective sheeting, and a combination thereof, wherein the polymeric material or the polymer of the reinforced polymer comprises a polyvinyl chloride, polyester, acrylic polymer, polycarbonate, polyurethane, polyethylene acrylic acid copolymer, or polyvinyl acetate; and
b) a flexible clear polyurethane applied as a layer on a surface of said substrate, said flexible polyurethane comprising a reaction product of,
i) a first component included one or more polyols having an equivalent weight in the range from about 28 to about 3000, optionally one or more diols having an equivalent weight in the range from about 30 to bout 4000, and a catalyst; and
ii) a second component comprising a primary aliphatic isocyanate crosslinker having at least 50 weight percent polyisocyanate,
wherein the first and second components together are solvent free.
21. An article as recited in
22. An article as recited in
23. An article as recited in
24. An article as recited in
0. 25. An article as recited in
26. An article as recited in claim 14 35, wherein the first component comprises greater than about 20 weight percent polyester.
27. An article as recited in
28. An article as recited in
29. An article as recited in
0. 30. An article as recited in
31. The article of
32. The article of
33. The article of
0. 34. The article of
0. 35. An article as recited in claim 14, wherein the clear protective polyurethane layer is a reaction product of:
(i) a first component comprising one or more diols selected from the group consisting of: polyester diols, polycarbonate diols, polyacrylate diols, polyalkylene diols, and polyether diols, or a combination thereof; and
(ii) a second component comprising the polyisocyanate component.
0. 36. An article as recited in claim 35, wherein the diols comprise up to about 65 weight percent of the first component.
0. 37. An article as recited in claim 35, wherein the one or more diols include a short chain diol having an equivalent weight in the range from about 30 to about 400 and a long chain diol having an equivalent weight in the range of from about 400 to about 4000.
0. 38. An article as recited in claim 14, wherein the clear protective polyurethane layer is a reaction product of:
(i) a first component comprising one or more polyols having an equivalent weight in the range from about 28 to about 3000, optionally one or more diols having an equivalent weight in the range from about 30 to about 4000, and a catalyst; and
(ii) a second component comprising at least 50 weight percent of the polyisocyanate component.
0. 39. An article as recited in claim 38, wherein the catalyst is a tin-based catalyst and the clear protective polyurethane layer, upon exposure to moisture or carboxyl groups, does not exhibit a substantial amount of outgassing.
0. 40. An article as recited in claim 14, wherein the clear protective polyurethane layer contains up to about 20 weight percent of polyether segments.
0. 41. An article as recited in claim 40, wherein the clear protective polyurethane layer contains up to about 15 weight percent of polyether segments.
0. 42. An article as recited in claim 14, wherein the substrate is a base substrate and one or more secondary articles are applied over the base substrate, each of the secondary articles comprising an adhesive attachment system, a substrate, and indicia.
0. 43. An article as recited in claim 42, wherein the base substrate includes indicia and the secondary articles are applied over the indicia of the base substrate.
0. 44. An article as recited in claim 14, further comprising:
c) an adhesive layer directly contacting a second surface of the substrate, wherein the second surface is opposite the first surface of said substrate.
0. 45. An article as recited in claim 14, wherein the clear protective polyurethane layer is a reaction product of a diol.
0. 46. An article as recited in claim 14, wherein the substrate comprises a polymeric material.
0. 47. An article as recited in claim 46, wherein the polymeric material comprises polyurethane.
0. 48. An article as recited in claim 47, wherein the clear protective polyurethane layer comprises a polyester polyurethane.
0. 49. An article as recited in claim 48, wherein the clear protective polyurethane layer further comprises a polyacrylate polyurethane.
0. 50. An article as recited in claim 14, wherein the clear protective layer is a reaction product of one or more diol or polyol compounds comprising polyesters, polycarbonates, polyacrylates, polyalkylenes, and polyethers, and combinations thereof.
|
|||||||||||||||||||||||||||||||||||||||||||
This is a divisional of application Ser. No. 09/064,490, filed Apr. 22, 1998 which is now U.S. Pat. No. 6,258,918.
This invention relates to a flexible, polyurethane material, more particularly, to a solvent free, two-component polyurethane and, even more particularly, to such a polyurethane which is transparent and exhibits improved flexibility, durability and weathering characteristics. The present invention also includes an article utilizing the polyurethane as a top coat, and a method of making such a polyurethane top coat.
Decorative articles often utilize a polyurethane top coat to cover or protect a base substrate and any indicia or decorative features located on the substrate. The articles may include various substrates upon which printing or profiled graphics have been applied. The polyurethane material is generally clear or optically transparent and functions as a lens in order to display the substrate or any indicia applied thereon. The decorative articles have a wide variety of uses in both interior and exterior applications. For example, model names for automobiles are often displayed in a decorative manner on an exterior surface of the vehicle. The polyurethane covers and protects the indicia displayed on the model nameplate.
Polyurethanes are generally applied onto articles or substrates as a solution or flowable reaction mass which is then cured to form a lens. The flow characteristics of the uncured polyurethane are important in developing a polyurethane coating at a sufficient and desired thickness upon curing.
Some polyurethanes, upon curing, are rigid, non-flexible polymers. The rigidity of the article is often due to the chemical structure of the components used in the formulation of the polyurethane. Rigid polyurethanes are susceptible to abrasion and scratching. Additionally, the materials do not demonstrate an appropriate level of self-healing. Self-healing describes the ability of the polyurethane to return to its original shape or appearance after being deformed, such as by scratching.
Polyurethanes are applied onto various types of substrates. However, some specific substrates are not suitable for use with conventional polyurethanes. Some substrates are susceptible to absorbing an amount of moisture which can react with the polyurethane to form bubbles in the cured polyurethane. The formation of bubbles in the polyurethane is termed outgassing. For polyurethanes containing an isocyanate, outgassing may also occur when certain porous substrates, for example polyvinyl chloride, are backed with adhesives containing carboxyl groups. The porous substrate permits the reaction of the isocyanate in the polyurethane with carboxyl groups in the adhesive. This reaction results in the release of carbon dioxide which generally becomes trapped in the polyurethane. The occurrence of outgassing in a cured polyurethane is aesthetically undesirable.
Conventional two-component polyurethanes are typically either solvent based or utilize polyethers as the primary hydroxyl source. The solvent based polyurethanes are generally not viscous enough to provide a desired thickness to the polyurethane lens. Additionally, solvent based polyurethanes, when applied as top coats, do not permit the complete evaporation of the solvent from the polyurethane. The incomplete evaporation can produce striations, parting lines, or bubbles in the polyurethane and therefore result in an aesthetically unacceptable top coat. Polyether based polyurethane mixtures can provide suitable flexible properties. However, they tend to degrade and yellow when exposed to sunlight. Thus, existing polyurethane compositions, and methods for producing them, often result in undesirable finished properties or are unsuitable for exterior applications.
There is a need to provide a polyurethane that is flexible, durable, and weather resistant. Additionally, such a polyurethane should be applicable to various substrates without experiencing a substantial amount of outgassing. A polyurethane having the noted properties would be suitable for use a protective coating on various substrates for both interior and/or exterior applications.
The present invention provides a two component polyurethane, an article utilizing the polyurethane, and a method of making the polyurethane. The cured polyurethane is flexible, durable and weather resistant. The optically transparent polyurethane is suitable for use as a protective coating on various substrates.
The polyurethane of the present invention has primary aliphatic isocyanate crosslinking. The polyurethane is the reaction product of two reaction components. The first reaction component includes one or more polyols. The polyol portion of the first component has an equivalent weight in the range from about 28 to about 3000. The first component also includes one or more diols having an equivalent weight in the range from about 30 to about 4000. The desired diol is a combination of a short chain diol, having an equivalent weight in the range from about 30 to about 400, and a polymeric diol, having an equivalent weight in the range from about 400 to about 4000. Polyol and diol compounds suitable for use in the first component may include polyesters, polycarbonates, polyacrylates, polyalkylenes, and polyethers, or combinations thereof. Additionally, a catalyst is included in the first component.
The second component includes a primary aliphatic polyisocyanate crosslinker. The noted polyisocyanate preferably represents at least about 50 weight percent of the total isocyanate present in the second component. The first and second components are combined to form a solvent-free admixture which may then be applied onto a desired substrate and cured. The viscosity of the admixture is generally in the range of about 400 cps to about 5000 cps at 25° C. The viscosity of the material enables the formation of a lens, or meniscus, over the substrate.
The cured, optically transparent polyurethane is flexible, durable and weather resistant. The flexibility of the polyurethane is demonstrated through the Shore A hardness test, the flexural modulus test, and the storage modulus test. The polyurethane has a Shore hardness of less than 94, a storage modulus of 1.0×108 pascals or less, and a flexural modulus of 1.0×108 pascals or less.
The durability and weather resistant properties of the present invention are demonstrated through such tests as the Hoffman scratch resistance test and the heat aging test. The polyurethane of the present invention has a surface with a Hoffmnan scratch-hardness test result of 2 or less. Additionally, the polyurethane exhibits a color shift value of 1 or less when subjected to the heat aging test.
It would be an advantage to provide a polyurethane that is flexible, durable, and weather resistant. A polyurethane having the noted properties would be suitable for use as a protective layer for both interior and exterior applications.
It would be a further advantage to provide a polyurethane that prevents outgassing when applied onto a substrate. The ability to prevent outgassing would enable the use of the polyurethane on a variety of substrates and decorative articles.
The above, as well as other advantages of the present invention, will become readily apparent to those skilled in the art from the following detailed description when considered in the light of the accompanying drawings in which:
The preferred polyurethane of the present invention has primary aliphatic isocyanate crosslinking. The polyurethane is the reaction product of a two component system. The resulting reaction mass of the two components is generally solvent-free. In accordance with the invention, solvent free means that the reaction mass contains an amount of water or organic solvents at levels that do not adversely affect the viscosity of the reaction mass and thereby prevent the formation of a lens. Additionally, the amount of water or organic solvent must sufficiently evaporate upon curing in order to prevent the formation of striations, parting lines, or bubbles in the cured polyurethane. Preferably, solvent-free means there is less than about five weight percent water or organic solvents in the combined admixture of the reaction components. More preferably, the solvent content in the combined reaction components is less than about one weight percent.
The first reaction component contains one or more polyols, optionally, one or more diols, and a catalyst. The polyols utilized in accordance with the present invention are compounds having 3 or more hydroxyl groups. The polyols are generally selected from the group consisting of polyesters, polycarbonates, polyacrylates, polyalkylenes, and polyethers, or combinations thereof. The polyol, or combined polyols, have an equivalent weight in the range of about 28 to about 3000. In the present invention, equivalent weight corresponds to the molecular weight of the material divided by the number of hydroxyl groups. Combinations of polyols within the noted equivalent weight limitation may be suitable for use with the invention. However, the amount of polyether in the first reaction component, whether provided as a polyol or diol, preferably should not exceed about 40 weight percent of the first component. Amounts of polyethers in excess of the noted limitation can adversely affect the clarity or the weathering properties of the present invention. Desirably, polyester based polyols and diols, forming greater than about 20 weight percent polyester in the first reaction component, are used in the present invention in order to improve outdoor durability. The polyol comprises in the range from greater than about 10 weight percent of the first reaction component.
Optionally, one or more diols are included in the first reaction component. The diols are compounds that have two hydroxyl groups. In addition to polyester diols, polycarbonate, polyacrylate, polyalkylene, and polyether diols, or combinations of the noted compounds, may be utilized in the present invention. The one or more diols have a combined equivalent weight in the range of about 30 to about 4000. Additionally, the diols comprise in the range up to about 65 weight percent of the first reaction component. Desirably, the diols include the combination of a short chain diol, having an equivalent weight in the range from about 30 to about 400, and a polymeric, or long chain diol having an equivalent weight in the range of from about 400 to about 4000. Additionally, it has been found that when a polyester and a polyether are utilized in the first reaction component, the combined amount of polyether, whether provided as a polyol or diol, preferably should not exceed about 40 weight percent of the first reaction component.
The first reaction component of the present invention also requires a catalyst. The isocyanate groups of the second component react with the hydroxyl groups of the first component under the influence of the catalyst to form urethane linkages. Conventional catalysts generally recognized for use in the polymerization of urethanes may be suitable for use with the present invention. For example, aluminum, bismuth, tin, vanadium, zinc, or zirconium based catalysts may be used with the present invention. Though not desired because of the their potential toxicity, mercury based catalyst may also be used. The desired catalysts are tin based catalyst. Tin based catalyst have been found to significantly reduce the amount of outgassing present in the polyurethane. Most desirable are dibutyl tin compounds. Even more desirable are the catalyst selected from the group consisting of dibutyltin diacetate, dibutyltin dilaurate, dibutyltin diacetylacetonate, dibutyltin dimercaptide, dibutyltin dioctoate, dibutyltin dimaleate, dibutyltin acetonylacetonate, and dibutyltin oxide. The catalyst is preferably included at levels of at least 200 ppm in the first component and more preferably at 300 ppm or greater.
Optionally, the first reaction component of the present invention can include various additives. For example, leveling agents may be utilized in the first reaction component to ensure a smooth finish to the exposed surface of the polyurethane. A polyethylene oxide modified polymethyl siloxane can be utilized in the present invention as a leveling agent. However, other leveling agents generally recognized by one of ordinary skill in the art may also be suitable for use with the invention. The leveling agents are desirably included in the range from about 0.01 weight percent to about 1 weight percent.
Another additive to the first component can include UV absorbers which improve the weather resistance of the polyurethane top coat. The UV absorbers generally recognized in the art may be suitable for use with the invention. Alternatively, a hindered amine radical scavenger can be included in the first reaction component or combined with an UV absorber. The hindered amine free radical scavengers generally recognized in the art contribute to photostabilization of the polyurethane by trapping alkoxy and hydroxy radicals produced by light-induced dissociation of hydroperoxides. The amount of UV absorber in the first component is desirably in the range from about 0.1 weight percent to about 4 weight percent. The amount of hindered amine radical scavenger in the first component in desirably in the range of about 0.1 weight percent to about 2 weight percent.
Additionally, moisture scavengers, antioxidants, and antifoaming agents can be included with the first reaction component. Conventional compounds of the noted categories generally recognized by those skilled in the art may be suitable for use in the present invention to improve the finished properties of the polyurethane. Moisture scavengers are desirably included at levels in the range of about 0.1 weight percent to about 3 weight percent. The antioxidant is desirably included in a range of about 0.1 weight percent to about 2 weight percent. Antifoaming agents are desirably included in an amount from about 0.2 weight percent or less.
Other compounds, such as coloring agents and decorative solids, can be added to the first component to enhance to the aesthetics of the finished polyurethane. Coloring agents, such as pigments or dyes, are included at various levels to obtain a desired effect. Decorative solids could include such items as metal flakes, polymeric flakes, glitter, beads, or other materials that provide a decorative feature to the finished polyurethane. The decorative solids are also included in various amounts to obtain a desired effect to the finished article.
In accordance with the present invention, a second component is provided which includes a primary aliphatic isocyanate crosslinker, and preferably a primary aliphatic polyisocyanate crosslinker. A primary isocyanate is defined as one having a carbon atom that has an —NCO group and two hydrogen atoms attached to the carbon atom. The primary isocyanate is an important factor in providing a flexible polyurethane that does not exhibit a substantial amount of outgassing. Outgassing can occur when the isocyanate component of the polyurethane undesirably reacts with a source of water or carboxyl groups and not the hydroxyl groups present in the first component.
In the present invention, it is preferred that the second reaction component include a primary polyisocyanate in an amount of about 50 weight percent or greater. This generally corresponds to polyisocyanate crosslinking of about 25 weight percent or greater in the cured polyurethane. The primary aliphatic polyisocyanate may be the only isocyanate source in the component or it may be combined with other primary aliphatic isocyanates, such as monomeric isocyanates. The utilization of secondary isocyanates can result in the rigid polyurethanes or polyurethanes which exhibit outgassing. Conventional primary aliphatic polyisocyanate crosslinkers may be suitable for use with the present invention. For example, Desmodur XP-7100 and Desmodur N-3300 from Bayer Chemical of Pittsburgh, Pa. are two polyisocyanates suitable for use with the invention. Additionally, the polyisocyanate may be a blocked polyisocyanate to further enhance the reduction of outgassing in the cured polyurethane. Blocked polyisocyanates will not react until a desired curing temperature is achieved, thereby further preventing the undesired reaction of the isocyanate with water or carboxyl groups. Polyisocyanate levels of at least about 50 weight percent of the total isocyanate present in the second component may substantially reduce outgassing in the cured polyurethane.
The crosslink density of a polyurethane is calculated by dividing the weight of the reaction components having a functionality of three or greater by the total weight of the polyurethane and multiplying by 100. Generally, rigid polyurethanes have relatively high cross link densities of 30% or higher. In accordance with the present invention, the use of a primary aliphatic polyisocyanate results in a flexible polyurethanes having a high crosslink density. When the polyisocyanate content of the second reaction component is about 50 weight percent or greater, crosslink densities are 30 percent or greater, and preferably 40 percent or greater. The flexibility of the resulting urethanes, according to the flexural modulus tests are generally 1.0×108 or less.
The first and second reaction components are combined to form a solvent-free admixture having an NCO:OH ratio of about 0.75 to about 1.25. The reaction components, prior to mixing, are desirably maintained at specified viscosity ranges. The viscosity measurements for the present invention were measured on a Brookfield Viscometer model RV with spindle number 4 at about 20 rpm. The viscosity of the first component is desirably maintained in the range from about 200 cps to about 5000 cps at 25° C. The viscosity of the second reaction component is desirably maintained in the range from about 100 cps to about 5000 cps at 25 C. Upon mixing, the viscosity of the admixture is in the range from about 400 cps to about 5000 cps at 25° C., and desirably in the range from about 600 cps to about 4000 cps.
The viscosity of the uncured polyurethane is important in achieving a desired thickness and continuity in the cured polyurethane lens when applied over a substrate. The viscosity limitation also provides a pourable reaction mass that flows well onto a substrate. It is desired that the reaction mass flow to the edge of the substrate and form a radius of curvature, without actually overflowing the substrate. The viscosity limitation also enhances the ability to achieve desired layer thicknesses. A higher viscosity than the noted limitation may result in striations or parting lines in the finished polyurethane. A lower viscosity will not permit the polyurethane to form the desired meniscus or lens over the substrate. The polyurethane of the present invention is capable of achieving thicknesses of greater than 0.13 mm, and preferably greater than 0.25 mm.
In accordance with the present invention, the admixture is applied onto a substrate and cured to form a polyurethane coating. The curing of the polymer may be accomplished by heating the material, applying infrared radiation, or curing at ambient temperatures. Other conventional curing techniques recognized by those skilled in the art may be suitable for use with the present invention. Desirably, the polyurethane is cured in a convection oven at 52° C. for about 10 hours. One advantage of the present invention over conventional polyurethane s is that the polyurethane is tack free after about one hour of curing at about 52° C. The tack free polyurethane can then be handled without being completely cured.
Upon curing, the polyurethane of the present invention exhibits desired flexibility, durability, and weather resistant properties. Preferably, the polyether segments, resulting from the use of polyether based polyols and diols in the first component, represent no more than 20 weight percent in the cured polyurethane. More preferably, the polyether segments in the cured polyurethane is about 15 weight percent or less. A polyether content in excess of the noted limitation may adversely impact the clarity and weathering properties of the cured polyurethane.
The flexibility of the present invention enables use of the polyurethane on various articles. For example, the present invention may be utilized as a protective layer on an adhesive backed substrate. The flexibility of the polyurethane of the present invention enables the application of the coated article on curved or non-planer surfaces. The flexibility significantly reduces the tendency of the polyurethane to spring back to its originally cured form after being bonded to a surface.
The flexibility of the polyurethane is demonstrated by the Shore A hardness properties, the storage modulus, and the flexural modulus. The Shore A hardness test of the present inventive polyurethane is generally less than 94, and preferably less than 92. Shore A hardness levels in excess of 94 are considered stiff or rigid. The storage modulus indicates the rigidity of the polyurethane under tension. The polyurethanes of the present invention have a storage modulus of 1.0×108 or less. The flexural modulus measures the flexibility of the polyurethane under tortional strain. The polyurethanes of the present invention have a flexural modulus of 1.0×108 or less. Additionally, the flexibility of the polyurethane is often indicated by its self-healing characteristics, or the ability to return to its original shape upon deformation.
The durability and weathering properties of the present invention are important features which enable the use of the polyurethane in various environments. For applications of the polyurethane in exterior environments, the polyurethane must not yellow or significantly change color when exposed to environmental conditions. The present invention, when subjected to a heat aging test in accordance with ASTM D2244-79, exhibits a color shift within 1 delta E. Other environmental tests utilized to indicate acceptable exterior performance are the salt spray test, the humidity resistance test, and the thermal shock test. A polyurethane should remain clear and not cloudy or opaque upon completion of the noted tests. The durability of the polyurethane top coat is measured by the Hoffman scratch resistance test which indicates the abrasion resistance of the material. The present invention generally has a Hoffman scratch resistance of 2 or less.
The polyurethane of the present invention may be applied to various substrates to form a layer on the substrate, or a portion of the substrate. The substrate may include wood, polymeric material, fiber reinforced polymers, metal, or combinations thereof. The choice of substrate is dependent upon the desired end use. Some examples of combined substrates would include metal coated polymer films and polymer sealed wood or wood veneer. The polyurethane of the present invention is ideally suited for applications with substrates containing moisture or applications permitting the direct or indirect contact of the isocyanate with carboxyl groups. For example, a porous substrate with an adhesive backing permits the indirect contact of the isocyanate in the polyurethane reaction mass with carboxyl groups in the adhesive.
The polyurethane of the present invention is ideally suited for use in forming decorative articles requiring a transparent layer. Some decorative articles utilize a substrate with indicia applied onto the substrate. Indicia includes any distinctive marks or representations. In accordance with the present invention, the polyurethane may be applied directly onto the substrate and the indicia.
In the present invention, indicia could include such items as printed graphics or three-dimensional graphics. Printed indicia may be applied onto the substrate, for example, with solvent based inks, water-based inks, UV inks, or powder inks. The printed indicia may be applied through various processes including screen printing, flexo-printing, gravure printing, digital printing, off-set printing, and pad printing. Three dimensional graphics may also be applied onto the substrate or may, by themselves, serve as the substrate. Three dimensional graphics may include for example, a cured polyurethane body with a tie layer bonded to the polyurethane. An adhesive is then applied to the opposing surface of the tie layer. An example of three-dimensional graphics would include those disclosed in EP 0392847, herein incorporated by reference. Other types and styles of indicia may also be utilized with the present invention.
Alternatively, the article may include several different types or styles of indicia applied, or layered upon the substrate. The polyurethane of the present invention is well suited for this style of application because it does not permit a substantial amount of outgassing. This layered style of indicia can directly expose an adhesive to the urethane top coat. This type of application with a conventional polyurethane often results in a significant amount of outgassing in the cured polyurethane. The present invention does not experience a substantial amount of outgassing, thereby enabling the direct exposure of the adhesive to the polyurethane.
Another embodiment of the present invention is depicted in
The following non-limiting examples further illustrate the present invention. Unless otherwise indicated, the following test procedures were used in the examples. The particular materials and amounts recited in these examples, as well as other conditions and details, are to be interpreted broadly in the art and should not be construed to unduly restrict or limit the invention in any way.
Hoffmnan Scratch and Mar Resistance Test:
The scratch and mar of the polyurethanes were measured by a Balanced-Beam Scrape tester described in ASTM-2197-86. The Hoffman stylus was held at 45 degrees from vertical with the top sloping in the direction of test sample travel. The stylus was held in place by a fulcrum elevated at 22 degrees. A 1000-Gram-weight was placed on the weight support. The beam was lowered until the loop rested on top of the test specimen, following which the sliding platform was slowly pushed across the specimen. The scratch test was performed at 25° C. A successful test will result in the polyurethane coat showing no permanent injury, scratch, or defect after 1 hour.
Humidity Resistance:
The polyurethanes were applied over a tin vapor coated polyester film and cured. Each sample was placed in a humidity condensing chamber with 100% relative humidity at 38° C. for 7 days. The samples were observed for cloudiness and corrosion upon removal from the chamber.
Heat Aging:
The polyurethanes were applied onto a white ink printed standard tin coated polyester substrate and cured. The samples were put in an 80° C. oven for 7 days. Upon removal, the polyurethane coat was observed to determine any significant yellowing in color. The color difference or change was measured by standard test ASTM D2244-79. The color difference (Delta E) was calculated by the CIE 1976 L* a* b* Uniform Color Space and Color-Difference Equation For successful results, the value of Delta E shall not exceed 1.
Salt Spray:
The polyurethanes were applied onto a tin coated polyester substrate and cured. The samples were put into a salt spray chamber, which had 5% NaCl solution atomized at 35° C. Upon removal after 10 days, the samples were observed for cloudiness and corrosion.
Shore A Hardness:
Shore A Hardness was measured by Shore A Durometer according to ASTM D-2240.
Thermal Shock:
The polyurethanes were applied onto tin coated polyester and cured. Each sample was tested at 10 cycles of the following tests:
4 Hours at −30° C.
5 minutes immersion at 85° C. water.
The samples were observed for cloudiness and corrosion.
Storage Modulus Test:
The E′ (storage modulus) is a measure of flexibility of a material. The storage modulus was measured at 25° C. in tension using Rheometric Solids Analyzer (RSA II) at a frequency of 6.28 rad/second. The tension was kept at 0.03% strain. The test sample, at a thickness of 1.8 mm and ranging in size from 3.5 mm to 6.5 mm, was mounted with clamps and tightened. In oscillatory flow, a periodic strain of predetermined amplitude and frequency is applied to the sample, and the stress response of the material is measured. The real part of the Fourier transform of the response gives the elastic modulus, E′ (storage modulus).
Flexural Modulus Test:
The flexural modulus was measured at 25° C. using Seiko DMS 110 at a frequency of 6.28 rad/second. A strip of sample, having a thickness of 1.8 mm and ranging from 10 mm to 13 mm in width and 20 mm in length, was mounted in the dual cantilever fixture. A strain amplitude of 30 microns was used to determine the flexural modulus of the sample.
Substrate (1) was prepared by screen printing a Scotchcal™ 7900 Series solvent-based phosphorescent ink using a 110 mesh screen on Scotchlite™ Reflective Engineering Sheeting both supplied from the Minnesota Mining and Manufacturing Company of St. Paul Minn. The ink was dried for 30 minutes at 80° C. Substrates (2)-(4) were standard Scotchcal™ p-series films from the Minnesota Mining and Manufacturing Company. Substrate (5) was prepared by digitally printing a standard powder toner onto a white PVC film. Substrate (6) was made by rotary printing Scotchcal™ 7900 Series solvent-based black metallic ink with carbon fiber pattern on silver PVC film. Substrate (7) was made by applying die-cut PVC graphics onto a hologram polyester film substrate. Substrate (8) was an uncleared and uncut standard 3-Dimensional Graphics from the Minnesota Mining and Manufacturing Co. Substrate (9) was made by applying uncleared/laser cut 3-Dimensional Graphics on PVC woodgrain film. Substrate (10) was prepared by screening Scotchcal™ 7900 Series solvent-based white ink with 230 mesh screen on tin metallized film. Substrate (11) was tin metallized film.
The first component, which was polyester polyols/diols based, was prepared by mixing 31.9 grams of Formrez-55-225, 30 grams of Formrez-55-112, and 30 grams of Tone-301 in a round bottom flask and heated to 70° C. The admixture was agitated and de-gassed for 4 hours by vacuum (below about 30 inch Hg) until all the bubbles were stripped off. The temperature of the admixture was cooled down to about 50° C. and 0.06 grams of T-12, 0.2 grams Silwet L-7607, 1.5 grams of Uvinul N-539 and 1 gram of Tinuvin-292 were then added into the admixture. The admixture was agitated for 15 minutes. The formulation of the first reaction component, by weight percent, is listed in Table 2.
The second reaction component included 100 grams of polyisocyanate (Desmodur XP-7100). The first and second reaction components were mixed in a one to one volume ratio and poured on the above noted eleven substrates. The polyurethanes were cured 10 hours at 52° C. in a convection oven. The cured polyurethane did not outgas on any of the substrates and had excellent optical clarity and flexibility.
The first component in comparative Examples 1 through 4 includes different polyether based polyols and diols. The Examples were prepared according to the same procedure described in Example 1. The polyols and diols utilized for each Example are noted in Table 1.
The second component for Comparative Example 1 was prepared by reacting 30 grams of Pluracol TP-4040 and 70 grams of Desmodur W for 4 hours at 80° C. The resulting second component was a mixture of a secondary polyisocyanate and monomeric isocyanate (Desmodur W). The second component used in Comparative Example 2 was prepared by reacting 73.5 grams of Desmodur I, with 23.5 grams of Desmophen L951, and 3 grams of Multranol-4011 for 4 hours at 80° C. The resulting Part B comprises a mixture of polyisocyanate with primary and secondary isocyanate functional groups and monomeric Desmodur I.
The polyurethanes were prepared by mixing the first and second reaction components in a one to one volume ratio and then poured onto the noted substrates (1) to (11). The polyurethanes were cured 10 hours at 52° C. The polyurethanes in Comparative Examples 1, 2 and 4 were still tacky when cured one hour at 52° C. convection oven or 10 minutes in IR oven and they had severe outgas on substrates (1) to (9). The polyurethanes were very rigid. The polyurethane in Comparative Example 3 was cloudy.
The first components used in Examples 2-6 were prepared according to the same procedure described in Example 1. The composition of the first component for each Example is listed in Table 1.
The second component used in Examples 2 was prepared by reacting 30 grams of Pluracol-538, and 70 grams of Vestanat IPDI for 4 hours at 80° C. The resulting second component included a mixture of polyisocyanate with primary and secondary isocyanate groups and monomeric Vestanat IPDI. The second component used in Example 3 was the same as the one utilized in Comparative Example 1. The second component in Example 3 comprises a mixture of secondary polyisocyanate and monomeric Desmodur W. The second component used in Example 4 was prepared by mixing 70 grams of polyisocyanate and 30 of Desmodur H. The second component used in Example 5 was prepared by mixing 50 grams of polyisocyanate and 50 g Desmodur H.
The polyurethanes were prepared by mixing the first component and the second component in a one to one volume ratio and then applied to substrates (1) through (11). The polyurethanes were cured for 10 hours at 52° C. The polyurethanes in Examples 2 and 3 showed severe outgas on substrates (1) through (9). Although not indicated in the Table, the weathering properties of the Examples 2 and 3 are improved over conventional polyurethanes. Additionally, Examples 2 and 3 were rigid. The flexible polyurethane in Examples 4 and 6 were clear and did not exhibit any outgassing on any of the substrates. The polyurethane in Example 5 exhibited outgassing on substrates (1), (5) and (9).
The polyester polyol/diol based first components in Examples 5 through 12 were prepared according to the same procedure described in Examples 1. The ingredients and amounts used for each Example are summarized in Table 4. The type of catalyst was varied for each Example. The various catalysts indicated in the Table.
The polyurethanes were prepared by mixing the first and second reaction components in a one to one volume ratio and then poured onto substrates (1) through (9). The polyurethanes were cured for 10 hours at 52° C. The polyurethane in Examples 7, 9, 10 and 12 didn't outgas and were flexible and optically clear. Comparative Examples 7 and 8 showed severe outgassing on all the substrates tested.
The first components utilized in Examples 13-17 were prepared according to the same procedure described in Example 1. The ingredients were varied in order to demonstrate the effect of varying polyether contents on the cured polyurethane. The ingredients and amounts utilized are summarized in Table 5. Additionally, Example 18 included a black pigment added to the first reaction component.
The second component in Example 16 was the same as the one used in Comparative Example 2. The second component in Example 17 was the same one utilized in Comparative Example 1. Examples 13 through 15 and 18 utilized a polyisocyanate. The amount of the second component used in each Example is listed in Table 5.
The polyurethanes for Examples 13-17 were prepared by mixing the first and second components in a one to one volume ratio and then poured onto substrates (1) through (11). The polyurethanes were cured for 10 hours at 52° C. The black pigmented polyurethane in Example 18 was only cast onto substrate (4), a black PVC film. The polyurethane in Example 18 was cured the same way as described in Examples 13-17. The polyurethane in Example 13 was cloudy and therefore unacceptable. The polyurethane in Examples 14 and 15 did not outgas and were clear and flexible. The polyurethanes in Examples 15 and 16 exhibited outgassing on all the substrates tested. Both the Examples were rigid. The pigmented polyurethane in Example 18 was flexible and did not exhibit any outgassing.
TABLE 1
Materials Used in The Invention.
Designation
Description
Supplier
Formrez ™-55-225
Polyester diol (—OH, Eq Wt = 245)
Witco Chemical, Tarrytown, N.Y.
Formrez ™-55-112
Polyester diol (—OH, Eq Wt = 500)
Witco Chemical, Tarrytown, N.Y.
Tone ™-301
Caprolactone-based polyester
Union Carbide, Danbury, CT
triol (—OH, Eq Wt = 100)
Tone ™- 305
Caprolactone-based polyester
Union Carbide, Danbury, CT
triol (—OH, Eq Wt = 180)
Pluracol ™ 538
Poly(propylene oxide) based
BASF, Mount Oliver, N.J.
triol (—OH, Eq Wt = 1603)
Pluracol ™ TP-4040
Poly(propylene oxide) based
BASF, Mount Oliver, N.J.
triol (—OH, Eq Wt = 1368)
Pluracol ™-220
Poly(propylene oxide) based
BASF, Mount Oliver, N.J.
triol (—OH, Eq Wt = 2078)
Multranol-4011
Poly(oxyalkylene) ether
Bayer Corp, Pittsburgh, PA
(Eq Wt = 100)
Desmophen L951
Poly(oxyalkylene) ether
Bayer Corp, Pittsburgh, PA
(Eq Wt = 213)
Vestanat ™ IPDI
Isophorone diisocyanate
HULS America Inc., Piscataway, N.J.
Desmodur ™ I
Isophorone diisocyanate
Bayer Corp, Pittsburgh, PA
Desmodur ™ W
Bis(4-isocyanatocyclohexyl)
Bayer Corp, Pittsburgh, PA
methane (Eq Wt = 132)
Tolanate ™ HDT-LV
Polyisocycanate (Eq Wt = 183)
Rhodia, Inc., Teaneck, N.J.
Desmodur ™ H
1,6-hexamethylene diisocyanate
Bayer Corp, Pittsburgh, PA
(—NCO, Eq Wt = 84)
Desmodur ™ XP-7100
Polyisocyanate (Eq Wt = 205)
Bayer Corp, Pittsburgh, PA
Metacure ™ T-12
Dibutyl tin dilaurate
Air Products and Chemicals,
Allentown, PA
Metacure ™ T-9
Stannous octoate
Air Products and Chemicals,
Allentown, PA
Cotin ™-222
Tin carboxylate
Caschem, Carlstadt, N.J.
Cotin ™-430
Diocyltin dicarboxylate
Caschem, Carlstadt, N.J.
Formrez ™ SUL-3
Dibutyl tin diacetate
Witco Chemical, Tarrytown, N.Y.
Formrez ™ UL-22
Dibutyl tin dimercaptide
Witco Chemical, Tarrytown, N.Y.
Formrez ™ UL-29
Dimethyl tin dimercaptide
Witco Chemical, Tarrytown, N.Y.
Octoate Z
Zinc ethyloctoate
Vanderbilt, Norwalk, CT
K-Ka ®-8201
Dibutyl tin bis(acetylacetonate)
King Industries, Norwalk, CT
Uvinul ™ N-539
UV-Light Absorber
BASF, Parsippany, N.J.
Tinuvin ™-292
Hindered Amine
Ciba-Geigy, Hawthorne, N.Y.
Irgarol ™-1051
Fungicide
Ciba-Geigy, Hawthorne, N.Y.
Skane M-8
Fungicide
Rhom and Haas, edison, N.J.
Silwet ™ L-7607
Polyethylene Oxide Modified
Witco Chemical, Tarrytown, N.Y.
Polymethylsiloxane
Silwet ™ L-77
Polyethylene Oxide Modified
Witco Chemical, Tarrytown, N.Y.
Polymethyl siloxane
Zapon ™ Black R Liquid
Water-Based Jet Black Dye
BASF, Rensselaer, N.Y.
Scotchlite ™ Engineering
Reflective Substrate with
3M, St. Paul, MN
Grade Reflective Sheeting
Pressure Sensitive Adhesive
3-Dimensional Graphics
3 Dimensional Graphics with
3M, St. Paul, MN
Pressure Sensitive Adhesive
TABLE 2
Polyether based Polyurethanes Cured on Various Substrates.
Comp.
Comp.
Comp.
Comp
1st component (grams)
Exp. 1
Exp. 2
Exp. 3
. Exp. 4
Pluracol-200
—
40.0
—
—
Multranol-4011
35.0
38.8
35.0
35.0
Pluracol 538
36.8
36.8
36.8
Desmophen L951
27.7
21.3
27.7
27.7
T-12
0.06
0.06
0.06
0.06
Uvinul N-539
1.0
1.0
1.0
1.0
Tinuvin-292
1.0
1.0
1.0
1.0
Silwet L-7607
0.3
0.3
0.3
0.3
Silwet L-77
2nd component:
100.0
—
—
—
30 grams Pluracol TP-4040 +
70 grams Desmodur W
2nd component:
—
100.0
—
100.0
73.5 grams Desmodur I +
23.5 grams of Desmophen L951 +
3 grams Multranol-4011
2nd component:
—
—
100.0
—
Desmodur XP-7100
X-link density (%)
50.9%
52.6%
85.9%
49.1%
(wt %) Polyether polyols/diols in
65%
63.3%
50%
63.3%
urethane top coat
Isocyanate used
2°
1° & 2°
1°
1° & 2°
Clarity of urethane top coat
Clear
Clear
Milky
Clear
White
Flexibility of urethane top coat
Rigid
Rigid
—
Rigid
(1) Cured on phosphorescent ink
Outgas
Outgas
—
Outgas
(2) Cured on blue pearl PVC film
Outgas
Outgas
—
Outgas
(P-5338)
(3) Cured on woodgrain PVC.
Outgas
Outgas
—
Outgas
(4) Cured on black PVC film
Outgas
Outgas
—
Outgas
(P-3098)
(5) Cured on 3M digital printed
Outgas
Outgas
—
Outgas
graphics on white PVC film
(6) Cured on 3M inks printed
Outgas
Outgas
—
Outgas
graphics on silver PVC film
(P-3450)
(7) Cured on PVC graphics on
Outgas
Outgas
—
Outgas
hologram polyester
(8) Cured on uncleared/uncut
Outgas
Outgas
—
Outgas
3-dimensional graphics.
(9) Cured on 3-dimensional
Outgas
Outgas
—
Outgas
graphics on woodgrain PVC
(10) White ink printed standard tin
OK
OK
—
OK
coated polyester substrate.
(11) Tin coated polyester substrate
OK
OK
—
OK
TABLE 3
Polyether-Based Polyurethanes Cured on Various Substrates.
1st component (grams)
Exp. 1
Exp. 2
Exp. 3
Exp. 4
Exp. 5
Exp. 6
Formrez-55-225
31.9
30.6
30.6
31.9
31.9
36.8
Formrez-55-112
30.0
30.5
30.5
30.0
30.0
—
Tone-305
—
26.1
26.1
—
—
59.8
Tone-301
30.0
—
—
30.0
30.0
—
T-12
0.06
0.06
0.06
0.06
0.06
0.045
Uvinul N-539
1.5
1.4
1.4
1.5
1.5
1.5
Tinuvin-292
1.0
1.4
1.4
1.0
1.0
1.0
Irgaro1-1051
—
—
—
—
—
0.8
Skane M-8
—
—
—
—
—
0.5
Silwet L-7607
0.2
—
—
0.5
0.5
0.3
Silwet L-77
—
0.15
0.15
—
—
—
2nd component:
—
—
100
—
—
—
30 grams Pluracol TP-4040 +
70 grams Desmodur W
2nd component:
—
100.0
—
—
—
—
70 grams Vestanat IPDI +
30 grams Pluracol-538
2nd component:
100.0
—
—
—
—
—
Desmodur XP-7100
2nd component:
—
—
—
—
—
100.0
Tolanate HDT-LV
2nd component:
—
—
—
75.0
—
—
Desmodur XP-7100/Desmodur H =
70/30 by weight
2nd component:
—
—
—
—
62.0
—
Desmodur XP-7100/Desmodur H =
50/50 by weight
X-link density (%)
65%
26.3%
28.0%
41.2%
30%
79.9%
Isocyanate used
1°
1° & 2°
2°
1°
1°
1°
Clarity of urethane top coat
Clear
Clear
Clear
Clear
Clear
Clear
Flexibility of urethane top coat
Flexible
Rigid
Rigid
Flexible
Flexible
Flexible
(1) Cured on phosphorescent ink
OK
Outgas
Outgas
OK
Outgas
OK
(2) Cured on blue pearl PVC
OK
Outgas
Outgas
OK
OK
OK
(P-5338)
(3) Cured on woodgrain PVC film
OK
Outgas
Outgas
OK
OK
OK
(4) Cured on black PVC film
OK
Outgas
Outgas
OK
OK
OK
(P-3098)
(5) Cured on 3M digital printed
OK
Outgas
Outgas
OK
Outgas
OK
graphics on white PVC film
(6) Cured on 3M inks printed
OK
Outgas
Outgas
OK
OK
OK
graphics on silver PVC film
(P-3450)
(7) Cured on PVC graphics on
OK
Outgas
Outgas
OK
OK
OK
hologram polyester substrate
(8) Cured on uncleared/uncut
OK
Outgas
Outgas
OK
OK
OK
3-dimensional graphics.
(9) Cured on 3-dimensional
OK
Outgas
Outgas
OK
Outgas
OK
graphics on woodgrain PVC film
(10) White ink printed standard tin
OK
OK
OK
—
—
OK
coated polyester substrate.
(11) Tin coated polyester substrate
OK
OK
OK
—
—
OK
TABLE 4
Polyurethanes Made from Polyester Polyols/Diols Comprising
Different Catalysts in the First Component and Cured on Various Substrates.
Comp.
Comp.
Comp.
Comp.
1″ component (grams)
Exp. 5
Exp. 7
Exp. 8
Exp. 9
Exp. 10
Exp. 11
Exp. 6
Exp. 7
Exp. 8
Exp. 12
Formrez-55-225
31.9
31.9
31.9
31.9
31.9
31.9
31.9
31.9
31.9
31.9
Formrez-55-112
30.0
30.0
30.0
30.0
30.0
30.0
30.0
30.0
30.0
30.0
Tone-301
30.0
30.0
30.0
30.0
30.0
30.0
30.0
30.0
30.0
30.0
1. Metacure T-9
0.06
—
—
—
—
—
—
—
—
—
2. Cotin-222
—
0.06
—
—
—
—
—
—
—
—
3. Cotin 430
—
—
0.06
—
—
—
—
—
—
—
4. Formrez SUL-3
—
—
0.06
—
—
—
—
—
—
5. Formrez UL-22
—
—
—
—
0.06
—
—
—
—
—
6. Formrez UL-29
—
—
—
—
—
0.06
—
—
—
—
7. Bismuth Neodecanoate, 20%
—
—
—
—
—
—
0.35
—
—
—
8. Zinc Neodecanoate, 16%
—
—
—
—
—
—
—
0.44
—
—
9. Octoate Z
—
—
—
—
—
—
—
—
0.5
—
10. K-Kat-8201
—
—
—
—
—
—
—
—
—
0.06
Uvinul N-539
1.5
1.5
1.5
1.5
1.5
1.5
1.5
1.5
1.5
1.5
Tinuvin-292
1.0
1.0
1.0
1.0
1.0
1.0
1.0
1.0
1.0
1.0
Silwet L-7607
0.3
0.3
0.3
0.3
0.3
0.3
0.3
0.3
0.3
0.3
2nd component:
100
100
100
100
100
100
100
100
100
100
Desmodur XP-7100
(1) Cured on phosphorescent ink
Severe
OK
OK
OK
OK
Outgas
Outgas
Severe
Severe
OK
Outgas
Outgas
Outgas
(2) Cured on blue pearl PVC film
OK
OK
OK
OK
OK
OK
OK
Severe
Severe
OK
(P-5338)
Outgas
Outgas
(3) Cured on woodgrain PVC film
OK
OK
OK
OK
OK
OK
OK
Severe
Severe
OK
Outgas
Outgas
(4) Cured on black PVC film
OK
OK
OK
OK
OK
OK
Outgas
Severe
Severe
OK
(P-3098)
Outgas
Outgas
(5) Cured on 3M digital printed
Outgas
OK
Outgas
OK
OK
Outgas
OK
Severe
Severe
OK
graphics on white PVC film
Outgas
Outgas
(6) Cured on 3M inks printed
OK
OK
OK
OK
OK
OK
OK
Severe
Severe
OK
graphics on silver PVC film
Outgas
Outgas
(P-3450)
(7) Cured on PVC graphics on
Outgas
OK
OK
OK
OK
OK
OK
Severe
Severe
OK
hologram polyester
Outgas
Outgas
(8) Cured on uncleared/uncut
OK
OK
OK
OK
OK
OK
OK
Severe
Severe
OK
3-dimensional graphic
Outgas
Outgas
(9) Cured on 3-dimensional
OK
OK
OK
OK
OK
OK
OK
Severe
Severe
OK
graphics on woodgrain PVC film
Outgas
Outgas
TABLE 5
Clarity of Polyurethanes Made from a Mixture of Polyester/Polyether
Polyols/Diols in the First Component and Cured by Primary and Secondary Polyisocyanates.
1st component (grams)
Exp. 13
Exp. 14
Exp. 15
Exp. 16
Exp. 17
Exp. 18
Tone-301
20.3
25.0
25.0
20.3
20.3
30.0
Pluracol-538
—
—
—
—
—
—
Formrez-55-225
—
—
—
—
—
31.9
Voranol 230-660
—
—
—
—
—
—
Formrez-55-112
—
—
—
—
—
30.0
Desmophen L-951
49.4
30.0
33.0
49.4
49.4
—
Formrez-33-112
29.5
43.0
—
29.5
29.5
—
Zapon black R liquid
—
—
—
—
—
1.5
Formrez-8056-143
—
—
41.2
—
—
—
Multrano1-4011
—
—
—
—
—
35.0
T-12
0.06
0.06
0.06
0.06
0.06
0.07
Silwet L-7607
0.3
0.4
0.4
0.3
0.3
0.30
Uvinul N-539
0.4
0.3
0.2
0.4
0.4
1.5
Tinuvin-292
—
0.2
0.2
—
—
1.5
2ndcomponent:
—
—
—
100
—
—
73.5 grams Desmodur I +
23.5 grams Desmophen L951 +
3 grams Multrano1-4011
2nd component:
—
—
—
—
100
—
30 grams Pluracol TP-4040 +
70 grams Desmodur
W
2nd component:
100
100
100
—
—
100
Desmodur XP-7100
Isocyanate used
1°
1°
1°
1° & 2°
2°
1°
X-link density (%)
60.1%
62.5%
62.5%
23.4%
25.1%
62.5%
(wt%) of Polyether polyols/diols
24.9%
15.0%
16.5%
52.7%
54.4%
64.2%
in urethane top coat
Clarity of urethane top coat
Milky
Clear
Clear
Clear
Clear
Clear
White
Flexibility of urethane top coat
—
Flexible
Flexible
Rigid
Rigid
Flexible
(1) Cured on phosphorescent ink.
—
OK
OK
Outgas
Outgas
—
(2) Cured on blue pearl PVC
—
OK
OK
Outgas
Outgas
—
(P-5338).
(3) Cured on woodgrain PVC film.
—
OK
OK
Outgas
Outgas
—
(4) Cured on black PVC (P-3098).
—
OK
OK
Outgas
Outgas
OK
(5) Cured on 3M digital printed
—
OK
OK
Outgas
Outgas
—
graphics on white PVC film.
(6) Cured on 3M inks printed
—
OK
OK
Outgas
Outgas
—
graphics on silver PVC (P-3450)
(7) Cured on PVC graphics applied
—
OK
OK
Outgas
Outgas
—
on hologram polyester film.
(8) Cured on uncleared/uncut
—
OK
OK
Outgas
Outgas
—
3-dimensional graphics.
(9) Cured on 3-dimensional
—
OK
OK
Outgas
Outgas
—
graphics on woodgrain PVC film.
(10) White ink printed standard tin
—
OK
OK
OK
OK
—
coated polyester substrate.
(11) Standard tin coated polyester.
—
OK
OK
OK
OK
—
TABLE 6
Specification Test Results
Comp.
Comp.
Comp.
Examples
Exp. 1
Exp. 2
Exp. 13
Exp. 14
Exp. 4
Exp. 1
Exp. 6
Type of Polyols/
Polyether
Polyether
Polyester/
Polyester/
polyether
polyester
polyester
Diols in Part A
polyether
polyether
Flexibility
94
98
81
81
97
84
89
(Shore A Hardness)
Storage Modulus
—
6.1 × 108
1.3 × 10
1.4 × 107
4.5 × 108
1.5 × 107
—
(Pascal)
Flexural Modulus
—
9.5 × 108
2.8 × 107
2.2 × 107
7.2 × 108
2.7 × 107
—
(Pascal)
Hoffman scratch test:
Scratched
Scratched
OK
OK
Scratched
OK
OK
(1 kg. Weight load).
(4)
(5)
(1)
(2)
(4)
(1)
(1)
(from a scale 1 to 5)
Color shift (DE*):
2.23
1.13
1.06
1.17
2.04
0.72
0.77
Heat age 7 days @ 80° C.
Salt spray: 10 days,
Clear
Slightly
Clear
Clear
Clear
Clear
Clear
5% NaCl (DIN50021)
Cloudy
Humidity resistance:
Clear
Clear
Cloudy
Cloudy
Clear
Clear
Clear
7 days @ 38° C.,
100% R.H.
Thermal Shock:
Clear
Slightly
Slightly
Slightly
Clear
Clear
Clear
Cloudy
Cloudy
Cloudy
Tables 2 and 3 illustrate the impact of primary and secondary isocyanates on the flexibility of the resulting polyurethanes. The Examples utilizing a primary isocyanate resulted in flexible polyurethanes. The Examples utilizing secondary isocyanates, or a combination of primary and secondary isocyanates, result in a rigid polyurethane. Additionally, the Examples indicate that the use of secondary isocyanates results in outgassing in the cured polyurethane. Comparative Example 3 in Table 2 indicates that the use of polyether compounds in an amount of about 50 weight percent resulted in an unclear polyurethane. Additionally, the Tables indicate that the Examples utilizing a primary aliphatic polyisocyanate resulted in flexible polyurethanes with crosslink densities at the same level or higher than the rigid polyurethanes.
Table 4 represents the results of bismuth, tin, and zinc based catalysts on the polyurethane of the present invention. The bismuth and zinc based catalysts resulted in outgassing in the cured polyurethane. The tin based performed much better and only exhibited outgassing on a few types of substrates. The dibutyl tin compounds did not exhibit any outgassing.
The results of the mixed polyether/polyester polyurethanes are listed in Table 5. The results indicate that secondary isocyanates produced rigid polyurethanes. Additionally, the use of secondary isocyanates results in outgassing. Example 13, with a polyether content in excess of 20 weight percent, was milky white. The Examples utilizing a primary polyisocyanate were flexible and did not outgas. Example 18 demonstrated the use of a black pigment in the first reaction component.
Table 6 illustrates flexibility, durability and weather resistant properties of the polyurethanes, The Examples 1,6, 13, and 14 indicate that the polyurethanes produced in accordance with the present invention exhibit improved flexibility and durability properties over the Comparative Examples. The flexibility and durability of the polyurethanes are demonstrated through the Shore A hardness, storage modulus, flexural modulus, and Hoffman scratch tests. Additionally, the polyester based polyurethanes exhibited improved weathering properties as represented through the salt spray, humidity resistance, and thermal shock tests.
In accordance with the provisions of the patent statutes, the present invention has been described in what is considered to represent its preferred embodiment. However, it should be noted that the invention can be practiced otherwise than as specifically illustrated and described without departing from its spirit and scope.
Ho, Charlie Chia-Tie, Fullbright, Jr., Clarence
| Patent | Priority | Assignee | Title |
| Patent | Priority | Assignee | Title |
| 3546148, | |||
| 3583945, | |||
| 3592787, | |||
| 3704023, | |||
| 3755262, | |||
| 3805532, | |||
| 3916050, | |||
| 4087412, | May 11 1976 | Minnesota Mining and Manufacturing Company | Organotin catalyst system for isocyanate reactions |
| 4100010, | Jun 12 1974 | The D. L. Auld Company | Method for making decorative emblems |
| 4386123, | Sep 28 1981 | CHROMA GRAPHICS CORPORATION | Article of manufacture and methods of manufacturing |
| 4518740, | Jun 24 1983 | Chemische Werke Huls Aktiengesellshcaft | Moisture-hardening varnishes with an isocyanate resin base |
| 4530859, | Dec 23 1981 | Minnesota Mining and Manufacturing Company | Method of preparing a polymeric coating composition from a blocked isocyanate-functional polymeric compound and a crosslinking agent which is insoluble in aprotic solvents |
| 4556588, | Aug 25 1982 | The D. L. Auld Company | Decorative emblem useful in customizing an automobile and other surfaces |
| 4556600, | Sep 03 1979 | Saint Gobain Vitrage | Laminated glasses using a non-thermoplastic adhesive insert layer |
| 4576850, | Jul 20 1978 | Minnesota Mining and Manufacturing Company | Shaped plastic articles having replicated microstructure surfaces |
| 4663213, | Nov 18 1985 | Minnesota Mining and Manufacturing Company | Transparent multi-layer cover film for retroreflective sheeting |
| 4745152, | Feb 22 1986 | Saint-Gobain Vitrage | Transparent coating of flexible, elastic polyurethane for transparent glass or synthetic resin substrates |
| 4808471, | Mar 01 1985 | Minnesota Mining and Manufacturing Company | Flat transparent top coat for retroreflective sheeting |
| 4808690, | Feb 29 1988 | PILKINGTON AEROSPACE INC | High heat distortion temperature transparent polyurethanes |
| 4839455, | Aug 28 1987 | Minnesota Mining and Manufacturing Company; Minnesota Mining & Manufacturing Company | One part moisture curable urethane composition |
| 4997901, | Mar 17 1987 | Asahi Glass Company Ltd | Reaction curable composition comprising a polyisocyanate component and a polyol component |
| 5091439, | Jun 17 1986 | Ciba Specialty Chemicals Corporation | Process for curing polyurethane coatings and compositions |
| 5117304, | Sep 21 1990 | Minnesota Mining and Manufacturing Company | Retroreflective article |
| 5124210, | Aug 28 1987 | Minnesota Mining and Manufacturing Company | Substrate coated with one part moisture curable urethane composition |
| 5127973, | Jun 13 1985 | Minnesota Mining and Manufacturing Company | Intersection markings |
| 5242751, | Apr 27 1989 | PPG Industries Ohio, Inc | Paint composites |
| 5338595, | May 08 1991 | Minnesota Mining and Manufacturing Company | Launderable retroreflective applique with metal-azo dye |
| 5462768, | Aug 09 1991 | Minnesota Mining and Manufacturing Company | Screen printing process using water-based chemical composition |
| 5502147, | Dec 21 1993 | Bayer Corporation | Aliphatic rim elastomers |
| 5508337, | Feb 14 1992 | Bayer Aktiengesellschaft | Powder coating compositions, a process for their preparation, and their use for the coating of heat resistant substrates |
| 5508340, | Mar 10 1993 | R. E. Hart Labs, Inc. | Water-based, solvent-free or low voc, two-component polyurethane coatings |
| 5587448, | Dec 29 1994 | Minnesota Mining and Manufacturing; Minnesota Mining and Manufacturing Company | Reaction system for producing a polyurethane and method of using same to seal a surface |
| 5656713, | Oct 18 1991 | Bayer Corporation | Thermoformable polyurethanes |
| 5681628, | Apr 26 1991 | PPG Industries Ohio, Inc | Pressurizable thermoplastic container having an exterior polyurethane layer and its method of making |
| 5798409, | Oct 03 1995 | Minnesota Mining & Manufacturing Company | Reactive two-part polyurethane compositions and optionally self-healable and scratch-resistant coatings prepared therefrom |
| 6197844, | Sep 13 1996 | 3M Innovative Properties Company | Floor finish compositions |
| 6258918, | Apr 22 1998 | 3M Innovative Properties Company | Flexible polyurethane material |
| CA2114043, | |||
| CA767695, | |||
| DE19709467, | |||
| EP83017, | |||
| EP230364, | |||
| EP392847, | |||
| EP68632, | |||
| EP82618, | |||
| EP87262, | |||
| GB1053383, | |||
| GB1317991, | |||
| GB1323312, | |||
| GB2104086, | |||
| JP10036478, | |||
| JP11166117, | |||
| JP3086719, | |||
| JP5051428, | |||
| JP5051556, | |||
| JP61028518, | |||
| JP6172620, | |||
| WO9222619, | |||
| WO9310167, | |||
| WO9600754, |
| Executed on | Assignor | Assignee | Conveyance | Frame | Reel | Doc |
| Apr 17 2015 | 3M Innovative Properties Company | (assignment on the face of the patent) | / |
| Date | Maintenance Fee Events |
| Date | Maintenance Schedule |
| Mar 27 2021 | 4 years fee payment window open |
| Sep 27 2021 | 6 months grace period start (w surcharge) |
| Mar 27 2022 | patent expiry (for year 4) |
| Mar 27 2024 | 2 years to revive unintentionally abandoned end. (for year 4) |
| Mar 27 2025 | 8 years fee payment window open |
| Sep 27 2025 | 6 months grace period start (w surcharge) |
| Mar 27 2026 | patent expiry (for year 8) |
| Mar 27 2028 | 2 years to revive unintentionally abandoned end. (for year 8) |
| Mar 27 2029 | 12 years fee payment window open |
| Sep 27 2029 | 6 months grace period start (w surcharge) |
| Mar 27 2030 | patent expiry (for year 12) |
| Mar 27 2032 | 2 years to revive unintentionally abandoned end. (for year 12) |