A method for etching a tungsten containing layer in an etch chamber is provided. A substrate is placed with a tungsten containing layer in the etch chamber. A plurality of cycles is provided. Each cycle comprises a passivation phase for forming a passivation layer on sidewalls and bottoms of features in the tungsten containing layer. Additionally, each cycle comprises an etch phase for etching features in the tungsten containing layer.
|
1. A method for etching a tungsten containing in an etch chamber, comprising:
placing a substrate with a tungsten containing layer in the etch chamber;
provide a plurality of cycles, wherein each cycle comprises:
a passivation phase for forming a passivation layer of silicon oxide on sidewalls and bottoms of features in the tungsten containing layer; and
an etch phase for etching features in the tungsten containing layer.
10. A method for forming a passivation layer on sidewalls of etched tungsten features, the method comprising:
forming etched features in a tungsten layer of a wafer, the etched features having sidewalls;
adsorbing a silicon precursor to the sidewalls; and
subsequent to the step of absorbing, oxygenating the silicon precursor adsorbed to the sidewalls;
wherein the silicon recursor is oxygenated using a plasma that contains SO2 and O2.
0. 15. A method for etching a tungsten containing layer in an etch chamber, comprising:
placing a substrate with a tungsten containing layer in the etch chamber; and
provide a plurality of cycles, wherein each cycle comprises:
a passivation phase for forming a silicon containing passivation layer on sidewalls or bottoms of features in the tungsten containing layer; and
an etch phase for etching features in the tungsten containing layer.
2. The method, as recited in
adsorbing a silicon precursor into the sidewalls of the features in the tungsten containing layer; and
exposing the tungsten containing layer to a plasma that scavenges Cl from the sidewalls.
3. The method, as recited in
4. The method, as recited in
providing an adsorption gas comprising SiCl4;
forming the adsorption gas into a plasma.
5. The method, as recited in
6. The method, as recited in
providing a scavenger gas comprising SO2; and
forming the scavenger gas into a plasma.
7. The method, as recited in
8. The method, as recited in
9. The method, as recited in
13. The method, as recited in
14. The method, as recited in
0. 16. The method, as recited in claim 15, wherein the passivation phase comprises:
adsorbing a silicon precursor into the sidewalls of the features in the tungsten containing layer; and
exposing the tungsten containing layer to a plasma that scavenges Cl from the sidewalls.
0. 17. The method, as recited in claim 16, wherein the silicon precursor is SiClx, where x is an integer between 1 and 4.
0. 18. The method, as recited in claim 16, wherein the adsorbing the silicon precursor into the sidewalls comprises:
providing an adsorption gas comprising SiCl4;
forming the adsorption gas into a plasma.
0. 19. The method, as recited in claim 16, wherein the silicon precursor is mixed with at least one inert gas.
0. 20. The method, as recited in claim 16, wherein the exposing the tungsten containing layer to a plasma that scavenges Cl from the sidewalls, comprises:
providing a scavenger gas comprising SO2; and
forming the scavenger gas into a plasma.
0. 21. The method, as recited in claim 15, wherein the passivation layer is etched more slowly than the tungsten containing layer.
0. 22. The method, as recited in claim 15, wherein the plurality of cycles further comprises an opening phase for opening the tungsten containing layer.
0. 23. The method, as recited in claim 22, wherein the opening phase comprises exposing the tungsten containing layer to at least one of perfluorocarbons, O2, SF6, NF, and Cl2.
0. 24. The method, as recited in claim 15, wherein the etch phase is subsequent to the passivation phase in each cycle.
|
This application claims priority under 35 U.S.C. § 119 from U.S. Provisional Patent Application No. 61/719,814, filed Oct. 29, 2012, entitled METHOD OF HIGH ASPECT RATIO TUNGSTEN ETCHING USING SIDEWALL PASSIVATION/DEPOSITION AND ETCHING FOR CD, PROFILE AND LOADING CONTROL UTILIZING THE MIXED MODE PULSING (MMP) PROCESS which is incorporated herein by reference for all purposes.
The invention relates to a method of forming semiconductor devices on a semiconductor wafer. More specifically, the invention relates to etching features in a tungsten-containing layer during the formation of semiconductor devices on a semiconductor wafer.
To achieve the foregoing and in accordance with the purpose of the present invention, a method for etching a tungsten containing layer in an etch diameter is provided. A substrate is placed with a tungsten containing layer in the etch chamber. A plurality of cycles is provided. Each cycle comprises a passivation phase for forming a passivation layer on sidewalls and bottoms of features in the tungsten containing layer. Additionally, each cycle comprises an etch phase for etching features in the tungsten containing layer.
In another manifestation of the invention, a method for forming a passivation layer on sidewalls of etched tungsten features is provided. Etched features having sidewalls are formed in a tungsten layer of a wafer. A halogenated silicon precursor is adsorbed to the sidewalls. The silicon precursor adsorbed to the sidewalls is oxygenated.
These and other features of the present invention will be described in more details below in the detailed description of the invention and in conjunction with the following figures.
The present invention is illustrated by way of example, and not by way of limitation, in the figures of the accompanying drawings and in which like reference numerals refer to similar elements and in which:
The present invention will now be described in detail with reference to a few preferred embodiments thereof as illustrated in the accompanying drawings. In the following description, numerous specific details are set forth in order to provide a thorough understanding of the present invention. It will be apparent, however, to one skilled in the art, that the present invention may be practiced without some or all of these specific details. In other instances, well known process steps and/or structures have not been described in detail in order to not unnecessarily obscure the present invention.
Methods are provided for forming passivation layers on the sidewalls of features of a tungsten layer on a wafer. In particular, a silicon precursor is adsorbed onto the sidewalls of features etched in tungsten. The silicon precursor is then oxygenated, which forms a passivation layer composed of silicon oxide. As such, the sidewalls of the etched tungsten features may have a passivation layer composed of silicon oxide. Further, methods discussed may also form a passivation layer on the bottoms of the features, which may be removed using a breakthrough process.
Passivation layers may be used to etch high aspect ratio features into layers on wafers. In particular, passivation layers may be formed on sidewalls of features. In particular, passivation layers may be used on features having sidewalls and at least one open front. An open front is an exposed area of a layer on a wafer that is to be etched. The open front may be bare, comprising only the material of the layer on the wafer itself. Alternatively, the open from may be modified, having a chemistry that is influenced by treatments used on the open portion of the layer on the wafer.
Sidewalls having a passivation layer may be etched more slowly than an open front of the feature. As such, sidewalls having a passivation layer may be used in high aspect ratio etching where the depth of a feature may be much greater than the width of the feature. A first embodiment of a mixed mode pulsing (MMP) process to be employed for etching a tungsten or tungsten containing layer includes three steps: passivation, breakthrough, and main etch. A second embodiment of a MMP process involves two steps: passivation and main etch. In the second embodiment, a sufficient bias is used in the main etch to effectively breakthrough portions of a passivation layer covering the bottom of etched tungsten features.
In both embodiments, a passivation layer is formed on exposed areas of etched tungsten features. Exposed areas may include sidewalls and bottoms. Once the passivation layer is formed, a breakthrough process may occur in a second step. During the breakthrough process, the bottoms of the features are opened. In particular, the bottoms of the features are opened when the portions of the passivation layer that cover the bottoms of the etched features are removed. Once the bottoms of the features are opened, they are able to be etched. At the same time, the portions of the passivation layer covering the sidewalls remain intact, leaving the sidewalls protected from etching. In a third step, the features are etched. In particular, an etching gas is provided to react with the open front on the bottoms of the features. Since the sidewalls of the features are protected by passivation layers, the etching of the features is preferentially towards the deepening of the feature.
Additionally, there is a breakthrough step (step 112) where portions of the passivation layer are removed. For example, the portions of the passivation that cover bottoms of etched features may be removed. More generally, areas of the etched features that are desired to be etched further may have the portions of the passivation layer that cover those areas removed. Further, there is an etching step (step 116) Where the tungsten layer is etched. In particular, the areas of the etched features that are desired to be etched may be etched.
Once the passivation-etching steps 108, 112, and 116 have been performed, there is determination of whether an etch stop layer has been reached (step 120). If there is a determination that the etch stop layer has been reached, the process stops (step 124). However, if there is a determination that the etch stop layer has not been reached, then the process cycles back to the beginning of the passivation-etching steps, starting at step 108.
In an embodiment of the invention, an exemplary method for etching a tungsten containing layer is provided. Initially, a substrate with a tungsten layer disposed under a mask is provided. Accordingly,
The substrate is placed in an etch chamber.
The plasma power supply 406 and the wafer bias voltage power supply 416 may be configured to operate at specific radio frequencies such as, for example, 13.56 MHz, 27 MHz, 2 MHz, 400 kHz, or combinations thereof. Plasma power supply 406 and wafer bias power supply 416 may be appropriately sized to supply a range of powers in order to achieve desired process performance. For example, in one embodiment of the present invention, the plasma power supply 406 may supply the power in a range of 300 to 10000 Watts, and the wafer bias voltage power supply 416 may supply a bias voltage of in a range of 10 to 1000 V. In addition, the TCP coil 410 and/or the electrode 420 may be comprised of two or more sub-coils or sub-electrodes, which may be powered by a single power supply or powered by multiple power supplies.
As shown in
Information transferred via communications interface 514 may be in the form of signals such as electronic, electromagnetic, optical, or other signals capable of being received by communications interface 514, via a communication link that carries signals and may be implemented using wire or cable, fiber optics, a phone line, a cellular phone link, a radio frequency link, and/or other communication channels. With such a communications interface, it is contemplated that the one or more processors 502 might receive information from a network, or might output information to the network in the course of performing the above-described method steps. Furthermore, method embodiments of the present invention may execute solely upon the processors or may execute over a network such as the Internet in conjunction with remote processors that shares a portion of the processing.
The term “non-transient computer readable medium” is used generally to refer to media such as main memory, secondary memory, removable storage, and storage devices, such as hard disks, flash memory, disk drive memory, CD-ROM and other forms of persistent memory and shall not be construed to cover transitory subject matter, such as carrier waves or signals. Examples of computer code include machine code, such as produced by a compiler, and files containing higher level code that are executed by a computer using an interpreter. Computer readable media may also be computer code transmitted by a computer data signal embodied in a carrier wave and representing a sequence of instructions that are executable by a processor.
The tungsten layer is opened (step 104). In this example, 1000 watts at 13.6 MHz of RF power are provided by the TCP coil 410. A bias of 100 V is also provided and the plasma processing chamber 404 is set at 10 mTorr. The wafer is maintained at 100° C. An opening gas comprising 10 sccm O2, 40 sccm Cl2, and 60 sccm NF3, 50 sccm inert gases is provided to the plasma processing chamber 404. An inert gas is a gas which does not undergo a chemical reaction under a set of given conditions. For example, inert gases include noble gases such as argon and neon. The RF power transforms the opening gas into a plasma. Alternatively, 600 watts at 13.56 MHz of RF power are provided by the TCP coil 410. A pulsing bias from 0-850V is also provided at a pulsing frequency of 100 Hz with Bias ON for 15% and the processing chamber 404 is set at 5 mTorr. The wafer is maintained at 60° C. An opening gas comprising of 110 sccm CF4, 90 sccm O2 and 15 sccm NF3 is provided to the processing chamber. Accordingly,
The open tungsten layer is passivated (step 108). In particular,
Once excess Cl− radicals have been removed from the tungsten layer, silicon precursors are deposited (step 208) on the tungsten layer. In particular, the silicon precursors are deposited on sidewalls of tungsten features in the tungsten layer. The silicon precursors are adsorbed to the sidewalls. In particular, the tungsten layer may be exposed to a silicon precursor, such as SiCl4. In this example, 1000 watts at 13.56 MHz of RF power are provided by the TCP coil 410. The plasma processing chamber 404 is set at 50 mTorr. The wafer is maintained at 120° C. A silicon precursor gas comprising 100 sccm SiCl4 is provided to the plasma processing chamber 404. In particular, the silicon precursor gas is provided to the plasma processing chamber 404 in a gaseous form so as to allow for uniform distribution across the exposed areas of the tungsten layer. Accordingly,
Other examples of a silicon precursor that may be used include SiF4,, SiCO4, SiH4, disilane, etc, or a combination of silicon precursors thereof. The silicon precursor may be adsorbed to the exposed areas of the etched tungsten features. In particular, the silicon precursor may be adsorbed to the exposed areas of the etched tungsten features using a gaseous distribution, allowing the silicon precursor to be adsorbed in a uniform manner. Further, the silicon precursor is provided in gaseous form. In embodiments, the silicon precursor may be mixed with inerts, such as He, Ar, N2, etc.
Further, the silicon precursors are oxygenated to form a protective layer (step 212). During the oxygenating step, excess halogens are scavenged by the oxygenating plasma. As such, the oxygenating plasma is a halogen scavenger. The oxygenating plasma also oxygenates the silicon component of the silicon precursors that are adsorbed to the tungsten features. Accordingly, after the silicon precursor has been adsorbed to the surface of the exposed areas of the etched tungsten features, an oxidizing plasma is provided. In this example, 1000 watts at 13.6 MHz of RF power are provided by the TCP coil 410. The plasma processing chamber 404 is set at 50 mTorr. The wafer is maintained at 120° C. An oxygenating gas comprising 200 sccm SO2, and 100 sccm inert gases is provided to the plasma processing chamber 404. Additionally, the RF power transforms the oxygenating gas into a plasma. Accordingly,
In this example, silicon precursor layer 314 is SiCl4. In particular, O radicals will react with the SiClx adsorbed to the exposed areas to form a silicon oxide such as SiOx, where “x” may vary. As such, the oxidizing plasma oxidizes the silicon precursor and also scavenges the excess Cl− radicals that result from the oxidation of the silicon precursor. The characteristic of the oxidizing plasma to scavenge the Cl− radicals prevents the Cl− radicals from forming a volatile etching component such as WOCl. Further, the oxidizing plasma interacts with the adsorbed silicon precursor at the surface of the tungsten features. This allows for the uniform formation of a passivation layer. In particular, since the silicon precursor layer is uniformly adsorbed to the surface of the etched tungsten features, the resulting oxidation at the points of adsorption is similarly uniform. Further, the formation of the SiOx passivation layer may be tuned by controlling the pressure, temperature, and/or dosage of the components. As such, the deposited film may be adjusted to aid in loading control. For example, a thicker film may be deposited in the open/perimeter areas and a thinner film may be deposited in the isolated or dense/array areas. This tunable deposition loading helps to achieve a tunable etch/loading control between dense and isolated features.
Once the passivation layer has been formed, a next (step 216) breakthrough process may be used to clear the deposited film from the open front (step 112), thereby opening it for subsequent etch step. This breakthrough process does not attack the sidewalls, but only the open front, as it is a very directional process. In discussed embodiments, the open front is at the bottom of the etched tungsten features. In further embodiments, however, the open front may refer to an area that is desired to be etched in the features. As such, in embodiments, an open front may be formed on a portion of a sidewall that is not desired to be protected.
In this example, 600 watts at 13.6 MHz of RF power are provided by the TCP coil 410. A bias of 850 V is also provided and the plasma processing chamber 404 is set at 10 mTorr. The wafer is maintained at 120° C. A breakthrough gas comprising, 100 sccm Cl2 is provided to the plasma processing chamber 404. Additionally, the RF power transforms the breakthrough gas into a plasma. Accordingly,
With the open front opened to expose the tungsten underneath, and with the sidewalls now protected by the deposited SiOx film, etching (step 116) can be continued with the etch chemistry (CF4, PFC's, O2, SF6, NF3, Cl2, COS, etc). A series of cycles using this cyclic deposition/passivation, breakthrough, and etch steps leads to tunable sidewall profiles, CD, and loading controls. This process can be accomplished using the MMP process as described herein for high throughput in production.
As such,
In this example, 600 watts at 13.6 MHz of RF power are provided by the TCP coil 410. A bias of 100 V is also provided and the plasma processing chamber 404 is set at 10 mTorr. The wafer is maintained at 100° C. An etching gas comprising 30 sccm O2, 40 sccm Cl2, 60 sccm NF3, and 100 sccm inert gases is provided to the plasma processing chamber 404. Additionally, the RF power transforms the etching gas into a plasma.
The embodiments as described provide formation of a passivation layer over etched tungsten features. In particular, the passivation chemistry that is used to form a passivation layer on the etched tungsten features is distinct from the passivation chemistry that may be used on other materials, such as silicon. In particular, prior to the present invention, there has been no known passivation chemistry that forms a passivation layer on etched tungsten. While there was a prior passivation chemistry for forming a passivation layer on silicon, the method used does not result in the formation of a passivation layer on etched tungsten. Rather, the prior method utilized SiCl4 that was oxidized using O2, which resulted in excess Cl− and O radicals that reacted with W to form WOCl, a volatile species that etches tungsten. Accordingly, in order to form a passivation layer on etched tungsten, an approach was needed that would avoid the formation of etching species, such as WOCl. As such, methods provided herein provide an oxidizing plasma that is able to scavenge excess ions, such as Cl−, that may result from the oxidation of a silicon precursor. Preferably, the steps of the first embodiment of the MMP process (passivation, breakthrough, and main etch) are not simultaneous. Rather, they are performed sequentially. Additionally, the steps of the second embodiment of the MMP process (passivation, main etch) are also not simultaneous. Rather, they are performed sequentially.
While this invention has been described in terms of several preferred embodiments, there are alterations, permutations, and various substitute equivalents, which fall within the scope of this invention. It should also be noted that there are many alternative ways of implementing the methods and apparatuses of the present invention. It is therefore intended that the following appended claims be interpreted as including all such alterations, permutations, and various substitute equivalents as fall within the true spirit and scope of the present invention.
Subramanian, Ramkumar, Yamaguchi, Yoko, Le Gouil, Anne
Patent | Priority | Assignee | Title |
Patent | Priority | Assignee | Title |
4992136, | Jul 29 1987 | Hitachi, Ltd. | Dry etching method |
5702983, | Nov 02 1993 | Sony Corporation | Method for manufacturing a semiconductor device with a metallic interconnection layer |
6461974, | Oct 06 2000 | Lam Research Corporation | High temperature tungsten etching process |
6746961, | Jun 19 2001 | Lam Research Corporation | Plasma etching of dielectric layer with etch profile control |
8609546, | Nov 29 2007 | Lam Research Corporation | Pulsed bias plasma process to control microloading |
20030092280, | |||
20030235994, | |||
20030235995, | |||
20060284272, | |||
20110151670, | |||
20110244686, |
Executed on | Assignor | Assignee | Conveyance | Frame | Reel | Doc |
May 08 2013 | LE GOUIL, ANNE | Lam Research Corporation | ASSIGNMENT OF ASSIGNORS INTEREST SEE DOCUMENT FOR DETAILS | 050031 | /0084 | |
May 09 2013 | SUBRAMANIAN, RAMKUMAR | Lam Research Corporation | ASSIGNMENT OF ASSIGNORS INTEREST SEE DOCUMENT FOR DETAILS | 050031 | /0084 | |
May 09 2013 | YAMAGUCHI, YOKO | Lam Research Corporation | ASSIGNMENT OF ASSIGNORS INTEREST SEE DOCUMENT FOR DETAILS | 050031 | /0084 | |
Mar 10 2017 | Lam Research Corporation | (assignment on the face of the patent) | / |
Date | Maintenance Fee Events |
Jul 05 2023 | M1552: Payment of Maintenance Fee, 8th Year, Large Entity. |
Date | Maintenance Schedule |
Oct 15 2022 | 4 years fee payment window open |
Apr 15 2023 | 6 months grace period start (w surcharge) |
Oct 15 2023 | patent expiry (for year 4) |
Oct 15 2025 | 2 years to revive unintentionally abandoned end. (for year 4) |
Oct 15 2026 | 8 years fee payment window open |
Apr 15 2027 | 6 months grace period start (w surcharge) |
Oct 15 2027 | patent expiry (for year 8) |
Oct 15 2029 | 2 years to revive unintentionally abandoned end. (for year 8) |
Oct 15 2030 | 12 years fee payment window open |
Apr 15 2031 | 6 months grace period start (w surcharge) |
Oct 15 2031 | patent expiry (for year 12) |
Oct 15 2033 | 2 years to revive unintentionally abandoned end. (for year 12) |