Embolic compositions

Abstract

Embolic compositions comprising macromers having a backbone comprising a polymeric backbone comprising units with a 1,2-diol or 1,3-diol structure, such as polyvinyl alcohol, and pendant chains bearing crosslinkable groups and, optionally, other modifiers. When crosslinked, the macromers form hydrogels having many properties advantageous for use as embolic agents to block and fill lumens and spaces. The embolic compositions can be used as liquid embolic agents and crosslinked in situ or as preformed embolic articles, such as microspheres.

Description

wherein p and q are zero or one and

R₉ and R₁₀ are each independently lower alkylene having from 2 to 8 carbon atoms, arylene having from 6 to 12 carbon atoms, a saturated divalent cycloaliphatic group having from 6 to 10 carbon atoms, arylenealkylene or alkylenearylene having from 7 to 14 carbon atoms or arylenealkylenearylene having from 13 to 16 carbon atoms, and

R₈ is as defined above.

Lower alkylene R₉ or R₁₀ preferably has from 2 to 6 carbon atoms and is especially straight-chained. Suitable examples include propylene, butylene, hexylene, dimethylethylene and, especially preferably, ethylene.

Arylene R₉ or R₁₀ is preferably phenylene that is unsubstituted or is substituted by lower alkyl or lower alkoxy, especially 1,3-phenylene or 1,4-phenylene or methyl-1,4-phenylene.

A saturated divalent cycloaliphatic group R₉ or R₁₀ is preferably cyclohexylene or cyclohexylene-lower alkylene, for example cyclohexylenemethylene, that is unsubstituted or is substituted by one or more methyl groups, such as, for example, trimethylcyclohexylenemethylene, for example the divalent isophorone radical.

The arylene unit of alkylenearylene or arylenealkylene R₉ or R₁₀ is preferably phenylene, unsubstituted or substituted by lower alkyl or lower alkoxy, and the alkylene unit thereof is preferably lower alkylene, such as methylene or ethylene, especially methylene. Such radicals R₉ or R₁₀ are therefore preferably phenylenemethylene or methylenephenylene.

Arylenealkylenearylene R₉ or R₁₀ is preferably phenylene-lower alkylene-phenylene having up to 4 carbon atoms in the alkylene unit, for example phenyleneethylenephenylene.

The groups R₉ and R₁₀ are each independently preferably lower alkylene having from 2 to 6 carbon atoms, phenylene, unsubstituted or substituted by lower alkyl, cyclohexylene or cyclohexylene-lower alkylene, unsubstituted or substituted by lower alkyl, phenylene-lower alkylene, lower alkylenephenylene or phenylene-lower alkylene-phenylene.

The group —R₉—NH—CO—O— is present when q is one and absent when q is zero. Macromers in which q is zero are preferred.

The group —CO—NH—(R₉—NH—CO—O)_q—R₁₀—O— is present when p is one and absent when p is zero. Macromers in which p is zero are preferred.

In macromers in which p is one, q is preferably zero. Macromers in which p is one, q is zero, and R₁₀ is lower alkylene are especially preferred.

All of the above groups can be monosubstituted or polysubstituted, examples of suitable substituents being the following: C₁-C₄ alkyl, such as methyl, ethyl or propyl, —COOH, —OH, —SH, C₁-C₄ alkoxy (such as methoxy, ethoxy, propoxy, butoxy, or isobutoxy), —NO₂, —NH₂, —NH(C₁-C₄), —NH—CO—NH₂, —N(C₁-C₄ alkyl)₂, phenyl (unsubstituted or substituted by, for example, —OH or halogen, such as Cl, Br or especially I), —S(C₁-C₄ alkyl), a 5- or 6-membered heterocyclic ring, such as, in particular, indole or imidazole, —NH—C(NH)—NH₂, phenoxyphenyl (unsubstituted or substituted by, for example, —OH or halogen, such as Cl, Br or especially I), an olefinic group, such as ethylene or vinyl, and CO—NH—C(NH)—NH₂.

Preferred substituents are lower alkyl, which here, as elsewhere in this description, is preferably C₁-C₄ alkyl, C₁-C₄ alkoxy, COOH, SH, —NH₂, —NH(C₁-C₄ alkyl), —N(C₁-C₄ alkyl)₂ or halogen. Particular preference is given to C₁-C₄ alkyl, C₁-C₄ alkoxy, COOH and SH.

For the purposes of this invention, cycloalkyl is, in particular, cycloalkyl, and aryl is, in particular, phenyl, unsubstituted or substituted as described above.

Modifiers

The macromers can include further modifier groups and crosslinkable groups. Some such groups are described in U.S. Pat. Nos. 5,508,317, 5,665,840, 5,807,927, 5,849,841, 5,932,674, 5,939,489, and 6,011,077. Crosslinkable groups and the optional further modifier groups can be bonded to the macromer backbone in various ways, for example through a certain percentage of the 1,3-diol units being modified to give a 1,3-dioxane, which contains a crosslinkable group, or a further modifier, in the 2-position. Modifiers that might be attached to the backbone include those to modify the hydrophobicity, active agents or groups to allow attachment of active agents, photoinitiators, modifiers to enhance or reduce adhesiveness, modifiers to impart thermoresponsiveness, modifiers to impart other types of responsiveness, and additional crosslinking groups. These modifiers may be attached to the hydroxyl groups in the backbone, or to other monomeric units included in the backbone.

Attaching a cellular adhesion promoter to the macromers can enhance cellular attachment or adhesiveness of the embolic agents formed by the embolic compositions. These agents are well known to those skilled in the art and include carboxymethyl dextran, proteoglycans, collagen, gelatin, glucosaminoglycans, fibronectin, lectins, polycations, and natural or synthetic biological cell adhesion agents such as RGD peptides.

Having pendant ester groups that are substituted by acetaldehyde or butyraldehyde acetals, for example, can increase the hydrophobicity of the macromers and the formed hydrogel. Hydrophobic groups can desirably be present in an amount from about 0 to 25%.

It may also be desirable to include on the macromer a molecule that allows visualization of the formed hydrogel. Examples include dyes and molecules visualizable by magnetic resonance imaging.

Degradable Regions

The macromers can form a hydrogel that is degradable. Suitable degradable systems are described in U.S. patent application Ser. No. 09/714,700, titled “Degradable Poly(Vinyl Alcohol) Hydrogels” and filed on Nov. 15, 2000. In the degradable systems described in that application, the macromers include a degradable region in the backbone or on a pendant chain. The degradable region is preferably degradable under in vivo conditions by hydrolysis. The degradable region can be enzymatically degradable. For example, the degradable region may be polymers and oligomers of glycolide, lactide, ϵ-caprolactone, other hydroxy acids, and other biologically degradable polymers that yield materials that are non-toxic or present as normal metabolites in the body. Preferred poly(α-hydroxy acids) are poly(glycolic acid), poly (DL-lactic acid) and poly(L-lactic acid). Other useful materials include poly(amino acids), poly(anhydrides), poly (orthoesters), poly(phosphazines), and poly(phosphoesters). Polylactones such as poly(ϵ-caprolactone), poly(ϵ-caprolactone), poly(δ-valerolactone) and poly(γ-butyrolactone), for example, are also useful. Enzymatically degradable linkages include poly(amino acids), gelatin, chitosan, and carbohydrates. The biodegradable regions may have a degree of polymerization ranging from one up to values that would yield a product that was not substantially water soluble. Thus, monomeric, dimeric, trimeric, oligomeric, and polymeric regions may be used. The biodegradable region could, for example, be a single methacrylate group.

Biodegradable regions can be constructed from polymers or monomers using linkages susceptible to biodegradation, such as ester, acetal, carbonate, peptide, anhydride, orthoester, phosphazine, and phosphoester bonds. The biodegradable regions may be arranged within the macromers such that the formed hydrogel has a range of degradability, both in terms of extent of degradation, whether complete or partial, and in terms of time to complete or partial degradation.

Synthesis of Macromers

The macromers can be made by general synthetic methods known to those skilled in the art. The specific macromers discussed above can be made as described in U.S. Pat. Nos. 5,508,317, 5,665,840, 5,807,927, 5,849,841, 5,932,674, 5,939,489, and 6,011,077.

The specific macromers described above are extraordinarily stable. Spontaneous crosslinking by homopolymerization does not typically occur. The macromers can furthermore be purified in a manner known per se, for example by precipitation with organic solvents, such as acetone, extraction in a suitable solvent, washing, dialysis, filtration, or ultrafiltration. Ultrafiltration is especially preferred. By means of the purification process the macromers can be obtained in extremely pure form, for example in the form of concentrated aqueous solutions that are free, or at least substantially free, from reaction products, such as salts, and from starting materials.

The preferred purification process for the macromers of the invention, ultrafiltration, can be carried out in a manner known per se. It is possible for the ultrafiltration to be carried out repeatedly, for example from two to ten times. Alternatively, the ultrafiltration can be carried out continuously until the selected degree of purity is attained. The selected degree of purity can in principle be as high as desired. A suitable measure for the degree of purity is, for example, the sodium chloride content of the solution, which can be determined simply in a known manner, such as by conductivity measurements.

The macromers are crosslinkable in an extremely effective and controlled manner.

Vinylic Comonomers

The process for polymerization of the macromers may comprise, for example, crosslinking a macromer comprising units of formula I, especially in substantially pure form, that is to say, for example, after single or repeated ultrafiltration, preferably in solution, especially in aqueous solution, in the absence or presence of an additional vinylic comonomer.

The vinylic comonomer may be hydrophilic or hydrophobic, or a mixture of a hydrophobic and a hydrophilic vinylic monomer. Generally, approximately from 0.01 to 80 units of a typical vinylic comonomer react per unit of formula I, especially from 1 to 30 units per unit of formula I, and especially preferably from 5 to 20 units per unit of formula I.

It is also preferable to use a hydrophobic vinylic comonomer or a mixture of a hydrophobic vinylic comonomer with a hydrophilic vinylic comonomer, the mixture comprising at least 50 percent by weight of a hydrophobic vinylic comonomer. In that manner the mechanical properties of the polymer can be improved without the water content falling substantially. In principle, however, both conventional hydrophobic vinylic comonomers and conventional hydrophilic vinylic comonomers are suitable for copolymerization with the macromer.

Suitable hydrophobic vinylic comonomers include, without the list being exhaustive, C₁-C₁₈ alkyl acrylates and methacrylates, C₃-C₁₈ alkyl acrylamides and methacrylamides, acrylonitrile, methacrylonitrile, vinyl-C₁-C₁₈ alkanoates, C₂-C₁₈ alkenes, C₂-C₁₈ haloalkenes, styrene, C₁-C₆ alkylstyrene, vinyl alkyl ethers, in which the alkyl moiety contains from 1 to 6 carbon atoms, C₂-C₁₀ perfluoroalkyl acrylates and methacrylates or correspondingly partially fluorinated acrylates and methacrylates, C₃-C₁₂ perfluoroalkyl-ethylthiocarbonylaminoethyl acrylates and methacrylates, acryloxy- and methacryloxy-alkylsiloxanes, N-vinylcarbazole, C₃-C₁₂ alkyl-esters of maleic acid, fumaric acid, itaconic acid, mesaconic acid and the like. C₁-C₄ alkyl esters of vinylically unsaturated carboxylic acids having from 3 to 5 carbon atoms or vinyl esters of carboxylic acids having up to 5 carbon atoms, for example, are preferred.

Examples of suitable hydrophobic vinylic comonomers include methyl acrylate, ethyl acrylate, propyl acrylate, isopropyl acrylate, cyclohexyl acrylate, 2-ethylhexyl acrylate, methyl methacrylate, ethyl methacrylate, propyl methacrylate, vinyl acetate, vinyl propionate, vinyl butyrate, vinyl valerate, styrene, chloroprene, vinyl chloride, vinylidene chloride, acrylonitrile, 1-butene, butadiene, methacrylonitrile, vinyltoluene, vinyl ethyl ether, perfluorohexylethylthiocarbonylaminoethyl methacrylate, isobornyl methacrylate, trifluoroethyl methacrylate, hexafluoroisopropyl methacrylate, hexafluorobutyl methacrylate, tris-trimethylsilyloxy-silyl-propyl methacrylate, 3-methacryloxypropylpentamethyldisiloxane and bis(methacryloxypropyl)tetramethyldisiloxane.

Suitable hydrophilic vinylic comonomers include, without the list being exhaustive, hydroxy-substituted lower alkyl acrylates and methacrylates, acrylamide, methacrylamide, lower alkyl acrylamides and methacrylamides, ethoxylated acrylates and methacrylates, hydroxy-substituted lower alkyl acrylamides and methacrylamides, hydroxy-substituted lower alkyl vinyl ethers, sodium ethylenesulfonate, sodium styrenesulfonate, 2-acrylamido-2-methylpropanesulfonic acid (AMPS® monomer from Lubrizol Corporation), N-vinylpyrrole, N-vinylsuccinimide, N-vinylpyrrolidone, 2- or 4-vinylpyridine, acrylic acid, methacrylic acid, amino- (the term “amino” also including quaternary ammonium), mono-lower alkylamino- or di-lower alkylamino-lower alkyl acrylates and methacrylates, allyl alcohol and the like. Hydroxy-substituted C₂-C₄ alkyl(meth)acrylates, five- to seven-membered N-vinyl lactams, N,N-di-C₁-C₄ alkyl(meth)acrylamides and vinylically unsaturated carboxylic acids having a total of from 3 to 5 carbon atoms, for example, are preferred.

Contrast Agents

It may be desirable to include a contrast agent in the embolic compositions. A contrast agent is a biocompatible (non-toxic) material capable of being monitored by, for example, radiography. The contrast agent can be water soluble or water insoluble. Examples of water soluble contrast agents include metrizamide, iopamidol, iothalamate sodium, iodomide sodium, and meglumine. Iodinated liquid contrast agents include Omnipaque®, Visipaque®, and Hypaque-76®. Examples of water insoluble contrast agents are tantalum, tantalum oxide, barium sulfate, gold, tungsten, and platinum. These are commonly available as particles preferably having a size of about 10 μm or less.

The contrast agent can be added to the embolic compositions prior to administration. Both solid and liquid contrast agents can be simply mixed with a solution of the liquid embolic compositions or with the solid articles. Liquid contrast agent can be mixed at a concentration of about 10 to 80 volume percent, more desirably about 20 to 50 volume percent. Solid contrast agents are desirably added in an amount of about 10 to 40 weight percent, more preferably about 20 to 40 weight percent.

Occlusive Devices

It may be desirable to use the embolic compositions in combination with one or more occlusive devices. Such devices include balloons, microcoils, and other devices known to those skilled in the art. The device can be placed at the site to be occluded or filled before, during, or after the embolic composition is administered. For example, an occlusive coil can be placed in an aneurysm sac to be filled and the liquid embolic composition can be injected into the sac to fill the space around the coil. An advantage of using an occlusive device along with the embolic composition is that it may provide greater rigidity to the filling.

Active Agents

An effective amount of one or more biologically active agents can be included in the embolic compositions. It may be desirable to deliver the active agent from the formed hydrogel. Biologically active agents that it may be desirable to deliver include prophylactic, therapeutic, and diagnostic agents including organic and inorganic molecules and cells (collectively referred to herein as an “active agent” or “drug”). A wide variety of active agents can be incorporated into the hydrogel. Release of the incorporated additive from the hydrogel is achieved by diffusion of the agent from the hydrogel, degradation of the hydrogel, and/or degradation of a chemical link coupling the agent to the polymer. In this context, an “effective amount” refers to the amount of active agent required to obtain the desired effect.

Examples of active agents that can be incorporated include, but are not limited to, anti-angiogenic agents, chemotherapeutic agents, radiation delivery devices, such as radioactive seeds for brachytherapy, and gene therapy compositions.

Chemotherapeutic agents that can be incorporated include water soluble chemotherapeutic agents, such as cisplatin (platinol), doxorubicin (adriamycin, rubex), or mitomycin C (mutamycin). Other chemotherapeutic agents include iodinated fatty acid ethyl esters of poppy seed oil, such as lipiodol.

Cells can be incorporated into the embolic compositions, including cells to encourage tissue growth or cells to secrete a desired active agent. For example, cells that can be incorporated include fibroblasts, endothelial cells, muscle cells, stem cells, etc. Cells can be modified to secrete active agents such as growth factors.

Active agents can be incorporated into the liquid embolic compositions simply by mixing the agent with the embolic composition prior to administration. The active agent will then be entrapped in the hydrogel that is formed upon administration of the embolic composition. Active agents can be incorporated into the preformed embolic articles through encapsulation and other methods known in the art and discussed further below. The active agent can be in compound form or can be in the form of degradable or nondegradable nano or microspheres. It some cases, it may be possible and desirable to attach the active agent to the macromer or to the preformed article. The active agent may also be coated onto the surface of the preformed article. The active agent may be released from the macromer or hydrogel over time or in response to an environmental condition.

Other Additives

It may be desirable to include a peroxide stabilizer in redox initiated systems. Examples of peroxide stabilizers are Dequest® products from Solutia Inc., such as for example Dequest® 2010 and Dequest® 2060S. These are phosphonates and chelants that offer stabilization of peroxide systems. Dequest® 2060S is diethylenetriamine penta(methylene phosphonic acid). These can be added in amounts as recommended by the manufacturer.

It may be desirable to include fillers in the embolic compositions, such as fillers that leach out of the formed hydrogel over a period of time and cause the hydrogel to become porous. Such may be desirable, for example, where the embolic composition is used for chemoembolization and it may be desirable to administer a follow up dose of chemoactive agent. Appropriate fillers include calcium salts, for example.

Characteristics that can be Modified

The embolic compositions are highly versatile. A number of characteristics can be easily modified, making the embolic compositions suitable for a number of applications. For example, as discussed above, the polymer backbones can include comonomers to add desired properties, such as, for example, thermoresponsiveness, degradability, gelation speed, and hydrophobicity. Modifiers can be attached to the polymer backbone (or to pendant groups) to add desired properties, such as, for example, thermoresponsiveness, degradability, hydrophobicity, and adhesiveness. Active agents can also be attached to the polymer backbone using the free hydroxyl groups, or can be attached to pendant groups.

The gelation time of the liquid embolic compositions can be varied from about 0.5 seconds to as long as 10 minutes, and longer if desired. However, the preferred gelation time for most liquid embolic applications will be less than about 5 seconds, desirably less than about 2 seconds. The desired gelation time will depend upon whether it is desired to form a plug near the catheter tip or to form a more diffuse network. A longer gelation time will generally be required if crosslinking is initiated a distance from the intended embolic site.

The gelation time will generally be affected by, and can be modified by changing at least the following variables: the initiator system, crosslinker density, macromer molecular weight, macromer concentration (solids content), and type of crosslinker. A higher crosslinker density will provide faster gelation time; a lower molecular weight will provide a slower gelation time. A higher solids content will provide faster gelation time. For redox systems the gelation time can be designed by varying the concentrations of the redox components. Higher reductant and higher oxidant will provide faster gelation, higher buffer concentration and lower pH will provide faster gelation.

The firmness of the formed hydrogel will be determined in part by the hydrophilic/hydrophobic balance, where a higher hydrophobic percent provides a firmer hydrogel. The firmness will also be determined by the crosslinker density (higher density provides a firmer hydrogel), the macromer molecular weight (lower MW provides a firmer hydrogel), and the length of the crosslinker (a shorter crosslinker provides a firmer hydrogel).

The swelling of the hydrogel is inversely proportional to the crosslinker density. Generally, no or minimal swelling is desired, desirably less than about 10 percent.

Elasticity of the formed hydrogel can be increased by increasing the size of the backbone between crosslinks and decreasing the crosslinker density. Incomplete crosslinking will also provide a more elastic hydrogel. Preferably the elasticity of the hydrogel substantially matches the elasticity of the tissue to which the embolic composition is to administered.

Making Preformed Embolic Articles

Preformed articles are made, in general, by dissolving macromers in an appropriate solvent, shaping the macromers such as by pouring the macromer solution in a mold, if desired, and crosslinking the macromers. A mold is suitable for use in making rod shaped articles, for example. Microparticles can be made by forming a hydrogel sheet and milling it into particles. Such particles will be irregular in size and shape.

In one embodiment, the preformed articles are spherical microparticles termed microspheres. Microparticles can be made by a number of techniques known to those skilled in the art, such as single and double emulsion, suspension polymerization, solvent evaporation, spray drying, and solvent extraction. Methods for making microspheres are described in the literature, for example, in Mathiowitz and Langer, J. Controlled Release 5:13-22 (1987); Mathiowitz et al., Reactive Polymers 6:275-283 (1987); Mathiowitz et al., J. Appl. Polymer Sci. 35:755-774 (1988); Mathiowitz et al., Scanning Microscopy 4:329-340 (1990); Mathiowitz et al., J. Appl. Polymer Sci., 45:125-134 (1992); and Benita et al., J. Pharm. Sci. 73:1721-1724 (1984).

In solvent evaporation, described for example in Mathiowitz et al., (1990), Benita et al. (1984), and U.S. Pat. No. 4,272,398, the macromers are dissolved in a solvent. If desired, an agent to be incorporated, either in soluble form or dispersed as fine particles, is added to the macromer solution, and the mixture is suspended in an aqueous phase that contains a surface active agent. The resulting emulsion is stirred until most of the solvent evaporates, leaving solid microspheres, which may be washed with water and dried overnight in a lyophilizer. The microspheres are polymerized, for example, by exposure to light.

In solvent removal, the macromers are dissolved in a solvent. The mixture can then be suspended in oil, such as silicon oil, by stirring, to form an emulsion. As the solvent diffuses into the oil phase, the emulsion droplets harden into solid polymer microspheres. The microspheres can be polymerized by exposure to light, for example.

Spray drying is implemented by passing the polymerizable macromers used to form the hydrogel through a nozzle, spinning disk or equivalent device to atomize the mixture to form fine droplets. The polymerizable macromers may be provided in a solution or suspension, such as an aqueous solution. The fine droplets are exposed to light, for example, to cause polymerization of the macromer and formation of the hydrogel microspheres.

In another embodiment, hydrogel particles are prepared by a water-in-oil emulsion or suspension process, wherein the polymerizable macromers and the substance to be incorporated, if desired, are suspended in a water-in-oil suspension and exposed to light to polymerize the macromers to form hydrogel particles incorporating the substance, such as a biologically active agent.

In another embodiment, microspheres can be formed by atomizing macromer solution into oil, followed by polymerization.

There are many variables that affect the size, size distribution, and quality of the micro spheres formed. An important variable is the choice of stabilizer. Good stabilizers have an HLB number from 1 to 4 and have some solubility in the oil phase. Some appropriate stabilizers include cellulose acetate butyrate (with 17% butyrate), sorbitan oleates, and dioctylsulphosuccinate. The amount and type of stabilizer will control the particle size and reduce coalescing of the particles during crosslinking. The oil can be a water-insoluble oil such as liquid paraffin, but water-insoluble halogenated solvents such as dichloroethane are commonly used. The ratio of water to oil is also important and desirably ranges from about 1:1 to 1:4.

Microspheres can be made in sizes ranging from about 10 microns to 2000 microns. In most applications it will be desirable to have a small size range of microspheres. The process used to make the microspheres can be controlled to achieve a particular desired size range of microspheres. Other methods, such as sieving, can be used to even more tightly control the size range of the microspheres.

Active agents can be included in the microspheres as described above. It may be desirable to coat the microspheres in modifiers or active agents, such as, for example, agents to increase cellular attachment. Such coating can be done by methods known to those skilled in the art.

II. Methods of Using the Embolic Compositions

The embolic compositions can be used for a variety of applications such as, but not limited to, vascular occlusion for treatment of tumors or fibroids, occlusion of vascular malformations, such as arteriovenous malformations (AVM), occlusion of the left atrial appendage, fillers for aneurysm sacs, endoleak sealants, arterial sealants, puncture sealants, and occlusion of other lumens such as fallopian tubes.

According to the general method, an effective amount of the embolic composition in an aqueous solvent is administered into a lumen or void. In one embodiment, the macromers are crosslinked in situ. The term “effective amount”, as used herein, means the quantity of embolic composition needed to fill or block the biological structure of interest. The effective amount of embolic composition administered to a particular patient will vary depending upon a number of factors, including the sex, weight, age, and general health of the patient, the type, concentration, and consistency of the macromers and the hydrogel that results from crosslinking, and the particular site and condition being treated. The macromers may be administered over a number of treatment sessions.

The methods of using the liquid embolic compositions involve combining the components, including any comonomers and other additives, under conditions suitable for crosslinking of the macromers. The crosslinking is suitably carried out in a solvent. A suitable solvent is in principle any solvent that dissolves the macromers, for example water, alcohols, such as lower alkanols, for example ethanol or methanol, also carboxylic acid amides, such as dimethylformamide, or dimethyl sulfoxide, and also a mixture of suitable solvents, such as, for example, a mixture of water with an alcohol, such as, for example, a water/ethanol or a water/methanol mixture. The combination of the macromers is preferably carried out in a substantially aqueous solution. In accordance with the invention, the criterion that the macromer is soluble in water denotes in particular that the macromer is soluble in a concentration of approximately from 3 to 90 percent by weight, preferably approximately from 5 to 60 percent by weight, in a substantially aqueous solution. Insofar as it is possible in an individual case, macromer concentrations of more than 90 percent are also included in accordance with the invention.

Within the scope of this invention, substantially aqueous solutions of the macromer comprise especially solutions of the macromer in water, in aqueous salt solutions, especially in aqueous solutions that have an osmolarity of approximately from 200 to 450 milliosmol per 1000 ml (mOsm/l), preferably an osmolarity of approximately from 250 to 350 mOsm/l, especially approximately 300 mOsm/l, or in mixtures of water or aqueous salt solutions with physiologically tolerable polar organic solvents, such as, for example, glycerol. Solutions of the macromer in water or in aqueous salt solutions are preferred.

The viscosity of the solution of the macromer in the substantially aqueous solution is, within wide limits, not critical, but the solution should preferably be a flowable solution that can be delivered through an appropriately sized catheter or syringe. For delivery through microcatheters, viscosities in the range of about 10 to 50 cp are desirable. The viscosity can be substantially higher for delivery through a syringe. The viscosity will generally be controlled by the molecular weight of the macromers, the solids content of the solution, and the type and amount of contrast agent present.

The solids content of the solution will preferably range from about 2 percent by weight to about 30 percent by weight, desirably from about 6 to 12 percent by weight.

In one embodiment, the macromers are crosslinkable via free radical polymerization. In one embodiment, the crosslinking initiator is mixed with the macromer solution before administration, during administration, or after administration. For example, a redox system can be mixed with the macromer solution at the time of administration. In one embodiment, the crosslinking initiator may be present at the site of administration. For example, the initiator could be a substance, such as charged blood components, present at the site. Macromers can be used that crosslink when they contact each other. These can be mixed before, during, or after administration. In one embodiment, the crosslinking initiator is an applied stimulus, such as light or heat, which causes crosslinking. Suitable initiators are known for thermal, photo, and redox initiated polymerization. In a redox initiated system employing ferrous ion, peroxide, and ascorbate, the desired amounts of the components will be determined by concerns related to gelation speed, toxicity, extent of gelation desired, and stability. Very generally, the concentration of iron will be about 20 to 1000 ppm; the concentration of hydrogen peroxide will be about 10 to 1000 ppm; the pH will be about 3 to 7; the buffer concentration will be about 10 to 200 mM; and ascorbate concentration will be about 10 to 40 mM.

It may be desirable, if initiator is added before administration, to use a system that provides delayed crosslinking so that the embolic composition does not gel too early. Moreover, using delayed curing, the composition can assume or be formed into a desired shape before complete curing has occurred.

In some embodiments, the embolic composition should be injected before substantial crosslinking of the macromers has occurred. This allows the macromers to continue crosslinking in situ and prevents blockage of the syringe needle or catheter with gelled polymer. In addition, such in situ crosslinking may allow anchoring of the hydrogel to host tissue by covalently bonding with collagen molecules present within the host tissue.

Since the embolic compositions preferably comprise no undesired low-molecular-weight constituents, the crosslinked hydrogel products also comprise no such constituents. The embolic agents obtainable by the embolic compositions are therefore distinguished, in an advantageous embodiment, by the fact that they are extremely clean.

The embolic compositions can be used in combination with other methods. For example, the embolic compositions can be used with thermal or laser ablation, where the liquid embolic agent may be placed initially, followed by thermal or laser ablation, to provide a synergistic effect with enhanced efficacy.

The preformed embolic articles can be administered similarly to how solid embolic agents are presently administered. The microspheres will desirably be supplied in physiological, sterile saline. A microcatheter, for example, can be used to deliver the microspheres to the desired administration site. It may be desirable to mix a contrast agent and/or chemotherapeutic agent with the microspheres before administration.

Delivery Devices

The compositions can be delivered to the intended site of embolism using delivery devices generally known to those skilled in the art. In most cases, a catheter or syringe is used. In many cases, a multi-lumen catheter is used to deliver the liquid embolic composition to the intended site of administration. Generally, a two or three lumen catheter will be used, wherein the components of the composition which crosslink or initiate crosslinking are maintained in separate lumens until the time of administration. For example, in the case of a macromer that crosslinks via redox initiated free radical polymerization, one solution containing the reducing agent is delivered through a first lumen while a solution containing the oxidizing agent is delivered through a second lumen. The macromer can be in one or both of the solutions. A third lumen can be used to deliver contrast agent or the contrast agent can be in either or both of the redox solutions. A guidewire can be inserted through any of the lumens, and removed prior to delivery of a solution through that lumen.

In one embodiment, the catheter includes a mixing chamber at its delivery tip. A side by side “double D” lumen can be used, wherein the interior wall has been removed at the distal end to form an area where the two solutions combine before they are injected into the lumen or void. Alternatively, a coaxial catheter can be used, where one of the inner or outer lumens extends further than the other. Other types of multilumen catheters are disclosed in the art.

Vascular Embolics

The embolic compositions can be used to form a plug in a variety of biological lumens. For example, the compositions can be delivered endovascularly to plug the feeder vessel(s) of a tumor or a uterine fibroid. It may be desirable in some cases to use a slowly crosslinking formulation as a liquid embolic composition so that the embolic composition diffuses before gelation and a network or web of polymerized hydrogel is formed. In other cases, where a more compact embolization is desired close to the site of administration, it is desirable to use a more quickly crosslinking formulation.

In one embodiment, a redox initiated macromer composition is used. Using a triple lumen catheter, a solution containing the reductant is introduced through one lumen, a solution containing the oxidant is introduced using a second lumen, and the third lumen is used for introducing liquid contrast to monitor the site before and after administration of the embolic composition. The macromer can be in one or both of the reductant and oxidant solutions. Desirably, a contrast agent is present in one or both of the reductant or oxidant solutions so that administration of the embolic composition can be monitored. The uterine artery, for example, to be embolized can be accessed through the femoral artery or transcervically.

Filling Aneurysm Sacs

Many aneurysms, particularly cerebral aneurysms, can be treated endovascularly by occluding the aneurysm with the embolic composition. The embolic composition is administered using a microcatheter. Methods of administering embolic agents are known to those skilled in the art and generally can be used with the embolic composition.

In one embodiment, a redox initiated macromer composition is used, as described above for lumen embolics. It may be desirable to use a balloon, a stent, or another mechanism, for temporarily isolating the aneurysm and providing a template for embolic formation.

AAAs and TAAs are currently treated endovascularly by the placement of a stent graft at the site of the aneurysm. Often, there are leaks into the excluded aneurysm sac, termed endoleaks, due to feeder vessels into the sac, spaces between the stent graft and the vessel wall, or holes in the stent graft wall. Such endoleaks can cause the aneurysm to further expand and to rupture. The embolic compositions disclosed herein can be used to seal endoleaks. In one embodiment, the embolic compositions are used to fill the aneurysm sac.

An excluded aneurysm sac can be accessed in at least three ways: using a catheter to access the sac through the stent graft side wall; using a syringe to access the excluded sac through the patient's back; or using a catheter to access the sac through blood vessels feeding the sac. Any of theses methods can be used to administer the embolic compositions into the sac. If the endoleak is due to a feeder vessel, it may be desirable to endovascularly access the sac through the feeder vessel. Using this method, the sac can be filled and the vessel embolized, if desired. In some cases, it may be difficult to endovascularly access the sac and it may be preferable to inject embolic composition directly into the sac using a syringe through the patient's back.

It may be desirable to use a more adhesive embolic composition, which will adhere to the vessel wall within the aneurysm sac and discourage leakage between the hydrogel mass and the vessel wall.

Chemoembolization

The embolic compositions can be used for chemoembolization. As described above, a chemotherapeutic agent is incorporated into the embolic compositions or simply mixed with the preformed embolic articles. The embolic composition is then administered as described above.

For chemoembolization, as well as other applications, it may be desirable to use an embolizing composition that forms a partially or fully degradable hydrogel. Current practice calls for several applications of chemotherapeutic agent at time intervals of about 4 to 8 weeks. The embolic compositions can be formulated to degrade, partially or fully, over a desired period of time, at which time the chemoembolic composition or just the chemotherapeutic agent can be readministered. In another embodiment, embolectomy methods can be used to recannulate the embolization to allow reapplication of chemotherapeutic agent.

In another embodiment, the chemoembolic composition forms a hydrogel that releases the chemotherapeutic agent over the entire desired treatment period.

EXAMPLES

The examples below serve to further illustrate the invention, to provide those of ordinary skill in the art with a complete disclosure and description of how the compounds, compositions, articles, devices, and/or methods claimed herein are made and evaluated, and are not intended to limit the scope of the invention. In the examples, unless expressly stated otherwise, amounts and percentages are by weight, temperature is in degrees Celsius or is at ambient temperature, and pressure is at or near atmospheric. The examples are not intended to restrict the scope of the invention.

Example 1

Embolization of Rabbit Renal Vasculature with Liquid Embolic Compositions

General Procedure:

Following general anaesthesia, the superficial femoral artery was surgically exposed and a microcatheter (three lumen, 3.4 Fr from ACT Medical unless otherwise noted) was introduced using a guidewire. One of the lumens was used to administer contrast agent to the animal. The microcatheter was advanced under fluoroscopic guidance to the left renal artery. The embolic composition was injected under fluoroscopic control. Following polymer injection, localization of the cured radio-opaque polymer was followed up by conducting an angiogram to assess whether complete blockage of the kidney vasculature was achieved.

The liquid embolic compositions were two part redox formulations having reductant and oxidant solutions. The macromer for all samples except F had a PVA backbone (14 kDa, 12% acetate incorporation) modified with 0.45 meq/g N-acrylamidoacetaldehyde di methyl acetal pendant polymerizable groups (about 6.3 crosslinks per chain). In Sample F, the macromer had a PVA backbone (6 kDa, 80% hydrolyzed from Polysciences) modified with 1.0 meq/g N-acrylamidoacetaldehyde dimethyl acetal and 0.5 meq/g acetaldehyde dimethyl acetal (a hydrophobic modifier). The macromers were made substantially as described in U.S. Pat. No. 5,932,674

The comonomer used was AMPS. The contrast agent was Omnipaque®. The buffer used in the oxidant solutions was IM acetate buffer, pH=4.1. None of the reductant solutions contained buffer.

TABLE 1
Composition Components
	A	B	C	D	E	F	G	H	I
Reductant Solution
Fe (ppm)	2240	2240	2240	2240	2240	2240	2240	2240	2240
Ascorbate (mM)	20.8	20.8	8.3	8.3	8.3	8.3	20.8	20.8	20.8
Macromer (%)	9	6	9	6	8	11.5	9	9	6
Comonomer (%)	—	3	5	5	5	5	—	—	—
Contrast (%)	30	30	20	45	30	30	30	30	—
Viscosity (cp)	33.9	32.6	33.6	29.3	33.5	36.7	34	32.7	13.5
Oxidant Solution
Peroxide (ppm)	150	250	200	250	250	250	250	250	150
Buffer (mM)	100	100	100	100	100	100	100	100	100
Macromer (%)	9	9	6	6	8	11.5	9	9	6
Comonomer (%)	—	—	3	5	5	5	—	—	—
Dequest ® (ppm)	100	100	100	100	100	100	100	100	100
Contrast (%)	30	30	50	45	30	30	30	30	30
Viscosity (cp)	34.6	32.5	31.0	29.6	34.6	36.2	32.8	33.4	12.9
	J	K	L	M	N	O	P
	Reductant Solution
	Fe (ppm)	2240	2240	2240	2240	2240	2240	2240
	Ascorbate (mM)	8.3	8.3	8.3	8.3	8.3	8.3	8.3
	Macromer (%)	6	9	6	9	6	6	6
	Comonomer (%)	3	5	3	5	5	5	5
	Contrast (%)	30	—	30	—	30	30	30
	Viscosity (cp)	16.3	18.3	14.8	18.2	17.0	16.7	16.7
	Oxidant Solution
	Peroxide (ppm)	200	200	250	250	250	250	250
	Buffer (mM)	100	100	100	100	100	100	100
	Macromer (%)	6	6	6	6	6	6	6
	Comonomer (%)	3	3	3	3	5	5	5
	Dequest ® (ppm)	100	100	100	100	100	100	100
	Contrast (%)	30	30	30	30	30	30	30
	Viscosity (cp)	15.0	15.6	14.8	15.1	17.1	16.8	16.5

TABLE 2
Results of Example 1
		Injection	Injection		In vitro
		volume	time	Flow	gel time
		(ml)	(sec)	Occlusion?	(sec)
	A	1.0	65	Yes	1.75
	B	0.8	15	Yes	1.2
	C	0.5	12	Yes	0.82
	D	0.8	14	Yes	0.70
	E	0.8	n.d.	Yes	0.74
	F	0.5	12	Yes	0.75
	G	0.5	10	Yes	1.2
	H	0.9	14	Yes	1.23
	I	1.4	45	Yes	2.79
	J	1.6	45	Yes	1.15
	K	1.4	20	No	0.87
	L	1.4	20	Yes	0.79
	M	1.4	32	No	0.85
	N	0.8	17	No	0.68
	O	3.2	45	Yes	0.85
	P	1.6	18	Yes	0.79

The liquid embolic compositions were easily injected through the catheter and easily visualized by fluoroscopy. The compositions flowed into small distal vessels within the kidneys before gelation. By fluoroscopy, the polymer following injection was located homogenously within the renal vasculature with small arteries being filled. No polymer was seen in the renal vein for any of the samples except K, M, and N.

Example 2

Microsphere Embolic Compositions

General Method of Making Microspheres:

300 ml of 1,2-dichloroethane (DCE) or paraffin was placed into a 500 ml dented kettle and stirred with a glass stir rod. Stabilizer was added (either cellulose acetate butyrate (CAB) or dioctyl sulfosuccinate (DOS) (the percent reported is based on the amount of DCE used)) while stirring until dissolved. Once all of the stabilizer was dissolved, stirring was ceased, and nitrogen was bubbled through the solution for 10 minutes.

The macromer solution as described in Table 3 (between 10-30% solids) was placed in a 100 ml flat-bottomed flask and stirred. 0.5% potassium persulfate was added (based on amount of DCE or paraffin used) to the macromer while stirring. Once the persulfate was dissolved, nitrogen was bubbled through the solution for 5 minutes.

The macromer solution was added to the DCE or paraffin solution dropwise, while stirring at 400 rpm. Once all of the macromer solution was added, a small positive pressure of nitrogen was applied. 0.5% N,N,N,N tetramethylethylenediamine (based on amount of DCE or paraffin used) was added to the solution. The solution was lowered into an oil bath at a temperature of 55° C. and allowed to react for three hours.

After three hours, the heat was removed and stirring was continued. Once cooled, the DCE or paraffin was vacuum filtered off, and the product was washed with DCE and acetone. The product was soaked in acetone for 30 minutes, the acetone was decanted off, and the product was soaked in water for at least 30 minutes. The water was vacuum filtered off the product. The microspheres were sonicated for 30 minutes and sieved into the desired size ranges of greater than 850 microns, between 850 and 500 microns, between 500 and 250 microns, and smaller than 250 microns. The macromer used in samples A through G had a PVA backbone (14 kDa, 12% acetate incorporation) modified with 0.45 meq/g N-acrylamidoacetaldehyde dimethyl acetal pendant polymerizable groups (about 6.3 crosslinks per chain). The macromer used in sample H had a backbone of PVA 8-88 (67 kDa, 12% acetate incorporation) modified with N-acrylamidoacetaldehyde dimethyl acetal pendant polymerizable groups (about 7 crosslinks per chain). The macromer used in sample I had a backbone of PVA 4-88 (31 kDa, 12% acetate incorporation) modified with N-acrylamidoacetaldehyde dimethyl acetal pendant polymerizable groups (about 7 crosslinks per chain). The stir speed was 400 rpm except for sample G which was 350 rpm.

TABLE 3
Preparation of Microspheres
	Macromer		Yield	Size Distribution (microns)
Sample	(%)	Stabilizer	(%)	>850	850-500	500-250	<250
A	20	0.8% CAB in DCE	101	0	3	80	17
B	20	0.5% CAB in DCE	115	34	41	19	6
C	30	1% DOS in paraffin	41	nd	nd	nd	nd
D	30	1% DOS in paraffin	134	16	60	19	5
E	20	1% CAB in DCE	96	0	14	72	13
F	20	0.8% CAB in DCE	96	0	32	57	11
G	10	0.8% CAB in DCE	96	3	0	22	76
H	11	0.8% CAB in DCE	150	0	10	84	6
I	20	0.8% CAB in DCE	92	6	60	31	3

The microsphere products had very little aggregates (except for sample D) and were mostly or all spherical.

Modifications and variations of the present invention will be apparent to those skilled in the art from the forgoing detailed description. All modifications and variations are intended to be encompassed by the following claims. All publications, patents, and patent applications cited herein are hereby incorporated by reference in their entirety.

Claims

1. A method for embolization, comprising the steps:

providing a composition comprising macromers having a polymeric backbone comprising units with a 1,2-diol or 1,3-diol structure and at least two pendant chains bearing crosslinkable groups and having the formula:

2. The method of claim 1, wherein the macromere further comprises pendant modifier groups.

3. The method of claim 1, further comprising administering an active agent.

4. The method of claim 3, wherein the active agent is a chemotherapeutic agent.

5. The method of claim 1, wherein the hydrogel is biodegradable.

6. The method of claim 1, wherein the composition further comprises a copolymerizable monomer.

7. The method of claim 1, wherein the method comprises using a delivery device to deliver the solutions separately and mixing the solutions to initiate crosslinking.

8. The method of claim 7 wherein the solutions are delivered to the intended site using a multilumen catheter.

9. The method of claim 8 wherein the solutions are mixed in the catheter.

10. The method of claim 1, wherein the embolization is used for treatment of a uterine fibroid, by delivering the embolic composition to a vessel feeding the fibroid to occlude the vessel.

11. The method of claim 1, wherein the embolization is used for treatment of a tumor, by delivering the embolic composition to a vessel feeding the tumor to occlude the vessel.

12. The method of claim 1, wherein the embolization is used for treatment of an endoleak by delivering the embolic composition to seal the endoleak.

13. The method of claim 12, wherein sealing the endoleak comprises partially or completely filling the aneurysm sac with the embolic composition.

14. The method of claim 1, wherein the embolization is used for treatment of an arteriovenous malformation by delivering the embolic composition to occlude the malformation.

15. A method of treating an animal, comprising:

providing a composition comprising macromers having a polymeric backbone comprising units with a 1,2-diol or 1,3-diol structure and at least two pendant chains bearing crosslinkable groups and having the formula:

16. The method of claim 15 wherein the composition is delivered to block or fill a lumen.

17. The method of claim 15 wherein the composition is delivered to block or fill a space.

18. The method of claim 15 wherein the composition is delivered to block or fill a cavity.

19. The method of claim 15, wherein the macromer further comprises pendant modifier groups.

20. The method of claim 15, wherein the composition includes an active agent.

21. The method of claim 15, wherein the hydrogel is biodegradable.

22. The method of claim 15, wherein the composition further comprises a copolymerizable monomer.

23. The method of claim 15, wherein the method comprises using a delivery device to deliver the solutions separately and mixing the solutions to initiate crosslinking.

24. The method of claim 15, wherein the solutions are delivered to the intended site using a multilumen catheter.

25. The method of claim 15, wherein the solutions are mixed in the catheter.